DE102017001210B4 - Apparatus and method for quench cooling, and method for producing a solution-annealed cast aluminum component - Google Patents
Apparatus and method for quench cooling, and method for producing a solution-annealed cast aluminum component Download PDFInfo
- Publication number
- DE102017001210B4 DE102017001210B4 DE102017001210.5A DE102017001210A DE102017001210B4 DE 102017001210 B4 DE102017001210 B4 DE 102017001210B4 DE 102017001210 A DE102017001210 A DE 102017001210A DE 102017001210 B4 DE102017001210 B4 DE 102017001210B4
- Authority
- DE
- Germany
- Prior art keywords
- component
- nozzles
- cooling
- cooled
- nozzle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Vorrichtung (100) zur Abschreckkühlung von Metallbauteilen (200), mit
- einer Abkühlkammer (110) zur Aufnahme wenigstens eines abzukühlenden Bauteils (200), und
- einer Vielzahl von in der Abkühlkammer (110) angeordneten Düsen (120) zur direkten Anströmung des abzukühlenden Bauteils (200) mit einem Kühlmedium (D), wobei die Düsen (120) unterschiedlich ausgerichtet und/oder die Düsenvolumenströme (V) unterschiedlich eingestellt und die Düsen (120) an zwei verfahrbaren Trägern (130) angeordnet sind, die aus entgegengesetzten Richtungen an das abzukühlende Bauteil (200) herangefahren werden können, sodass die Düsen (120) das Bauteil (200) umschließen.
Device (100) for quench cooling of metal components (200), with
- A cooling chamber (110) for receiving at least one component to be cooled (200), and
- A plurality of in the cooling chamber (110) arranged nozzles (120) for direct flow of the component to be cooled (200) with a cooling medium (D), wherein the nozzles (120) aligned differently and / or the nozzle volume flows (V) set differently and the nozzles (120) are arranged on two movable carriers (130) which can be moved from opposite directions to the component (200) to be cooled so that the nozzles (120) enclose the component (200).
Description
Die Erfindung betrifft eine Vorrichtung und zwei Verfahren zur Abschreckkühlung von Metallbauteilen. Die Erfindung betrifft ferner ein Verfahren zur Herstellung eines lösungsgeglühten Aluminiumgussbauteils.The invention relates to an apparatus and two methods for quench cooling of metal components. The invention further relates to a method for producing a solution-annealed cast aluminum component.
Wärmebehandlungen von Metallbauteilen, wie bspw. das Lösungsglühen, sehen mitunter eine zügige Abkühlung des Bauteils vor, was auch als Abschreckung bezeichnet wird. Die Abschreckung kann bspw. in einer Abkühlkammer erfolgen, in der das Bauteil mit einem mittels Ventilator erzeugten und im Wesentlichen homogenen Luftvolumenstrom abgekühlt wird.Heat treatments of metal components, such as solution heat treatment, sometimes provide rapid cooling of the component, which is also referred to as quenching. The quenching can be carried out, for example, in a cooling chamber, in which the component is cooled by means of a fan generated and substantially homogeneous air flow.
Die
Die
Die
Die Erfindung soll Möglichkeiten aufzeigen, wie das Abschreckkühlen verbessert werden kann.The invention is intended to show ways in which quench cooling can be improved.
Dies gelingt mit der erfindungsgemäßen Vorrichtung entsprechend dem Patentanspruch 1 und mit den erfindungsgemäßen Verfahren entsprechend den nebengeordneten Patentansprüchen. Bevorzugte Weiterbildungen und Ausgestaltungen der Erfindung ergeben sich analog für alle Erfindungsgegenstände aus den abhängigen Patentansprüchen, der nachfolgenden Beschreibung und der Zeichnung.This is achieved with the device according to the invention according to the patent claim 1 and with the inventive method according to the independent claims. Preferred developments and embodiments of the invention will become apparent for all subject matter of the dependent claims, the following description and the drawings.
