DE2136199A1 - Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer staehle - Google Patents

Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer staehle

Info

Publication number
DE2136199A1
DE2136199A1 DE2136199A DE2136199A DE2136199A1 DE 2136199 A1 DE2136199 A1 DE 2136199A1 DE 2136199 A DE2136199 A DE 2136199A DE 2136199 A DE2136199 A DE 2136199A DE 2136199 A1 DE2136199 A1 DE 2136199A1
Authority
DE
Germany
Prior art keywords
melt
free
austenitic steels
treated
steels
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE2136199A
Other languages
German (de)
English (en)
Inventor
Gerhard Dipl Ing Koehlert
Wolfgang Stawicky
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ver Deutsche Metallwerke AG
Original Assignee
Ver Deutsche Metallwerke AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ver Deutsche Metallwerke AG filed Critical Ver Deutsche Metallwerke AG
Priority to DE2136199A priority Critical patent/DE2136199A1/de
Priority to AT490972A priority patent/ATA490972A/de
Priority to ZA724261A priority patent/ZA724261B/xx
Priority to CA147,105A priority patent/CA966667A/en
Priority to FR7225399A priority patent/FR2146759A5/fr
Priority to IT26989/72A priority patent/IT962847B/it
Priority to BE786385A priority patent/BE786385A/xx
Priority to DD164501A priority patent/DD100496A5/xx
Priority to SE7209506A priority patent/SE7209506L/sv
Priority to GB3377972A priority patent/GB1383561A/en
Priority to CH1084772A priority patent/CH581702A5/xx
Publication of DE2136199A1 publication Critical patent/DE2136199A1/de
Pending legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21C—PROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OF WROUGHT-IRON OR STEEL; TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS
    • C21C7/00—Treating molten ferrous alloys, e.g. steel, not covered by groups C21C1/00 - C21C5/00
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/24—Selection of soldering or welding materials proper
    • B23K35/30—Selection of soldering or welding materials proper with the principal constituent melting at less than 1550°C
    • B23K35/3053—Fe as the principal constituent
    • B23K35/308—Fe as the principal constituent with Cr as next major constituent
    • B23K35/3086—Fe as the principal constituent with Cr as next major constituent containing Ni or Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21C—PROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OF WROUGHT-IRON OR STEEL; TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS
    • C21C7/00—Treating molten ferrous alloys, e.g. steel, not covered by groups C21C1/00 - C21C5/00
    • C21C7/10—Handling in a vacuum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Mechanical Engineering (AREA)
  • Arc Welding In General (AREA)
  • Treatment Of Steel In Its Molten State (AREA)
DE2136199A 1971-07-20 1971-07-20 Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer staehle Pending DE2136199A1 (de)

Priority Applications (11)

Application Number Priority Date Filing Date Title
DE2136199A DE2136199A1 (de) 1971-07-20 1971-07-20 Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer staehle
AT490972A ATA490972A (de) 1971-07-20 1972-06-07 Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer stahle
ZA724261A ZA724261B (en) 1971-07-20 1972-06-21 Process of producing austenitic steels which can be welded without a formation of drops
CA147,105A CA966667A (en) 1971-07-20 1972-07-13 Process of producing austenitic steels which can be welded without a formation of drops
FR7225399A FR2146759A5 (enExample) 1971-07-20 1972-07-13
IT26989/72A IT962847B (it) 1971-07-20 1972-07-14 Procedimento per la produzione di acciai austenitici saldabili sen za formazione di gocce
BE786385A BE786385A (fr) 1971-07-20 1972-07-17 Procede pour la fabrication d'aciers austentiques ne formant pas de perles au soudage
DD164501A DD100496A5 (enExample) 1971-07-20 1972-07-18
SE7209506A SE7209506L (enExample) 1971-07-20 1972-07-19
GB3377972A GB1383561A (en) 1971-07-20 1972-07-19 Process for producing austentic steels which can be welded without the formation of drops
CH1084772A CH581702A5 (enExample) 1971-07-20 1972-07-20

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
DE2136199A DE2136199A1 (de) 1971-07-20 1971-07-20 Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer staehle

Publications (1)

Publication Number Publication Date
DE2136199A1 true DE2136199A1 (de) 1973-02-01

Family

ID=5814229

Family Applications (1)

