DE3335848A1 - Verfahren zum verbinden eines aluminiumdrahtes - Google Patents

Verfahren zum verbinden eines aluminiumdrahtes

Info

Publication number
DE3335848A1
DE3335848A1 DE19833335848 DE3335848A DE3335848A1 DE 3335848 A1 DE3335848 A1 DE 3335848A1 DE 19833335848 DE19833335848 DE 19833335848 DE 3335848 A DE3335848 A DE 3335848A DE 3335848 A1 DE3335848 A1 DE 3335848A1
Authority
DE
Germany
Prior art keywords
wire
aluminum wire
base
load
connection
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19833335848
Other languages
English (en)
Other versions
DE3335848C2 (de
Inventor
Yoshiyuki Hiratsuka Ohzawa
Kanji Higashiyamato Otsuka
Masao Kunitachi Sekibata
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hitachi Ltd
Original Assignee
Hitachi Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hitachi Ltd filed Critical Hitachi Ltd
Publication of DE3335848A1 publication Critical patent/DE3335848A1/de
Application granted granted Critical
Publication of DE3335848C2 publication Critical patent/DE3335848C2/de
Granted legal-status Critical Current

Description

ο -ν? γ; ο / ο
O -j O vJ O M O
HITACHI, LTD., Tokyo
Japan
Verfahren zum Verbinden eines Aluminiumdrahtes
Die Erfindung bezieht sich auf ein Verfahren zum Verbinden eines Drahtes mit einem Sockel einer elektronischen Schaltung. Insbesondere bezieht sich die Erfindung auf ein Verfahren zum Verbinden eines Drahtes, das sich zum Verbinden einer Anzahl von Aluminiumdrähtenfmi t einer sehr kleinen Fläche, wie z. B. der in einem Hybridmodul, eignet.
Ein elektronisches Schaltungsmodul, wie z. B. ein Hybridmodul, ist so aufgebaut, daß Halbleiterplättchen auf einem Vielschichtkeramikmodui montiert sind. Im elektronischen Modul wird es unvermeidlich, die Verdrahtung aufgrund von Änderungen oder Fehlern in der Auslegung zu ändern. Beim Ändern ist es unmöglich, die Verdrahtung des Moduls an sich zu erneuern, sooft eine solche Änderung vorgenommen wird. In einem solchen Fall wird daher die Verbindungstechnik unter Verwendung eines Sockels für technische Änderungen (im folgenden "EC-Sockel bezeichnet), der auf dem Modul vorgesehen ist und auf dem einzelne
Jü
Drähte angebracht werden, angewandt. Sie ist in "Precise Numerical Control for the Thermal Conduction Module" von M. A. Sanborn of IBM J. Res. Den. (Vol. 27. No. 1) beschrieben.
Es ist für mit den EC-Sockeln verwendete Drähte erforderlich, daß jeweils der Draht einen kleinen Durchmesser mit einer höheren Festigkeit und Leitfähigkeit, als üblicherweise verwendet, hat und eine darauf aufgebrachte Isolation trägt.
Herkömmlich wird ein Kupferdraht als der diese Anforderungen erfüllende Draht verwendet. Der Kupferdraht wird mit Gold zur Vermeidung der Verschlechterung der Verbindung aufgrund einer Oxidation beschichtet, und seine Oberfläche wird mit einer Isolierschicht aus einem Harz, wie z. B. Polytetraf1uoräthylen, Polyurethan usw., überzogen.
Ein allgemeines Verfahren zum Verbinden ist dann die Entfernung dieser Isolierschicht unter Verwendung von Ultraschallwellen und nachher die Bewirkung der Verbindung durch Thermokompressionsverbindung. Dieses Verfahren hat jedoch Nachteile insofern, als der überzogene Draht dick wird und eine Erweiterung der Verbindungsfläche verursacht, als ein Zweischrittvorgang der Entfernung der Überzugsschicht und danach der Durchführung der Thermokompressionsverbindung benötigt werden, wodurch eine Verlängerung der Arbeitszeit verursacht wird, als die Entfernung der Überzugsschicht im ganzen schwierig ist, so daß die Verbindung von geringer Verläßlichkeit wird, usw. Diese Probleme sind nicht auf die Drahtverbindung für eine technische Änderung begrenzt, sondern können allgemein auftreten, wenn eine
/Λ ~> — Γ" ρ .' Q
OCoJOHO
Drahtverbindung an sehr kleinen Flächen vorgenommen wird.
Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren zu entwickeln, das sich zum Verbinden von Drähten mit hoher Verläßlichkeit in sehr kleinen Flächen eignet.
Je geringer die Verbindungsfläche für Drähte ist, umso kleiner muß der Drahtdurchmesser sein. Zu diesem Zweck sollte der überzug auf dem Draht vorzugsweise von geringer Dicke gemacht werden. Beim Verbindungsverfahren gemäß der Erfindung wächst der Arbeitswirkungsgrad, wenn die Überzugsbeseitigung und die Verbindung gleichzeitig durchgeführt werden können. Weiter ist es vom Standpunkt der Verläßlichkeit vorzuziehen, daß kein Überzugsrückstand auf dem Verbindungsabschnitt verbleibt.
Gegenstand der Erfindung, womit die genannte Aufgabe gelöst wird, ist ein Verfahren zum Verbinden eines Drahtes mit einem Sockel einer elektrischen Schaltung, gemäß dem ein mit einer Isolierschicht überzogener Draht an den Sockel gedrückt und ein von der Isolierschicht befreiter Drahtbereich mit dem Sockel verbunden wird, mit dem Kennzeichen, daß man einen anodisierten Aluminiumdraht als den zu verbindenden Draht herstellt, den Aluminiumdraht mittels eines Keilstücks gegen den Sockel drückt und unter Einwirkung einer Belastung auf den Aluminiumdraht das Keilstück Ultraschal1 schwingungen zur Bewirkung der Verbindung des Aluminiumdrahtes mit dem Sockel aussetzt.
Ausgestaltungen dieses Verfahrens sind in den Unteransprüchen gekennzeichnet.
Die Erfindung wird anhand des in der Zeichnung veranschaulichten Ausführungsbeispiels näher erläutert; darin zeigen:
Fig. 1 einen Grundriß zur Veranschaulichung eines Moduls, bei dem die Erfindung angewendet wird;
Fig. 2 eine Seitenansicht nach Fig. 1;
Fig. 3 eine Darstellung eines Beispiels nach dem Stand der Technik;
Fig. 4 eine Darstellung zur Veranschaulichung der Erfindung; und
Fig. 5 eine Darstellung zur Veranschaulichung des Hauptteils einer Verbindungseinrichtung.
Fig. 1 ist ein Grundriß eines Hybridmoduls, bei dem die Erfindung angewandt wird, und Fig. 2 ist eine zugehörige Seitenansicht. Eine Modulplatte 2 besteht aus einer Viel schichtschaltungsplatte, die beispielsweise aus Aluminiumoxid-Keramikmaterial hergestellt ist/und weist zwei darauf montierte Halbleiterplättchen 4 auf wobei sie außerdem an der Rückseite mit Leitern 5 zum äußeren Anschluß versehen ist. EC-Sockel 3 sind rings um den Umfang der Plättchen 4 angeordnet. Die Sockel 3 sind jeweils auf ihren Oberflächen mit einer Au-Beschichtung in einer Dicke von 1 bis&ym versehen. Drähte 1 und 1' für eine technische Änderung sind mit einigen der Sockel 3 verbunden. Mit einem Sockel 3 sind ein oder zwei Drähte verbunden. Gelegentlich kreuzen sich die Drähte 1,1' und können miteinander in Kontakt sein, weshalb es erforderlich ist, daß ihre Oberfläche isoliert ist.
