CN1906340B - 制备聚(对苯二甲酸1，3-丙二醇酯)纤维的方法以及用该纤维制成的地毯 - Google Patents

制备聚(对苯二甲酸1，3-丙二醇酯)纤维的方法以及用该纤维制成的地毯 Download PDF

Info

Publication number
CN1906340B
CN1906340B CN200580001824XA CN200580001824A CN1906340B CN 1906340 B CN1906340 B CN 1906340B CN 200580001824X A CN200580001824X A CN 200580001824XA CN 200580001824 A CN200580001824 A CN 200580001824A CN 1906340 B CN1906340 B CN 1906340B
Authority
CN
China
Prior art keywords
yarn
filament
filaments
terephthalic acid
long filament
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN200580001824XA
Other languages
English (en)
Chinese (zh)
Other versions
CN1906340A (zh
Inventor
J·-C·常
R·L·多梅尔
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
EIDP Inc
Original Assignee
EI Du Pont de Nemours and Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by EI Du Pont de Nemours and Co filed Critical EI Du Pont de Nemours and Co
Publication of CN1906340A publication Critical patent/CN1906340A/zh
Application granted granted Critical
Publication of CN1906340B publication Critical patent/CN1906340B/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Links

Images

Classifications

    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F6/00—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
    • D01F6/58—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolycondensation products
    • D01F6/62—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolycondensation products from polyesters
    • D—TEXTILES; PAPER
    • D02—YARNS; MECHANICAL FINISHING OF YARNS OR ROPES; WARPING OR BEAMING
    • D02G—CRIMPING OR CURLING FIBRES, FILAMENTS, THREADS, OR YARNS; YARNS OR THREADS
    • D02G1/00—Producing crimped or curled fibres, filaments, yarns, or threads, giving them latent characteristics
    • D02G1/02—Producing crimped or curled fibres, filaments, yarns, or threads, giving them latent characteristics by twisting, fixing the twist and backtwisting, i.e. by imparting false twist
    • D—TEXTILES; PAPER
    • D02—YARNS; MECHANICAL FINISHING OF YARNS OR ROPES; WARPING OR BEAMING
    • D02G—CRIMPING OR CURLING FIBRES, FILAMENTS, THREADS, OR YARNS; YARNS OR THREADS
    • D02G1/00—Producing crimped or curled fibres, filaments, yarns, or threads, giving them latent characteristics
    • D02G1/20—Combinations of two or more of the above-mentioned operations or devices; After-treatments for fixing crimp or curl
    • D—TEXTILES; PAPER
    • D02—YARNS; MECHANICAL FINISHING OF YARNS OR ROPES; WARPING OR BEAMING
    • D02J—FINISHING OR DRESSING OF FILAMENTS, YARNS, THREADS, CORDS, ROPES OR THE LIKE
    • D02J1/00—Modifying the structure or properties resulting from a particular structure; Modifying, retaining, or restoring the physical form or cross-sectional shape, e.g. by use of dies or squeeze rollers
    • D02J1/08—Interlacing constituent filaments without breakage thereof, e.g. by use of turbulent air streams
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2331/00—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products
    • D10B2331/04—Fibres made from polymers obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. polycondensation products polyesters, e.g. polyethylene terephthalate [PET]
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2503/00—Domestic or personal
    • D10B2503/04—Floor or wall coverings; Carpets

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Fluid Mechanics (AREA)
  • General Chemical & Material Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Artificial Filaments (AREA)
  • Spinning Methods And Devices For Manufacturing Artificial Fibers (AREA)
  • Polyesters Or Polycarbonates (AREA)
  • Yarns And Mechanical Finishing Of Yarns Or Ropes (AREA)
  • Carpets (AREA)
CN200580001824XA 2004-01-06 2005-01-06 制备聚(对苯二甲酸1，3-丙二醇酯)纤维的方法以及用该纤维制成的地毯 Expired - Fee Related CN1906340B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US10/752,399 2004-01-06
US10/752,399 US20050147784A1 (en) 2004-01-06 2004-01-06 Process for preparing poly(trimethylene terephthalate) fiber
PCT/US2005/000774 WO2005068695A1 (en) 2004-01-06 2005-01-06 Process for preparing poly(trimethylene terephthalate) fiber

Publications (2)

Publication Number Publication Date
CN1906340A CN1906340A (zh) 2007-01-31
CN1906340B true CN1906340B (zh) 2012-07-04

