DE20101474U1 - Vormaterial aus einer Aluminiumbasislegierung - Google Patents

Vormaterial aus einer Aluminiumbasislegierung

Info

Publication number
DE20101474U1
DE20101474U1 DE20101474U DE20101474U DE20101474U1 DE 20101474 U1 DE20101474 U1 DE 20101474U1 DE 20101474 U DE20101474 U DE 20101474U DE 20101474 U DE20101474 U DE 20101474U DE 20101474 U1 DE20101474 U1 DE 20101474U1
Authority
DE
Germany
Prior art keywords
mpa
hours
temperature
period
yield strength
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE20101474U
Other languages
English (en)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ALUMINIUM RANSHOFEN WALZWERK G
Original Assignee
ALUMINIUM RANSHOFEN WALZWERK G
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ALUMINIUM RANSHOFEN WALZWERK G filed Critical ALUMINIUM RANSHOFEN WALZWERK G
Publication of DE20101474U1 publication Critical patent/DE20101474U1/de
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt

Claims (3)

1. Vormaterial für Bau- oder Formteile aus einer Aluminiumbasislegierung enthaltend in Gew.-%
0,3 bis 1, 8 Silizium (Si)
0,25 bis 1,6 Magnesium (Mg)
0,005 bis 0,6 Eisen (Fe)
bis 0,15 Titan (Ti)
bis 1,5 Kupfer (Cu)
bis 1,5 Mangan (Mn)
bis 0,25 Chrom (Cr)
bis 0,16 Zirkonium (Zr)
Rest Aluminium (Al) und
herstellungsbedingte Verunreinigungen, welches nach einer Lösungsglühung thermisch vorbehandelt ist, dadurch gekennzeichnet, daß der Werkstoff nach einer aus zumindest dreimaligem Erwärmen und Abkühlen bestehenden Vorbehandlung, bei welcher der letzte Warmbehandlungsschritt zur Stabilisierung der Keimstruktur mit abgesenkter Temperatur erfolgt, zumindest für 420 Stunden, vorzugsweise für zumindest 1000 Stunden, eine stabilisierte Keimstruktur mit den mechanischen Kennwerten
Härte HB ≦ 65 (2,5/62,5/16)
Dehngrenze Rp0.2 ≦ 140 MPa, vorzugsweise = 130
Zugfestigkeit Rm ≦ 270 MPa, vorzugsweise = 240
Gleichmaßdehnung Ag ≧ 18%
aufweist und gegebenenfalls nach einer Ausformung des Teiles dieser bei einer Temperatur zwischen 165°C und 190°C innerhalb einer Zeitdauer von 12 bis 38 Minuten ausscheidungshärtbar ist.
2. Vormaterial nach Anspruch 1, dadurch gekennzeichnet, daß der daraus hergestellte ausscheidungsgehärtete Bau- oder Formteil folgende mechanische Kennwerte besitzt
Härte HB ≧ 80
Dehngrenze Rp0.2 ≧ 190 MPa, vorzugsweise = 210
Zugfestigkeit Rm ≧ 240 MPa, vorzugsweise = 260
Gleichmaßdehnung Ag ≧ 12%
3. Vormaterial nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß innerhalb einer Zeitspanne von zumindest 1000 Stunden, vorzugsweise von zumindest 2000 Stunden, nach einer Stabilisierung der Keimstruktur die durch eine Aushärtung bei einer Temperatur zwischen 165°C und 190°C innerhalb einer Zeitdauer von 12 bis 38 Minuten erreichten Werte für die Streckgrenze Rp0.2 um weniger als 10% erniedrigt und die Dehnwerte mindestens gleichbleibend, vorzugsweise erhöht, sind.
DE20101474U 2000-09-14 2001-01-29 Vormaterial aus einer Aluminiumbasislegierung Expired - Lifetime DE20101474U1 (de)