848
-7 -
Fig. 3 zeigt eine Anordnung, in der zwei herkömmliche Drähte, die mit einem Isolierüberzug versehen sind, mit dem Sockel 3 verbunden sind. Die Bezugsziffer 7 bezeichnet einen Cu-Kerndraht, der mit der Au-Beschichtung versehen ist, und die Bezugsziffer 6 bezeichnet einen Isolierüberzug aus dem oben erwähnten Kunstharz, wie z. B. Polytetrafluorethylen, Polyurethan od. dgl. Wenn der Kerndraht 7 so hergestellt ist, daß er einen Außendurchmesser von 50 pm hat, ist der/überzug 6 5 bis 10 μπι dick, und als Ergebnis ist der Außendurchmesser des gesamten Drahtes 60 bis 70 μπι. Da der Cu-Kerndraht 7 hart ist und daher im Vergleich mit Au oder Al nur wenig verformt werden kann, läßt sich die unter Einwirkung einer Last durchgeführte Ultraschal1 verbindung auf den Kerndraht 7 nicht anwenden, falls nicht die Ultraschalleistung, die Dauer der Einwirkung der Ultraschallwellen und die einwirkende Last gesteigert werden. Jedoch bricht, wenn diese Leistung, Dauer und Belastung gesteigert werden, das Metall an der Verbindungsschicht, so daß das Problem auftritt, daß die Bindefestigkeit niedrig wird. Aus diesem Grund ist es besser, eine Au-Au-diffundierte Verbindung durch Thermokompressionsverbindung zu verwenden, da eine solche Verbindungsschicht nicht bricht und die erhaltene Bindefestigkeit hoch ist. Nach dem Stand der Technik werden jedoch zunächst Ultraschallwellen zur Entfernung des Überzugs verwendet, wodurch an einem Teil des Drahtes sein überzug durch seine Reibung an dem Sockel 3 entfernt wird. Dann wird der Draht durch Druck mit dem Sockel unter einer Last von 200 bis 500 g mittels eines auf 400 bis 500 0C erhitzten spitzen Organs verbunden. Nach diesem bekannten Verfahren wird der überzug 6 im Verbindungsbereich zerstört und der Verbindungsbereich wird auf eine
drei- bis viermal so große Abmessung wie die ursprüngliche Abmessung erweitert, so daß er eine Weite von etwa 280 pm (= 70 χ 4) erreicht, wie in Fig. 3 durch das Bezugszeichen L angedeutet ist. Dies erfordert die Verwendung eines großen Sockels 3. Weiter schmilzt der überzug 6 und bleibt in der Nähe des Verbindungsbereichs, so daß dieser Rest in den Verbindungsbereich gelangt und eine Senkung der Bindefestigkeit sowie eine Verschmutzung der Fläche in der Nähe des Verbindungsbereichs verursacht.
Die Erfinder führten Versuche mit verschiedenen Drähten durch und verglichen die Versuchsergebnisse, um die beim Stand der Technik angetroffenen Probleme zu lösen. Als Ergebnis fanden sie, daß sich ein anodisierter Aluminiumdraht zur Erfüllung der oben erwähnten verschiedenen Anforderungen eignet und gleichzeitig gute Ergebnisse bringt. Wo ein Draht an einem solchen wie dem in Fig. 1 gezeigten Modul angebracht wird, ist es unter Berücksichtigung der Festigkeit und Leitfähigkeit eines Kerndrahtes an sich erwünscht, daß sein Durchmesser 30 bis 60 pm ist. Wenn man den Kerndraht aus Aluminium mit einem Durchmesser von 50 [im macht und die Dicke des Alumits auf 0,1 bis 1 Mm Durchmesser einstellt, erhält
man ein Isolationsvermögen von 1 χ 10 Sl oder mehr, und der Außendurchmesser des Drahtes braucht nur angenähert 51 [im zu sein. Andererseits ist die Verbindung dieses anodisierten Aluminiumdrahtes allein mit einer Einwirkung von Ultraschal1 schwingungen unter einer Belastung möglich und erfordert kein kompliziertes Verfahren wie beim bekannten Verbindungsverfahren.
