DE1134352B - Method of stiffening tissues - Google Patents

Method of stiffening tissues

Info

Publication number
DE1134352B
DE1134352B DEE9811A DEE0009811A DE1134352B DE 1134352 B DE1134352 B DE 1134352B DE E9811 A DEE9811 A DE E9811A DE E0009811 A DEE0009811 A DE E0009811A DE 1134352 B DE1134352 B DE 1134352B
Authority
DE
Germany
Prior art keywords
precondensates
subjected
rubber
dispersion
fabrics
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DEE9811A
Other languages
German (de)
Inventor
Dr-Ing Egon Eloed
Dr Helmut Joerder
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
IRENE VON SZENTPALY GEB ELOED
MARIE ELOED GEB FAUSER
Original Assignee
IRENE VON SZENTPALY GEB ELOED
MARIE ELOED GEB FAUSER
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by IRENE VON SZENTPALY GEB ELOED, MARIE ELOED GEB FAUSER filed Critical IRENE VON SZENTPALY GEB ELOED
Priority to DEE9810A priority Critical patent/DE1150043B/en
Priority to DEE9811A priority patent/DE1134352B/en
Priority to GB3181755A priority patent/GB816506A/en
Priority to GB3181855A priority patent/GB816330A/en
Priority to FR1141478D priority patent/FR1141478A/en
Priority to FR1137878D priority patent/FR1137878A/en
Publication of DE1134352B publication Critical patent/DE1134352B/en
Pending legal-status Critical Current

Description

Die Erfindung betrifft ein Verfahren, minderwertige, dünne, leichte, lockere Gewebe, wie weitmaschige Mullgewebe, die aus billigen Abfallstoffen, insbesondere Baumwolle, Zellwolle oder beiden, hergestellt werden, unter Erhaltung ihrer textlien Eigenschaften in hochwertige, elastische und sprungelastische, alterungsbeständige und gegen chemische Reinigungsmittel beständige Gebilde überzuführen, die im Gegensatz zu dem Ausgangsgut als formhaltende Versteifungseinlagen für Kleidungsstücke verwendbar sind.The invention relates to a method of inferior, thin, light, loose fabrics, such as wide mesh Gauze made from cheap waste, especially cotton, rayon, or both are converted into high-quality, elastic and resilient, elastic properties while maintaining their textile properties. transferring structures that are resistant to aging and chemical cleaning agents, in contrast to the original material as shape-retaining stiffening inserts for items of clothing are usable.

Das Verfahren ist dadurch gekennzeichnet, daß die zu veredelnden leichten, lockeren Gewebe mit wäßrigen Dispersionen oder Emulsionen imprägniert werden, die natürlichen und bzw. oder künstlichen Kautschuk als Bindemittel und außerdem noch in Wasser unlösliche, verätherte Zwischenkondensate von Kunstharzen mit reaktionsfähigen Methylolgruppen in einer Menge enthalten, welche die Menge des vorhandenen Kautschuks überwiegt, und vorteilhaft noch Härtungskatalysatoren für die Zwischenkondensate enthalten, worauf das imprägnierte Gewebe einer Wärmebehandlung unterworfen wird. Bei dieser Wärmebehandlung wirken die reaktionsfähigen Gruppen der Zwischenkondensate auf korrespondierende Gruppen des Kautschukmoleküls unter Vernetzung ein, und das so imprägnierte Gewebe wird in ein sprungelastisches, alterungsbeständiges und gegen chemische Reinigungsmittel beständiges Gebilde übergeführt, das als formhaltende Versteifungseinlage für Bekleidungsstücke verwendet werden kann.The method is characterized in that the light, loose fabric to be finished is coated with aqueous Dispersions or emulsions are impregnated, the natural and / or artificial Rubber as a binding agent and, in addition, etherified intermediate condensates which are insoluble in water of synthetic resins with reactive methylol groups in an amount which corresponds to the amount of the existing rubber predominates, and advantageously also curing catalysts for the intermediate condensates included, whereupon the impregnated fabric is subjected to a heat treatment. During this heat treatment, the reactive groups of the intermediate condensates act on corresponding ones Groups of the rubber molecule with crosslinking, and the fabric so impregnated becomes elastic, non-aging and resistant to chemical cleaning agents Transferred structure that is used as a shape-retaining stiffening insert for items of clothing can be.

