DE1966231C3 - Verfahren zur Herstellung von Transformatorblechen - Google Patents
Verfahren zur Herstellung von TransformatorblechenInfo
- Publication number
- DE1966231C3 DE1966231C3 DE1966231*A DE1966231A DE1966231C3 DE 1966231 C3 DE1966231 C3 DE 1966231C3 DE 1966231 A DE1966231 A DE 1966231A DE 1966231 C3 DE1966231 C3 DE 1966231C3
- Authority
- DE
- Germany
- Prior art keywords
- less
- silicon
- sheets
- carbon
- annealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1244—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest
- C21D8/1261—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest following hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1216—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the working step(s) being of interest
- C21D8/1233—Cold rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1244—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest
- C21D8/1266—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest between cold rolling steps
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Electromagnetism (AREA)
- Manufacturing & Machinery (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Manufacturing Of Steel Electrode Plates (AREA)
- Soft Magnetic Materials (AREA)
Claims (1)
- Patentanspruch:Verfahren zur Herstellung von Transformatorblechen mit (110) [OOlJ-Textur aus einer Legierung, bestehend aus 0 bis 4% Silizium, weniger als 0,085% Kohlenstoff, 0,01 bis 0,65% säurelöslichem Aluminium, Rest Eisen mit den üblichen herstellungsbedingten Verunreinigungen, bei dem eine Bramme warmgewalzt, das warmgewalzte Blech 30 Sekunden bis 30 Minuten bei 750 bis 1250° C mit der Maßgabe geglüht wird, daß die Temperatur bei dieser Glühung in dem angegebenen Temperaturbereich in Abhängigkeit von dem Kohlenstoff- und SiliziumgchaJt so gewählt wird, daß wenigstens eine teilweise «-/-Umwandlung erfolgt, worauf von den niedrigsten nach dieser Maßgabe zulässigen Glühtemperatur in der Zeit von 2 bis 2(M) Sekunden auf 400° C abgeschreckt wird, wobei ferner das Blech nunmehr mit einem von dem Siliziumgehalt abhängigen Verformungsgrad zwischen 65 und 95% in einem oder mehreren Stichen auf Endstärke kaltgewalzt, entkohlend geglüht und bei Temperaturen oberhalb 800° C schlußgeglüht wird, nach Hauptpatent 1 920968, dadurch gekennzeichnet, daß das Verfahren auf eine Legierung angewandt wird, die außerdem noch bis weniger als 0,1% Selen und/oder bis weniger als 0,2% Tellur enthält.Di«; Erfindung betrifft ein Verfahren zur Herstellung von Transformatorblechen mit (110) [001 j-Textur aus Eisen-Silizium-Legierungen.In dem nicht vorveröffentlichten, prioritätsgleichen Hauptpatent 1 920968 ist ein Verfahren zur Herstellung von Transformatorblechen mit (110) [001 !-Textur aus einer Legierung, bestehend aus 0 bis 4% Silizium, weniger als 0,085 % Kohlenstoff, 0,01 bis 0,65 % säurelöslichem Aluminium, Rest Eisen mit den üblichen herstellungsbedingten Verunreinigungen beschrieben, bei dem eine Bramme warmgewalzt, das warmgewalzte Blech 30 Sekunden bis 30 Minuten bei bis 1250° C mit der Maßgabe geglüht wird, daß die Temperatur bei der Glühung in dem angegebenen Temperaturbereich in Abhängigkeit von dem Kohlenstoff- und Siliziumgehalt so gewählt wird, daß wenigstens eine teilweise η-γ-Umwandlung erfolgt, worauf von der niedrigsten nach dieser Maßgabe zulässigen Glühtemperatur in der Zeit von 2 bis 200 Sekunden auf 400° C abgeschreckt wird, wobei ferner das Blech nunmehr mit einem von dem Siliziumgehalt abhängigen Vcrfonnungsgrad /.wischen 65 und 95% in einem oder mehreren Stichen auf Endstärke kaltgewalzt, entkohlend geglüht und hei Temperaturen oberhalb 800° C schlußgeglüht wird.Einfach-orientierte Stahlbleche als weichmagnetische Materialien werden in den meisten Fällen für die Eisenkerne von Transformatoren und anderen elektrischen Geräten verwendet. Dabei w-:nl es in jüngster Zeit immer wichtiger, derartige Magnetblcehe für hohe magnetische Induktionen herzustellen, d. h. Bleche, die einen hohen Bs-Wert besitzen und bei denen über einen weiten Si-Bereich von beispielsweise 0 bis 4 % sekundäre Rekristallisationskörncr der sehr gut selektierten (110) | lüOJ-Orientierung vorlie-1S gen. Je höher die mögliche magnetische Induktion für derartige Bleche ist, desto kleiner lassen sich elektrische Elemente wie etwa Transformatoren herstellen, eine Forderung, die insbesondere von den Herstellern elektrischer Geräte erhoben wird, die nach Möglich-t0 keit immer kleinerund leichter hergestellt werden sollen.Der vorliegenden Erfindung liegt die Aufgabe zugrunde, das Verfahren nach dem Hauptpatent dahingehend zu verbessern, daß das Endprodukt eine noch'5 ausgeprägtere Texturausbildung besitzt.Diese Aufgabe wird erfindungsgemäß dadurch gelöst, daß die Verfahrensschritte des Hauptpatentes auf eine Ausgangslegierung angewandt werden, die außer 0 bis 4% Silizium, weniger als 0,085% Kohlenstoff, 0,01 bis 0,065 % säurelöslichem Aluminium und Rest Eisen mit den üblichen herstellungsbedingten Verunreinigungen noch bis zu weniger als 0,1 % Selen und/ oder bis zu weniger als 0,2% Tellur enthäSt.Es wurde festgestellt, daß der Zusatz der genannten Elemente einen wesentlichen Einfluß auf die Ausbildung der Sekundärrekristallisation besitzt. Die das Wachstum der Kristallkörner hemmende Wirkung dieser Elemente bewirkt eine Beschleunigung der sekundären Rekristallisation, was eine weitere Bevorzugung der (110) [lOOj-Orientierung zur Folge hat.die durch die Ausbildung von AIN verursacht wird.Es ist jedoch bei der erfindungsgemäßen Zugabedieser Elemente besonders darauf zu achten, daß diese Ablagerungen bildenden Elemente die Ausbildung von AIN nicht behindern. Dies ist besonders deshalb zu berücksichtigen, da diese Elemente zur Ausbildung von Carbidablagerungen neigen. Die erfindungsgemäße Zugabe von Selen und/oder Tellur behindert die erwünschte Ausbildung von AiN nicht und ergibt einen vorteilhaften Wachstum hemmenden Effekt bei der sekundären Rekristallisation. Es ließen sich durch das erfindungsgemäße Verfahren Magnetbleche herstellen, die magnetische Induktionen von wenigstens 18 500 Gauß bis 20 100 Gauß zulassen.