DE2143965B2 - Lot zum flußmittelfreien Löten von Aluminiumwerkstoffen - Google Patents

Lot zum flußmittelfreien Löten von Aluminiumwerkstoffen

Info

Publication number
DE2143965B2
DE2143965B2 DE2143965A DE2143965A DE2143965B2 DE 2143965 B2 DE2143965 B2 DE 2143965B2 DE 2143965 A DE2143965 A DE 2143965A DE 2143965 A DE2143965 A DE 2143965A DE 2143965 B2 DE2143965 B2 DE 2143965B2
Authority
DE
Germany
Prior art keywords
solder
aluminum
flux
free soldering
aluminum materials
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE2143965A
Other languages
English (en)
Other versions
DE2143965A1 (de
DE2143965C3 (de
Inventor
Heinz 5301 Alfter Schoer
Werner Dr. 5300 Bonn Schultze
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Vereinigte Aluminium Werke AG
Original Assignee
Vereinigte Aluminium Werke AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Vereinigte Aluminium Werke AG filed Critical Vereinigte Aluminium Werke AG
Priority to DE2143965A priority Critical patent/DE2143965C3/de
Priority to IT69603/72A priority patent/IT970830B/it
Priority to FR7228979A priority patent/FR2150763B2/fr
Priority to AT691172A priority patent/AT313667B/de
Priority to DK401372A priority patent/DK136806C/da
Priority to NO2967/72A priority patent/NO135662C/no
Priority to NLAANVRAGE7211342,A priority patent/NL178572C/xx
Priority to BE787789A priority patent/BE787789R/xx
Priority to ZA725745A priority patent/ZA725745B/xx
Priority to SU1823102A priority patent/SU474125A3/ru
Priority to CH1256372A priority patent/CH557717A/de
Priority to GB3987872A priority patent/GB1376778A/en
Priority to SE7211175A priority patent/SE374042B/xx
Priority to US00285100A priority patent/US3811177A/en
Priority to CA150,539A priority patent/CA981941A/en
Priority to LU65985A priority patent/LU65985A1/xx
Priority to JP47087227A priority patent/JPS4834747A/ja
Publication of DE2143965A1 publication Critical patent/DE2143965A1/de
Publication of DE2143965B2 publication Critical patent/DE2143965B2/de
Priority to JP1062078A priority patent/JPS53131253A/ja
Application granted granted Critical
Publication of DE2143965C3 publication Critical patent/DE2143965C3/de
Expired legal-status Critical Current

