DE19549138A1 - Laminate board - Google Patents

Laminate board

Info

Publication number
DE19549138A1
DE19549138A1 DE19549138A DE19549138A DE19549138A1 DE 19549138 A1 DE19549138 A1 DE 19549138A1 DE 19549138 A DE19549138 A DE 19549138A DE 19549138 A DE19549138 A DE 19549138A DE 19549138 A1 DE19549138 A1 DE 19549138A1
Authority
DE
Germany
Prior art keywords
sheets
layers
impregnated
board
resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19549138A
Other languages
German (de)
Other versions
DE19549138C2 (en
Inventor
Alzualde Javier Ayestaran
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Prodema SA
Original Assignee
Prodema SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to GB9525085A priority Critical patent/GB2307882B/en
Priority to FR9515610A priority patent/FR2742091B1/en
Application filed by Prodema SA filed Critical Prodema SA
Priority to DE19549138A priority patent/DE19549138C2/en
Priority to NL1002038A priority patent/NL1002038C2/en
Publication of DE19549138A1 publication Critical patent/DE19549138A1/en
Application granted granted Critical
Publication of DE19549138C2 publication Critical patent/DE19549138C2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

A board, consists of two sheets of timber m 1 , m 2 which are laminated, each with a thickness e of between 0.4 and 1.5 mm, treated with a high dry-extract phenolic resin, with a core a between them consisting of sheets k 1 , k 2 ... of absorbent sheets of high-substance cellulose impregnated with phenolic resin. On the sheets of timber m 1 , m 2 of face C 1 and backface C 2 two films, pigmented or not, translucent/transparent, or of absorbent cellulose impregnated with polymerizing resins and a third film with specific fillers may be provided in accordance with the use of the board.

Description

Die Erfindung betrifft eine Schichtstoff-Tafel, die beispielsweise auf Fußbö­ den verlegt oder zum Verkleiden von Wänden und Fassaden verwendet werden kann.The invention relates to a laminate board, for example, on gust the laid or used to clad walls and facades can be.

Bekannte Tafeln oder Platten dieser Art, die einen aus Holz- oder Pressholz-Lagen bestehenden Kern enthalten, haben eine schlechte Alterungsbestän­ digkeit und werden nur für ganz bestimmte Zwecke verwendet, beispiels­ weise um einen ästhetischen Anblick zu dienen.Known boards or plates of this type, which are made of wood or pressed wood layers existing core contain poor aging and are only used for very specific purposes, for example wise to serve an aesthetic sight.

Die Anmelderin hat eine neuartige Tafel aus Verbundmaterial nach dem Sandwich-Typ entwickelt, die aus verschiedenen, den Kern von den Außen­ flächen unterscheidenden Schichten aufgebaut ist. Diese neuen Tafeln bieten das Aussehen einer Oberfläche aus natürlichem Holz und sind aufgrund ei­ ner Reihe hochwertiger Eigenschaften geeignet, auf weit ausgedehnten An­ wendungsfeldern in der Konstruktionstechnik, im Bauwesen, im Innenaus­ bau, zur Raumausstattung, als Dekorationen usw. eingesetzt zu werden; dar­ über hinaus besitzen sie ein optimales Alterungsverhalten und hohe Dauer­ haltbarkeit.The applicant has a new type of composite material panel according to the Sandwich type developed from different, the core from the outside surface differentiating layers. These new boards offer the appearance of a surface made of natural wood and are due to egg suitable for a wide range of high-quality properties fields of application in construction technology, in construction, in the interior construction, to be used for interior decoration, as decorations, etc.; represents  they also have an optimal aging behavior and a long duration durability.

Die fertigen Tafeln zeichnen sich auch dadurch aus, daß für ihre Oberflä­ chen eine große Vielfalt an natürlichen Hölzern und unterschiedlichen Farbtönen zur Verfügung steht; auch können die Endprodukte mit bestimm­ ten Arten von Design-Mustern versehen werden.The finished boards are also characterized in that for their surface a wide variety of natural woods and different ones Shades is available; the final products can also be determined ten types of design patterns.

