CN1995254A - 粘合剂组合物及其用途 - Google Patents
粘合剂组合物及其用途 Download PDFInfo
- Publication number
- CN1995254A CN1995254A CN 200610000425 CN200610000425A CN1995254A CN 1995254 A CN1995254 A CN 1995254A CN 200610000425 CN200610000425 CN 200610000425 CN 200610000425 A CN200610000425 A CN 200610000425A CN 1995254 A CN1995254 A CN 1995254A
- Authority
- CN
- China
- Prior art keywords
- binder composition
- cellulose
- acrylic ester
- ester polymer
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种用于记录全息图像信息的粘合剂组合物，主要用于激光模压全息烫印膜、精细定位脱铝全息标以及人民币安全线上模压全息图像的记录。所述组合物包括占组合物总重量10％－50％的树脂，所述树脂选自中分子量或高分子量丙烯酸酯聚合物和醇溶或脂溶性纤维素或纤维素衍生物；2.5％－5％的增塑剂；以及40％－87％的溶剂，其中，所述丙烯酸酯聚合物软化点在30－100℃，分子量在30,000－150,000；所述纤维素或所述纤维素衍生物的含氮量在10.8－12.6％之间。本发明的全息成像层粘结牢固，柔软性及耐高温性能好，耐潮热，没有微裂纹产生，能保证很好的全息亮度，可在人民币造纸中使用。
Description
技术领域
本发明涉及粘合剂组合物，特别是涉及适用于作为激光全息烫印膜、精细定位脱铝全息标以及人民币安全线上的全息成像层的粘合剂组合物。
背景技术
激光全息防伪技术是80年代末、90年代初发展起来的一项综合防伪技术，它的主要制作工艺为：将激光全息图案通过电铸制成母版，再翻成压印版，由压印版在一定温度和压力下将全息图像转移到涂敷有一层成像层的透明薄膜上。由于人民币流通的特殊性以及对防伪有严格的要求，因此对承载全息图像所用粘合剂组合物所必须的各种性能也有着极其严格的要求，粘合剂组合物涂布于薄膜上，烘干后的涂层要求足够柔软，粘结牢固，能够在较高的温度下成型，经过多次高温烘烤以及在纸张中施放后要保证全息图像中的微裂纹很少或没有，即能够保证足够的全息亮度。能达到这些要求的成像层用粘合剂组合物很少，只有极少数拥有国际领先水平的专业防伪企业才能生产和开发这一产品。然而同一配方的所生产的清漆因为地区性的差异以及所用的涂布设备、薄膜性能的不同而导致其性能不能完全发挥出来。
发明内容
本发明的目的在于提供一种粘合剂组合物，主要用于承载全息图像，能够达到人民币安全线生产的各项性能指标，能够承受近190℃的高温，在抄纸过程经过纸浆的浸泡和烘缸的高温烘烤后亮度也没有明显下降，几乎没有微裂纹产生。
本发明的另一目的在于提供本发明的粘合剂组合物在激光全息烫印膜、精细定位脱铝全息标以及人民币安全线全息成像层上的用途。
