CN1995533A - Ice printing adhesive cement and ice printing fabric production method - Google Patents
Ice printing adhesive cement and ice printing fabric production method Download PDFInfo
- Publication number
- CN1995533A CN1995533A CN 200610130083 CN200610130083A CN1995533A CN 1995533 A CN1995533 A CN 1995533A CN 200610130083 CN200610130083 CN 200610130083 CN 200610130083 A CN200610130083 A CN 200610130083A CN 1995533 A CN1995533 A CN 1995533A
- Authority
- CN
- China
- Prior art keywords
- ice
- rubber cement
- starch
- escutcheon
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an ice-grain-like printing mucilage and the manufacturing method for ice-grain-like printing fabric. The mucilage comprises starch and water. After the mucilage is prepared by starch and water, whose weight proportion is 5-4095-60, it is heated and mixed. It is infused for 20-120 minutes under the temperature of 100DEG C and said ice-grain-like printing mucilage is prepared. In the manufacturing method for said ice-grain-like printing fabric said ice-grain-like printing mucilage is adopted. The process is that 1, preparing mucilage; 2, applying mucilage; 3 drying mucilage film; 4, preparing ice-grain; 5; printing the ice-grain; 6, dye fixation treatment; 7, washing treatment. The mucilage is applied in wide range for fiber, especially the high-temperature dyeing. It is provided with quick speed for molding, easily drying, low cost and slurry degradation. The manufacturing method for said ice-grain-like printing fabric is applied in industrial continuous production. The dyeing waster water can degraded. The discharge has not pollution. It is provided with simple process, low cost and easy operation.
Description
Technical field
The present invention relates to a kind of printing and dyeing process technology, being specially a kind of is main object with fabric, manufacturing has the stamp processing rubber cement of ice line effect and uses it to come the manufacture method of processed ice escutcheon loom figured, and international monopoly Main classification number plan is Int.Cl.DO6B 11/00 (2006.01).
Background technology
Ice escutcheon loom figured is the personalized textiles that current one big class has national characters and stylishness, can be widely used in and make clothes, furnishings and household textiles etc.Ice the escutcheon loom figured owing to have special pattern, aesthetic feeling style and not reproducible personalization features, thereby favored by consumer both domestic and external, and have very high surcharge.
Technology that ice escutcheon loom figured is actually a kind of " the anti-dyeing of wax ".Traditional process is manual processing method: earlier the paraffin of fusing or the mixture of paraffin and beeswax are applied on the pattern of fabric with picture wax instrument, and according to designer's intention, produce the position of texture at needs and carry out broken wax processing, put it into then in the dye tank that is adapted at dyeing under the cryogenic conditions and contaminate; After dyeing finishes, clean the dyestuff loose colour of cloth cover, boil with clear water then and boil, the wax on the grey cloth is heated to melt and is floated in the water reusable heat water rinse.Remove wax and since have wax local dyestuff can not on dye, simultaneously because broken wax is handled the irregular grain that produces, remove dewax after cloth cover just promptly present the white floral designs that have unique ice line feature.
The resist agent that the industrialization batik is produced is to have substituted paraffin and beeswax with rosin.Rosin is fallen the people melt the wax pond, by being coiled in the thermo oil boiler pipeline heating in the pond.The temperature of melting wax is about 180.For guaranteeing that the rosin-cerate face on the fabric is not destroyed adding man-hour, can add some auxiliary agents when changing wax, as turpentine oil or waterglass etc., to play the effect of softening wax face.Seal wax equipment has two kinds, and a kind of employing cylinder seal wax, another kind are roller seal wax.The former wax face is thicker, and the wax line of being printed is rough, meticulous deficiency.Cylinder is spent back bigger, the suitable bulk face flower type of printing.The wax face that the latter prints wax is thinner, and the wax line of its appearance is meticulousr, as imitative hair wax line and imitative porcelain wax line.Roller letter seal snuff returns less, should not print bulk face flower type.At present, most of batik factory adopts cylinder seal wax.