Es ist von Bedeutung, daß die vorteilhaften Eigenschaften der erfindungs­ gemäßen Tafeln sowohl hinsichtlich der Oberfläche (Undurchlässigkeit, Ab­ riebsfestigkeit, Widerstandsfähigkeit gegen Streifenbildung, UVA-Strahlung usw.) als auch hinsichtlich des gesamten Sandwich-Verbunds (physikalisch­ chemische, mechanische, strukturelle Festigkeit usw.) ihrerseits zu Bauele­ menten im Sinne eines Baumaterials führen, das für eine Verwendung unter externen Umgebungsbedingungen bewitterungsfest (mit Widerstandsfähig­ keit gegen Regen, Frost, Schnee und Sonne usw.) und bestens geeignet ist.It is important that the advantageous properties of the Invention according to the tables both with regard to the surface (impermeability, Ab abrasion resistance, resistance to streaking, UVA radiation etc.) as well as with regard to the entire sandwich network (physically chemical, mechanical, structural strength, etc.) in turn to Bauele lead in the sense of a building material that is suitable for use under external environmental conditions weatherproof (with resistant against rain, frost, snow and sun etc.) and is ideally suited.

Um den Erfindungsgegenstand besser verstehen zu können, ist in den Zeich­ nungen eine bevorzugte Ausfürungsform wiedergegeben, in der in mehrfa­ cher Hinsicht Änderungen möglich sind, ohne vom Grundgedanken der Erfindung abzuweichen. Es zeigen, jeweils schematisch, In order to better understand the subject of the invention is in the drawing a preferred embodiment reproduced in which in several cases cher respect changes are possible without departing from the spirit of the invention to deviate. Each shows schematically  

Fig. 1 einen Querschnitt der Tafel nach der Erfindung und Fig. 1 shows a cross section of the panel according to the invention and

Fig. 2 einen abgebrochenen Querschnitt in Explosionsdarstellung einer praktischen Ausführungsform der erfindungsgemäßen Tafel mit ih­ ren verschiedenen, für ein besseres Verständnis voneinander ge­ trennt dargestellten Schichten. Fig. 2 is a broken cross-section in an exploded view of a practical embodiment of the panel according to the invention with their ren, for a better understanding of each other ge layers shown.

Entsprechend den Zeichnungen sind zwei Holzplatten m₁ und m₂ vorgese­ hen, die über die gesamte Fläche geschichtet sind bzw. aus Holzlaminaten (Lagen, Blättern) bestehen, eine Dicke e zwischen 0,4 und 1,5 mm haben und mit einem Phenol-Formaldehyd-Harz flüssigkeitsabweisend getränkt behandelt sind, das auf alkoholischer Basis einen hohen Trockenauszug von mindestens 50% aufweist.According to the drawings, two wooden panels m₁ and m₂ are vorese hen that are layered over the entire surface or made of wood laminates (Layers, sheets) exist, have a thickness e between 0.4 and 1.5 mm and soaked with a phenol-formaldehyde resin to repel liquid are treated, the alcohol-based has a high dry extract of has at least 50%.

Andere Eigenschaften/Anforderungen der Holzplatten m₁ und m₂ wie ihre Festigkeit, Feuchtigkeitsgehalt und dergleichen sind konventioneller Art und ergeben sich aus dem Folgenden.Other properties / requirements of wood panels m₁ and m₂ as theirs Strength, moisture content and the like are conventional and result from the following.

Um die Tafel 1 an ihrer Außenseite feuerfest zu machen, werden die Platten m₁ und m₂ in (eine Lösung aus) feuerhemmende Salze (ammoniakhaltige Phosphate) getaucht, bevor man sie mit den zuvor genannten Phenol-Formaldehyd-Harzen behandelt.In order to make the panel 1 fireproof on the outside, the plates m 1 and m 2 are immersed in (a solution of) fire-retardant salts (ammonia-containing phosphates) before they are treated with the aforementioned phenol-formaldehyde resins.

Die Tafel 1 weist eine als Sichtfläche bestimmte Vorderseite C₁ und eine Rückseite C₂ auf, die bei Bedarf ebenfalls Sichtfläche sein kann.The table 1 has a front face C 1 and a rear face C 2 , which can also be a face if necessary.