Fig. 4 zeigt einen Zustand, wo zwei Drähte 71 mit dem Sockel 3 nach dem erfindungsgemäßen Verfahren verbunden sind, während Fig. 5 einen wesentlichen Teil einer Verbindungseinrichtung hierfür zeigt. In Fig. 5 wird der Draht 7' gegen den Sockel 3 durch Aufbringen einer Belastung unter Verwendung eines Keilstücks 10 gepreßt, und Ultraschallschwingungen werden durch das Keilstück 10 mittels eines Schwingungserzeugers 11 zur Einwirkung gebracht. Beim Verbindungsvorgang wird der Draht zunächst durch das Keilstück 10 ohne Einwirkung irgendeinenUltraschallschwingung darauf angedrückt, und dann werden Ultraschallschwingungen darauf zur Einwirkung gebracht. Wenn man das Anpressen des Drahtes 71 anfange, während Ultraschal1 schwingungen einwirken, würde der Draht 71 verschoben oder bewegt, was zu einem Fehler beim Andrücken des Drahtes mit hoher Genauigkeit führen müßte.
Der Verbindungsvorgang wurde unter den folgenden Bedingungen bei Verwendung des anodisierten Aluminiumdrahtes durchgeführt, der einen Durchmesser von 50 \im aufweist, während die Alumitdicke 1 \im beträgt.
Ultraschallfrequenz 60 kHz + 3 %
Dauer der Einwirkung der ο 4 s Ultraschallschwingungen '
Ultraschalleistung 0,04 W
Belastung 40 g
Gemäß diesem Versuch ist die Breite L' des angedrückten Drahtes der 1,5 bis 2fache Durchmesser des nicht gedrückten Aluminiumdrahts, und auch im Fall des zweifachen Wertes, d. h. 102 pm (= 51 χ 2), nur die Hälfte oder weniger der
- ίο -
Breite der herkömmlichen Verbindungsfläche. Allgemein soll die Bindefestigkeit wenigstens 30 % der Zugfestigkeit eines Drahtes an sich sein. Erfindungsgemäß war die Zugfestigkeit des Aluminiumdrahtes mit 50 Mm Durchmesser für sich etwa 28 g, und die Bindefestigkeit erreichte einen ebenso hohen oder größeren Wert als diesen Wert.
Alumit ist hart und brüchig. Daher bricht, wenn das Aluminium als Basismaterial durch Einwirkung der Ultraschallenergie und des Drucks beim Verbinden verformt und verbreitert wird, das Alumit und schält sich vom Aluminiumbasismaterial ab, wobei die Verbindung mit dem Sockel an diesem freigelegten Bereich erfolgt. Alumit trennt sich in dieser Weise leicht vom Basismaterial, was im Gegensatz zu dem bekannten Harzüberzug steht. Alumit hat daher weniger unerwünschte Wirkungen auf die Verbindung und verschmutzt außerdem die Nachbarfläche des Verbindungsbereichs nicht. Der Aluminiumdraht hat weiter seine ausreichend hohe Bindeverläßlichkeit bis zu 500 0C. Daher ist es möglich, seine Bindeverläßlichkeit ausreichend auch dann aufrechtzuerhalten, wenn nach dem Verbinden darauf Hitze, beispielsweise im Fall eines Lötvorgangs usw.,* .einwirkt.