Die erfindungsgemäße Vorrichtung zur Abschreckkühlung von Metallbauteilen umfasst:
- - eine Abkühlkammer zur Aufnahme wenigstens eines abzukühlenden (Metall)Bauteils, und
- - eine Vielzahl von in der Abkühlkammer angeordneten Düsen zur direkten Anströmung des zu kühlenden Bauteils mit einem Kühlmedium, wobei die Düsen unterschiedlich ausgerichtet und/oder die Düsenvolumenströme unterschiedlich eingestellt sind, womit gemeint ist, dass nicht alle Düsen dieselbe Ausrichtung aufweisen und/oder gleiche Düsenvolumenströme aufweisen bzw. erzeugen, und wobei die Düsen an zwei verfahrbaren Trägern angeordnet sind, die aus entgegengesetzten Richtungen an das abzukühlende Bauteil herangefahren werden können, sodass die Düsen das Bauteil umschließen.
- - A cooling chamber for receiving at least one to be cooled (metal) component, and
- - A plurality of arranged in the cooling chamber nozzles for direct flow of the component to be cooled with a cooling medium, wherein the nozzles are aligned differently and / or the nozzle volume flows are set differently, which means that not all nozzles have the same orientation and / or same nozzle volume flows or generate, and wherein the nozzles are arranged on two movable carriers, which can be moved from opposite directions to the component to be cooled, so that the nozzles enclose the component.
Bevorzugt sind die Düsen individuell bzw. einzeln ausgerichtet und eingestellt, d. h. jede Düse kann grundsätzlich eine andere Ausrichtung und/oder Düsenvolumenstromeinstellung aufweisen, wobei mehrere Düsen auch identische Ausrichtungen und/oder Einstellungen aufweisen können.Preferably, the nozzles are individually and individually aligned and adjusted, d. H. each nozzle may in principle have a different orientation and / or nozzle volume flow setting, wherein a plurality of nozzles may also have identical orientations and / or settings.
Die Düsen können eine unveränderliche Ausrichtung und Düsenvolumenstromeinstellung aufweisen. Die erfindungsgemäße Vorrichtung ist dann z. B. auf einen bestimmten Bauteiltyp festgelegt. Bevorzugt sind die Ausrichtungen der Düsen und/oder die Einstellungen der Düsenvolumenströme jedoch veränderbar, womit insbesondere gemeint ist, dass an jeder Düse sowohl die Düsen- bzw. Strahlausrichtung als auch der Kühlmedium- bzw. Düsenvolumenstrom individuell eingestellt werden kann, bzw. dass die bestehenden Einstellungen verändert werden können. Gegebenenfalls können die Düsen auch einzeln oder in Gruppen aktiviert und deaktiviert werden. Die erfindungsgemäße Vorrichtung kann somit individuell eingestellt und auch flexibel für verschiedene Bauteiltypen verwendet werden. Die bauliche Auslegung, die Ausrichtungen der Düsen und die Einstellungen der Düsenvolumenströme können anhand von Computerberechnungen bzw. -simulationen ermittelt und/oder durch Versuche bestimmt werden.The nozzles may have fixed orientation and nozzle volume flow adjustment. The device of the invention is then z. B. set to a specific type of component. However, the orientations of the nozzles and / or the settings of the nozzle volume flows are preferably variable, which means in particular that the nozzle or beam alignment as well as the cooling medium or nozzle volume flow can be individually adjusted at each nozzle, or that the existing Settings can be changed. Optionally, the nozzles can also be activated and deactivated individually or in groups. The device according to the invention can thus be set individually and also used flexibly for different types of components. The structural design, the orientations of the nozzles and the settings of the nozzle volume flows can be determined on the basis of computer calculations or simulations and / or determined by tests.
