CN1982389A - 一种合成树脂幕墙弹性封闭着色涂料 - Google Patents
一种合成树脂幕墙弹性封闭着色涂料 Download PDFInfo
- Publication number
- CN1982389A CN1982389A CN 200610035941 CN200610035941A CN1982389A CN 1982389 A CN1982389 A CN 1982389A CN 200610035941 CN200610035941 CN 200610035941 CN 200610035941 A CN200610035941 A CN 200610035941A CN 1982389 A CN1982389 A CN 1982389A
- Authority
- CN
- China
- Prior art keywords
- resin
- curtain wall
- synthetic
- agent
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种合成树脂幕墙的弹性封闭着色涂料,其特点在于:一种合成树脂幕墙的弹性封闭着色涂料,由A、B两组分构成。1.A组分有下列组成物及重量百分比:羟基丙烯酸树脂50%~85%;有机溶剂0~15%;分散剂0.1%~1.0%;颜料10%~30%;防沉剂0~30%;消泡剂0.1%~1.0%;流平剂0.1%~1.0%;曾柔剂1.0%~30%;填料0~15%。2.B组分有下列组成物及重量百分比:缩二脲0~95%;有机溶剂0~60%;弹性聚异氰酸酯固化剂5%~100%;A组与B组分按2~10∶1比例混合配比。本发明的优点在于:将合成树脂稀分墙系统的封闭着色中层涂料制成弹性产品,整个涂层的抗裂纹能力都明显增强,因而降低了合成树脂幕墙产生裂纹的可能性。
Description
技术领域
本发明涉及一种合成树脂幕墙的弹性封闭着色涂料
背景技术
合成树脂幕墙是一种新的幕墙装饰工艺,以该工艺制作幕墙效果无需钢挂结构,而是在水泥抹灰基面或旧瓷砖墙、旧涂层、保温层上直接施工找平腻子,然后采用喷涂的方法施工系统涂层,制成幕墙效果,该法成本低,效果好,节省钢材、铝材,有利于环保。
目前投入市场使用的合成树脂幕墙产品已经历两代:第一代合成树脂幕墙主要工艺为:粗腻子找平→细腻子找平→油性抛光腻子抛光→透明封闭底漆→中层涂料→金属面漆。
第二代合成树脂幕墙产品主要从环保(VOC排放)、金属面漆稳定性、工艺简化等方面对第一代产品进行了改进,主要工艺为:粗腻子找平→细腻子找平→水性抛光腻子抛光→二合一封碱中涂→金属面漆。
目前市场上第一代产品和第二代产品均有应用,但第二代产品已成为主流产品,第一代产品和第二代产品从抛光腻子开始均为非弹性产品。
经过上述两代产品的应用实践,合成树脂幕墙己成功解决了金属颜料稳定性、平整度、起泡掉皮等技术难题,但裂纹问题一直无法改决。许多施工完成时堪称完美的合成树脂幕墙工程,在经历了2~3年的风雨及冷暖循环后,裂纹问题逐渐显现。
发明内容
本发明的目的在于解决合成树脂幕墙的裂纹问题,提供一种具备一定弹性的封闭中层涂料,其特征在于:
由A、B两组分构成:
A组分组成物及重量百分比为:
羟基丙烯酸树脂:50%~85%
有机溶剂:0~15%
分散剂:0.1%~1.0%
颜料:10%~30%
防沉剂:0~3.0%
消泡剂:0.1%~1.0%
流平剂:0.1%~1.0%
增柔剂:0~30%
填料:0~15%
B组分组成物及重量百分比为:
缩二脲:0~95.0%
有机溶剂:0~60%
弹性聚异氰酸酯固化剂:5%~100%
A组分与B组分按2~10∶1比例混合配比
本发明和本公司另一已申报国家专利的产品弹性抛光腻子一起作为第三代合成树脂幕墙的标志性产品,其施工工艺为:
粗腻子找平一封固底漆加固——弹性抛光腻子抛光——弹性封闭中涂一金属面漆
具体实施方案
本发明主要利用调配的羟基丙烯酸树脂、有机溶剂、助剂、固化剂等,对经本公司腻子处理后的建筑物表面进行封闭着色处理。
取羟基丙烯酸树脂78.5g,分散剂0.5g,颜料(如钛白粉)20g,消泡剂:0.5g,流平剂0.5g,用高速分散机分散均匀,加入E-402-90T:30g,稀释剂(专用)45g,调好后用喷涂的方法施工。
经检验,本发明的主要质量技术指标如下:
序号 检验项目 技术指 检验结果
1 干燥时间h ≤2 2
2 对比率(白色及浅色) ≥0.93 0.94
3 耐水性(168h) 无异常 无异常
4 耐碱性(168h) 无异常 无异常
5 耐洗刷性、次 ≥5000 超5000
6 耐口老化性、粉化1级 2000h 2000h不起泡
变色2级 不起泡 1级变色,不剥落
不剥落 无粉化,无裂纹
无裂纹
7 涂层耐温变性(20次循环) 无异常 无异常
8 光泽(60°入射角) ≥80° 90°
9 耐弯曲性 ≤2mm 1mm
10 耐酸性(168h) 无异常 无异常
11 耐冲击性(50cm) 无异常 无异常
12 耐盐雾测试(2000h) 无异常 无异常
13 断裂延伸率 ≥25% 110%
Claims (7)
1、一种合成树脂幕墙弹性封闭中层涂料,由A、B两组分构成,
A组分有下列组成物及重量百分比:
羟基丙烯酸树脂:50%~85%
有机溶剂:0~15%
分散剂:0.1%~1.0%
颜料:10%~30%
防沉剂:0~3.0%
消泡剂:0.1%~1.0%
流平剂:0.1%~1.0%
增柔性:0%~30%
填料:0~15%
B组分有下列组成物及重量百分比:
缩二脲:0~95.0%
有机溶剂:0~60.0%
弹性聚异氰酸酯固化剂:5%~100%
A组分与B组分按2~10∶1比例混合配比;
2、权利要求书所述的一种封闭中层涂料,其特征在于:有机溶剂是异氟尔酮、二价酸酯,150#芳烃溶剂、环己酮、CAC、二甲苯或它们的混合物。
3、权利要求书所述的一种合成树脂幕墙弹性封闭中层涂料,其特征在于:羟基丙烯酸树脂也可以是聚醚多元醇、环氧树脂、氟碳树脂、醇酸树脂或它们的混合物。
4、权利要求书所述的一种合成树脂幕墙弹性封闭中层涂料,其特征在于:增柔剂是液态氯化石腊、环氧大豆油树脂、弹性丙烯酸树脂、蓖麻油树脂、弹性聚酯树脂或它们的混合物。
5、权利要求书所述的一种合成树脂幕墙弹性封闭中层涂料,其特性在于:缩二脲也可以是六亚甲基二异氰酸酯三聚体或它们的混合物
6、权利要求书所述的一种合成树脂幕墙弹性封闭中层涂料,其特征在于:弹性聚异氰酸酯固化剂是旭化成公司生产的E-402-90T、E-405-80T、TSE-100或它们的混合物,或其它不黄变弹性聚异氰酸酯固化剂。
7、权利要求书所述的一种合成树脂幕墙弹性封闭中层涂料,其特征在于:填料是超细碳酸钙、滑石粉、高岭土、重晶石粉、其它粉状填充物或它们的混合物。