Auf der als Sichtfläche bestimmten Vorderseite C₁ ist oben auf der Holzplat­ te m₁ eine Gruppe f von unterschiedlichen Filmen oder Schichten f₁, f₂, f₃ vorgesehen, die aus absorbierenden und lichtdurchlässigen oder durchsichti­ gen Zellulose-Folien bestehen, so daß ein Benutzer u von außen die Mase­ rung der Holzplatte m₁ und gegebenenfalls auch die der Holzplatte m₂ auf der Rückseite C₂ sehen kann.On the front face determined as a visible surface C 1 is on top of the wooden plate te m₁ a group f of different films or layers f₁, f₂, f₃ provided that of absorbent and translucent or see-through cellulose foils exist so that a user u from the outside the mast tion of the wooden panel m₁ and possibly also that of the wooden panel m₂ the back can see C₂.

Einige Schichten f₁, f₂ haben ästhetische Funktionen, wozu ihre Folien mit phenolhaltigen Harzen oder anderen gleichwertigen polymerisierbaren Har­ zen imprägniert sind, die nach Bedarf Pigmente beinhalten, um zwischen absoluter Farblosigkeit/Transparenz bis zu einer bestimmten Farbe und ent­ sprechenden Übergangsfarbtönen variieren zu können. Wenn z. B. die Farbe bzw. der Naturton der Platte m₁ sichtbar sein solle wird den Filmen f₁, f₂ ein durchsichtiges Pigment (Füllstoff) beigegeben, oder wenn ein Zwischenton erwünscht ist, können ein durchsichtiger Film f₁ und ein anderer mit Farbe pigmentierter Film f₂ usw. nach Belieben zur Anwendung kommen.Some layers f₁, f₂ have aesthetic functions, which is why their foils phenolic resins or other equivalent polymerizable resin zen are impregnated, which contain pigments as required to between absolute colorlessness / transparency up to a certain color and ent speaking transition colors can vary. If e.g. B. the color  or the natural tone of the plate should be visible m₁ the films f₁, f₂ transparent pigment (filler) added, or if an intermediate tone is desired, a transparent film f₁ and another with color pigmented film f₂ etc. can be used as desired.

Weitere Schichten oder Filme f₃ usw. haben Anwendungs- und Gebrauchs­ funktionen, wozu andere Harze mit anderen beigemischten Füllstoffen oder Additiven verwendet werden (z. B. Silizium, feuerhemmende Stoffe, usw.).Other layers or films f₃ etc. have application and use functions, for which other resins with other admixed fillers or Additives are used (e.g. silicon, fire retardant substances, etc.).

Wenn beispielsweise die Tafel 1 gegen Abnutzung oder Abrieb widerstands­ fest sein soll, wird der Film f₃ mit Melamin und Silizium bzw. deren Mi­ schung imprägniert. Wenn sich die Farben der Platte(n) durch Einwirkung von UVA-Strahlen nicht verändern sollen, wird für den Film f₃ eine Imprä­ gnierung mit einem acrylhaltigen Harz verwendet. Die Reihenfolge der Fil­ me f₁, f₂, f₃ ist in Fig. 2 nur beispielhaft angegeben, es ist jede andere be­ liebige sinnvolle Reihenfolge möglich.If, for example, the table 1 is to be resistant to wear or abrasion, the film f 3 is impregnated with melamine and silicon or their mixture. If the colors of the plate (s) should not change due to the action of UVA rays, an impregnation with an acrylic resin is used for the film f₃. The order of the Fil me f₁, f₂, f₃ is only given as an example in Fig. 2, it is possible any other meaningful order.