Application Number Title Priority Date Filing Date
DE2136199A Pending DE2136199A1 (de) 1971-07-20 1971-07-20 Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer staehle

Country Status (11)

Country Link
AT (1) ATA490972A (enExample)
BE (1) BE786385A (enExample)
CA (1) CA966667A (enExample)
CH (1) CH581702A5 (enExample)
DD (1) DD100496A5 (enExample)
DE (1) DE2136199A1 (enExample)
FR (1) FR2146759A5 (enExample)
GB (1) GB1383561A (enExample)
IT (1) IT962847B (enExample)
SE (1) SE7209506L (enExample)
ZA (1) ZA724261B (enExample)

Also Published As

Publication number Publication date
ATA490972A (de) 1975-04-15
CH581702A5 (enExample) 1976-11-15
IT962847B (it) 1973-12-31
DD100496A5 (enExample) 1973-09-20
ZA724261B (en) 1973-05-30
CA966667A (en) 1975-04-29
FR2146759A5 (enExample) 1973-03-02
BE786385A (fr) 1972-11-16
GB1383561A (en) 1974-02-12
SE7209506L (enExample) 1973-01-22

Similar Documents

Publication Publication Date Title
DE10017069B4 (de) Unlegierter Stahldraht mit ausgezeichneter Beständigkeit gegen Rißbildung in Längsrichtung, ein Stahlprodukt für denselben und Verfahren zur Herstellung desselben
DE69330326T2 (de) Formstahl hoher Festigkeit, Zähigkeit und Hitzebeständigkeit und Formstahlherstellungsverfahren durch Walzen
DE69710664T2 (de) Verfahren zur herstellung von wärmebehandeltem stahlguss und stahlgussstück
DE2919156A1 (de) Verfahren zur herstellung von hochwertigen schienen mit hoher schweissbarkeit
DE60105929T2 (de) Hochfeste, hochzähe, nahtlose stahlrohre für leitungsrohre
DE2733750C2 (de) Verfahren zum Einstellen des Kohlenstoffgehalts eines Stahls
DE60103598T2 (de) Nicht-gefrischter stahl mit verminderter anisotropie und ausgezeichneter festigkeit, zähigkeit und verarbeitbarkeit
DE2513763C3 (de) Verfahren zur Herstellung einer Walze mit einer oder mehreren Umfangsnuten
DE60216824T2 (de) Schwefelfreier schneidstahl für maschinenbauzwecke
DE3640131C2 (enExample)
DE1440588A1 (de) Lichtbogenschweissverfahren
DE3701815A1 (de) Verfahren zum herstellen eines plattierten formkoerpers
DE60020522T2 (de) Stahl für geschweisste strukturen, wobei die zähigkeit unabhängig vom wärmeeintrag ist, und herstellungsverfahren
EP3131691A1 (de) Verfahren zur berechnung der sich einstellenden eigenschaftskombination für einen umformbaren leichtbaustahl
DE2553402A1 (de) Verfahren und vorrichtung zur herstellung von verbundwalzen
DE3416521A1 (de) Warmfester stahl
DE2262415A1 (de) Verfahren zum einstellen der kuehlgeschwindigkeit von schweissungen
DE2420347A1 (de) Verfahren zur herstellung von kupfermaschinendraht
DE2136199A1 (de) Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer staehle
DE112006003553B4 (de) Dicke Stahlplatte für eine Schweißkonstruktion mit ausgezeichneter Festigkeit und Zähigkeit in einem Zentralbereich der Dicke und geringen Eigenschaftsänderungen durch ihre Dicke und Produktionsverfahren dafür
DE2356640A1 (de) Schweissdraht mit flussmittelseele
DE3129154C2 (de) Verfahren zur Verhinderung der Rißbildung der Oberfläche beim Stranggießen eines 9%-Ni-Stahls
DE19520833A1 (de) Verfahren zur Herstellung eines nahtlosen warmgefertigten Rohres
DE1964751B2 (de) Lichtbogen-SchweiBverfahren mit hoher Kerbschlagzähigkeit in der Nahtübergangszone und Elektrode hierfür
DE3739156A1 (de) Stickstoffhaltiges zusatzmittel fuer stahlschmelzen