DE2136199A1 - Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer staehle - Google Patents
Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer staehleInfo
- Publication number
- DE2136199A1 DE2136199A1 DE2136199A DE2136199A DE2136199A1 DE 2136199 A1 DE2136199 A1 DE 2136199A1 DE 2136199 A DE2136199 A DE 2136199A DE 2136199 A DE2136199 A DE 2136199A DE 2136199 A1 DE2136199 A1 DE 2136199A1
- Authority
- DE
- Germany
- Prior art keywords
- melt
- free
- austenitic steels
- treated
- steels
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Links
- 229910000831 Steel Inorganic materials 0.000 title claims description 20
- 239000010959 steel Substances 0.000 title claims description 20
- 238000000034 method Methods 0.000 title claims description 8
- 238000004519 manufacturing process Methods 0.000 title claims description 5
- OYPRJOBELJOOCE-UHFFFAOYSA-N Calcium Chemical compound [Ca] OYPRJOBELJOOCE-UHFFFAOYSA-N 0.000 claims description 11
- 229910052791 calcium Inorganic materials 0.000 claims description 11
- 239000011575 calcium Substances 0.000 claims description 11
- 239000000155 melt Substances 0.000 claims description 10
- 239000000203 mixture Substances 0.000 claims description 6
- 238000005275 alloying Methods 0.000 claims description 4
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 claims description 4
- 239000001301 oxygen Substances 0.000 claims description 4
- 229910052760 oxygen Inorganic materials 0.000 claims description 4
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 claims description 2
- 229910052799 carbon Inorganic materials 0.000 claims description 2
- 238000010891 electric arc Methods 0.000 claims description 2
- 238000009489 vacuum treatment Methods 0.000 claims description 2
- 239000003795 chemical substances by application Substances 0.000 claims 1
- 238000003466 welding Methods 0.000 description 13
- 230000015572 biosynthetic process Effects 0.000 description 11
- XKRFYHLGVUSROY-UHFFFAOYSA-N Argon Chemical compound [Ar] XKRFYHLGVUSROY-UHFFFAOYSA-N 0.000 description 4
- 230000005291 magnetic effect Effects 0.000 description 4
- 238000012360 testing method Methods 0.000 description 4
- 239000010936 titanium Substances 0.000 description 4
- 229910052719 titanium Inorganic materials 0.000 description 4
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 description 3
- IJGRMHOSHXDMSA-UHFFFAOYSA-N Atomic nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 description 2
- NRTOMJZYCJJWKI-UHFFFAOYSA-N Titanium nitride Chemical compound [Ti]#N NRTOMJZYCJJWKI-UHFFFAOYSA-N 0.000 description 2
- 238000009825 accumulation Methods 0.000 description 2
- 229910052782 aluminium Inorganic materials 0.000 description 2
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 2
- 229910052786 argon Inorganic materials 0.000 description 2
- 230000008901 benefit Effects 0.000 description 2
- 238000007664 blowing Methods 0.000 description 2
- 238000005266 casting Methods 0.000 description 2
- 238000011835 investigation Methods 0.000 description 2
- 239000000463 material Substances 0.000 description 2
- 210000004243 sweat Anatomy 0.000 description 2
- 229910004709 CaSi Inorganic materials 0.000 description 1
- 229910004534 SiMn Inorganic materials 0.000 description 1
- 230000008094 contradictory effect Effects 0.000 description 1
- 238000005260 corrosion Methods 0.000 description 1
- 230000007797 corrosion Effects 0.000 description 1
- 230000007547 defect Effects 0.000 description 1
- 230000005292 diamagnetic effect Effects 0.000 description 1
- 238000002474 experimental method Methods 0.000 description 1
- 239000007789 gas Substances 0.000 description 1
- 229910052751 metal Inorganic materials 0.000 description 1
- 239000002184 metal Substances 0.000 description 1
- 229910052757 nitrogen Inorganic materials 0.000 description 1
