DE3142587A1 - Decorative laminate and process for its production - Google Patents

Decorative laminate and process for its production

Info

Publication number
DE3142587A1
DE3142587A1 DE19813142587 DE3142587A DE3142587A1 DE 3142587 A1 DE3142587 A1 DE 3142587A1 DE 19813142587 DE19813142587 DE 19813142587 DE 3142587 A DE3142587 A DE 3142587A DE 3142587 A1 DE3142587 A1 DE 3142587A1
Authority
DE
Germany
Prior art keywords
layer
laminate according
base layer
paper
resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19813142587
Other languages
German (de)
Inventor
Renée Elizabeth Rio de Janeiro Degens
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of DE3142587A1 publication Critical patent/DE3142587A1/en
Withdrawn legal-status Critical Current

Description

»IPU-INCi. GKRIlAKIl I1UtS EUROPEANPATENTATTORNEYS »IPU-INCi. GKRIlAKIl I 1 utS EUROPEANPATENTATTORNEYS

WPU-CHHM.DR.K.LKK.MWKVUNPEC.HMANNWPU-CHHM.DR.K.LKK.MWKVUNPEC.HMANN DR.-ING. DIETEk UEHRENSDR.-ING. DIETEk UEHRENS D1PL.-ING.; DIPL.-WIRTSCH.-ING. RUPERT GOETZD1PL.-ING .; DIPL.-WIRTSCH.-ING. RUPERT GOETZ

1A/G-55 164 D-8000 MÜNCHEN 901A / G-55 164 D-8000 MUNICH 90

SCHWEIGERSTRASSE 2SCHWEIGERSTRASSE 2

Anm.: Renee Elizabeth DegensNote: Renee Elizabeth Degens

telefon: (089) 6620 51phone: (089) 6620 51

TELEGRAMM: -1'ROTKCTPATENtTELEGRAM: -1'ROTKCTPATENt

Telex: 524070Telex: 524070

Beschreibungdescription

Dekoratives Laminatund Verfahren zu dessen Herstellung.Decorative laminate and process for its manufacture.

Die vorliegende Erfindung bezieht sich auf dekorative Laminate, insbesondere auf solche Laminate, in denen getrocknete Pflanzen oder Blumen eingeschlossen sind, um deren ästhetisches Aussehen zu verbessern. Laminate nach der Erfindung können als Material für Lampenschirme, Wandtapeten oder dekorative MöbelfMchen oder als Oberfläche für Spanplatten und ähnliches verwendet werden.The present invention relates to decorative laminates, particularly to those laminates in which dried plants or flowers are included to improve their aesthetic appearance. Laminates according to the invention can be used as a material for lampshades, wall paper or decorative furniture can be used as a surface for chipboard and the like.

Bekannt sind Laminate, auf die Dekorationen durch Malen, Prägen oder Reliefdruck aufgebracht werden, aber bisher ist keine Arbeitsweise entwickelt worden, mit deren Hilfe getrocknete Blätter, Blumen oder Pflanzen in das Laminat mit eingeschlossen werden können.Laminates are known to which decorations are applied by painting, embossing or relief printing, but so far no way of working has been developed to use dried leaves, flowers or plants in the Laminate can be included.

Es ist daher Aufgabe der vorliegenden Erfindung, dekoratives Laminat bereitzustellen, welches die Dauerhaftigkeit der bekannten Laminate mit den dekorativen Eigenschaften von getrockneten Blumen, Blättern und Pflanzen vereinigt, sov/ie ein Verfahren zu seiner Herstellung,It is therefore an object of the present invention to provide decorative laminate which has durability the well-known laminates with the decorative properties of dried flowers, leaves and plants united, as / ie a process for its production,

/2/ 2

1A/G-55 1641A / G-55 164

Die Aufgabe wird mit Hilfe des erfindungsgemäßen dekorativen Laminats und Verfahrens gelöst, welches vorsieht, daß man eine Grundschicht, eine Zwischenschicht aus getrockneten Blättern, Blumen und/oder Gräsern und eine Außen- oder Deckschicht aus einem durchscheinenden Papier imprägniert mit nicht- oder halbpolymerisiertem Harz oder Leim zu einem Schichtmaterial vereinigt und darauf dieses Schichtmaterial preßt.
10The object is achieved with the help of the decorative laminate and method according to the invention, which provides that a base layer, an intermediate layer of dried leaves, flowers and / or grasses and an outer or top layer of a translucent paper impregnated with non- or semi-polymerized resin or Glue is combined to form a layer material and this layer material is pressed onto it.
10

Wird ein nicht- oder halbpolymerisiertes Harz verwendet, so wird beim Pressen gleichzeitig mit dem Druck auch Hitze angewandt.If a non- or semi-polymerized resin is used, so when pressing, heat is also applied at the same time as pressure.

