CN1896140A - Material for producing workmanship by human bone phosphate and its production - Google Patents
Material for producing workmanship by human bone phosphate and its production Download PDFInfo
- Publication number
- CN1896140A CN1896140A CN 200510129934 CN200510129934A CN1896140A CN 1896140 A CN1896140 A CN 1896140A CN 200510129934 CN200510129934 CN 200510129934 CN 200510129934 A CN200510129934 A CN 200510129934A CN 1896140 A CN1896140 A CN 1896140A
- Authority
- CN
- China
- Prior art keywords
- dead
- ashes
- adopts
- manufacture technology
- mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A material for handicraft from human bone phosphate and its production are disclosed. The material consists of unsaturated polyester resin, human bone phosphate, anyone selected from lime or burnt kaolin, improver and curing agent. The process is carried out by making mould, sizing, preparing mould, forming and trimming made-up article to obtain finished product. It is convenient and has excellent practical function and art value.
Description
Technical field:
The present invention relates to a kind of method that adopts the material of ashes of the dead manufacture technology product and adopt these material manufacture technology product.
Background technology:
At present, to adopt cremation mostly after the people is dead, afterwards again by relatives select the graveyard with its placement of cinerary casket in the graveyard, whenever festa, relatives go to hold a memorial ceremony in the graveyard.But like this can be As time goes on, the graveyard is more and more, causes the soil by the phenomenon that the graveyard occupies in a large number on the contrary, causes the serious waste in soil.And at this situation, country does not have good terms of settlement now yet.Simultaneously because the stationarity of graveyard, whenever festa, again because of relatives far away from alien land, hold a memorial ceremony for the graveyard that can not arrive in the very nick of time, and makes relatives be difficult to free the feelings of cherishing the memory of to the dead.Sometimes can see also that having the people that the relatives' that die bone ash is put into cinerary casket carries, but cause many inconvenience to others like this.
Summary of the invention:
The object of the present invention is to provide a kind of novel material that adopts ashes of the dead manufacture technology product.
Another object of the present invention is to provide a kind of method that adopts these material manufacture technology product.
First purpose of the present invention is implemented by following technical scheme: adopt the material of ashes of the dead manufacture technology product, include the following composition in parts by weight:
Artwork unsaturated polyester resin: 60-150 part;
Any of ashes of the dead and stone flour or calcined kaolin: 30 parts-75 parts, wherein by weight ratio, ashes of the dead: stone flour or calcined kaolin are (10-100): (90-0);
Promotor is 0.05-0.15 part;
Solidifying agent is 0.01-0.1 part.
Adopt the material of ashes of the dead manufacture technology product, its preferred value is as follows: in the described following composition of parts by weight:
Artwork unsaturated polyester resin: 90-120 part;
Any of ashes of the dead and stone flour or calcined kaolin: 45 parts-60 parts, wherein by weight ratio, ashes of the dead: stone flour or calcined kaolin are (10-100): (90-0);
Promotor: 0.08-0.12 part;
Solidifying agent: 0.02-0.08 part.
Described stone flour is imitative beautiful powder, marble flour, agate powder, titanium dioxide, talcum powder, porcelain powder.
Described artwork unsaturated polyester resin is crystal resin, agate resin, artificial Dali resin.
Described promotor is any of metallic naphthenate, isocaprylic acid metal-salt, cobaltous linoleate, xylidene(s), methyl ethyl diketone, lauryl mercaptan, xylidene(s) or methyl ethyl diketone.
Described metallic naphthenate is any of cobalt naphthenate, manganese naphthenate, zinc naphthenate, naphthenic acid vanadium, and the isocaprylic acid metal-salt is a cobalt iso-octoate, isocaprylic acid cadmium, isocaprylic acid potassium, isocaprylic acid tin, any of calcium iso-octoate.
Described solidifying agent is ketone peroxide class or dibenzoyl peroxide.
Described ketone peroxide class is methylethyl ketone peroxide, cyclohexanone peroxide, methylethyl ketone peroxide.
Another object of the present invention is implemented by following technical scheme: a kind of method that adopts ashes of the dead manufacture technology product, and it includes following steps: (1), Mold Making: manufacture inner membrance-rubber mold, and external mold-gypsum mold; (2), pulping process; (3), prepare mould; (4), moulding process; (5), repaired biscuit is made finished product;
(1), Mold Making: manufacture inner membrance-rubber mold, and external mold-gypsum mold: sample is placed on the plank, with brush mold glue is brushed on sample, brush and treat for one time to brush the 2nd time behind its complete drying, brush successively 3-7 time, the sample that rolls that does not stop makes glue even, finishes brush coating work in the most handy 3-7 days; Outer treat to take off after the gypsum sets with the protection of two halves calcium plaster at it behind the complete drying, then adventitia-gypsum mold is promptly made, will become the glue of mould to take off again and be inner membrance-rubber mold.