Bevorzugt erzeugt jede Düse wenigstens einen und bevorzugt nur einen auf das abzukühlende Bauteil gerichteten, insbesondere direkt gerichteten, Kühlmediumstrahl, der mit einem Kühlmediumvolumenstrom durch die Düse, dem Düsenvolumenstrom, einhergeht. Durch die Vielzahl der Düsen wird das zu kühlende Bauteil also mit einer Vielzahl von Kühlmediumstrahlen bzw. Kühlmediumvolumenströmen beaufschlagt, die sich sowohl in ihren durch die Düsenausrichtung vorgegebenen Strömungsrichtungen als auch in den Durchflussraten, Drücken und/oder Strömungsgeschwindigkeiten unterscheiden können, um eine optimale Anströmung des zu kühlenden Bauteils zu erreichen, insbesondere auch bei komplexen Bauteilformen. Zum einen werden dadurch hohe Abkühlgeschwindigkeiten bzw. -raten, bspw. von 7 K/s bis 25 K/s und insbesondere von 10 K/s bis 20 K/s, ermöglicht, wodurch der Abschreckeffekt verbessert, hohe Werkstofffestigkeiten erreicht und kurze Taktzeiten ermöglicht werden (durch Gas- bzw. Luftabkühlung, insbesondere mit einem homogenen Luftvolumenstrom, werden bisweilen nur Abkühlraten von maximal 5 K/s erreicht). Das Werkstoffpotential, insbesondere im Hinblick auf Leichtbau, kann besser ausgenutzt werden. Durch die erhöhten Abkühlraten ist es bspw. auch möglich bei gleicher oder sogar geringerer Lösungsglühtemperatur und Reduktion der aushärtenden Elementgehalte, z. B. Magnesium und Kupfer, einerseits die erzielbare Festigkeit beizubehalten oder sogar noch zu erhöhen und andererseits die Duktilität zu steigern bzw. die Sprödigkeit zu verringern. Zum anderen können gewünschte Abkühleffekte, wie insbesondere eine homogene oder inhomogene Abkühlung des Bauteils, erzielt werden, wie nachfolgend noch näher erläutert.Preferably, each nozzle generates at least one and preferably only one directed to the component to be cooled, in particular directly directed, cooling medium jet, which is accompanied by a cooling medium volume flow through the nozzle, the nozzle volume flow. Due to the large number of nozzles, the component to be cooled is thus subjected to a multiplicity of cooling medium streams or cooling medium volume flows, which are located both in Their flow directions, pressures and / or flow velocities can be differentiated by their flow directions, pressures and / or flow velocities, which are predetermined by the nozzle orientation, in order to achieve optimum flow to the component to be cooled, in particular even in the case of complex component shapes. On the one hand, this enables high cooling rates or rates, for example from 7 K / s to 25 K / s and in particular from 10 K / s to 20 K / s, which improves the quenching effect, achieves high material strengths and enables short cycle times By gas or air cooling, in particular with a homogeneous air flow, sometimes only cooling rates of a maximum of 5 K / s can be achieved). The material potential, especially with regard to lightweight construction, can be better utilized. Due to the increased cooling rates, it is, for example, also possible with the same or even lower solution annealing temperature and reduction of the hardening element contents, for. As magnesium and copper, on the one hand to maintain or even increase the achievable strength and on the other hand to increase the ductility and to reduce the brittleness. On the other hand, desired cooling effects, such as, in particular, a homogeneous or inhomogeneous cooling of the component, can be achieved, as explained in more detail below.