Entsprechend den Zeichnungen enthält die Tafel 1 zwischen den Platten m₁ und m₂ einen Kern a, der aus Bündeln oder Paketen k₁, k₂, . . . kn gebildet ist, die aus absorbierenden Zellulose-Blättern/-Lagen/-Bogen mit einem ho­ hen Grammgewicht, beispielsweise 190 g/m² im unbehandelten Zustand bestehen und mit einem phenolhaltigen Harz zur Bildung von pre-pegs im­ prägniert sind. Solche Blätter sind unter der Bezeichnung "Kraft" bekannt.According to the drawings, the table 1 contains between the plates m₁ and m₂ a core a, which consists of bundles or packages k₁, k₂,. . . k n is formed which consist of absorbent cellulose sheets / sheets / sheets with a high gram weight, for example 190 g / m 2 in the untreated state and are impregnated with a phenolic resin to form pre-pegs. Such sheets are known under the name "Kraft".

Die Bündel k₁, k₂ . . . kn bestehen beispielsweise aus 10 Blättern (die Anzahl der Bündel und die Anzahl von Blättern pro Bündel sind abhängig von der End-Dicke des Kerns a und vom Grad der gewünschten Gleichmäßigkeit). Die Blätter können einzeln und/oder in den aufeinanderfolgenden Bündeln k₁, k₂ . . . abwechselnd mit unterschiedlichen Winkeln kn zueinander ange­ ordnet sein, damit eine multidirektionale Ausrichtung der Zellulosefasern im Verband des Kerns a zustande kommt.The bundle k₁, k₂. . . For example, k n consist of 10 sheets (the number of bundles and the number of sheets per bundle depend on the final thickness of the core a and the degree of uniformity desired). The leaves can be individually and / or in the successive bundles k₁, k₂. . . alternately with different angles k n to each other, so that a multidirectional alignment of the cellulose fibers in the association of the core a comes about.

Die Rückseite C₂ der Tafel besteht aus einer Gruppe f′ von Schichten oder Filmen f′₁, f′₂, f′₃, die wie die Schichten f₁, f₂, f₃ der Vorderseite C₁ oder ähnlich wie oben beschrieben aufgebaut sein können. Für den Fall, daß die Rückseite C₂ dazu bestimmt ist, auf einem Boden, an einer Wand oder an einer Mauer angeklebt, angeheftet oder sonstwie angebracht zu werden, ist auf der Holzplatte m₂ mindestens ein Bündel oder Lagenpaket f′₁ vom Kraft-Typ aufgebracht, wie es entsprechend den vorhergehenden Erläute­ rungen für den Kern a verwendet wird.The back C₂ of the board consists of a group f 'of layers or Films f'₁, f'₂, f'₃, which like the layers f₁, f₂, f₃ the front or C₁ can be constructed similarly as described above. In the event that Back C₂ is intended to be on a floor, on a wall or on is stuck to a wall, pinned or otherwise attached on the wooden plate m₂ at least one bundle or layer package f'₁ from  Force type applied as explained in the previous explanation is used for core a.

Die Vorderseite C₁ und die Rückseite C₂ können mit einem Design oder einem Relief-Muster ausgestattet sein, das mit Hilfe von Druckformen auf­ gebracht wird, die das aufzudruckende/einzuprägende Design aufweisen und zwischen der Tafel 1 und dem Gesenk einer Presse für die Herstellung der Tafel 1 angeordnet werden.The front C₁ and the back C₂ can be equipped with a design or a relief pattern, which is brought up with the help of printing forms that have the design to be printed / embossed and between the plate 1 and the die of a press for the production of the plate 1 can be arranged.

Vorzugsweise werden für die Vorderseite C₁ zwei oder drei Schichten f₁, f₂, f₃ benutzt.Preferably, two or three layers f 1 are used for the front C 1, f₂, f₃ used.

Die Bedingungen, unter denen die vorbeschriebenen Deck- und Zwischen­ schichten zu einer einheitlichen Tafel 1 verpreßt werden und harten, wie Feuchtigkeitsgrad, Temperaturen und Preßdauer, können den beim Stand der Technik üblichen entsprechen.The conditions under which the above-described cover and intermediate layers are pressed into a uniform sheet 1 and hard, such as the degree of moisture, temperatures and pressing time, can correspond to those customary in the prior art.

Die Tafel 1 wird danach in Stücke geschnitten, deren Größe und Form den Wünschen der Anwender entsprechen und an den für sie bestimmten Ver­ wendungszweck angepaßt sind.The table 1 is then cut into pieces, the size and shape of the users' wishes and are adapted to the intended use for them.