Family

ID=34711624

Family Applications (1)

Application Number Title Priority Date Filing Date
CN200580001824XA Expired - Fee Related CN1906340B (zh) 2004-01-06 2005-01-06 制备聚(对苯二甲酸1，3-丙二醇酯)纤维的方法以及用该纤维制成的地毯

Country Status (9)

Country Link
US (1) US20050147784A1 (cg-RX-API-DMAC10.html)
EP (1) EP1702092A4 (cg-RX-API-DMAC10.html)
JP (1) JP2007521422A (cg-RX-API-DMAC10.html)
KR (1) KR20060123432A (cg-RX-API-DMAC10.html)
CN (1) CN1906340B (cg-RX-API-DMAC10.html)
CA (1) CA2552662A1 (cg-RX-API-DMAC10.html)
MX (1) MXPA06007683A (cg-RX-API-DMAC10.html)
TW (1) TW200602525A (cg-RX-API-DMAC10.html)
WO (1) WO2005068695A1 (cg-RX-API-DMAC10.html)

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8015726B2 (en) * 2005-06-23 2011-09-13 Whirlpool Corporation Automatic clothes dryer
US8021736B2 (en) * 2006-07-13 2011-09-20 E.I. Du Pont De Nemours And Company Substantially flame retardant-free 3GT carpet
JP5431460B2 (ja) * 2008-05-23 2014-03-05 エーリコン テクスティル ゲゼルシャフト ミット ベシュレンクテル ハフツング ウント コンパニー コマンディートゲゼルシャフト マルチフィラメント糸を溶融紡糸し、延伸しかつ巻き上げる方法並びにこの方法を実施する装置
CN101735608B (zh) * 2009-12-14 2011-07-20 杭州师范大学 吸湿性细旦/超细旦锦纶母粒、锦纶poy长丝及其制备方法
EP2659037B1 (en) * 2010-12-28 2017-07-26 E. I. du Pont de Nemours and Company Carpets prepared from yarns comprising a fluorinated polyester blend
CN102618947B (zh) * 2012-04-06 2014-08-06 缪爱国 Ptt螺旋型三维中空纤维的生产方法
CN102758604B (zh) * 2012-07-30 2014-12-17 中国石油集团川庆钻探工程有限公司长庆井下技术作业公司 压裂施工纤维的膨化技术
DE102017100488A1 (de) 2017-01-12 2018-07-12 Trützschler GmbH & Co Kommanditgesellschaft Vorrichtung und Verfahren zur Erzeugung eines texturierten Filamentes oder Garnes
DE102017100487A1 (de) * 2017-01-12 2018-07-12 Trützschler GmbH & Co Kommanditgesellschaft Vorrichtung und Verfahren zur Erzeugung eines mehrfarbigen Garnes

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5645782A (en) * 1994-06-30 1997-07-08 E. I. Du Pont De Nemours And Company Process for making poly(trimethylene terephthalate) bulked continuous filaments
CN1369026A (zh) * 1999-07-22 2002-09-11 齐默尔股份公司 不连续聚对苯二甲酸丙二酯纤维及其制造方法
US20020132116A1 (en) * 2000-11-03 2002-09-19 Dietmar Wandel Method of spinning, spooling, and stretch texturing polyester filaments and polyesters thereby produced
US20020130433A1 (en) * 2000-10-10 2002-09-19 Hwo Charles Chiu-Hsiung Spin draw process of making partially oriented yarns from polytrimethylene terephthalate
US20020147298A1 (en) * 1999-11-12 2002-10-10 Yanhui Sun Polyamide compounds
WO2003038162A1 (en) * 2001-10-31 2003-05-08 Teijin Limited Poly(trimethylene terephthalate) filament yarn and method for production thereof