But the flower of ice escutcheon for a long time textiles always is employing manual method processing and fabricating, and labour intensity is big, and production capacity is limited, and resist agent rosin reclaims trouble, promotes being subjected to very big restriction.On the other hand, the conventional method of ice escutcheon loom figured processing need adopt natural beeswax, the mixture of rosin and paraffin is as resist agent, these resist agent only can maintain hard fragility energy and resist printing performance below 60 ℃, the line effect just can appear icing in following process, so painted middle cryogenic conditions that only limits to man-hour below 60 ℃ that adds, the restriction of dyeing and coloring principle in addition, the resist agent of prior art only is fit to the silk of natural fiber material, the painted processing of COTTON FABRIC, and for the fabric that needs high-temp dyeing, especially fabrics of polyester is then powerless.In addition, the wax in traditional resist agent needs just can wax after the heating and melting, and wax liquid melts the requirement that temperature is had strictness, it is very big to process difficulty, if processing is very high to the production equipment conditional request continuously in industrialization, can not industrialization promotion use.For example, patent documentation " method of white ice vein wax printing (ZL00112713.6) " has been reported a kind of method of white ice vein wax printing, and it is single to have used paraffin to make resist agent, solidify the back kneading goes out to ice line, dewaxes, fades under the normal temperature and pressure; Patent documentation " method for production (03135625.7) of the special ice line of a kind of textiles " has also been reported the preparation method of the special ice line of a kind of textiles, it is also single to have used paraffin to make resist agent, " surface at the textiles of desiring dye transfer is coated with last layer resist agent earlier; reserve the position of this pattern in figuratum place, treats that paraffin cooling back kneading goes out to ice the line crack ".But all to be single employing paraffin make resist agent for they, to the temperature requirement strictness, repeatedly move back wax, slop wax contamination vessel and stop up sewer pipe etc., the continuation that influence is produced, and wash and contain a large amount of rosin-cerates or saponification rosin-cerate etc. in the wax waste water, cause serious exhaust emission.Dyeing waste water be difficult to the degraded, the discharging pollution is arranged, and apply, " kneading " and the continuous production requirements of the also all inapplicable industrialization of process procedure such as " reservation patterns ", can't large-scale production.
Also has a kind of fabric that is known as indigo printing fabric in the prior art, its processing mode is to adopt the mixture of soybean starch and quick lime to make the resist printing slurry to print on the textiles, adopt indigo dyeing then, because the resist printing effect of resist printing slurry, be printed on the part of resist printing slurry, dyestuff can not dye, thereby can obtain the blue PRINTED FABRIC of white effect of decorative patterns.The pattern of this technology is not iced complex pattern, aesthetic effect and the personalization technology effect of line decorative pattern by manual drawing, and the stamp object also only limits to pure cotton fabric, and range of application has very big limitation, and cost of manufacture is also higher simultaneously.
Summary of the invention
At the deficiencies in the prior art, the technical problem that quasi-solution of the present invention is determined provides a kind of manufacture method of icing escutcheon flower rubber cement and ice escutcheon loom figured.This rubber cement suitable fibers scope is wide, needing to be particularly suitable for the fabric requirement of high-temp dyeing, but and have industrialization and use, with low cost, do not pollute characteristics such as easy to manufacture; The method of using this rubber cement to make ice escutcheon loom figured is suitable for industrial continuous production and processing, the dyeing waste water degradable, and discharging is not polluted, and technology is simple, and is with low cost, implements characteristics such as easy.