Das Verfahren wird z. B. so durchgeführt, daß als Vernetzungsmittel Vor- oder Zwischenkondensate von Formaldehyd mit Harnstoff oder Melamin in abgewandeltem Zustand, d. i. mit Alkoholen, wie Butanol, verätherte, in organischen Flüssigkeiten lösliche Produkte in Form von wäßrigen Dispersionen oder Emulsionen zur Anwendung gebracht werden.The method is e.g. B. carried out so that precondensates or intermediate condensates as crosslinking agents of formaldehyde with urea or melamine in a modified state, d. i. with alcohols, like Butanol, etherified products soluble in organic liquids in the form of aqueous dispersions or emulsions can be used.

Die erfindungsgemäß veredelten Gewebe werden vorteilhaft noch einer Nachbehandlung mit einer wäßrigen Lösung oder Dispersion von Vorkondensaten oder Zwischenkondensaten von Aminoplasten, z. B. mit einer Lösung oder Dispersion eines wasserlöslichen Vor- oder Zwischenkondensats von Formaldehyd mit Harnstoff oder Melamin unterworfen, getrocknet und gegebenenfalls noch einer weiteren Wärmebehandlung unterworfen.The fabrics finished according to the invention are advantageously subjected to an after-treatment with a aqueous solution or dispersion of precondensates or intermediate condensates of aminoplasts, z. B. with a solution or dispersion of a water-soluble precondensate or intermediate condensate of formaldehyde subjected to urea or melamine, dried and optionally another one Subjected to heat treatment.

Die erfindungsgemäß einzusetzenden Dispersionen werden vorteilhaft in Schaumform zur Anwendung gebracht.The dispersions to be used according to the invention are advantageously used in foam form brought.

Die Verarbeitung von sehr dünnen Geweben, wie Verfahren zur Versteifung von GewebenThe processing of very thin fabrics, such as methods of stiffening fabrics

Anmelder:Applicant:

Marie Elöd, geb. Fauser,Marie Elöd, née Fauser,

und Irene von Szentpaly, geb. Elöd,and Irene von Szentpaly, née Elöd,

Badenweiler, Blauenstr. 17Badenweiler, Blauenstr. 17th

Dr.-Ing. Egon Elödt, Badenweiler,Dr.-Ing. Egon Elödt, Badenweiler,

und Dr. Helmut Jörder, Freiburg (Breisgau),and Dr. Helmut Jörder, Freiburg (Breisgau),

sind als Erfinder genannt wordenhave been named as inventors

Verbandsmull u. dgl., kann mit Vorteil auch derart erfolgen, daß man den Mull in mehreren Lagen, gegebenenfalls kreuzweise, aufeinanderlegt und das so erhaltene Mehrschichtgebilde dem vorliegenden Veredlungsverfahren unterwirft. Hierbei werden die einzelnen Lagen durch Verklebung fest miteinander verbunden. In manchen Fällen hat es sich als vorteilhaft erwiesen, die zu behandelnden Gewebe einseitig oder beidseitig aufgerauht zur Anwendung zu bringen. Die Imprägnierung der zu veredelnden leichten Gewebe kann nach an sich bekannten Methoden erfolgen. Vorteilhaft wird die anzuwendende Dispersion zunächst in einen stabilen Schaum übergeführt und dieser durch Einpressen in das Gewebe eingeführt. Bandage gauze and the like can advantageously also be made in such a way that the gauze is in several layers, optionally crosswise, placed one on top of the other and the multilayer structure obtained in this way to the present one Subject to processing procedures. Here, the individual layers are firmly bonded to one another tied together. In some cases it has proven to be advantageous to treat the tissue on one side or roughened on both sides. The impregnation of the light ones to be refined Tissue can be made by methods known per se. The dispersion to be used becomes advantageous first converted into a stable foam and this inserted into the tissue by pressing.

