CN85100057A - 高温应变粘结剂 - Google Patents
高温应变粘结剂 Download PDFInfo
- Publication number
- CN85100057A CN85100057A CN 85100057 CN85100057A CN85100057A CN 85100057 A CN85100057 A CN 85100057A CN 85100057 CN85100057 CN 85100057 CN 85100057 A CN85100057 A CN 85100057A CN 85100057 A CN85100057 A CN 85100057A
- Authority
- CN
- China
- Prior art keywords
- temperature
- temperature strain
- binding agent
- strain
- sustainable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明高温应变粘结剂属于高温下结构应力测试时制作和粘贴高温应变片用的新型应变粘结剂。该粘结剂由磷酸二氢铝水溶液、氧化铝和氧化硅等按专门配方工艺制成。用它可制作和粘贴高温应变片，除了适用于耐热合金材料外，尤其能成功地粘贴于碳—陶瓷、碳—碳复合材料及石墨材料。具有高温绝缘性和良好传递应变能力，最高工作温度为600℃，且比陶瓷喷涂方法经济简便。
Description
本发明属于高温下结构应力测试时所用的高温应变粘结剂。
相近技术可参阅：
英国专利 790117
LN-3型高温应变胶，成都工学院科学技术成果，1976.4，
现有高温应变粘结剂，如英国U529胶及国内的LN-3型胶是一种只适用于将高温应变片粘贴在某些金属材料上的粘结剂，而不能将高温应变片粘贴在碳复合材料上。因而不能满足高温下某些结构应力测试的需要。
针对上述粘结剂存在的问题，本发明目的是研制一种能将高温应变片粘贴在耐高温碳复合材料上的新型高温应变粘结剂。
本发明的具体内容有：高温应变粘结剂除了含有少量的CrO3、Cr2O3和MgO外，主要由磷酸二氢铝水溶液、氧化铝和氧化硅组成。其中Al（H2PO4）3对应变粘结剂性能影响较大，因此适当增大Al（H2PO4）3水溶液的含量而减少Al2O3和SiO2的含量，将对性能产生不同影响。经过多次试验证明，一般采用浓度48～50%的Al（H2PO4）3水溶液占总配量57～62%，而Al2O3为325目细粉占总配量16～20%，SiO2为250目细粉占总配量14～18%为宜。
本发明的高温应变粘结剂的配制工艺是，事先将Al2O3、MgO和Cr2O3分别经过800℃、600℃、450～550℃灼烧一小时的热处理，将Al（H2PO4）3水溶液与MgO在玛瑙研钵中碾磨反应后，再将各粉料先后放入玛瑙研钵中搅拌均匀，经碾磨一小时，即成高温应变粘结剂。
本发明的施涂方法是，将待涂表面先用砂布打磨后，用甲苯、丙酮清洗，再用5～10%H3PO4溶液擦洗，晾乾，再将搅拌均匀的高温应变粘结剂用石英玻璃棒在该表面上涂一层底胶，待晾乾后，再经过半小时的180℃加温处理，冷却后，再将该粘结剂制作的高温应变片粘贴在该表面上，同时加压和半小时180℃热处理。卸压后再经400℃和550℃各一小时高温处理即可用于测量。
实施例：
高温应变粘结剂是由48%浓度的Al（H2PO4）35.7克，Al2O31.9～2.0克和SiO21.7～1.8克及少量CrO3、Cr2O3、MgO配成，经用于制作高温应变片、并将该应变片粘贴于碳-陶瓷复合材料试件上，在550℃高温下其传递应变＞5000με，绝缘电阻＞5MΩ，该应变片最高工作温度为600℃。
本发明的粘结剂除了能将应变片粘贴在耐热合金材料外，尚能用于粘贴在碳-陶瓷、碳-碳复合材料及石墨材料，粘贴牢固，绝缘性好，较用陶瓷喷涂法经济简便。
Claims (4)
1、一种高温应变粘结剂，其特征在于该粘结剂是由占总配比量为57～62%其浓度为48～50%的Al(H2PO4)3水溶液占总配比量为16～20%，325目的Al2O3细粉，和占总配比量为14～18%，250目的SiO2细粉，及少量的CrO3、Cr2O3、MgO专门配方工艺制成。
2、按照权利要求1所述的粘结剂，其特征在于该粘结剂是由48%浓度的Al（H2PO4）35.7克、Al2O31.9～2.0克和SiO21.7～1.8克及少量的CrO3、Cr2O3、MgO配成。
3、按照权利要求1-2所述的高温应变粘结剂其特征在于配制工艺中将Cr2O3经450℃～550℃灼烧。
4、按照权利要求1-2所述的高温应变粘结剂其特征在于施涂方法是用5～10%H3PO4溶液擦洗待涂表面，并在将高温应变片粘贴在表面上后经加压同时半小时180℃热处理，卸压后再经过400℃和550℃各一小时高温处理。