- 230000005298 paramagnetic effect Effects 0.000 description 1
- 238000012545 processing Methods 0.000 description 1
- 230000001681 protective effect Effects 0.000 description 1
- -1 titanium nitrides Chemical class 0.000 description 1
- 238000012549 training Methods 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21C—PROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OF WROUGHT-IRON OR STEEL; TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS
- C21C7/00—Treating molten ferrous alloys, e.g. steel, not covered by groups C21C1/00 - C21C5/00
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
- B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
- B23K35/24—Selection of soldering or welding materials proper
- B23K35/30—Selection of soldering or welding materials proper with the principal constituent melting at less than 1550 degrees C
- B23K35/3053—Fe as the principal constituent
- B23K35/308—Fe as the principal constituent with Cr as next major constituent
- B23K35/3086—Fe as the principal constituent with Cr as next major constituent containing Ni or Mn
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21C—PROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OF WROUGHT-IRON OR STEEL; TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS
- C21C7/00—Treating molten ferrous alloys, e.g. steel, not covered by groups C21C1/00 - C21C5/00
- C21C7/10—Handling in a vacuum
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Mechanical Engineering (AREA)
- Arc Welding In General (AREA)
- Treatment Of Steel In Its Molten State (AREA)
Priority Applications (11)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| DE2136199A DE2136199A1 (de) | 1971-07-20 | 1971-07-20 | Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer staehle |
| AT490972A ATA490972A (de) | 1971-07-20 | 1972-06-07 | Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer stahle |
| ZA724261A ZA724261B (en) | 1971-07-20 | 1972-06-21 | Process of producing austenitic steels which can be welded without a formation of drops |
| CA147,105A CA966667A (en) | 1971-07-20 | 1972-07-13 | Process of producing austenitic steels which can be welded without a formation of drops |
| FR7225399A FR2146759A5 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) | 1971-07-20 | 1972-07-13 | |
| IT26989/72A IT962847B (it) | 1971-07-20 | 1972-07-14 | Procedimento per la produzione di acciai austenitici saldabili sen za formazione di gocce |
| BE786385A BE786385A (fr) | 1971-07-20 | 1972-07-17 | Procede pour la fabrication d'aciers austentiques ne formant pas de perles au soudage |
| DD164501A DD100496A5 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) | 1971-07-20 | 1972-07-18 | |
| GB3377972A GB1383561A (en) | 1971-07-20 | 1972-07-19 | Process for producing austentic steels which can be welded without the formation of drops |
| SE7209506A SE7209506L (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) | 1971-07-20 | 1972-07-19 | |
| CH1084772A CH581702A5 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) | 1971-07-20 | 1972-07-20 |
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| DE2136199A DE2136199A1 (de) | 1971-07-20 | 1971-07-20 | Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer staehle |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| DE2136199A1 true DE2136199A1 (de) | 1973-02-01 |
Family
ID=5814229
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| DE2136199A Pending DE2136199A1 (de) | 1971-07-20 | 1971-07-20 | Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer staehle |
Country Status (11)
-
1971
- 1971-07-20 DE DE2136199A patent/DE2136199A1/de active Pending
-
1972
- 1972-06-07 AT AT490972A patent/ATA490972A/de not_active Application Discontinuation
- 1972-06-21 ZA ZA724261A patent/ZA724261B/xx unknown
- 1972-07-13 FR FR7225399A patent/FR2146759A5/fr not_active Expired