The technical scheme that the present invention solves described ice escutcheon flower rubber cement technical problem is: design a kind of ice escutcheon flower rubber cement, this rubber cement comprises starch and water, behind the percentage by weight preparation slurry according to starch: water=5-40: 95-60, heat while stirring, to 100 ℃ of following infusion 20-120 minutes, can make described ice escutcheon flower rubber cement; Described native starch comprise in wheaten starch, cornstarch, farina, glutinous rice starch or the soybean starch any one or multiple; Described modified starch be meant in oxidized starch, denaturated starch by acid, crosslinked starch, esterification starch or the etherification starch any one or multiple; Described graft starch be meant the monomer of starch polymer chain and acrylonitrile, acrylic acid, methyl methacrylate, polyacrylamide, Glucomannan, ethyl methacrylate, alkene or oligomer carry out in the product that graft reaction obtains any one or multiple.
The technical scheme that the present invention solves the manufacture method technical problem of described ice escutcheon loom figured is: design a kind of manufacture method of icing the escutcheon loom figured, it adopts following technology:
1. preparation rubber cement: according to ice escutcheon flower rubber cement formulated ice escutcheon flower rubber cement of the present invention;
2. apply rubber cement: take to brush, scrape or the stamp mode is applied to the rubber cement of being prepared on the fabric;
3. oven dry serous coat: adopt contactless mode with the oven dry of the rubber cement film on the fabric, bake out temperature 80-100 ℃, drying time is 5-15min;
4. make the ice line: the oven dry fabric is installed on the setting machine stretches, perhaps be installed in to squeeze on the padding machine and roll, the rubber cement film of oven dry is produced ice the cracked lines of line shape;
5. the ice escutcheon is spent: according to the requirement of coloration of textile materials character, select the corresponding dye ligand seal carving flower dye solution that can make fibre staining, adopt spray process, silk screen printing, padding method, any one is applied to described thickening agent solution on the fabric of ice line rubber cement crackle in infusion process or the spread coating;
6. fixation treatment: on pad-dry-cure dyeing machine or setting machine, handle through the high temperature curing fixation of 180-220 ℃, 1-3 minute for pure dacron; Other fabric then takes the vapour steaming colour fixing of 100 ℃, 20-40 minute to handle, the superheated steam fixation treatment of perhaps 105-120 ℃, 5-15 minute;
7. carrying out washing treatment: wash with water except that rubber cement film and loose colour on the fabric, can make described ice escutcheon loom figured after the oven dry.
Compared with prior art, ice escutcheon of the present invention flower rubber cement suitable fibers scope is wide, is particularly suitable for the fabric requirement of high-temp dyeing, and it is fast, easily dry, with low cost to have a film forming speed, and the slurry degradable is easy to manufacture, but characteristics such as industrialization use; The method of using this rubber cement to make ice escutcheon loom figured is suitable for industrial continuous production and processing, the dyeing waste water degradable, and discharging is not polluted, and technology is simple, and is with low cost, implements characteristics such as easy.
Description of drawings
Fig. 1 ices escutcheon flower rubber cement and the prepared a kind of ice escutcheon flower nylon fabric of ice escutcheon loom figured manufacture method Application Example photo figure in kind for the present invention;
Fig. 2 ices escutcheon flower rubber cement and the prepared another kind of ice escutcheon flower dacron of ice escutcheon loom figured manufacture method Application Example photo figure in kind for the present invention;
Fig. 3 ices escutcheon flower rubber cement and prepared another the ice escutcheon flower pure cotton fabric of ice escutcheon loom figured manufacture method Application Example photo figure in kind for the present invention;
Fig. 4 ices escutcheon flower rubber cement and prepared another the ice escutcheon flower real silk fabric of ice escutcheon loom figured manufacture method Application Example photo figure in kind for the present invention;
Fig. 5 ices escutcheon flower rubber cement and the obtained a kind of manual ice escutcheon flower pure ramie fabric of ice escutcheon loom figured manufacture method Application Example photo figure in kind for the present invention.