Bevorzugt sind die Düsen bauteilgeometrieabhängig angeordnet. Insbesondere sind die Düsen, zumindest während der Abschreckkühlung, konturnah zum abzukühlenden Bauteil angeordnet. Unter konturnah wird verstanden, dass sich die Düsen, bevorzugt alle Düsen, beim Abkühlen nahe der Oberfläche des abzukühlenden Bauteils befinden, bspw. mit einem Abstand (Nennabstand) von nicht mehr als 100 mm, bevorzugt nicht mehr als 75 mm, besonders bevorzugt nicht mehr als 50 mm und insbesondere nicht mehr als 30 mm. Bevorzugt weisen alle Düsen einen im Wesentlichen gleichen Abstand zur Bauteiloberfläche auf (einheitlicher Düsenabstand) oder sind zumindest bezüglich eines Nennabstands in einem Bereich von +/-10 mm und bevorzugt +/- 5 mm angeordnet. Durch die konturnahe Anströmung wird stellen- bzw. bereichsweise eine sehr genaue Beaufschlagung des abzukühlenden Bauteils mit dem Kühlmedium ermöglicht. Die Düsen sind dabei bevorzugt verteilt angeordnet, insbesondere so, dass im Wesentlichen die gesamte Oberfläche des abzukühlenden Bauteils mit Kühlmediumstrahlen beaufschlagbar ist (wobei bestimmte Bauteilbereiche auch gezielt ausgespart sein können). Die Anzahl an Düsen kann wenigstens 20, bevorzugt wenigstens 50, besonders bevorzugt wenigstens 100 und insbesondere wenigstens 200 betragen. Als Kühlmedium kann Wasser, Luft bzw.. Druckluft, Gas oder auch ein Wasser-Luft-Gemisch (Wassernebel) verwendet werden. Die Erfindung ist vor allem auch für die Serienfertigung geeignet.Preferably, the nozzles are arranged depending on component geometry. In particular, the nozzles, at least during quench cooling, are arranged close to the contour of the component to be cooled. Under Konturnah is understood that the nozzles, preferably all nozzles, when cooling are close to the surface of the component to be cooled, for example. With a distance (nominal distance) of not more than 100 mm, preferably not more than 75 mm, particularly preferably not more than 50 mm and in particular not more than 30 mm. Preferably, all nozzles have a substantially equal distance to the component surface (uniform nozzle spacing) or are arranged at least with respect to a nominal distance in a range of +/- 10 mm and preferably +/- 5 mm. Due to the flow near the contour, a very precise admission of the component to be cooled with the cooling medium is made possible in areas or areas. The nozzles are preferably arranged distributed, in particular so that substantially the entire surface of the component to be cooled can be acted upon by cooling medium jets (whereby certain component areas can also be deliberately recessed). The number of nozzles may be at least 20, preferably at least 50, particularly preferably at least 100 and in particular at least 200. As a cooling medium, water, air or .. compressed air, gas or a water-air mixture (water mist) can be used. The invention is particularly suitable for mass production.
Die Düsen sind an verfahrbaren bzw. bewegbaren Haltern bzw. Trägern angeordnet und können über diese Träger auch mit dem auszubringenden Kühlmedium versorgt werden, wozu die Träger Bohrungen, Kanäle, Schläuche und dergleichen aufweisen können. Die bewegbaren Träger können zusammen mit den daran angeordneten Düsen an das abzukühlende Bauteil herangefahren und nach dem Abkühlen wieder weggefahren werden. Es sind zwei Träger vorgesehen, die aus entgegengesetzten Richtungen an das abzukühlende Bauteil herangefahren werden können, so dass die Düsen das Bauteil dann quasi umschließen. Bevorzugt sind die Düsen beweglich an den Trägern befestigt, womit insbesondere gemeint ist, dass deren Lage und/oder Ausrichtung veränderbar ist. Außerdem kann vorgesehen sein, dass auch der Spritzwinkel und/oder der Düsenquerschnitt der Düsen einstellbar bzw. veränderbar ist. Selbsterklärend können auch mehr als zwei Träger bzw. Düsenträger vorgesehen sein, die in gleichen oder unterschiedlichen Richtungen verfahrbar sein können. Ferner können anstatt eines großen Trägers mehrere kleinere Träger vorgesehen sein.The nozzles are arranged on movable or movable holders or carriers and can be supplied via this carrier with the auszubringenden cooling medium, including the carrier holes, channels, hoses and the like may have. The movable carriers can be moved up together with the nozzles arranged thereon to the component to be cooled and be moved away again after cooling. Two carriers are provided which can be moved from opposite directions to the component to be cooled, so that the nozzles then virtually surround the component. Preferably, the nozzles are movably attached to the carriers, which means in particular that their position and / or orientation is variable. In addition, it can be provided that also the spraying angle and / or the nozzle cross-section of the nozzles is adjustable or changeable. Self-explanatory, more than two carriers or nozzle carrier can be provided, which can be moved in the same or different directions. Further, a plurality of smaller carriers may be provided instead of a large carrier.