Family Cites Families (60)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3525134A (en) * 1969-02-17 1970-08-25 Du Pont Yarn fluid treating apparatus
US3998042A (en) * 1972-09-26 1976-12-21 E. I. Du Pont De Nemours And Company Mixed shrinkage yarn
US6113825A (en) * 1995-05-08 2000-09-05 Shell Oil Company Process for preparing poly(trimethylene terephthalate) carpet yarn
BR9602162A (pt) * 1995-05-08 1997-12-30 Shell Int Research Processo para a preparação de fio de fibra de poli(teraftalato de trimetileno) e tapete
US6315934B1 (en) * 1995-05-08 2001-11-13 Shell Oil Company Process for preparing poly(thimethylene therephthalate) carpet yarn
US6242558B1 (en) * 1996-11-27 2001-06-05 Shell Oil Company Modified polytrimethylene terephthalate
US6093786A (en) * 1996-11-27 2000-07-25 Shell Oil Company Process for preparing polytrimethylene terephthalate
US5804115A (en) * 1996-12-13 1998-09-08 Basf Corporation One step, ready-to-tuft, mock space-dyed multifilament yarn
DE19705249A1 (de) * 1997-02-12 1998-08-13 Zimmer Ag Verfahren zur Herstellung von Polypropylenterphthalat
US6652964B1 (en) * 1997-08-18 2003-11-25 Asahi Kasei Kabushiki Kaisha Polyester fiber and fabric prepared therefrom
ATE287979T1 (de) * 1997-09-03 2005-02-15 Asahi Chemical Ind Polyesterfaser und gewebe daraus
US6284370B1 (en) * 1997-11-26 2001-09-04 Asahi Kasei Kabushiki Kaisha Polyester fiber with excellent processability and process for producing the same
US5840957A (en) * 1998-03-16 1998-11-24 E. I. Du Pont De Nemours And Company Transesterification process using lanthanum compound catalyst
US6109015A (en) * 1998-04-09 2000-08-29 Prisma Fibers, Inc. Process for making poly(trimethylene terephthalate) yarn
US5994451A (en) * 1998-04-24 1999-11-30 Shell Oil Company Polytrimethylene terephthalate composition
MXPA01003740A (es) * 1998-10-15 2004-09-10 Asahi Chemical Ind Fibra politrimetilentereftalato.
WO2000026301A1 (en) * 1998-10-30 2000-05-11 Asahi Kasei Kabushiki Kaisha Polyester resin composition and fiber
HK1044807B (zh) * 1999-03-15 2004-05-21 旭化成株式会社 聚对苯二甲酸亚丙基酯纤维及其制备方法
US6350895B1 (en) * 1999-03-26 2002-02-26 E. I. Du Pont De Nemours And Company Transesterification process using yttrium and samarium compound catalystis
US6331264B1 (en) * 1999-03-31 2001-12-18 E. I. Du Pont De Nemours And Company Low emission polymer compositions
DE69905856T2 (de) * 1999-04-22 2003-12-18 Shell Internationale Research Maatschappij B.V., Den Haag Verfahren zur Herstellung von Polytrimethylenterephthalat (PTT)
US6277947B1 (en) * 2000-04-21 2001-08-21 Shell Oil Company Process of producing polytrimethylene terephthalate (PTT)
US6512080B2 (en) * 1999-04-22 2003-01-28 Shell Oil Company Process of producing polytrimethylene terephthalate (PTT)
US6297315B1 (en) * 1999-05-11 2001-10-02 Shell Oil Company Process for preparing polytrimethylene terephthalate
TW522179B (en) * 1999-07-12 2003-03-01 Asahi Chemical Ind Polyester yarn and producing method thereof
DE19937729A1 (de) * 1999-08-10 2001-02-15 Lurgi Zimmer Ag Hochfeste Polyesterfäden und Verfahren zu deren Herstellung
JP5283298B2 (ja) * 1999-08-25 2013-09-04 イー・アイ・デュポン・ドウ・ヌムール・アンド・カンパニー ジ（１，３−プロピレングリコール）低レベル含有ポリ（トリメチレンテレフタレート）の調製
CN1214137C (zh) * 1999-09-30 2005-08-10 旭化成株式会社 聚对苯二甲酸1,3－丙二醇酯复丝
US6255442B1 (en) * 2000-02-08 2001-07-03 E. I. Du Pont De Nemours And Company Esterification process
US6353062B1 (en) * 2000-02-11 2002-03-05 E. I. Du Pont De Nemours And Company Continuous process for producing poly(trimethylene terephthalate)
MXPA02007740A (es) * 2000-02-11 2002-10-23 Du Pont Proceso continuo para la produccion de poli(trimetilen tereftalato).
US6528579B2 (en) * 2000-02-17 2003-03-04 Shell Oil Company Zero-heel polyester process