The specific embodiment
Be described in further detail the present invention below in conjunction with embodiment and accompanying drawing thereof:
A kind of ice escutcheon flower rubber cement (hereinafter to be referred as rubber cement) of the present invention's design, this rubber cement comprises starch and water, behind the percentage by weight preparation slurry according to starch: water=5-40: 95-60, heats while stirring, to 100 ℃ of following infusion 20-120 minutes, can make described ice escutcheon flower rubber cement; Described starch is function ingredients, at least a in native starch, modified starch or the graft starch; Described native starch comprise in wheaten starch, cornstarch, farina, glutinous rice starch or the soybean starch any one or multiple; Described modified starch be meant in oxidized starch, denaturated starch by acid, crosslinked starch, esterification starch or the etherification starch any one or multiple; Described graft starch be meant the monomer of starch polymer chain and acrylonitrile, acrylic acid, methyl methacrylate, polyacrylamide, Glucomannan, ethyl methacrylate, alkene or oligomer carry out in the product that graft reaction obtains any one or multiple.
Compare with the resist agent of prior art, it is function ingredients with each kind of starch that the present invention ices escutcheon flower rubber cement, wide material sources, low price, do not pollute, needing to be particularly suitable for the dacron requirement of high temperature (as 180-200 ℃) dyeing, this point be textile fibers properties or processing temperature required all be that prior art can't be accomplished.
The further feature of rubber cement of the present invention is also to contain flexible improver in the described rubber cement prescription, and it comprises at least a in polyvinyl alcohol, butter, white glue with vinyl, carboxymethyl cellulose, peach gum, gelatin or the gelatine; The percentage by weight addition of flexible improver is: starch: flexible improver=80-90: 20-10.After described flexible improver (or component) added, adhesive force strengthens after the serous coat drying of ice escutcheon flower processing, and was soft and flexible, but hard brittleness descends.Add flexible improver, then serous coat is not easily broken, and the ice line that then forms on fabric is sparse, and texture is thin and weak.
The further feature of rubber cement of the present invention is also to contain hardness improving agent in the described rubber cement prescription, and it comprises at least a in bentonite, pulverized limestone or the talcum powder; The percentage by weight addition of hardness improving agent is: starch: hardness improving agent=80-90: 20-10.After described hardness improving agent added, the hard after drying brittleness of serous coat of ice escutcheon flower processing improved, but adhesive force reduces.Add hardness improving agent, make the serous coat of formation hard crisp and easily cracked, it is many to produce ice line quantity, and texture is thick and hard straight, therefore will control technology in the pattern-printing and dyeing process well, prevents that serous coat from coming off and influence ice line pattern effect.
After adding the flexible improver or hardness improving agent of described Different Weight percentage in the rubber cement prescription of the present invention, the only relative ratio that reduces or reduce starch gets final product, and the method that adds water preparation slurry and manufacturing rubber cement does not change, and process is simple equally.After adding the flexible improver or hardness improving agent of described Different Weight percentage during rubber cement of the present invention is filled a prescription, can obtain the serial rubber cement of different gentle elastic energys or hard fragility energy.Utilize this series rubber cement printing and dyeing treating fiber webs, the ice escutcheon loom figured that just can obtain different charming patterns and have personalized not reproducible ice line effect.
Rubber cement of the present invention is seen the ice escutcheon flower that is applicable to various fabrics in principle from processing object, owing to have resistant to elevated temperatures characteristic, thereby be specially adapted to the ice escutcheon flower of pure dacron; Both saw and to process by hand from processing mode, also can mechanization industry produce.In addition, the cost of rubber cement of the present invention is very low, and can biodegradation, so dyeing waste water can directly discharge, and need not reclaim, and reduces reclaimer investment and operation cost, simultaneously environment is not polluted yet, and be a kind of green printing technology.
The present invention has designed a kind of manufacture method of icing the escutcheon loom figured simultaneously, and it uses ice escutcheon flower rubber cement of the present invention to come processed ice escutcheon loom figured, and adopts following technology:
1. preparation rubber cement: according to rubber cement formulated ice escutcheon flower rubber cement of the present invention;
2. apply rubber cement: take brushing, scrape or the stamp mode is prepared rubber cement with institute and is applied on the fabric;
3. oven dry serous coat: adopt contactless mode with the oven dry of the rubber cement film on the fabric, bake out temperature 80-100 ℃, the time is 5-15min.