Claims (8)

1. Schichtstoff-Tafel mit einer Vorderseite (C₁) und einer Rückseite (C₂), gekennzeichnet durch
  • a) zwei Holzplatten (m₁) und (m₂) mit einem geschichteten Laminat-Aufbau von einer Dicke (e) zwischen 0,4 und 1,5 mm, die mit einem Phenolharz mit hohem Trockenauszug getränkt sind,
  • b) zwischen denen ein Kern (a) angeordnet ist, der aus Bündeln (k₁), (k₂) . . . absorbierender Zellulose-Blätter/-Bahnen besteht, die ein hohes Grammge­ wicht aufweisen und mit phenolhaltigem Harz imprägniert sind,
  • c) wobei auf der die Vorderseite (C₁) der Tafel (1) bildenden Holzplatte (m₁) mehrere lichtdurchlässige und/oder durchsichtige Folien oder Schichten (f₁), (f₂) aus absorbierender, mit einem polymerisierbaren Harz imprägnier­ ter Zellulose angeordnet sind.
1. Laminated board with a front (C₁) and a back (C₂), characterized by
  • a) two wooden panels (m₁) and (m₂) with a layered laminate structure with a thickness (e) between 0.4 and 1.5 mm, which are impregnated with a phenolic resin with high dry extraction,
  • b) between which a core (a) is arranged, which consists of bundles (k₁), (k₂). . . absorbent cellulose sheets / sheets, which have a high grammage and are impregnated with phenolic resin,
  • c) wherein on the front (C₁) of the board ( 1 ) forming wooden plate (m₁) a plurality of translucent and / or transparent films or layers (f₁), (f₂) of absorbent cellulose impregnated with a polymerizable resin are arranged.
2. Tafel nach Anspruch 1, dadurch gekennzeichnet, daß die Blätter- oder Bahnenbündel (k₁), (k₂) . . . im Kern (a) übereinanderliegend abwechselnd mit unterschiedlichen Winkeln zueinander angeordnet sind. 2. Table according to claim 1, characterized in that the leaves or Path bundles (k₁), (k₂). . . alternating in the core (a) one above the other are arranged at different angles to each other.   3. Tafel nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß mindestens eine der Schichten (f₁), (f₂) einen pigmentierten Füllstoff enthält.3. Table according to claim 1 or 2, characterized in that at least one of the layers (f₁), (f₂) contains a pigmented filler. 4. Tafel nach einem der vorhergehenden Ansprüche, dadurch gekennzeich­ net, daß ihre Rückseite (C₂) aus mehreren Schichten (f′₁), (f′₂) besteht, die denen der Vorderseite (C₁) gleichartig sind.4. Board according to one of the preceding claims, characterized net that their back (C₂) consists of several layers (f'₁), (f'₂), the those of the front (C₁) are similar. 5. Tafel nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß die Rückseite (C₂) mindestens aus einem Bündel absorbierender Blätter/Bahnen besteht, die ein hohes Grammgewicht aufweisen und mit phenolhaltigem Harz imprägniert sind.5. Table according to one of claims 1 to 3, characterized in that the Back (C₂) at least from a bundle of absorbent sheets / sheets exists that have a high gram weight and with phenol Resin impregnated. 6. Tafel nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß eine der Schichten mit Melamin als Harz und Silizium als Füllstoff gebildet ist.6. Table according to one of claims 1 to 4, characterized in that one of the layers is formed with melamine as the resin and silicon as the filler is. 7. Tafel nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß eine der Schichten mit einem acrylhaltigen Harz imprägniert ist.7. Board according to one of claims 1 to 4, characterized in that one of the layers is impregnated with an acrylic resin. 8. Tafel nach einem der vorhergehenden Ansprüche, dadurch gekennzeich­ net, daß die außenliegende Oberfläche ein Reliefmuster aufweist.8. Board according to one of the preceding claims, characterized net that the outer surface has a relief pattern.
DE19549138A 1995-12-07 1995-12-29 Laminate board Expired - Fee Related DE19549138C2 (en)