Vorzugsweise besteht die Grundschicht aus einem feinen Baumwollstoff oder gefärbtem Papier und die Außenoder Deckschicht aus oC-Cellulose, imprägniert mit nicht- oder halbpolymerisiertem Melaminharz, wenn ein dünnes, flexibles Laminat angestrebt wird. Ein durchscheinendes Laminat wird erhalten, wenn als Grundschicht das Textilmaterial verwendet wird; wird hingegen als Grundschicht ein gefärbtes Papier eingesetzt, so erhält man ein opakes Laminat in der Farbe des Papiers.The base layer preferably consists of a fine cotton fabric or colored paper and the outer or Top layer made of oC cellulose, impregnated with non-polymerised or semi-polymerised melamine resin if a thin, flexible laminate is desired. A translucent laminate is obtained when the textile material is used as the base layer; will however If a colored paper is used as the base layer, an opaque laminate is obtained in the color of the Paper.

Das durchscheinende Laminat kann für Lampenschirme verwendet werden und das opake gefärbte Laminat als Oberoder Außenfläche von Span- oder Holzplatten oder zum Aufbringen auf andere steife glatte Flächen, z. B.The translucent laminate can be used for lampshades and the opaque colored laminate as the upper or outer surface of chipboard or wood panels or for Application to other stiff smooth surfaces, e.g. B.

als Tapete. Die Gesamtstärke des Laminats beträgt in solchen Fällen vorzugsweise etwa 0,23 mm. Jedes beliebige Textilmaterial oder anderes Bahnmaterial kann als Grundschicht für das durchscheinende Laminat Verwendung finden, d. h. aus natürlichen oder synthetischen Fasern bestehen, vorausgesetzt, daß diese sich gegenüber den beim Pressen angewandten Bedingungen während des Herstellungsverfahrens als beständig erweisen,.as wallpaper. The total thickness of the laminate in such cases is preferably about 0.23 mm. Any Textile material or other sheet material can be used as the base layer for the translucent laminate find, d. H. consist of natural or synthetic fibers, provided that they are opposite to each other prove to be stable to the conditions used in pressing during the manufacturing process.

/3/ 3

1A/G-55 1641A / G-55 164

Bei der Herstellung von steifen oder starren Laminaten wird eine Stärke von etwa 0,8 bis 1,3 mm angestrebt« Die Grundschicht kann aus Kraftpapier bestehen entweder mit oder ohne aufgedrucktes Muster und gegebenenfalls flammverzögernde Stoffe enthalten.When manufacturing stiff or rigid laminates, a thickness of around 0.8 to 1.3 mm is aimed for « The base layer can consist of Kraft paper either with or without a printed pattern and optionally contain flame retardant substances.

Für Tapeten kann die Grundschicht aus jedem Papier bestehen, das für diesen Zweck geeignet ist, d. h. die notwendige Festigkeit, Flexibilität usw. aufweisto For wallpaper, the base layer can be any paper suitable for the purpose, i. H. has the necessary strength, flexibility, etc. o

Die Zwischenschicht wird durch einfaches Verteilen von getrockneten Blättern, Blumen und/oder Gräsern auf der Grundschicht erzeugt.The intermediate layer is created by simply spreading dried leaves, flowers and / or grasses generated by the base layer.