4. make the ice line: in drying course,, make the rubber cement film of oven dry produce the cracked lines of ice line shape because the rubber cement water evaporates makes rubber cement condense, solidify and shrink.Also can adopt the method that applies external force simultaneously, for example the oven dry fabric is installed on the setting machine and stretch, perhaps be installed in and squeeze the method for rolling on the padding machine and increase or quicken ice line slight crack, form the abundanter ice line effect of cloth cover.This serous coat curing, contraction and cracked be nature, formed ice line slight crack is irregular, has randomness and personalization features, is that the manual drawing pattern can not be realized, thereby can not duplicates fully.It is described that to squeeze the technology roll in the technology that stretches on the setting machine or on padding machine all be prior art.
5. the ice escutcheon is spent: according to the character requirement of fabric, select corresponding dyestuff that can make fibre staining and preparation thickening agent solution, adopt spray process, silk screen printing, padding method, any one is applied to described thickening agent solution on the fabric of ice line rubber cement crackle in infusion process or the spread coating, and it is painted that dye solution can infiltrate ice line crack, thereby produce ice escutcheon flower effect, and have required dyefastness.Corresponding dyestuff that can make fibre staining and preparation thickening agent solution are selected in described character requirement by fabric, are the contents that those skilled in the art should be familiar with: comprise that existing DISPERSE DYES is used for dyeing terylene; REACTIVE DYES is used for cotton, silk, wool, nylon fabric dyeing; ACID DYES is used for silk, wool, nylon fabric dyeing; Cation dyes are used for acrylic fibres dyeing; Reducing dye, direct dyes, azoic dyes are used for cotton fabric dyeing process etc., and to use these dye ligand seal carving flower dye solutions etc. all be prior art.
6. fixation treatment: on pad-dry-cure dyeing machine or setting machine, cure fixation treatment through the high temperature of 180-220 ℃, 1-3 minute for pure dacron; Other fabric then takes the vapour steaming colour fixing of 100 ℃, 20-40 minute to handle, the superheated steam fixation treatment of perhaps 105-120 ℃, 5-15 minute.
7. carrying out washing treatment: wash with water except that rubber cement film and loose colour on the fabric, can make ice escutcheon loom figured after the oven dry.
After above step is processed, can make ice escutcheon loom figured of the present invention.As required, it can also further carry out traditional dyeing and printing and back arrangement to ice escutcheon loom figured once more, and acquisition ices the escutcheon floral pattern with the present invention or effect is the PRINTED FABRIC or the textiles of shading.
Any fabric of (comprising) that rubber cement of the present invention is applicable to that production method routinely obtains through pre-treatment such as starching, destarch, refining, bleaching etc.; Described fabric can be natural fiber materials such as cotton, hair, silk, fiber crops, also can be fibers materials such as terylene, acrylic fibers, viscose glue, polyamide fibre, can also be in the blending of any ratio or the fabric that interweaves by natural fiber material and fibers material.Described textiles can be that various grey cloths, clothes, shoes and hats, family spin finished product or semi-finished product such as ornaments, fibre packing materials.On the basis of existing technology, use rubber cement of the present invention and using method thereof, according to processing object, adopt that craft or Printing Machinery equipment can process on described fabric or textiles that various patterns are charming, lines is strange, rich color, dye-in-the-wood individual character, the ice escutcheon loom figured that effect is not reproducible.
What need supplementary notes is, though the embodiment of rubber cement of the present invention and application process thereof only limits to all kinds of fabrics, but it does not get rid of it on other similar (for example leather, timber, paper etc.) or not similar (for example glass, metal, plastics etc.) material, prints, makes and produce the application of ice line effect.To the application of described these material aspects, in correlative technology field, even the corresponding adjustment of the unsubstantiality that rubber cement prescription of the present invention and application process thereof and technology are made also should belong to protection scope of the present invention.
