CN101104767B - 油性环保自洁外墙漆 - Google Patents

油性环保自洁外墙漆 Download PDF

Info

Publication number
CN101104767B
CN101104767B CN2007100495451A CN200710049545A CN101104767B CN 101104767 B CN101104767 B CN 101104767B CN 2007100495451 A CN2007100495451 A CN 2007100495451A CN 200710049545 A CN200710049545 A CN 200710049545A CN 101104767 B CN101104767 B CN 101104767B
Authority
CN
China
Prior art keywords
environmental protection
exterior wall
paint
wall paint
cleaning
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2007100495451A
Other languages
English (en)
Other versions
CN101104767A (zh
Inventor
高华桥
叶维建
李彪
刘伟平
郭云龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bauhinia coating (Shanghai) Co., Ltd.
Original Assignee
BAUHINIA PAINTS (CHENGDU) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BAUHINIA PAINTS (CHENGDU) Co Ltd filed Critical BAUHINIA PAINTS (CHENGDU) Co Ltd
Priority to CN2007100495451A priority Critical patent/CN101104767B/zh
Publication of CN101104767A publication Critical patent/CN101104767A/zh
Application granted granted Critical
Publication of CN101104767B publication Critical patent/CN101104767B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种不含纯苯、甲苯、二甲苯的环保外墙漆，同时该环保外墙漆还具有自洁功能。本环保内墙漆的重量百分比组成为：脂肪族碳氢化合物溶剂16-31，含酸性基团的丙稀酸酯共聚物0.2-0.5，牛顿型热塑性丙烯酸树脂10-20，金红石型钛白粉20-30，超细重质碳酸钙30-50，硅藻土1-3，氯化石蜡2-3。本油性环保自洁外墙漆具有环保，低毒、表面涂层微粉化脱落以自洁保持墙面整洁的显著特点。另外本产品配方简单，成本低廉，具有较高的性价比。