Die Erfindung wird nun anhand der beigefügten Zeichnung und zweier Ausführungsformen gemäß den folgenden Beispielen näher erläutert. In der Zeichnung zeigen:The invention will now be explained with reference to the accompanying drawing and two embodiments according to the following examples explained in more detail. In the drawing show:

Fig. 1 den allgemeinen Schichtaufbau des erfindungsgemäßen Laminats aus Grundschicht (1), Zwischenschicht (2) und Außen- bSEW. Deckschicht (3),1 shows the general layer structure of the laminate according to the invention comprising base layer (1), intermediate layer (2) and exterior bSEW. Top layer (3),

Fig. 2 den Schichtaufbau eines erfindungsgemäßen Laminats mit mehrlagiger Grundschicht, bei dem die (erste) Grundschicht (1) mit einer flammverzögernden Schicht (4) und einer bedruckten Schicht (5) kombiniert ist,2 shows the layer structure of a laminate according to the invention with a multi-layer base layer, at which the (first) base layer (1) with a flame retardant layer (4) and a printed one Layer (5) is combined,

Fig. 3 das erfindungsgemäße Laminat in Drauf sieht,, Beispiel 1 3 shows the laminate according to the invention in plan, example 1

Eine Gruppe von 84 wahlweise durchscheinenden oder opaken Laminaten, geeignet zum Einbringen in eineA group of 84 optionally translucent or opaque laminates suitable for incorporation into a

/4/ 4

1A/G-55 1641A / G-55 164

Hochdruckpresse, wurde erzeugt und in Formeines Sandwich wie folgt hergestellt:High pressure press, made and in the form of a sandwich manufactured as follows:

Durchscheinendes Laminat I: 1 Bahn Hi-Tex*Translucent laminate I: 1 strip Hi-Tex *

2 Bahnen trockenes Kraftpapier (165 g/m ) 1 Bahn Hi-Tex* 1 Bahn White Overlay RI 5037** getrocknete Pflanzen, Blumen usw. 1 Bahn Baumwollstoff2 lanes of dry Kraft paper (165 g / m) 1 lane Hi-Tex * 1 lane White Overlay RI 5037 ** dried plants, flowers etc. 1 strip of cotton fabric

Opakes Laminat II:Opaque laminate II:

1 Bahn Hi-Tex*1 lane Hi-Tex *

2 Bahnen trockenes Kraftpapier (165 g/m ) 1 Bahn Hi-Tex* 1 Bahn White Overlay RI 5037** getrocknete Pflanzen 1 Bahn gefärbte poröse oG-Cellulose 1 Bahn Hi-Tex* 2 Bahnen trockenes Kraftpapier (165 g/m ) 1 Bahn Hi-Tex*.2 lanes of dry Kraft paper (165 g / m) 1 lane Hi-Tex * 1 lane White Overlay RI 5037 ** dried plants 1 lane of colored porous oG cellulose 1 lane of Hi-Tex * 2 lanes of dry kraft paper (165 g / m) 1 lane of Hi-Tex *.

"Hi-Te»" ist ein Handelsname für ein nicht-klebendes Papier beschichtet mit einem Alkydharz, das ein Silan-Vernetzungsmittel enthält. Dieses Papier hat die Eigenschaft, daß es nicht an Melaminharz haftet."Hi-Te» "is a trade name for a non-adhesive Paper coated with an alkyd resin, which is a silane crosslinking agent contains. This paper has the property that it does not adhere to melamine resin.

"White Overlay RI 5037" ist ein 06-Cellulose-Papier imprägniert mit nicht-katalysiertem Melaminharz."White Overlay RI 5037" is a 06 cellulose paper impregnated with non-catalyzed melamine resin.

Der Stapel aus 84 Laminaten wurde so angeordnet, daß jedes Laminat von seinem Nachbarn durch zwei Blätter oder Bahnen Kraftpapier zwischen zwei Blättern oder Bahnen Hi-Tex getrennt war. Dies stellte sicher, daß die Laminate nicht beschädigt wurden und nach der Herausnahme aus der Presse leicht voneinander getrennt werden konnten.The stack of 84 laminates was arranged so that each laminate was separated from its neighbor by two sheets or webs of kraft paper was separated between two sheets or webs of Hi-Tex. This ensured that the laminates were not damaged and were easily separated from each other after removal from the press could become.