The place that the inventive method is not addressed is applicable to prior art.
Introduce specific embodiments of the invention below, but the present invention is not subjected to the restriction of embodiment:
Embodiment 1
Technological process: rubber cement preparation → printing rubber cement → oven dry → sprinkling DISPERSE DYES → thermosol dyeing → post processing.
The preparation rubber cement: according to mass ratio, farina 70%, polyvinyl alcohol 30% mixes, and this mixture is added water 85% by 15% concentration, is warming up to 85 ℃ and boils 45min under stirring condition, makes required rubber cement, and it is stand-by to reduce to room temperature;
Rubber cement is printed and the ice line is made: the rubber cement for preparing is added the seal stock tank, by pulp absorbing pump rubber cement is squeezed into cylinder, machine.The seal glue speed of a motor vehicle is 30m/min.Described rubber cement is completely scraped through rotary screen printing machines through the pure terylene silk fabric of refining, dry being equipped with on the dryer of needle plate, bake out temperature is 120 ℃, and the speed of a motor vehicle is generally at 80m/min.And apply tension force while drying, the rubber cement serous coat is pulled out cracked ice line.
Dyeing and fixation: adopt the method for spraying to be sprayed at red, yellow, blue disperse dye solutions on the fabric at random, dye solution just infiltrates among the slit of into drawing broken serous coat like this, the pad-dry-cure dyeing machine that enters 190 ℃ afterwards carries out fixation 2min, has just formed red, yellow, blue three looks colour mixture random or random distribution and has iced the line pattern;
Post processing: the rubber cement film is struck off gently, wash, soap and dry, soft finish can obtain icing escutcheon loom figured (referring to Fig. 2).
Embodiment 2
Technological process: preparation rubber cement → printing rubber cement → oven dry → sprinkling ACID DYES → vapour steaming colour fixing → post processing.
1. preparation rubber cement: according to mass ratio, 80% acrylic acid grafted starch accounted for 20% polyethylene mix, this mixture is added water 88% by 12% concentration, and be warming up to 75 ℃ boil 50min and become required rubber cement under stirring condition, it is stand-by to reduce to room temperature;
2. rubber cement is printed and the making of ice line: fabric is the silk broadcloth through destarch, refining and bleaching, and other are with embodiment 1;
3. dye and fixation: adopt the method for spraying to be sprayed at red, yellow, blue acidity material solution on the fabric at random then, dye solution just infiltrates among the slit of into drawing broken serous coat like this, the rapid steamer that enters 100 ℃ afterwards carries out fixation, time 18min has just formed red, yellow, blue three looks colour mixture random or random distribution and has iced the line pattern;
4. post processing can obtain real silk ice escutcheon loom figured (referring to Fig. 4) with example 1.
Embodiment 3
Preparation rubber cement → printing rubber cement → oven dry → sprinkling ACID DYES → vapour steaming colour fixing → aftertreatment technology.
1. preparation rubber cement: according to mass ratio, glutinous rice starch 80%, farina 15%, butter 5% mix, and this mixture is added water 82% by 18% concentration, be warming up to 90 ℃ and boil 45min and become required rubber cement under stirring condition, and it is stand-by to reduce to room temperature.
2. rubber cement is printed and the making of ice line: fabric is the pure polyamide fibre silk fabric through destarch, and other are with embodiment 1;
3. dye and fixation: with embodiment 2;
4. post processing can obtain polyamide fibre ice escutcheon loom figured (referring to Fig. 1) with example 1.
Embodiment 4
The stamp (conventional stamp) of preparation rubber cement → printings rubber cement → oven dry → all Lamine indigo plant salt colour developing → post processing (mechanical curettage rubber cement, wash, soap, dry) → once more.