EP1183409B1 (en) * 2000-03-03 2005-11-16 E.I. Du Pont De Nemours And Company Poly(trimethylene terephthalate) yarn
US6663806B2 (en) * 2000-03-03 2003-12-16 E. I. Du Pont De Nemours And Company Processes for making poly (trimethylene terephthalate) yarns
US6287688B1 (en) * 2000-03-03 2001-09-11 E. I. Du Pont De Nemours And Company Partially oriented poly(trimethylene terephthalate) yarn
JP3856617B2 (ja) * 2000-04-04 2006-12-13 帝人ファイバー株式会社 仮撚加工用ポリエステル繊維
MY127766A (en) * 2000-04-21 2006-12-29 Shell Int Research Optimum dipropylene glycol content polytrimethylene terephthalate compositions
GB2361925A (en) * 2000-05-02 2001-11-07 Shell Internat Res Maatschhapp High temperature solid state polymerisation of poly(trimethylene terephthalate)
BR0110733A (pt) * 2000-05-12 2003-02-11 Asahi Chemical Ind Pacote de fio preorientado de tereftalato de politrimetileno e processo para sua produção
US6667003B2 (en) * 2000-05-25 2003-12-23 Zimmer A.G. Method for the manufacture of synthetic fibers from a melt mixture based on fiber forming polymers
BR0112153A (pt) * 2000-07-06 2004-02-10 Asahi Chemical Ind Bobina de fio estirado de politereftalato de trimetileno e processo para a sua produção
US20020116802A1 (en) * 2000-07-14 2002-08-29 Marc Moerman Soft and stretchable textile fabrics made from polytrimethylene terephthalate
KR100339275B1 (ko) * 2000-07-21 2002-06-03 조정래 이염성(易染性) 폴리에스테르 섬유
US6403762B1 (en) * 2000-08-21 2002-06-11 Shell Oil Company Solid state polymerization process for poly(trimethylene terephthalate) utilizing a combined crystallization/preheating step
US6752945B2 (en) * 2000-09-12 2004-06-22 E. I. Du Pont De Nemours And Company Process for making poly(trimethylene terephthalate) staple fibers
US6702864B2 (en) * 2000-10-11 2004-03-09 Shell Oil Company Process for making high stretch and elastic knitted fabrics from polytrimethylene terephthalate
US20020130437A1 (en) * 2000-11-03 2002-09-19 Dietmar Wandel Method of spinning, spooling, and stretch texturing Polyester filaments and polyesters thereby produced
US20030004301A1 (en) * 2000-11-03 2003-01-02 Dietmar Wandel Method of spinning, spooling, and stretch texturing polyester filaments and polyester filaments thereby produced
US6667096B2 (en) * 2000-11-03 2003-12-23 Zimmer A.G. Method of spinning, spooling, and stretch texturing polyester filaments and polyester filaments produced
US6740400B2 (en) * 2001-02-07 2004-05-25 Asahi Kasei Kabushiki Kaisha Poly (trimethylene terephthalate) and a process for producing the same
KR100397621B1 (ko) * 2001-05-14 2003-09-13 주식회사 효성 카페트용 폴리(트리메틸렌 테레프탈레이트) ｂｃｆ이형단면사
KR100397620B1 (ko) * 2001-05-14 2003-09-13 주식회사 효성 폴리(트리메틸렌 테레프탈레이트) 카페트의 제조방법
DE10125677B4 (de) * 2001-05-25 2013-05-16 Lurgi Zimmer Gmbh Verfahren und Vorrichtung zur Herstellung von Polytrimethylenterephthalat
TW584645B (en) * 2001-06-01 2004-04-21 Robert Lawrence Blackbourn A method for producing polytrimethylene terephthalate
US6740276B2 (en) * 2001-06-29 2004-05-25 E. I. Du Pont De Nemours And Company Process for preparing pigmented shaped articles comprising poly (trimethylene terephthalate)
EP1435367B1 (en) * 2001-10-11 2007-06-13 Asahi Kasei Fibers Corporation Pellet of polytrimethylene terephthalate and process for producing the same
US6740733B2 (en) * 2001-11-30 2004-05-25 Shell Oil Company Process and apparatus for crystallization of polytrimethylene terephthalate (PTT)
TWI287053B (en) * 2002-02-20 2007-09-21 Shell Int Research A process for making stable polytrimethylene terephthalate packages
US20030175522A1 (en) * 2002-03-13 2003-09-18 Kurian Joseph Varapadavil Poly(trimethylene terephthalate) carpets
US20030111171A1 (en) * 2002-09-09 2003-06-19 Casey Paul Karol Poly(trimethylene) terephthalate texile staple production