为了达到上述目的，本发明的粘合剂组合物包括占组合物总重量10％-50％的树脂，所述树脂包括：丙烯酸酯聚合物，和醇溶或脂溶性纤维素或者纤维素衍生物；2.5％-5％的增塑剂；以及40％-87％的溶剂，所述丙烯酸酯聚合物软化点在30-100℃，分子量在30,000-150,000，醇溶或脂溶性的纤维素或纤维素衍生物的含氮量在10.8-12.6％之间。
在发明的优选实施方案中，所述丙烯酸酯聚合物和所述纤维素或纤维素衍生物在组合物中的相对重量比例为1∶0.5-5。
本发明的粘合剂组合物还可以包括0.5％-5％的附着力促进剂。
可用于本发明的附着力促进剂可为钛螯合物或有机硅烷偶联剂。在本发明的一优选实施方案中所述附着力促进剂为钛螯合物GBA。但也可以使用有机硅烷偶联剂YC-1027。
在本发明的优选实施方案中，所述丙烯酸聚合物可以为甲基丙烯酸低级烷基酯的共聚物，或为含羟基官能团的丙烯酸酯聚合物。
可用于本发明的增塑剂优选为邻苯二甲酸酯类增塑剂中的一种或多种。在本发明的一优选实施方案中所述增塑剂为邻苯二甲酸二辛酯。
本发明的组合物中，溶剂可选自苯、取代苯、低级脂肪酸低级烷基酯、低级酮、低级醇中的一种或多种。所述溶剂更优选选自甲苯、二甲苯、丁醇、双丙酮醇、乙酸乙酯、乙酸丁酯、丙酮、丁酮中的一种或多种。显然，所选择的溶剂应该是使树脂可在该溶剂中可溶解的。
通过本发明的粘合剂组合物各组分的合理配比，使得组合物使用后，有足够的柔软度，粘结牢固，能够在较高的温度下成型。本发明的粘合剂组合物还可广泛地用于各种对全息图像要求较高的防伪产品上。如可应用在激光全息烫印膜、精细定位脱铝全息标以及人民币安全线全息成像层上。
具体实施方式
本发明的粘合剂组合物主要用于激光模压全息烫印膜、精细定位脱铝全息标以及人民币安全线全息图像的记录。由于安全线本身的特点，本发明的粘合剂组合物的显著特征是其中包含的混合树脂和其它组分以及各组分之间的特定配比。可用于本发明的树脂包括中分子量或高分子量的丙烯酸树脂和醇溶性或脂溶性的纤维素和纤维素衍生物。
树脂的使用量可占组合物的总重量的10％-50％。其中丙烯酸酯和纤维素或纤维素衍生物的重量比优选为1∶0.5-5。
可用于本发明的中分子量或高分子量丙烯酸酯也可为丙烯酸酯的均聚物，但软化点以在50-100℃，分子量在30,000-150,000之间为宜。
本发明的粘合剂组合物中可包含占组合物重量40％-87％的溶剂，选自苯、被一个或多个取代基取代的苯、低级脂肪酸低级烷基酯、低级酮、低级醇中的一种或多种。
除非另有说明，本发明中，术语“低级烷基酯”和“低级脂肪酸”中的低级意指含1-10个碳原子，优选含1-6个碳原子，更优选含1-4个碳原子。
本发明中的所用术语“低级烷基”表示直链或支链烷基。术语“取代基”表示卤素、羟基、C1-4烷基、卤代C1-4烷基等。烷基的具体例子包括：甲基、乙基、丙基、异丙基、丁基、异丁基，卤素包括：氟、氯、溴。优选的取代基数目为1-3个，更优选为1-2个。
所述溶剂的优选例子包括但不限定于：甲苯、氯苯、二甲苯、丙酮、丁酮、甲基异丁基酮，乙酸乙酯、乙酸丁酯、丁醇、异丙醇、双丙酮醇等。
本发明中使用的增塑剂为邻苯二甲酸酯类增塑剂中的一种或多种。在本发明中，增塑剂可占组合物总重的2.5％-5％。
本发明中使用的附着力促进剂为钛螯合物或有机硅烷偶联剂。在本发明的具体实施例中使用了钛螯合物GBA。但也可以使用有机硅烷偶联剂YC-1027。在本发明中，附着力促进剂可占组合物总重的0.5％-5％。
本发明的组合物当然还可包含粘合剂组合物中常用的其它添加剂如抗氧化剂等。本领域的普通技术人员根据实际使用的组分可容易掌握。