Description

Gegenstand der Patentanmeldung P 1 962 760.2,24 ist ein Lot zum flußmittelfreien Löten von Aluminiumwerkstoffen, dessen Merkmal darin besteht, daß es aus 4 bis 20% Silicium und aus 0,01 bis 10%, vorzugsweise 0,05 bis 2% Wismut, Strontium, Barium und/ oder Antimon, Rest Aluminium und herstellungsbedingte Verunreinigungen, besteht.
In weiterer Ausgestaltung der Erfindung wurde nun gefunden, daß an Stelle oder zusammen mit Wismut, Strontium, Barium und/oder Antimon auch ein Gehall von Beryllium in Mengen von 0,00001 bis 1,0, vorzugsweise 0,0002 bis 0,1, zweckmäßig ist. Auf diese Weise sind die gleichen vorteilhaften Wirkungen beim flußmittelfreien Löten von Aluminiumwerkstoffen erzielbar, wie sie in der Hauptpatentanmeldung beschrieben werden.
Zwar ist einerseits durch die USA.-Patentschrift 3 081534 ein Al-Si-Lot zum flußmittelfreien Löten von Aluminium bekannt, das aus 4,9 bis 10% Si, 0 bis 4% Cu, 0,1 bis ; % Li, Rest Aluminium besteht, während es andererseits durch die britische Patentschrift 1 067 024 zum Stand der Technik gehört, zum gleichen Zweck ein Lot mit bis zu 15% Si, wenigstens 0,4 Mg, 0 bis 25% Cu, Rest Aluminium, in einer nicht oxidierenden Atmosphäre zu verwenden, und schließlich auch durch die USA.-Patentschrift 3 395 001 ebenfalls zum flußmittelfreien Löten von Aluminium ein Lot, bestehend aus unter anderem 4 bis 13% Si, 0,001 bis 0,1% Scandium, Yttrium oder Seltenen Erdmetallen, Rest Aluminium, vorgeschlagen worden ist, jedoch wäre es unrichtig, daraus den Schluß auf das Naheliegen des Anmeldungsgegenstandes zu ziehen. Denn wenn augh das Lithium der ersten Nebengruppe des Periodischen Systems, Scandium, Yttrium und die Seltenen Erdmetalle dessen dritter Nebengruppe und schließlich das Beryllium der dazwischen liegenden zweiten Nebengruppe als Spitzenelement angehören, so sind doch die Eigenschaften und Wirkungen der genannten Elemente, insbesondere von Magnesium und Beryllium, nicht miteinander zu vergleichen, wobei zu
to berücksichtigen ist, daß dem Magnesium gemäß der genannten britischen Patentschrift die Aufgabe zufällt, im dampfförmigen Zustand auf die AlsO3-Haut reduzierend zu wirken, sie zu durchdringen und aufzubrechen, damit das Metall an den zu verbindenden Flächen benetzt wird, während erfindungsgemäß höchstens Mg-Gehalte vorliegen, die erheblich unterhalb des in der britischen Patentschrift geforderten Minimalgehaltes von 0,4% liegen. Das erfindungsgemäß vorgesehene Beryllium kann nicht dieselbe Funktion haben wie das Magnesium laut der britischen Patentschrift, denn es müßte dazu ebenso wie das Magnesium bei relativ niedrigen Temperaturen einen hohen Dampidruck aufweisen und außerdem in Aluminium etwa gleichermaßen löslich sein wie Magnesium.
Ausführungsbeispiele
Si 12,1 2. Si 11,9
Mn 0,10 Mn 0,08
Mg 0,02 Mg 0,01
Fe 0,38 Fe 0,32
Ti 0,02 Ti 0,01
Cu 0,01 Cu 0,02
Zn 0,04 Zn 0,03
Be 0,004 Bi 0,04
Rest Aluminium Be 0,014
Rest Aluminium
Si 7,4 4. Si 9,8
Mn 0,06 Mn 0,05
Mg 0,03 Mg 0,02
Fe 0,48 Fe 0,27
Ti 0,02 Ti 0,01
Cu 0,03 Cu 0,02
Zn 0,10 Zn 0,08
Be 0,083 Bi 0,75
Rest Aluminium Be 0,036
Rest Aluminium
Die gleichen Wirkungen werden erzielt, wenn an Ste'le oder zusammen mit Wismut Strontium, Barium und/oder Antimon als Legierungsbestandsteile verwendet werden.

Claims (1)

  1. Patentanspruch:
    Lot zum flußmittelfreien Löten von Aluminiumwerkstoffen, bestehend aus 4 bis 20% Silicium und aus 0,01 bis 10%, vorzugsweise 0,05 bis 2% Wismut, Strontium, Barium und/oder Antimon, Rest Aluminium und herstellungsbedingte Verunreinigungen nach Patentanmeldung P I 962 760.2.24, dadurch gekennzeichnet, daß an Stelle oder zusammen mit Wismut, Strontium, Barium und/oder Antimon ein Gehalt an Beryllium in Mengen von 0,00001 bis 1,0, vorzugsweise 0,0002 bis 0,1, vorhanden ist.
DE2143965A 1969-12-15 1971-09-02 Verwendung eines Lotes zum flußmittelfreien Hartlöten von Aluminiumwerkstoffen in Schutzgas, Inertgas oder Vakuum Expired DE2143965C3 (de)