1. rubber cement preparation: according to mass ratio, farina 30%, soya bean starch 55%, quick lime 15% mix, this mixture is added water 80% by 20% concentration be warming up to 90 ℃ boil 45min and become required rubber cement under stirring condition, it is stand-by to reduce to room temperature;
2. rubber cement is printed and iced line and make: fabric is pure cotton fabric process destarch, kiering and bleaching and the bottoming of process azoic coupling component, and other are with embodiment 1;
3. dye and fixation: fabric passes through from the blue salt chromophoric solution in all Lamines fast, and the blue salt chromophoric solution in all like this Lamines just infiltrates among the slit of into drawing broken serous coat, forms blue colour mixture random or random distribution and ices the line pattern;
4. post processing can obtain textile ice escutcheon loom figured (referring to Fig. 3) with embodiment 1.
Embodiment 5
Stamp (conventional the stamp) → ice escutcheon loom figured of preparation rubber cement → printings rubber cement → oven dry → all Lamine indigo plant salt colour developing → aftertreatment technology → once more.
1. preparation rubber cement: according to mass ratio, farina 40%, glutinous rice starch 60% mix, and this mixture is added water 80% by 20% concentration, under stirring condition, are warming up to 80 ℃ and boil 30min, make required rubber cement, and it is stand-by to reduce to room temperature.
2. rubber cement is printed and iced line and make: fabric is the cotton silk fabric of mulberry process destarch, kiering and bleaching and the bottoming of process azoic coupling component, and other are with embodiment 1;
3. dye and fixation: with embodiment 4;
4. post processing can obtain icing the escutcheon loom figured with example 4.
Embodiment 6
Technological process: preparation rubber cement → printing rubber cement → oven dry, ice line processing → sprinkling ACID DYES → vapour steaming colour fixing → aftertreatment technology.
1. preparation rubber cement: with embodiment 5;
2. rubber cement is printed and the ice line is made: fabric is the pure wool valetin through destarch, and the rubber cement printing method is with embodiment 2, dries on the dryer of needle plate being equipped with then, and bake out temperature is 120 ℃, and the speed of a motor vehicle is generally at 100m/min.Be to squeeze under the 2.5MPa condition to roll at padding machine pressure then, the rubber cement serous coat shut out split the trash ice line;
3. dye and fixation: red, yellow, blue ACID DYES solution is sprayed on the fabric at random, and dye solution just infiltrates among the slit of into drawing broken serous coat like this, and the rapid steamer that enters 100 ℃ afterwards carries out fixation, time 20min;
4. post processing can obtain icing the escutcheon loom figured with example 1.
Embodiment 7
Technological process: preparation rubber cement → printing rubber cement → oven dry, ice line processing → sprinkling DISPERSE DYES → thermosol dyeing → aftertreatment technology.
1. preparation rubber cement: with embodiment 5;
2. rubber cement is printed and the ice line is made: fabric is the washing of stamp/viscose filament yarn synthetic fibre silk fabric that interweaves, and other are with embodiment 1;
3. dye and fixation: dyestuff is the mixture of REACTIVE DYES and DISPERSE DYES, and other are with embodiment 1.
4. post processing can obtain icing the escutcheon loom figured with embodiment 1.
Embodiment 8
Make ice escutcheon flower pure ramie fabric by hand.
One, technological process:
Rubber cement → oven dry → ice line making → hand swabbing → aftertreatment technology is scribbled in preparation rubber cement → craft.