Die erfindungsgemäße Vorrichtung kann ferner eine Vielzahl von Ventilen, insbesondere ansteuerbaren Ventilen, aufweisen, wobei jeder Düse ein Ventil zum Ein- und Ausschalten und/oder zur individuellen Einstellung des jeweiligen Kühlmedium- bzw. Düsenvolumenstroms zugeordnet ist. Bevorzugt bilden Düse und Ventil jeweils eine Baueinheit. Ferner können mehrere Düsen auch gruppiert werden und durch ein gemeinsames Gruppenventil geschaltet und/oder eingestellt werden.The device according to the invention may further comprise a plurality of valves, in particular controllable valves, wherein each nozzle is associated with a valve for switching on and off and / or for individual adjustment of the respective cooling medium or nozzle volume flow. Preferably, nozzle and valve each form a structural unit. Further, a plurality of nozzles may also be grouped and switched and / or adjusted by a common group valve.
Die Düsen können als Einstoffdüsen oder als Mehrstoffdüsen, insbesondere als Zweistoffdüsen (bspw. zur Ausbringung eines Wasser-Luft-Gemischs), ausgebildet sein. Mehrstoffdüsen ermöglichen auch die Veränderung des Kühlmediums während der Abkühlung (bspw. zuerst Luft, dann Wasser oder Wasser-Luft-Gemisch).The nozzles can be designed as single-substance nozzles or as multi-substance nozzles, in particular as dual-substance nozzles (for example for the application of a water-air mixture). Multi-fluid nozzles also allow the change of the cooling medium during cooling (eg first air, then water or water-air mixture).
Das erste erfindungsgemäße Verfahren zur Abschreckkühlung eines Metallbauteils umfasst die Schritte:
- - Bereitstellen einer erfindungsgemäßen Vorrichtung;
- - Einbringen des abzukühlenden Bauteils in deren Abkühlkammer; und
- - Abkühlen des Bauteils (in der Abkühlkammer), insbesondere nachdem die Düsen um das in die Abkühlkammer eingeführte abzukühlende Bauteil angeordnet wurden, wobei die Düsen so ausgerichtet und/oder die Düsenvolumenströme so eingestellt sind, dass eine gleichmäßige Abkühlung über das gesamte Bauteil erzielt wird.
- - Providing a device according to the invention;
- - Introducing the component to be cooled in the cooling chamber; and
- Cooling the component (in the cooling chamber), in particular after the nozzles have been arranged around the cooling component introduced into the cooling chamber, wherein the nozzles are aligned and / or the nozzle volume flows are adjusted so that a uniform cooling over the entire component is achieved.