本发明用以下实施例进行进一步具体说明。
实施例1
甲基丙烯酸酯共聚物(Elvacite 4036) 10
醋酸纤维素(CAB-551-0.2) 10
丁酮 30
乙酸丁酯 25
甲苯 15
二丙酮醇 6
邻苯二甲酸二辛酯 4
将10重量份的醋酸纤维素(伊士曼CAB-551-0.2)加入到由30重量份的丁酮、25重量份的乙酸丁酯、15重量份的甲苯、6重量份的二丙酮醇组成的混合溶剂中。进行搅拌，至完全溶解后加入10重量份的甲基丙烯酸酯共聚物(Elvacite 4036、璐彩特国际公司生产)，搅拌溶解。最后加入4重量份的作为增塑剂的邻苯二甲酸二辛酯，搅拌均匀，由此可获得本发明的粘合剂组合物。
实施例2
甲基丙烯酸酯共聚物(Elvacite 4062) 10
硝酸纤维素 10
丁酮 30
乙酸丁酯 20
甲苯 15
二丙酮醇 7
邻苯二甲酸二辛酯 5
GBA 3
将10重量份的硝酸纤维素(美国Hercules Inc.生产)加入到由30重量份的丁酮、20重量份的乙酸丁酯、15重量份的甲苯、7重量份的二丙酮醇组成的混合溶剂中。进行搅拌，至完全溶解后加入10重量份的甲基丙烯酸酯共聚物(Elvacite 4062、璐彩特国际公司生产)，搅拌溶解。最后加入5重量份的作为增塑剂的邻苯二甲酸二辛酯和3重量份的作为附着力促进剂的GBA(美国杜邦公司生产)，搅拌均匀，由此可获得本发明的粘合剂组合物。
虽然本发明用上述描述和实施例进行了具体说明，但本发明并不受此限制。本发明的保护范围由所附权利要求书中的权利要求限定，任何对权利要求中技术特征进行的等同替换，都应属于本发明所限定的范围。
Claims (10)
1.一种粘合剂组合物，包括占组合物总重量：
10％-50％的树脂，包括丙烯酸酯聚合物和醇溶性或者脂溶性的纤维素或纤维素衍生物；
2.5％-5％增塑剂；
40％-87％溶剂，
其中，所述丙烯酸酯聚合物软化点在30-100℃，分子量在30,000-150,000；所述纤维素或所述纤维素衍生物的含氮量在10.8-12.6％之间。
2.根据权利要求1所述的粘合剂组合物，其特征在于，所述丙烯酸酯聚合物和所述纤维素或纤维素衍生物在组合物中的相对重量比例为1∶0.5-5。
3.根据权利要求1或2所述的粘合剂组合物，其特征在于，进一步包括占粘合剂组合物总重量0.5％-5％的附着力促进剂。
4.根据权利要求3所述的粘合剂组合物，其特征在于，所述附着力促进剂为钛螯合物或有机硅烷偶联剂。
5.根据权利要求4所述的粘合剂组合物，其特征在于，所述有机硅烷偶联剂为YC-1027，所述钛螯合物为GBA。
6.根据权利要求1到5任一项权利要求所述的粘合剂组合物，其特征在于，所述丙烯酸酯聚合物为甲基丙烯酸低级烷基酯的共聚物，或为含羟基官能团的丙烯酸酯聚合物。
7.根据权利要求1到6任一项权利要求所述的粘合剂组合物，其特征在于，所述增塑剂为邻苯二甲酸酯类增塑剂中的一种或多种。
8.根据权利要求1到7任一项权利要求所述的粘合剂组合物，其特征在于，所述溶剂选自苯、取代苯、低级脂肪酸低级烷基酯、低级酮、低级醇中的一种或多种。
9.根据权利要求8的粘合剂组合物，其特征在于，所述溶剂为甲苯、二甲苯、丁醇、双丙酮醇、乙酸乙酯、乙酸丁酯、丙酮、丁酮中的一种或多种。
10.权利要求1-9的粘合剂组合物在激光全息烫印膜、精细定位脱铝全息标以及人民币模压全息成像层上的用途。