/5/ 5

1A/G-55 164 ) 1A / G-55 164 )

Der Stapel wurde dann in die Presse gegeben und esThe pile was then put into the press and there

ρ pρ p

wurde ein Druck von etwa 42 daN/cm (etwa 43 kg/cm ) angewandt. Die aufeinander aufgeschichteten Laminate wurden während mindestens 13 Minuten bei einer Temperatur bis zu 126,6 0C und nicht unter 110 °C gehalten. In diesem Beispiel hatte jedes Laminat folgende Abmessungen: a pressure of about 42 daN / cm (about 43 kg / cm) was applied. The successive stacked laminates were maintained for at least 13 minutes at a temperature up to 126.6 0 C and not lower than 110 ° C. In this example, each laminate had the following dimensions:

Länge 3,08 m, Breite 1,25 m und Dicke bzw. Stärke 0,23 mm.Length 3.08 m, width 1.25 m and thickness or thickness 0.23 mm.

Nach der Herausnahme aus der Presse wurden die 84 Laminate voneinander getrennt und waren gebrauchsfertig. Jedes durchscheinende Laminat sah so aus, als ob darin eine Reihe von getrockneten Blättern und Blumen verteilt sind, wodurch ein sehr dekorativer Effekt erzielt wurde.Upon removal from the press, the 84 laminates were separated and ready for use. Each translucent laminate looked like a row of dried leaves and Flowers are distributed, creating a very decorative effect.

Beispiel 2Example 2

Eine Gruppe von 16 steifen Laminaten wurde hergestellt durch Vorbereiten eines Verbundmaterials für jede Platte einer Hochdruckpresse, wie folgt:A group of 16 rigid laminates were made by preparing a composite material for each Plate of a high pressure press, as follows:

Erstes Laminat:
1 flammhemmende TrennbahnFirst laminate:
1 flame retardant separating liner

1 Schicht auf Melaminharzbasis in Form eines mit Melamlnharz imprägnierten Stoffs1 layer based on melamine resin in the form of one impregnated with melamine resin Fabric

flammhemmende Füllung in Form von Kraftpapier · imprägniert mit einem flammverzögernden oder flammhemmenden Harz
1 Bahn bedrucktes Papier
getrocknete Pflanzen
1 Bahn White Overlay mit nicht-katalysiertem Melaminharzflame retardant filling in the form of kraft paper · impregnated with a flame retardant or flame retardant resin
1 lane of printed paper
dried plants
1 lane of white overlay with non-catalyzed melamine resin

• · I*·• · I * ·

1A/G-55 1641A / G-55 164

Zweites Laminat:
1 Bahn Hi-Tex
1 Bahn White Overlay mit nicht-katalysiertem Melaminharz
- getrocknete PflanzenSecond laminate:
1 track Hi-Tex
1 lane of white overlay with non-catalyzed melamine resin
- dried plants

1 Bahn bedrucktes Papier1 lane of printed paper

- flammhemmende Füllung in Form von Kraftpapier imprägniert mit einem flammhemmenden.Harz- flame retardant filling in the form of kraft paper impregnated with a flame retardant resin

- Melaminharzschicht in Form von Papier, imprägniert mit Melaminharz- Melamine resin layer in the form of paper, impregnated with melamine resin

1 flammhemmende Trennbahn.1 flame retardant separating liner.

Der aus den einzelnen Bahnen gebildete Stapel wurde wie im Beispiel 1 gepreßt, wobei jedoch die einzelnen Laminate umgekehrt angeordnet waren, bezogen auf die benachbarten Laminate, d. h„ abwechselnd mit der Oberseite nach oben und nach unten, und von den benachbarten Laminaten durch dazwischen angeordnete flammhemmende Trennbahnen getrennt waren.The stack formed from the individual webs was pressed as in Example 1, but the individual Laminates were reversed with respect to the adjacent laminates; h "alternating with the top up and down, and from the adjacent laminates by interposed flame retardant Parting lines were separated.

Der Stapel wurde einem Druck von etwa 42 daN/cm (etwa 43 kg/cm ) unterworfen und einer Temperatur von mindestens 135 0C, jedoch nicht mehr als 140,5 0C, während einer Zeitspanne von etwa 13 Minuten ausgesetzt»The stack was subjected to a pressure of about 42 daN / cm (about 43 kg / cm) and a temperature of at least 135 0 C, but not more than 140.5 0 C, exposed for a period of about 13 minutes »

Die Abmessungen der Bahnen waren die gleichen wie in Beispiel 1, mit der Abwandlung, daß die Gesamtstärke im Mittel etwa 1,3 mm betrug und üblicherweise zwischen 0,8 und 2,0 mm schwankte.The dimensions of the webs were the same as in Example 1, with the modification that the overall thickness averaged about 1.3 mm and usually varied between 0.8 and 2.0 mm.