Im Fall des anodisierten Aluminiumdrahtes mit einem Durchmesser von 30 bis 60 μηι kann die Verbindung unter den gleichen wie den oben erwähnten Verbindungsbedingungen mit Ausnahme der Belastung durchgeführt werden. Und zwar ist ein Bereich zwischen O,35js und 0,45 s, hauptsächlich 0j4 s, für die Dauer der Einwirkung der Ultraschallschwingungen vorzuziehen, und ein Bereich zwisch-en 0,035 W
O O ~- E Q / Q
O ..J- O O O 4
- 11 -
und 0,045 W, hauptsächlich 0,04 W/ist für die Ultraschalleistung vorzuziehen. Was die Belastung betrifft, kann die Belastung umso kleiner oder niedriger sein, je kleiner der Durchmesser des Kerndrahtes ist. Demgemäß ist die Belastung von 18 bis 45 g zweckmäßig. Insbesondere kann die Belastung etwa 40 g sein, wo der Drahtdurchmesser 50 bis 60 pm ist, und die Belastung kann etwa 20 g sein, wo der Drahtdurchmesser so klein wie 30 bis 40 μπι ist. Wenn die Verbindung unter diesen Verbindungsbedingungen ausgeführt wurde, hatte die Bindefestigkeit einen Wert, der höher als der entsprechend 30 % der Zugfestigkeit des anodisierten Aluminiumdrahtes an sich war. Falls die Einwirkungszeitdauer, die Leistung und die Belastung jeweils geringere als die oben erwähnten Werte haben, wird die Verbindung unzureichend. FaI1s die Einwirkungszeitdauer, die Leistung und die Belastung größere Werte als die oben erwähnten aufweisen, bricht das Metall am Verbindungsbereich, so daß die Bindefestigkeit sinkt. Wenn, wie oben erwähnt, die Ultraschalldrahtverbindung unter Verwendung des anodisierten Aluminiumdrahtes durchgeführt wird, macht die Verwendung sogar des Drahtes mit einem Durchmesser von 51 μπι es möglich, ausreichend zwei solcher Drähte mit dem Sockel zu verbinden, wo dessen Durchmesser bis zu etwa 0,4 mm reicht. Außerdem wird die Wärmebeständigkeitseigenschaft befriedigend aufrechterhalten, und daher kann der Aluminiumdraht ein Löten oder einen anderen Erhitzungsvorgang aushalten. Zusätzlich wird, wenn der im Verbindungs querschnitt betroffene Teil nach dieser Verteilung der EC-Drähte hermetisch abgedichtet wird, ein Bruch des Drahtes aufgrund von Erosion verhindert, so daß er eine sehr lange Betriebslebensdauer haben kann. In der Ver-
3^
335848
- 12 -
gangenheit wurden Produkte mit damit verbundenen Aluminiumdrähten einer besonders weit getriebenen Reinigung zur Entfernung der Stoffe, wie z. B. Halogenionen (F", Cl", Br od. dgl.) oder anderer Stoffe unterworfen, die zur Erosion des Aluminiumdrahtes neigen, um dadurch die Verbindungsverläßlichkeit mit der Verwendung einer Harzabdichtung allein zu erhalten. Nach diesem Verfahren (Kunstharzabdichtung) ist es natürlich möglich, die Verbindungsverläßlichkeit zu erreichen.

Claims (4)

  1. Patentansprüche
    1 . Verfahren zum Verbinden eines Drahtes mit einem Sockel e~iner elektronischen Schaltung, gemäß dem ein mit einer Isolierschicht überzogener Draht an den Sockel gedrückt und ein von der Isolierschicht befreiter Drahtbereich mit dem Sockel verbunden wird,
    da'durch gekennzeichnet, daß man einen anodisierten Aluminiumdraht (71) als den zu verbindenden Draht herstellt,
    den Aluminiumdraht (71) mittels eines Keilstücks (10) gegen den Sockel (3) drückt und
    unter Einwirkung einer Belastung auf den Aluminiumdraht (7') das Keilstück (10) Ultraschal1 schwingungen zur Bewirkung der Verbindung des Aluminiumdrahtes (71) mit dem Sockel (3) aussetzt.
  2. 2. Verfahren nach Anspruch 1,
    dadurch gekennzeichnet,
    daß man die Ultraschal1 schwingungen aufbringt, nachdem der Aluminiumdraht (71) mittels des Keilstücks (10) gegen den Sockel (3) gedrückt ist und dadurch unter Einwirkung einer
    Belastung steht.
  3. 3. Verfahren nach Anspruch 2,
    dadurch gekennzeichnet,
    daß der Ausgangsdurchmesser des Aluminiumdrahtes (71)
    81-(Abi13-02)-TF
    30 bis 60 μπι, die Dauer, während der die Ultraschallschwingungen einwirken, 0,35 bis 0,45 s, die Ultraschalleistung 0,035 bis 0,045 W und die einwirkende Belastung 18 bis 45 g betragen.
  4. 4. Verfahren nach Anspruch 3,
    dadurch gekennzeichnet,
    daß die Ultraschallfrequenz angenähert 60 kHz ist.
DE19833335848 1982-10-04 1983-10-03 Verfahren zum verbinden eines aluminiumdrahtes Granted DE3335848A1 (de)