Die Nachbehandlung des imprägnierten und getrockneten Gewebes mit einer Lösung oder Dispersion von Aminoplastharzen wird vorteilhaft unter Anwendung von Vor- oder Zwischenkondensaten von Formaldehyd mit Melamin oder Melaminabkömmlingen durchgeführt. Nach der Nachbehandlung werden die Produkte getrocknet und das Harz durch Erhitzen in den unlöslichen Endzustand übergeführt. Dieser Vorgang kann in bekannter Weise durch Zugabe von Kondensationskatalysatoren begünstigt werden. Durch die Nachbehandlung können die Eigenschäften des erfindungsgemäß veredelten Gewebes mit Bezug auf Griff, Sprungelastizität, Alterungsbeständigkeit und Beständigkeit gegen chemische Reinigungsmittel noch verbessert werden.
Es ist bekannt, daß Phenolharze Vulkanisations-Wirkungen auf Kautschuk ausüben.The aftertreatment of the impregnated and dried fabric with a solution or dispersion of aminoplast resins is advantageously carried out using pre- or intermediate condensates of formaldehyde with melamine or melamine derivatives. After the aftertreatment, the products are dried and the resin is converted into the final insoluble state by heating. This process can be promoted in a known manner by adding condensation catalysts. As a result of the aftertreatment, the properties of the fabric refined according to the invention with regard to grip, elasticity, resistance to aging and resistance to chemical cleaning agents can be further improved.
It is known that phenolic resins have vulcanizing effects on rubber.

Es ist weiterhin bekannt, die Gebrauchstüchtigkeit von Textilien dadurch zu verbessern, daß sie durchIt is also known to improve the serviceability of textiles by having them

209 629/258209 629/258

Imprägnieren mit Kunstharzvorkondensaten und zusätzliche Behandlung mit Latex-Emulsionen knitterfest gemacht werden. Hierbei werden sehr geringe Mengen von Kautschuk, bezogen auf das Kunstharzgewicht, zur Anwendung gebracht, während bei vorliegender Erfindung Kautschuk das eigentliche Verklebungsmittel darstellt.Impregnation with synthetic resin precondensates and additional treatment with latex emulsions, crease-proof be made. Very small amounts of rubber, based on the weight of the synthetic resin, brought into use, while in the present invention rubber is the actual adhesive represents.

Es ist auch bereits bekannt, Wolle durch eine Kombination von synthetischem Butadien-1,3-Poly-It is also already known to make wool through a combination of synthetic butadiene-1,3-poly

Beispiel 2Example 2

Ein weitmaschiges Mullgewebe aus Baumwollfasern von 25 g/m2 Gewicht wird mit einer Dispersion, die man — wie nachstehend beschrieben — erhält, foulardiert, getrocknet und 10 Minuten auf 100° C erhitzt.A wide-meshed gauze made of cotton fibers weighing 25 g / m 2 is padded with a dispersion which is obtained as described below, dried and heated to 100 ° C. for 10 minutes.

Herstellung der DispersionPreparation of the dispersion

In 100 Teile einer 60%igen Lösung eines mit Bu-In 100 parts of a 60% solution of a

merisat mit einem Harnstoff- bzw. Melamin-Form- io tanol verätherten Melamin-Formaldehyd-Vorkondenaldehydvorkondensat schrumpffest auszurüsten. sates in Butanol werden 20 Teile einer 50%igenmerisate with a urea or melamine formio tanol etherified melamine-formaldehyde precondensate aldehyde precondensate to be shrink-proof. sates in butanol are 20 parts of a 50% strength