Im Gegensatz zu der eingangs beschriebenen Abkühlung mit einem homogenen Luftvolumenstrom können die einzelnen Kühlmediumvolumenströme eine stellen- bzw. bereichsweise unterschiedliche und somit inhomogene Kühlwirkung bewirken mit dem Ziel, eine gleichmäßige bzw. homogene Abkühlung über das gesamte Bauteil zu erreichen (d. h. an jeder Bauteilstelle bzw. überall wird im Wesentlichen die gleiche Abkühlrate erreicht). Bei einem Bauteil mit unterschiedlichen Wandstärken bzw. Wanddicken können die Düsen so ausgerichtet und/oder die Düsenvolumenströme so eingestellt werden, dass trotz der Wandstärkenunterschiede eine homogene Abkühlung erreicht wird, so dass sich praktisch eine Wandstärkenunabhängigkeit ergibt. Dies hat sowohl gleichmäßigere bzw. homogenere Bauteileigenschaften (homogenes Eigenschafsprofil), insbesondere mechanische Eigenschafen, als auch geringere Geometrieabweichungen durch Verzug (trotz z. T. deutlich gesteigerter Festigkeit) zur Folge. Die Bauteilqualität wird verbessert und der Richtaufwand entfällt oder wird zumindest verringert. Mitunter können auch die Wärmebehandlungstemperaturen verringert werden. Somit werden die Effektivität gesteigert und Kosten gesenkt. Optimale Düsenausrichtungen und -einstellungen können durch Simulation und/oder Versuche ermittelt werden. In contrast to the cooling with a homogeneous air volume flow described above, the individual cooling medium volume flows may cause a different or inhomogeneous cooling effect with the goal of achieving uniform or homogeneous cooling over the entire component (ie at each component location or location). essentially the same cooling rate is achieved everywhere). In the case of a component with different wall thicknesses or wall thicknesses, the nozzles can be aligned and / or the nozzle volume flows can be adjusted in such a way that, despite the wall thickness differences, a homogeneous cooling is achieved, so that practically a wall thickness independence results. This results in both more uniform or homogeneous component properties (homogeneous property profile), in particular mechanical properties, as well as lower geometric deviations due to distortion (despite in some cases markedly increased strength). The component quality is improved and the straightening effort is eliminated or at least reduced. Occasionally, the heat treatment temperatures can be reduced. This increases the effectiveness and reduces costs. Optimal nozzle orientations and settings can be determined by simulation and / or experimentation.
Das zweite erfindungsgemäße Verfahren zur Abschreckkühlung eines Metallbauteils umfasst die Schritte:
- - Bereitstellen einer erfindungsgemäßen Vorrichtung;
- - Einbringen des abzukühlenden Bauteils in deren Abkühlkammer; und
- - Abkühlen des Bauteils (in der Abkühlkammer), insbesondere nachdem die Düsen um das in die Abkühlkammer eingeführte abzukühlende Bauteil angeordnet wurden, wobei die Düsen so ausgerichtet und/oder die Düsenvolumenströme so eingestellt sind, dass eine ungleichmäßige Abkühlung des Bauteils erzielt wird.
- - Providing a device according to the invention;
- - Introducing the component to be cooled in the cooling chamber; and
- Cooling the component (in the cooling chamber), in particular after the nozzles have been arranged around the cooling component introduced into the cooling chamber, wherein the nozzles are aligned and / or the nozzle volume flows are adjusted so that an uneven cooling of the component is achieved.
Das zweite erfindungsgemäße Verfahren unterscheidet sich zum ersten erfindungsgemäßen Verfahren im Wesentlichen dadurch, dass eine stellen- bzw. bereichsweise unterschiedliche und somit inhomogene Kühlwirkung gezielt zur Ausbildung unterschiedlicher Bauteileigenschaften genutzt wird, so dass das Bauteil schließlich ein inhomogenes Eigenschafsprofil, wie bspw. unterschiedliche Festigkeiten, aufweist.The second method according to the invention differs from the first method according to the invention essentially in that a cooling action which is different in area or region and thus inhomogeneous is specifically used to form different component properties, so that the component finally has an inhomogeneous property profile, such as different strengths ,
Die Erfindung kann zur Abschreckkühlung eines Metallbauteils und insbesondere eines Stahlbauteils oder Aluminiumbauteils verwendet werden. Hierbei kann es sich sowohl um ein Gussteil als auch um ein Dreh-/Frästeil oder ein Umformteil handeln. Ein solches Bauteil ist insbesondere ein Karosseriestrukturbauteil für ein Kraftfahrzeug, wie bspw. ein Federbeindom, der komplex geformt ist und der bspw. Füge- bzw. Befestigungsflansche, Verrippungen, Verschraubungsdome und dergleichen aufweisen kann.The invention can be used for quench cooling of a metal component and in particular a steel component or aluminum component. This can be either a cast part or a turned / milled part or a formed part. Such a component is in particular a body structural component for a motor vehicle, such as, for example, a strut tower, which is of complex shape and which may have, for example, fastening or fastening flanges, ribs, bolting domes and the like.