- 1972-07-13 CA CA147,105A patent/CA966667A/en not_active Expired
- 1972-07-14 IT IT26989/72A patent/IT962847B/it active
- 1972-07-17 BE BE786385A patent/BE786385A/xx unknown
- 1972-07-18 DD DD164501A patent/DD100496A5/xx unknown
- 1972-07-19 SE SE7209506A patent/SE7209506L/sv unknown
- 1972-07-19 GB GB3377972A patent/GB1383561A/en not_active Expired
- 1972-07-20 CH CH1084772A patent/CH581702A5/xx not_active IP Right Cessation
Also Published As
| Publication number | Publication date |
|---|---|
| CA966667A (en) | 1975-04-29 |
| GB1383561A (en) | 1974-02-12 |
| ZA724261B (en) | 1973-05-30 |
| CH581702A5 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) | 1976-11-15 |
| DD100496A5 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) | 1973-09-20 |
| FR2146759A5 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) | 1973-03-02 |
| SE7209506L (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) | 1973-01-22 |
| IT962847B (it) | 1973-12-31 |
| ATA490972A (de) | 1975-04-15 |
| BE786385A (fr) | 1972-11-16 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| DE602004010699T2 (de) | Kaltgewalztes Stahlblech mit einer Zugfestigkeit von 780 MPa oder mehr, einer hervorragenden lokalen Formbarkeit und einer unterdrückten Schweißhärteerhöhung | |
| DE10017069B4 (de) | Unlegierter Stahldraht mit ausgezeichneter Beständigkeit gegen Rißbildung in Längsrichtung, ein Stahlprodukt für denselben und Verfahren zur Herstellung desselben | |
| DE69330326T2 (de) | Formstahl hoher Festigkeit, Zähigkeit und Hitzebeständigkeit und Formstahlherstellungsverfahren durch Walzen | |
| DE69710664T2 (de) | Verfahren zur herstellung von wärmebehandeltem stahlguss und stahlgussstück | |
| DE2919156A1 (de) | Verfahren zur herstellung von hochwertigen schienen mit hoher schweissbarkeit | |
| DE60105929T2 (de) | Hochfeste, hochzähe, nahtlose stahlrohre für leitungsrohre | |
| DE2733750C2 (de) | Verfahren zum Einstellen des Kohlenstoffgehalts eines Stahls | |
| DE60103598T2 (de) | Nicht-gefrischter stahl mit verminderter anisotropie und ausgezeichneter festigkeit, zähigkeit und verarbeitbarkeit | |
| DE60216824T2 (de) | Schwefelfreier schneidstahl für maschinenbauzwecke | |
| DE2513763B2 (de) | Verfahren zur Herstellung einer Walze mit einer oder mehreren Umfangsnuten | |
| DE3640131C2 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) | ||
| DE3701815A1 (de) | Verfahren zum herstellen eines plattierten formkoerpers | |
| DE112006003553B4 (de) | Dicke Stahlplatte für eine Schweißkonstruktion mit ausgezeichneter Festigkeit und Zähigkeit in einem Zentralbereich der Dicke und geringen Eigenschaftsänderungen durch ihre Dicke und Produktionsverfahren dafür | |
| DE60020522T2 (de) | Stahl für geschweisste strukturen, wobei die zähigkeit unabhängig vom wärmeeintrag ist, und herstellungsverfahren | |
| EP3131691A1 (de) | Verfahren zur berechnung der sich einstellenden eigenschaftskombination für einen umformbaren leichtbaustahl | |
| DE2553402A1 (de) | Verfahren und vorrichtung zur herstellung von verbundwalzen | |
| DE3416521A1 (de) | Warmfester stahl | |
| DE2262415A1 (de) | Verfahren zum einstellen der kuehlgeschwindigkeit von schweissungen | |
| DE2420347A1 (de) | Verfahren zur herstellung von kupfermaschinendraht | |
| DE2136199A1 (de) | Verfahren zur herstellung tropfenfrei verschweissbarer austenitischer staehle | |
| DE2356640A1 (de) | Schweissdraht mit flussmittelseele | |
| DE3129154C2 (de) | Verfahren zur Verhinderung der Rißbildung der Oberfläche beim Stranggießen eines 9%-Ni-Stahls | |
| DE19520833A1 (de) | Verfahren zur Herstellung eines nahtlosen warmgefertigten Rohres | |
| DE1964751B2 (de) | Lichtbogen-SchweiBverfahren mit hoher Kerbschlagzähigkeit in der Nahtübergangszone und Elektrode hierfür | |
| DE3739156A1 (de) | Stickstoffhaltiges zusatzmittel fuer stahlschmelzen |