Nach dem Entfernen aus der Presse wurden die 16 Laminate voneinander getrennt. Jedes Laminat hatte das Aussehen eines steifen Bahnmaterials mit einem gedruckten Muster und darin verteilten getrockneten Pflanzen.After removal from the press, the 16 laminates were separated from one another. Every laminate had the look a rigid sheet material with a printed pattern and dried plants scattered therein.

/7/ 7

• ο · β• ο · β

iiaa ο . a a » *iiaa ο. a a »*

1A/G-55 164 Ϋ1A / G-55 164 Ϋ

Selbstverständlich können, obwohl nur zwei Ausführungsformen der vorliegenden Erfindung beschrieben sind, Änderungen vorgenommen werden in der Auswahl der Stoffe, ohne hierdurch den Rahmen der Erfindung zu verlassen.Of course, although only two embodiments of the present invention are described, Changes are made in the selection of substances without thereby departing from the scope of the invention.

Beispielsweise können die Trennbahnen oder Trennschichten aus einem anderen Material als Hl-Tex bestehen und sie brauchen auch nicht flammhemmend oder flammverzögernd ausgerüstet zu sein. Die Grundschicht kann, wie erwähnt, aus einem beliebigen Material bestehen, entweder mit oder ohne dekorativen Druck oder dekorative Prägung.For example, the separating sheets or separating layers consist of a different material than Hl-Tex and they also do not need to be flame retardant or flame retardant to be equipped. As mentioned, the base layer can consist of any material, either with or without decorative printing or embossing.

Je nach der vorgesehenen Verwendung des Produktes, d. h. der für das Produkt benötigten Eigenschaften hinsichtlich Dauerhaftigkeit, Biegsamkeit, Lichtdurchlässigkeit uswo kann die Grundschicht auch eine zusammengesetzte Schicht aus einem Melaminharz bzw„ aus damit imprägniertem Papier und einem Füllmaterial aus bedrucktem Kraftpapier sein, wie in Beispiel 2 beschrieben. Darüberhinaus sind im Rahmen der Erfindung andere Kombinationen möglich, wie in den anliegenden Patentansprüchen beschrieben.Depending on the intended use of the product, i. H. the properties required for the product in terms of durability, flexibility, light transmission uswhere the base layer can also be a composite Layer made from a melamine resin or from paper impregnated therewith and a filler material printed Kraft paper as described in Example 2. In addition, are within the scope of the invention other combinations are possible, as described in the appended claims.

72497249

to . Leerseite to. Blank page

Claims (11)