Bevorzugt wird die Erfindung zur Abschreckkühlung nach einem Lösungsglühen verwendet, d. h. die beiden zuvor erläuterten Verfahren dienen bevorzugt der Abschreckkühlung eines Metall- und insbesondere eines Stahl- oder Aluminiumbauteils nach dem Lösungsglühen, wozu das betreffende Bauteil aus dem Lösungsglühofen entnommen und im noch heißen Zustand in die Abkühlkammer der erfiridungsgemäßen Vorrichtung eingebracht und darin durch die vielen Kühlmediumstrahlen bzw. Düsenvolumenströme bis zur Entnahmetemperatur abgekühlt wird.Preferably, the invention is used for quench cooling after solution heat treatment, i. H. the two methods explained above are preferably used for the quench cooling of a metal and in particular a steel or aluminum component after the solution annealing, for which the relevant component removed from the solution annealing and introduced while still hot in the cooling chamber of erfiridungsgemäßen device and therein by the many cooling medium jets or Nozzle volume flows are cooled down to the discharge temperature.
Ein Aluminiumbauteil ist insbesondere aus einer aushärtbaren Aluminiumlegierung, wie bspw. einer AlSiMg-Legierung oder AICuMg-Legierung (Duraluminium), gebildet. Bevorzugt handelt es sich um ein Aluminiumgussbauteil und insbesondere um ein Aluminiumdruckgussbauteil.An aluminum component is formed in particular from a hardenable aluminum alloy, such as, for example, an AlSiMg alloy or AICuMg alloy (duralumin). It is preferably an aluminum casting component and in particular an aluminum die casting component.
Das erfindungsgemäße Verfahren zur Herstellung eines lösungsgeglühten Aluminiumgussbauteils bzw. eines Aluminiumdruckgussbauteils, wobei es sich insbesondere um ein Karosseriestrukturbauteil handelt (s. o.), umfasst die Schritte:
- - Urformen des Bauteils durch Gießen, insbesondere durch Druckgießen;
- - Lösungsglühen des gegossenen Bauteils, insbesondere in einem Lösungsglühofen, bspw. bei 460 °C bis 500 °C und 20 min. bis 60 min.;
- - Abschrecken bzw. Abschreckkühlen des lösungsgeglühten Bauteils mit einer erfindungsgemäßen Vorrichtung und/oder mit einem der beiden oben beschriebenen erfindungsgemäßen Verfahren, insbesondere nachdem das Bauteil zuvor aus dem Lösungsglühofen entnommen und noch im heißen Zustand in die Abkühlkammer der Vorrichtung eingebracht bzw. darin angeordnet wurde;
- - gegebenenfalls noch Auslagern bzw. Auslagerung (Kalt- oder Warmauslagerung) des Bauteils.
- - Urformen of the component by casting, in particular by die casting;
- Solution heat treatment of the cast component, in particular in a solution annealing furnace, eg. At 460 ° C to 500 ° C and 20 min. up to 60 minutes;
- Quenching or quench cooling of the solution-annealed component with a device according to the invention and / or with one of the two methods described above, in particular after the component has previously been removed from the solution annealing furnace and introduced into the cooling chamber of the device while still hot;
- - If necessary, outsourcing or outsourcing (cold or hot aging) of the component.
Die Erfindung wird nachfolgend mit Bezug auf die Zeichnung näher erläutert. Die in der Zeichnung gezeigten und/oder nachfolgend erläuterten Merkmale können, auch losgelöst von konkreten Merkmalskombinationen, allgemeine Merkmale der Erfindung sein und die Erfindung weiterbilden.
-
1 veranschaulicht in einer schematischen Darstellung die Abkühlung eines Metallbauteils in einer erfindungsgemäßen Vorrichtung.
-
1 illustrates a schematic representation of the cooling of a metal component in a device according to the invention.
Bei dem in
Die an einem Träger
Während der gezeigten Abschreckkühlung sind die Düsen
Die Vorrichtung
Die Düsen
Ebenso können die Düsen
Claims (8)