DE2353694B2 - Verfahren zur herstellung einer mehrschichtplatte - Google Patents

Verfahren zur herstellung einer mehrschichtplatte

Info

Publication number
DE2353694B2
DE2353694B2 DE19732353694 DE2353694A DE2353694B2 DE 2353694 B2 DE2353694 B2 DE 2353694B2 DE 19732353694 DE19732353694 DE 19732353694 DE 2353694 A DE2353694 A DE 2353694A DE 2353694 B2 DE2353694 B2 DE 2353694B2
Authority
DE
Germany
Prior art keywords
mixture
silico
alkaline
layer
mineral
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19732353694
Other languages
English (en)
Other versions
DE2353694C3 (de
DE2353694A1 (de
Inventor
Joseph Saint-Quentin Davidovits (Frankreich)
Original Assignee
Coordination et Developpement de !'Innovation S.A. CORDI, Saint-Quentin, Aisne (Frankreich)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from FR7238746A external-priority patent/FR2204999A5/fr
Priority claimed from FR7335979A external-priority patent/FR2246382A2/fr
Application filed by Coordination et Developpement de !'Innovation S.A. CORDI, Saint-Quentin, Aisne (Frankreich) filed Critical Coordination et Developpement de !'Innovation S.A. CORDI, Saint-Quentin, Aisne (Frankreich)
Publication of DE2353694A1 publication Critical patent/DE2353694A1/de
Publication of DE2353694B2 publication Critical patent/DE2353694B2/de
Application granted granted Critical
Publication of DE2353694C3 publication Critical patent/DE2353694C3/de
Expired legal-status Critical Current

Description

Die Erfindung betrifft ein Verfahren zur Herstellung einer Mehrschichtplatte, bei welchem auf eine Schicht aus einer ersten Mischung aus anorganischen Stoffen und einem Bindemittel eine Schicht aus einer zweiten Mischung aus Spänen und/oder Fasern organischer oder mineralischer Herkunft und einem organischen Bindemittel und darauf gegebenenfalls eine weitere Schicht aus einer dritten Mischung aus anorganischen Stoffen und einem Bindemittel aufgebracht wird und die Schichten unter Erwärmung auf wenigstens 80° C gleichzeitig zur Mehrschichtplatte verpreßt werden.
Bei derartigen bekannten Verfahren zur Herstellung feuerhemmender Mehrschichtplatten (DT-AS 04 36(. DT-AS 11 26 119, DT-AS 12 96 381) wird als erste bzw. dritte Mischung jeweils eine Mischung aus einem unbrennbaren mineralartigen Material, wie Asbestfasern, porösen natürlichen und/oder synthetischen Mineralstoffen oder aufgeblätterten, sich in der jeweiligen Schicht gegenseitig überlappenden Vermiculitteilchen, und einem organischen Bindemittel eingesetzt, welches regelmäßig dem organischen Bindemittel f>s der zweiten Mischung entspricht Bei höheren Temperaturen verlieren die Bindemittel derartiger Mehrschichtplatten infolge Verkohlung sehr schnell ihre Bindekraft so daß keine ausreichenden Festigkeitseigenschaften mehr gegeben sind.
Der Erfindung liegt die Aufgabe zugrunde, anzugeben, wie man nut einem Verfahren der eingangs genannten Gattung Mehrschichtplatten mit erhöhter Festigkeit, insbesondere bei höheren Temperaturen, erzeugen kann.
Die Erfindung besteht darin, daß als erste bzw. dritte Mischung jeweils eine durch siliko-alkalische Reaktion eine Mineralschicht bildende siliko-alkalische Mischung eingesetzt wird.
Die Erfindung nutzt hierbei die Erkenntnis, daß die bisher nur zur Herstellung von einzelnen Mineralkörpern, wie Kunststeinen, eingesetzten siliko-alkalischen Reaktionen siliko-alkafischer Mischungen ohne weiteres auch für die Hersteilung von Mineralschichten in Mehrschichtplatten brauchbar sind, daß diese Mineralschichten gleichsam im Eingangverfahren zusammen mit üblichen Spanplatten u.dgl. erzeugt werden können, weil die entsprechenden Verfahrensparameter praktisch einander entsprechen, und daß die auf diese Weise erzeugten Mehrschichtplatten infolge des homogenen chemischen Verbundes in den Mineraldeckschichten besonders hohe Festigkeit aufweisen und zwar auch bei höheren Temperaturen. Hierin sind die durch die Erfindung erreichten Vorteile hauptsachlich zu sehen. Darüber hinaus besitzen die erfindungsgemäßen Mehrschichtplatten aber auch eine verbesserte Wärmeisolations- bzw. Feuerhemmungswirkung.
Für die weitere Ausgestaltung bestehen im Rahmen der Erfindung mehrere Möglichkeiten. Als siliko-alkalische Misch>mg für die Deckschichten der Mehrschichtplatten eignet sich grundsätzlich jede Mischung, die unter den gegebenen Verfahrensbedingungen durch siliko-alkalische Reaktion eine Mineralschicht bildet. Bevorzugt wird jedoch als siliko-alkalische Mischung eine Mischung aus tonartigem Material und einer Alkalilauge, wie Natronlauge, oder Kalziumoxid oder Natriumkarbonat oder eine Mischung aus tonartigem Material und Sand oder eine Mischung aus Kaolin und Natriumchlorid. Anstelle natürlicher Tonarten können auch synthetische Silikate, wie sie beispielsweise in FR-PS 15 84 873 und FR-PS 20 71 019 beschrieben sind, verwendet werden. Der siliko-alkalischen Mischung können neben Sand auch Teilchen anderer mineralischer Stoffe, wie Stein, Ziegel, Schiefer, Glas, Steinwolle, Vermiculit Asbest und Blähton, zusätzlich als Füllstoffe beigegeben werden, um die physikalischen Eigenschaften der Mineraldeckschichten den gewünschten Anforderungen anzupassen. Zur Erzielung besonders harter und dichter Deckschichten empfiehlt die Erfindung einen Zusatz von 1 bis 10% Alkalimetallsilikat zur siliko-alkalischen Mischung.
Im folgenden wird die Erfindung anhand eines Ausführungsbeispiels erläutert.
Auf eine feste oder bewegliche Unterlage gibt man eine 5 mm dicke Schicht aus einem Gemisch, das zu 50 Teilen aus Kaolin und zu 50 Teilen aus feinem Sand, welchem 6% Natriumhydroxid und 12% Wasser beigegeben wurden, besteht Auf diese Schicht streut man eine Schicht aus einem Gemisch von 100 Teilen Holzsägespänen und 10 Teilen wärmehärtemdem Harnstoff-Formaldehyd-Harz, und zwar in einer derartigen Mengen, daß die endgültige Dicke 20 mm beträgt. Das Ganze wird anschließend für 4,5 min bei einem Druck von 20 kp/cm2 und einer Temperatur von 170° C verpreßt Man erhält so eine beschichtete Holzfaserplatte, deren Deckschicht weiß, glatt hart und
[ai^esjöngt Hol ' ah.
«weite* «aus
SoMoeieach
Gemisch aus Kaolin,
Tut HersteDung einer dretscfiicfa^en Hatte trägt
tallsiJiikatesbeL
,^. Ysrmindenung.der
liAineraldecksqbiehtea gibt tnan dem ι noch 1 bis 10 % eines Alkaiime-