PATKNTANWiWsTB ...%.* V„° .:. dr.-inc ρκλν/ mim WUESTHOFF-v. PECHMANN-BEHRENS-GOETZ - DIPL.-INC;. (il'RllAKU I'UIS EUROPEAN PATENTATTORNEYS «,pl-ciiem. dx. e. pr,„h>.rr von «c.mann DRYING. DIETER BEHRENS DIPL.-ING.; DIPL.-VIRTSCH.-ING. RUPERT GOETZ 1A/G-55 164 D-8000 MÜNCHEN 90 Anm. : Renee Elizabeth Degens schwei.gerstrasse2 telefon: (089) 66 20 51 Telegramm: protectpatent tblex: j 24070 AnsprüchePATKNTANWiWsTB ...%. * V "°.:. dr.-inc ρκλν / mim WUESTHOFF-v. PECHMANN-BEHRENS-GOETZ - DIPL.-INC ;. (il'RllAKU I'UIS EUROPEAN PATENTATTORNEYS ", pl-ciiem. dx. e. pr," h> .rr by "c.mann DRYING. DIETER BEHRENS DIPL.-ING .; DIPL.-VIRTSCH.-ING. RUPERT GOETZ 1A / G-55 164 D-8000 MÜNCHEN 90 Note: Renee Elizabeth Degens schwei.gerstrasse2 phone: (089) 66 20 51 Telegram: protectpatent tblex: j 24070 Claims 1. Dekoratives Laminat aus mehreren miteinander verbundenen Schichten bestehend aus einer Grundschicht (1), einer Zwischenschicht (2) und einer Außen- oder Deckschicht (3)» wobei als Zwischenschicht getrocknete Pflanzen, Blätter, Blumen oder Gräser vorhanden sind und die Außen- oder Deckschicht aus einem lichtdurchlässigen, mit Harz oder Leim behandelten Material, besteht. 1. Decorative laminate made of several interconnected layers consisting of a base layer (1), an intermediate layer (2) and an outer or top layer (3) »with dried as an intermediate layer Plants, leaves, flowers or grasses are present and the outer or top layer consists of a translucent, material treated with resin or glue. 2. Laminat nach Anspruch 1, dadurch gekennzeichnet , daß die Außen- oder Deckschicht durchsichtig ist.2. Laminate according to claim 1, characterized in that the outer or cover layer is transparent. 3. Laminat nach Anspruch 1, dadurch g e k e η η zeichnet, daß die Außen- oder Deckschicht ein mit Harz imprägniertes durchscheinendes Papier ist»3. Laminate according to claim 1, characterized in that g e k e η η, that the outer or top layer is a translucent paper impregnated with resin » 4. Laminat nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß die Außen- oder Deckschicht ein o^-Cellulose-Papier und das Harz ein Melaminharz ist.4. Laminate according to one of claims 1 to 3, characterized in that the outer or top layer an o ^ cellulose paper and the resin is a melamine resin. /2/ 2 1A/G-55 164 - 2 -1A / G-55 164 - 2 - 5. Laminat nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß die Grundschicht poröses OC-Cellulose-Papier ist«,5. Laminate according to one of claims 1 to 4, characterized in that the base layer porous OC cellulose paper is «, 6. Laminat nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet , daß die Grundschicht Kraftpapier ist,-6. Laminate according to one of claims 1 to 4, characterized in that the base layer Kraft paper is, 7. Laminat nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet , daß zwischen Grundschicht (1) und Zwischenschicht (2) zusätzlich eine flammverzögernde Bahn (4) vorhanden ist.7. Laminate according to one of claims 1 to 6, characterized in that between Base layer (1) and intermediate layer (2) also have a flame-retardant sheet (4). 8. Laminat nach einem der Ansprüche 1 bis 7,8. Laminate according to one of claims 1 to 7, dadurch gekennzeichnet , daß die Grundschicht bedruckt oder gemustert ist oder zusätzlich ein bedrucktes oder gemustertes Bahnmaterial (5) vorhanden ist.characterized in that the base layer is printed or patterned or in addition a printed or patterned sheet material (5) is present. 9. Laminat nach einem der Ansprüche 1 bis 8, dadurch gekennze ichnet , daß die Grundschicht aus natürlichen oder synthetischen Fasern besteht. 9. Laminate according to one of claims 1 to 8, characterized in that the base layer consists of natural or synthetic fibers. 10. Verfahren zur Herstellung des dekorativen Laminats nach einem der Ansprüche 1 bis 9, dadurch gekennzeichnet , daß man ein Schichtmaterial bestehend aus der gegebenenfalls mehrlagigen Grundschicht, der Zwischenschicht aus getrockneten Pflanzen, Blättern, Blumen oder Gräsern und der Außenoder Deckschicht aus einem mit nicht- oder halbpolymerisiertem Harz oder mit Leim imprägnierten lichtdurchlässigen Papier erzeugt und dieses Schichtmaterial preßt.10. A method for producing the decorative laminate according to any one of claims 1 to 9, characterized characterized in that a layer material consisting of the optionally multilayered Base layer, the intermediate layer of dried plants, leaves, flowers or grasses and the outer or Top layer made of a translucent layer impregnated with non- or semi-polymerized resin or with glue Paper produced and this layer material pressed. 11. Verfahren nach Anspruch 10, daß man beim Pressen Wärme anwendet.
724911. The method according to claim 10, that one applies heat during pressing.
7249
DE19813142587 1980-10-29 1981-10-27 Decorative laminate and process for its production Withdrawn DE3142587A1 (en)