Two, implementation step
1. fabric preliminary treatment: after utilizing REACTIVE DYES according to layout requirement Freehandhand-drawing or manual stencilling stamp, stand-by through the azoic coupling component bottoming;
2. preparation rubber cement: according to mass ratio, farina 50%, glutinous rice starch 40%, soybean protein 10% mix, and this mixture is added water 80% by 20% concentration, be warming up to 85 ℃ and boil 50min under stirring condition, make required rubber cement, it is stand-by to reduce to room temperature;
3. apply rubber cement and the ice line is made: by decorative pattern requirement be coated with the pure ramie fabric that be drawn in stamp on by writing brush or homemade copper tool rubber cement, it is inserted in the hot-air oven, took out in 3 minutes at 100 ℃ of following dryings, manual folding broken serous coat, produces cracked at random ice line;
4. hand swabbing: manual have the position of rubber cement with the blue salt chromophoric solution brushing of all Lamines on fabric, make this position colour developing, and produce the colour mixture ice line pattern of random or random distribution;
5. post processing: strike off the rubber cement film by hand, wash again, soap and air dry and flatiron, can make manual ice escutcheon flower pure ramie fabric (referring to Fig. 5).
More than all fabric panels all can be made into clothes, home textile product, furnishings or handicraft.
Claims (4)
1. an ice escutcheon is spent rubber cement, and this rubber cement comprises starch and water, behind the percentage by weight configuration slurry according to starch: water=5-40: 95-60, heats while stirring, and to 100 ℃ of following infusion 20-120 minutes, can make described ice escutcheon flower resist printing rubber cement; Described starch is at least a in native starch, modified starch or the graft starch; Described native starch comprise in wheaten starch, cornstarch, farina, glutinous rice starch or the soybean starch any one or multiple; Described modified starch be meant in oxidized starch, denaturated starch by acid, crosslinked starch, esterification starch or the etherification starch any one or multiple; Described graft starch be meant the monomer of starch polymer chain and acrylonitrile, acrylic acid, methyl methacrylate, polyacrylamide, Glucomannan, ethyl methacrylate, alkene or oligomer carry out in the product that graft reaction obtains any one or multiple.
2. ice escutcheon flower rubber cement according to claim 1 is characterized in that containing flexible improver in the described ice escutcheon flower rubber cement prescription, and its percentage by weight addition is: starch: flexible improver=80-90: 20-10; Described flexible improver comprises at least a in polyvinyl alcohol, butter, white glue with vinyl, carboxymethyl cellulose, peach gum, gelatin or the gelatine.
3. ice escutcheon flower rubber cement according to claim 1 is characterized in that containing hardness improving agent in the described ice escutcheon flower rubber cement prescription, and its percentage by weight addition is: starch: hardness improving agent=80-90: 20-10; Described hardness improving agent comprises at least a in bentonite, pulverized limestone or the talcum powder.
4. manufacture method of icing the escutcheon loom figured, it adopts following technology:
(1). preparation rubber cement: according to claim 1,2 or 3 described ice escutcheon flower rubber cement formulated ice escutcheon flower rubber cements;
(2). apply rubber cement: take to brush, scrape or the stamp mode is applied to the rubber cement of being prepared on the fabric;
(3). the oven dry serous coat: adopt contactless mode with the oven dry of the rubber cement film on the fabric, bake out temperature 80-100 ℃, drying time is 5-15min;
(4). make the ice line: the oven dry fabric is installed on the setting machine stretches, perhaps be installed in to squeeze on the padding machine and roll, the rubber cement film of oven dry is produced ice the cracked lines of line shape;
(5). ice escutcheon flower: according to the requirement of coloration of textile materials character, select the corresponding dye ligand seal carving flower dye solution that can make fibre staining, adopt spray process, silk screen printing, padding method, any one is applied to described thickening agent solution on the fabric of ice line rubber cement crackle in infusion process or the spread coating;
(6). fixation treatment: on pad-dry-cure dyeing machine or setting machine, handle through the high temperature curing fixation of 180-220 ℃, 1-3 minute for pure dacron; Other fabric then takes the vapour steaming colour fixing of 100 ℃, 20-40 minute to handle, the superheated steam fixation treatment of perhaps 105-120 ℃, 5-15 minute;
(7). carrying out washing treatment: wash with water except that rubber cement film and loose colour on the fabric, after the oven dry, can make described ice escutcheon loom figured.