Claims (6)

  1. Patentansprüche:
    t. Verfahren sur Herstellung einer Mehrschichtplatte, bei welchem auf eine Schicht aus einer ersten Mischung aus anorganischen Stoffen und einem Bindemittel eine Schicht aus einer zweiten Mischung aus Spänen und/oder Pasern organischer oder mineralischer Herkunft und einem organischen Bindemittel und darauf gegebenenfalls eine weitere Schicht aus einer dritten Mischung aus anorganischen Stoffen und einem Bindemittel aufgebracht wird und die Schichten unter Erwärmung auf wenigstens 80° C gleichzeitig zur Mehrschichtplatte verpreßt werden, dadurch gekennzeichnet, daß als erste bzw. dritte Mischung jeweils eine durch siliko-aJkalische Reaktion eine Mineralschicht bildende siliko-alkalische Mischung eingesetzt wird.
  2. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß als siliko-alkalische Mischung eine Mischung aus tonartigem Material und einer Akalilauge, wie Natronlauge, oder Kalziumoxid oder Natriumkarbonat eingesetzt wird.
  3. 3. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß als siliko-alkalische Mischung eine Mischung aus tonartigem Material und Sand eingesetzt wird.
  4. 4. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß als siliko-alkalische Mischung eine Mischung aus Kaolin und Natriumchlorid eingesetzt wird.
  5. 5. Verfahren nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet daß der siliko-alkalischen Mischung Teilchen mineralischer Stoffe, wie Stein, Ziegel, Schiefer, Glas, Steinwolle, Vermiculit, Asbest und Blähton, zugesetzt werden.
  6. 6. Verfahren nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß zur Erzielung besonders harter und dichter Deckschichten der siliko-alkalischen Mischung 1 bis 10% Alkalimetallsilikat zugesetzt wird.
DE19732353694 1972-11-02 1973-10-26 Verfahren zur Herstellung einer Mehrschichtplatte Expired DE2353694C3 (de)