Es ist weiterhin bekannt, zwecks Erhöhung der wäßrigen Lösung eines anionaktiven Fettalkohol-Knitteriestigkeit, zur Versteifung und zur Vermin- surfonates durch intensivesRühreneinemulgiert. Unter derung des Glanzes Textilien mit Mischungen von weiterem Rühren wird mit 100 Teilen Wasser verKautschuk-Dispersionen und Kondensationsharzen 15 dünnt. Dann gibt man 40 Teile einer 40%igen auszurüsten, wobei letztere im Überschuß angewendet
werden. Hierbei handelt es sich um die Anwendung
wasserlöslicher Vorkondensate.It is also known to emulsify in an emulsified form by intensive stirring in order to increase the aqueous solution of an anion-active fatty alcohol crease resistance, for stiffening and for minimizing. Under the shine of textiles with mixtures by further stirring, 100 parts of water are used to dilute rubber dispersions and condensation resins 15. Then you give 40 parts of a 40% finish, the latter being used in excess
will. This is the application
water-soluble precondensates.

Keine dieser Veröffentlichungen war geeignet, der Fachwelt das Problem der Überführung minderwertiger, leichter, lockerer Gewebe in hochwertige, elastische und sprungelastische, als Einlagen für Bekleidungsstücke verwendbare Gewebe mit besonders wertvollen Eigenschaften nahezulegen. Noch viel weniger war die Lösung dieses Problems im Sinne der vorliegenden Erfindung aus dem Vorveröffentlichungen zu entnehmen.None of these publications was suitable to solve the problem of the transfer of inferior, lighter, looser fabric in high quality, elastic and elastic, as insoles for To suggest garments usable fabrics with particularly valuable properties. Yet Much less was the solution to this problem in the sense of the present invention from the prior publications refer to.

Beispiel 1example 1

Ein weitmaschiges Mullgewebe aus Zellwolle von 30 g/m2 Gewicht wird mit einer 24%igen wäßrigen Dispersion, deren Herstellung nachstehend beschrieben wird, foulardiert und bei 100° C getrocknet. Durch die Behandlung tritt eine erhebliche Versteifung des Mullgewebes ein; außerdem verleiht die Ausrüstung dem Mullgewebe sprungelastische Eigenschaften, so daß dieses als Einlagestoff in der Bekleidungsindustrie eingesetzt werden kann.A wide-meshed gauze made of rayon of 30 g / m 2 weight is padded with a 24% strength aqueous dispersion, the production of which is described below, and dried at 100.degree. The treatment results in a considerable stiffening of the gauze fabric; In addition, the finish gives the gauze elastic properties so that it can be used as an interlining material in the clothing industry.

man 41) leüe einerman 41) lie one

Ammoniumnitratlösung und 100 Teile einer 4O°/oigen Butadien-Acryrnitril-Mischpolymerisat-Dispersion zu. Die Dispersion wird auf einen Festgehalt von 25°/o verdünnt.Ammonium nitrate solution and 100 parts of a 40% strength butadiene-acrylonitrile copolymer dispersion. The dispersion is diluted to a solids content of 25%.

Das mit dieser Dispersion veredelte Mullgewebe weist hervorragende sprungelastische Eigenschaften auf.The gauze fabric finished with this dispersion has excellent elastic properties on.

3535

4040

Herstellung der DispersionPreparation of the dispersion

Aus 100 Teilen einer 6O°/oigen Lösung eines wasserunlöslichen, mit Butanol verätherten und mit 30% eines Alkydharzes aus Adipinsäure und Trimethylolpropan modifizierten Harnstoff-Formaldehyd-Vorkondensates in Butanol stellt man durch Zugabe von 3 Teilen einer anionaktiven hochsulfonierten Fettsäure, 50 Teilen einer l%igen Caseinlösung und weiteres Verdünnen mit Wasser unter energischem Rühren eine 40%ige Dispersion her. Zu der Dispersion setzt man 8 Teile einer 40%igen wäßrigen Lösung von Ammoniumnitrat zu und stellt die Dispersion mit Ammoniak auf einen pH-Wert von 6,5 bis 7,5 ein.From 100 parts of a 60% solution of a water-insoluble urea-formaldehyde precondensate in butanol, etherified with butanol and modified with 30% of an alkyd resin composed of adipic acid and trimethylolpropane, 50 parts of a 1% igen casein solution and further dilution with water while vigorously stirring a 40% dispersion. To the dispersion are employed 8 parts of a 40% aqueous solution of ammonium nitrate are added and the dispersion with ammonia to a pH value of 6.5 to 7.5 a.