Description

油性环保自洁外墙漆
技术领域
本发明涉及建筑材料技术领域，具体地说，是涉及一种油性环保自洁外墙漆。
背景技术
在涂料制造行业为了使涂料中的极性基料溶解，需要使用含有芳香烃和酯类的极性溶剂溶解，从而使得涂料中含有纯苯、甲苯、二甲苯等对人体有害的易挥发有机化合物，从而使得油性漆的使用受到限制。为了克服上述缺陷，让现有的油性漆更加符合现代社会人们对于涂料环保的要求，发挥油性漆的优势，同时让油性外墙漆具有良好的自洁性，本发明采用新型基料和溶剂体系，从而实现产品环保和自洁的目的，同时在产品的各项性能指标上也达到或超过国家标准。
发明内容
本发明的目的旨在为用户提供一种不含纯苯、甲苯、二甲苯的环保外墙漆，同时该环保外墙漆还具有自洁功能。在保留油性漆优点的同时，达到环保和保持墙面清洁的效果。
本环保外墙漆的重量百分比组成为：
脂肪族碳氢化合物溶剂               16-31
含酸性基团的丙稀酸酯共聚物         0.2-0.5
牛顿型热塑性丙烯酸树脂             10-20
金红石型钛白粉                     20-30
超细重质碳酸钙                     30-50
硅藻土                             1-3
氯化石蜡                           2-3
所述脂肪族碳氢化合物溶剂为C4-C11的烷烃，烯烃，环烷烃等组成的化合物。所述超细重质碳酸钙的粒度为500-1000目。
本发明是采用如下方法制备的：
5-10米/秒速度搅拌下加入脂肪族碳氢化合物溶剂，含酸性基团的丙稀酸酯共聚物和丙烯酸树脂并逐步提高搅拌速度至15-20米/秒，高速分散大约45-60分钟，直到树脂完全溶解。10-15米/秒搅拌下加入金红石型钛白粉和超细重质碳酸钙，逐步提高搅拌速度至18-22米/秒，高速分散大约15-20分钟至细度为40-50um。5-10米/秒搅拌10分钟左右，加入硅藻土和氯化石蜡，同时分散温度应控制在50℃以内。调节涂料的粘度为90-140KU/30℃(stomer粘度计)。
本发明所使用的主体基料为苯乙烯和丙烯酸的共聚物，可以直接溶解在环保价廉的脂肪族碳氢化合物溶剂体系中，从而使得本油性环保自洁外墙漆不含纯苯、甲苯、二甲苯。同时本发明采用的颜填料具有较大的亲水亲油平衡值，而所采用的主体基料具有适度的亲水性，涂料表面涂层微粉化使得表面涂层每年脱落几个微米，粉化的涂层连同涂层上附着的污物，在雨水的包裹下脱落而达到自洁功能。
本发明与现有技术相比具有以下特点：
本发明的油性环保自洁外墙漆具有环保，低毒、表面涂层微粉化脱落以自洁保持墙面整洁的显著特点。另外本产品配方简单，成本低廉，具有较高的性价比。
具体实施方式
实施例1
5-10米/秒速度搅拌下加入脂肪族碳氢化合物溶剂16％，含酸性基团的丙稀酸酯共聚物0.2％和丙烯酸树脂10％并逐步提高搅拌速度至15-20米/秒，高速分散大约45-60分钟，直到树脂完全溶解。10-15米/秒搅拌下加入金红石型钛白粉28％和超细重质碳酸钙42.8％，逐步提高搅拌速度至18-22米/秒，高速分散大约15-20分钟至细度为40-50um。5-10米/秒搅拌10分钟左右，加入硅藻土1％和氯化石蜡2％，同时分散温度应控制在50℃以内。调节涂料的粘度为90-140KU/30℃(stomer粘度计)，得到成品。理化检验结果见表1。
实施例2
5-10米/秒速度搅拌下加入脂肪族碳氢化合物溶剂23.5％，含酸性基团的丙稀酸酯共聚物0.5％和丙烯酸树脂20％并逐步提高搅拌速度至15-20米/秒，高速分散大约45-60分钟，直到树脂完全溶解。10-15米/秒搅拌下加入金红石型钛白粉20％和超细重质碳酸钙30％，逐步提高搅拌速度至18-22米/秒，高速分散大约15-20分钟至细度为40-50um。5-10米/秒搅拌10分钟左右，加入硅藻土3％和氯化石蜡3％，同时分散温度应控制在50℃以内。调节涂料的粘度为90-140KU/30℃(stomer粘度计)，得到成品。理化检验结果见表1。
实施例3
5-10米/秒速度搅拌下加入脂肪族碳氢化合物溶剂28％，含酸性基团的丙稀酸酯共聚物0.25％和丙烯酸树脂15％并逐步提高搅拌速度至15-20米/秒，高速分散大约45-60分钟，直到树脂完全溶解。10-15米/秒搅拌下加入金红石型钛白粉22.5％和超细重质碳酸钙30％，逐步提高搅拌速度至18-22米/秒，高速分散大约15-20分钟至细度为40-50um。5-10米/秒搅拌10分钟左右，加入硅藻土2％和氯化石蜡2.25％，同时分散温度应控制在50℃以内。调节涂料的粘度为90-140KU/30℃(stomer粘度计)，得到成品。理化检验结果见表1。
表1产品与国标GB/T9757-2001要求对比表
Figure S07149545120070814D000041

Claims (3)

1.一种油性环保自洁外墙漆，其特征在于：本油性环保自洁外墙漆的重量百分比组成为：
脂肪族碳氢化合物溶剂         16-31
含酸性基团的丙烯酸酯共聚物   0.2-0.5
牛顿型热塑性丙烯酸树脂       10-20
金红石型钛白粉               20-30
超细重质碳酸钙               30-50
硅藻土                       1-3
氯化石蜡                     2-3
所述脂肪族碳氢化合物溶剂为C4-C11的烷烃，烯烃，环烷烃组成的混合物。
2.根据权利要求1所述的一种油性环保自洁外墙漆，其特征在于：所述超细重质碳酸钙的粒度为500-1000目。
3.根据权利要求1所述的一种油性环保自洁外墙漆，其特征在于：所述牛顿型热塑性丙烯酸树脂为苯乙烯和丙烯酸的共聚物。
CN2007100495451A 2007-07-18 2007-07-18 油性环保自洁外墙漆 Active CN101104767B (zh)