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5645782A (en) * 1994-06-30 1997-07-08 E. I. Du Pont De Nemours And Company Process for making poly(trimethylene terephthalate) bulked continuous filaments
CN1369026A (zh) * 1999-07-22 2002-09-11 齐默尔股份公司 不连续聚对苯二甲酸丙二酯纤维及其制造方法
US20020147298A1 (en) * 1999-11-12 2002-10-10 Yanhui Sun Polyamide compounds
US20020130433A1 (en) * 2000-10-10 2002-09-19 Hwo Charles Chiu-Hsiung Spin draw process of making partially oriented yarns from polytrimethylene terephthalate
US20020132116A1 (en) * 2000-11-03 2002-09-19 Dietmar Wandel Method of spinning, spooling, and stretch texturing polyester filaments and polyesters thereby produced
WO2003038162A1 (en) * 2001-10-31 2003-05-08 Teijin Limited Poly(trimethylene terephthalate) filament yarn and method for production thereof

Also Published As

Publication number Publication date
TW200602525A (en) 2006-01-16
EP1702092A1 (en) 2006-09-20
WO2005068695A1 (en) 2005-07-28
JP2007521422A (ja) 2007-08-02
CA2552662A1 (en) 2005-07-28
MXPA06007683A (es) 2006-09-01
CN1906340A (zh) 2007-01-31
KR20060123432A (ko) 2006-12-01
US20050147784A1 (en) 2005-07-07
EP1702092A4 (en) 2007-12-05

Similar Documents

Publication Publication Date Title
CN100453714C (zh) 双组分纤维的高速纺丝方法
JP5247860B2 (ja) ２成分繊維の高速紡糸方法
CN116716670B (zh) 一种直接织造用涤纶预取向丝及其制备方法
JP4741161B2 (ja) 溶融紡糸材料をコンディショニングする方法および装置
CN102517660A (zh) 涤纶超棉柔绒纤维的制造方法
CN104213228A (zh) 一种粗旦有光高强尼龙6全牵伸纤维的生产工艺
CN102418169B (zh) 一种海岛纤维及其制备方法
CN102586905A (zh) 热牵伸型高特纶预取向长丝纺丝卷绕联合制造工艺
CN1187485C (zh) 不连续聚对苯二甲酸丙二酯纤维及其制造方法
US20050147784A1 (en) Process for preparing poly(trimethylene terephthalate) fiber
CN1338011A (zh) 聚酯基混纤丝的制造方法
CN104562250B (zh) 一种多孔微细旦尼龙6三异纤维及其制备方法与应用
TW568963B (en) Method for producing polyester fiber suitable for a draw-texturing raw yarn
US7070723B2 (en) Method for spin-drawing of melt-spun yarns
JP2004124338A (ja) 細デニールポリエステル中空予備延伸糸の製造方法及びその方法から製造された細デニールポリエステル中空予備延伸糸
CN1584136B (zh) 生产细纤维的方法
JP5964437B2 (ja) ポリ（トリメチレンアリーレート）繊維、その作製方法、およびそれから作製された布地
CN100408733C (zh) 聚酰胺纱制造工艺和聚酰胺纱
HACIOĞULLARI et al. A REVIEW ON LABORATORY SCALE MACHINES SUPPORTING R&D STUDIES USED IN FILAMENT YARN TECHNOLOGY.
JP2014526621A (ja) ポリ（トリメチレンアリーレート）繊維、その作製方法、およびそれから作製された布地
CN103930602A (zh) 用于制备包含聚(对苯二甲酸丙二醇酯)的双组分纤维的方法
US20020132116A1 (en) Method of spinning, spooling, and stretch texturing polyester filaments and polyesters thereby produced
CN118516774A (zh) 一种高强高模低缩丝生产方法
Hacıoğulları et al. FİLAMENT İPLİK TEKNOLOJİSİNDE KULLANILAN VE AR-GE ÇALIŞMALARINI DESTEKLEYEN LABORATUVAR ÖLÇEKLİ MAKİNALAR ÜZERİNE BİR İNCELEME
HK1053155B (en) Method for high-speed spinning of bicomponent fibers

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
CF01 Termination of patent right due to non-payment of annual fee
CF01 Termination of patent right due to non-payment of annual fee

Granted publication date: 20120704

Termination date: 20200106