Diese Dispersion mischt man mit 120 Teilen einer neutral eingestellten 30%igen Dispersion eines Butadien-Aeryhiitril-Mischpolymerisates mit 25 fl/o Acrylnitril. Dann gibt man 20 Teile einer lOVoigen Gelatinelösung zu und verdünnt die Dispersion auf einen Festgehalt von 25%.This dispersion is mixed with 120 parts of a neutral 30% strength dispersion of a butadiene-aerohiitrile copolymer with 25 fl / o acrylonitrile. Then 20 parts of a 10% gelatin solution are added and the dispersion is diluted to a solids content of 25%.

Claims (3)

PATENTANSPRÜCHE:PATENT CLAIMS: 1. Verfahren zur Versteifung von Geweben durch deren Behandeln mit wäßrigen Dispersionen, welche Vorkondensate von mit Formaldehyd kondensierbaren Stoffen und Kautschuk enthalten, dadurch gekennzeichnet, daß leichte, lockere Gewebe, insbesondere aus Baumwolle, Zellwolle oder beiden bestehende Mullgewebe, mit wäßrigen Dispersionen oder Emulsionen imprägniert werden, die natürlichen und bzw. oder künstlichen Kautschuk als Bindemittel und außerdem noch in Wasser unlösliche, verätherte Zwischenkondensate von Kunstharzen mit reaktionsfähigen Methylolgruppen, in einer Menge enthalten, welche die Menge des vorhandenen Kautschuks überwiegt, und vorteilhaft noch Härtungskatalysatoren für die Zwischenkondensate enthalten, worauf das imprägnierte Gewebe einer Wärmebehandlung unterworfen wird.1. A method for stiffening fabrics by treating them with aqueous dispersions which contain precondensates of formaldehyde-condensable substances and rubber, characterized in that light, loose fabrics, in particular made of cotton, rayon or both existing gauze fabrics, are impregnated with aqueous dispersions or emulsions which contain natural and / or artificial rubber as a binder and also water-insoluble, etherified intermediate condensates of synthetic resins with reactive methylol groups, in an amount that outweighs the amount of rubber present, and advantageously also contain curing catalysts for the intermediate condensates, whereupon the impregnated fabric is subjected to a heat treatment. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß das nach Anspruch 1 ausgerüstete Gut einer Nachbehandlung mit einer wäßrigen Lösung oder Dispersion von Vorkondensaten oder Zwischenkondensaten von Aminoplasten, z. B. Harnstoff- oder Melamin-Vorkondensaten, unterworfen, getrocknet und gegebenenfalls noch einer weiteren Wärmebehandlung unterworfen wird.2. The method according to claim 1, characterized in that that the goods equipped according to claim 1 undergo aftertreatment with an aqueous solution or dispersion of precondensates or intermediate condensates of aminoplasts, e.g. B. urea or melamine precondensates, subjected, dried and, if necessary, a further heat treatment is subjected. 3. Verfahren nach Anspruch 1 und 2, dadurch gekennzeichnet, daß die Dispersionen in Schaumform angewendet werden.3. The method according to claim 1 and 2, characterized in that the dispersions are in foam form be applied. In Betracht gezogene Druckschriften: Britische Patentschriften Nr. 486 926, 519 734; USA.-Patentschrift Nr. 2467233; Faserforschung und Textiltechnik, 1951, S. 409 bis 418.References considered: British Patent Nos. 486,926, 519,734; U.S. Patent No. 2467233; Fiber research and textile technology, 1951, p. 409 to 418. © 209 629/258 7.© 209 629/258 7.
DEE9811A 1954-11-08 1954-11-08 Method of stiffening tissues Pending DE1134352B (en)