CN1962943A - 一种镁合金表面处理工艺 - Google Patents

一种镁合金表面处理工艺 Download PDF

Info

Publication number
CN1962943A
CN1962943A CN 200510100992 CN200510100992A CN1962943A CN 1962943 A CN1962943 A CN 1962943A CN 200510100992 CN200510100992 CN 200510100992 CN 200510100992 A CN200510100992 A CN 200510100992A CN 1962943 A CN1962943 A CN 1962943A
Authority
CN
China
Prior art keywords
magnesium alloy
plating
vacuum splashing
water flushing
polishing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200510100992
Other languages
English (en)
Other versions
CN100471998C (zh
Inventor
王江锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitac Precision Technology Shunde Ltd
Original Assignee
Mitac Precision Technology Shunde Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitac Precision Technology Shunde Ltd filed Critical Mitac Precision Technology Shunde Ltd
Priority to CNB2005101009926A priority Critical patent/CN100471998C/zh
Publication of CN1962943A publication Critical patent/CN1962943A/zh
Application granted granted Critical
Publication of CN100471998C publication Critical patent/CN100471998C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种镁合金表面处理工艺，包含预处理、水冲洗、氟化处理、水冲洗、真空溅镀等步骤，在镁合金工件表面形成一层致密的金属膜。经该工艺处理后的镁合金具有良好的耐蚀性和耐磨性，同时该工艺过程简单，操作简便，效率高且具有较好的环保性，适宜于大规模的工业化应用。

Description

一种镁合金表面处理工艺
技术领域
本发明涉及金属表面的处理技术，具体涉及一种对镁合金进行表面处理的工艺。
背景技术
镁合金具有很高的比强度、比刚度、比弹性模量和良好的导热导电性，同时具有良好的阻尼减震和电磁屏蔽功能，广泛应用于汽车制造、航空航天、电子通讯领域等，被誉为“二十一世纪的绿色工程材料”。然而由于镁合金本身的化学活性较高，在空气中很容易氧化，极易在各种环境条件下发生腐蚀，从而阻碍了镁合金的广泛应用。
对镁合金表面进行化学改性，特别是在镁合金表面上化学镀覆一层金属层，是提高镁合金耐腐蚀性能的有效途径之一。传统的对镁合金进行表面处理的方法是，首先采用六价铬离子对镁合金表面进行钝化处理，以防止其氧化，然后再采用化学方法在其表面镀覆一层金属膜。但是这种方式工艺复杂，过程难以控制，操作困难，而且由于六价铬离子对环境和人体都存在重大危害，该工艺正逐步被限制或禁止使用。因而，开发一种高效简便且具有较好环保性的镁合金表面处理工艺，成为业界的当务之急。
发明内容
本发明的目的在于针对上述现有技术的不足，提供一种镁合金表面处理工艺，该工艺过程简单，操作简便，效率高且具有较好的环保性。
本发明提供的镁合金表面处理工艺，其特征在于，包含如下操作步骤：
1)预处理：将镁合金工件表面进行机械抛光、打磨、脱脂除油；
2)水冲洗：对打磨后的镁合金工件表面进行水冲洗，除去表面残渣，并烘干待用；
3)氟化处理：利用氢氟酸对镁合金工件进行处理，以在其表面形成一层致密的氟化镁层；
4)水冲洗：以去离子水对工件进行冲洗，并烘干；
5)真空溅镀：采用真空溅镀的方式在镁合金工件表面镀覆一层金属层。
上述工艺步骤中，还可以包括在步骤5)真空溅镀完成后，在镀层上进行化学镀镍的步骤。
上述工艺中的氟化处理的工艺条件为在10ml/L～150ml/L的40％的氢氟酸中处理10～50分钟。
上述工艺中的真空溅镀步骤中所采用的靶材是不锈钢、镍或铬。
实施本发明提供的镁合金表面处理工艺，经处理后的镁合金具有良好的耐蚀性和耐磨性，同时该工艺过程简单，操作简便，效率高且具有较好的环保性，适宜于大规模的工业化应用。
附图说明
图1是本发明工艺一个实施例中的镁合金涂层示意图。
图2是本发明工艺另一个实施例中的镁合金涂层示意图。
具体实施方式
下面结合具体实施例详述本发明。
实施例1
将镁合金工件按如下步骤进行处理：
预处理：将镁合金工件1表面进行机械抛光、打磨、脱脂除油；
水冲洗：对打磨后的镁合金工件表面进行水冲洗，除去表面残渣，并烘干待用；
氟化处理：利用100ml/L的40％的氢氟酸中处理10分钟，以在镁合金表面形成一层致密的氟化镁层2；
水冲洗：以去离子水对工件进行冲洗，并烘干；
真空溅镀：以不锈钢为靶材，采用真空溅镀的方式在镁合金工件表面镀覆一层不锈钢金属层3。
所得到的经表面处理的镁合金工件如附图1所示。
实施例2
将镁合金工件按如下步骤进行处理：
预处理：将镁合金工件1表面进行机械抛光、打磨；
水冲洗：对打磨后的镁合金工件表面进行水冲洗，除去表面残渣，并烘干待用；
氟化处理：利用10ml/L的40％的氢氟酸中处理30分钟，以在镁合金表面形成一层致密的氟化镁层2；
水冲洗：以去离子水对工件进行冲洗，并烘干；
真空溅镀：以铬为靶材，采用真空溅镀的方式在镁合金工件表面镀覆一层铬金属层3。
化学镀镍：在经过真空溅镀后的镁合金表面进行化学镀镍处理，得到一层镍金属层4。
所得到的经表面处理的镁合金工件如附图2所示。
实施例3
将镁合金工件按如下步骤进行处理：
预处理：将镁合金工件表面进行机械抛光、打磨；
水冲洗：对打磨后的镁合金工件表面进行水冲洗，除去表面残渣，并烘干待用；
氟化处理：利用10ml/L的40％的氢氟酸中处理50分钟，以在镁合金表面形成一层致密的氟化镁层；
水冲洗：以去离子水对工件进行冲洗，并烘干；
真空溅镀：以镍为靶材，采用真空溅镀的方式在镁合金工件表面镀覆一层镍金属层。

Claims (4)

1.一种镁合金表面处理工艺，其特征在于，按如下步骤操作：
1)预处理：将镁合金工件表面进行机械抛光、打磨、脱脂除油；
2)水冲洗：对打磨后的镁合金工件表面进行水冲洗，除去表面残渣，并烘干待用；
3)氟化处理：利用氢氟酸对镁合金工件进行处理，以在其表面形成一层致密的氟化镁层；
4)水冲洗：以去离子水对工件进行冲洗，并烘干；
5)真空溅镀：采用真空溅镀的方式在镁合金工件表面镀覆一层金属层。
2.根据权利要求1所述的表面处理工艺，其特征在于，其中还包括在步骤5)真空溅镀后在镀层上进行化学镀镍的步骤。
3.根据权利要求1所述的表面处理工艺，其特征在于，其中氟化处理的工艺条件为在10ml/L～150ml/L的40％的氢氟酸中处理10～50分钟。
4.根据权利要求1所述的表面处理工艺，其特征在于，其中真空溅镀中所采用的靶材是不锈钢、镍或铬。
CNB2005101009926A 2005-11-08 2005-11-08 一种镁合金表面处理工艺 Expired - Fee Related CN100471998C (zh)