Described (2) pulping process: be described stone flour to be joined in the described unsaturated polyester resin in as above ratio mix, stir; Add described promotor in ratio as mentioned above again, stir slurry standby;
(3), prepare mould: the in type anhydrite overcoat of die needed usefulness is surrounded, fix adventitia-gypsum mold; The internal surface of cleaning inner membrance-rubber mold reaches and do not have other foreign material, and is ready;
(4), moulding process: measure described standby slurry with container, add described solidifying agent in as above ratio, make mixture slurry, after described mixture slurry mixed, rapidly a spot of described mixture slurry is poured in inner membrance-rubber mold of having got ready, gently rub described rubber mold rapidly, full described mixture slurry is filled in each corner in the described rubber mold that makes, to fill the described rubber mold of full described mixture slurry again and put into gypsum mold, pour remaining described mixture slurry afterwards again into, the rotation gypsum mold makes the slurry in the rubber mold evenly fully fill each corner; Treat its drying about 10-20 minute, taking off gypsum and rubber mold is that moulding is finished.
Choose the color paste toning of pigment of all kinds or dyestuff; Put into the described mixture slurry that step (4) prepares with mixing up the pigment of all kinds of look or the mill base of dyestuff, mix, pour into again in the described rubber mold.
Choose the color paste toning of pigment of all kinds or dyestuff; Put into the described mixture slurry that step (4) prepares with mixing up the pigment of all kinds of look or the mill base of dyestuff, mix, pour into again in the described rubber mold.
Step (5) repaired biscuit is made after the finished product, chosen the color paste toning of pigment of all kinds or dyestuff, the mill base of described pigment of all kinds or dyestuff is evenly sprayed at the finished product outside surface.
After step (4) moulding, carry out fill process again, promptly measure required described standby slurry by the volume in the in type product, add the as above described solidifying agent of proportioning, uniform mixing is a mixture slurry, pours into rapidly in the in type product, keep the moulding product opening part vertically upward, be placed on stable place and leave standstill, to the slurry curing of filling, filling is finished.
Choose the color paste toning of pigment of all kinds or seven material; The mixture slurry of the mill base that mixes up the pigment of all kinds of look or dyestuff being put into fill process gets final product.
Fill ashes of the dead in the finished product after described moulding.
The described finished product of making is put into potassium permanganate solution, take out rapidly, will wipe attached to the potassium permanganate solution on the finished surface of making, described finished product is a finished product modelled after an antique.
The invention has the advantages that: because after cremating at present, by the arrangement of present most of people to relatives, still adopt the graveyard to deposit the form of bone ash, brought great inconvenience so not only for annual sweeping a grave, simultaneously for alien away from relatives, feelings to dead relatives' miss, but can not arrive in the very nick of time and hold a memorial ceremony for before relatives' tomb, also there are simultaneously graveyard and arable land to strive the problem on ground, and the invention solves above-mentioned existing problem, not only the relatives' that pass away bone ash can be made artwork to carry, also the relatives' that pass away bone ash can be made workmanship, with filling remaining bone ash in it, like this, where not only walk, can carry relatives' bone ash easily, just as relatives not away from oneself, the same at one's side at oneself can not bring inconvenience to other people simultaneously yet all the time.And greatly reduce the expense of funeral and interment.
Embodiment:
Embodiment 1: adopt the material of ashes of the dead manufacture technology product, include following composition: crystal resin: 600 grams; Ashes of the dead 300 grams, cobalt naphthenate 0.5 gram, methylethyl ketone peroxide 0.1 gram.
Adopt the method for above-mentioned materials manufacture technology product, it includes following steps: (1), Mold Making: manufacture inner membrance-silicon rubber mould, and external mold-gypsum mold; (2), pulping process; (3), prepare mould; (4), choose the toning of pigment of all kinds or dyestuff; (5), moulding process; (6) fill process; (7), repaired biscuit is made finished product;
(1), Mold Making: manufacture inner membrance-silicon rubber mould, and external mold-gypsum mold: sample is placed on the plank, with brush mold glue-silicon rubber is brushed on sample, brush and treat for one time to brush the 2nd time behind its complete drying, brush successively 3-7 time, the sample that rolls that does not stop makes glue even, finishes brush coating work in the most handy 3-7 days; Outer treat to take off after the gypsum sets with the protection of two halves calcium plaster at it behind the complete drying, then adventitia-gypsum mold is promptly made, will become the glue of mould to take off again and be inner membrance-rubber mold.
(2) pulping process: be ashes of the dead to be joined in the described water fat resin in as above ratio mix, stir; Add promotor cobalt naphthenate 0.5 gram in as above ratio again, stir slurry standby;
(3), prepare mould: the in type anhydrite overcoat of die needed usefulness is surrounded, fix adventitia-gypsum mold; The internal surface of cleaning inner membrance-rubber mold reaches and do not have other foreign material, and is ready;
(4), choose the toning of pigment of all kinds or dyestuff;
(5), moulding process: measure above-mentioned standby slurry with container, add solidifying agent methylethyl ketone peroxide 0.1 gram according to the above ratio, make mixture slurry, the pigment of all kinds or the dyestuff that mix up look are put into mixture slurry, after mixing, rapidly a spot of mixture slurry is poured in inner membrance-rubber mold of having got ready, gently rub rubber mold rapidly, full mixture slurry is filled in each corner in the rubber mold that makes, to fill the rubber mold of full mixture slurry again and put into gypsum mold, pour remaining mixture slurry afterwards again into, the rotation gypsum mold makes the slurry in the rubber mold evenly fully fill each corner; Treat its drying about 10-20 minute, taking off gypsum and rubber mold is that moulding is finished.
(6), fill process: fill ashes of the dead in the finished product after moulding.
(7), repaired biscuit is made finished product.
Embodiment 2: adopt the material of ashes of the dead manufacture technology product, include following composition: crystal resin: 1500 grams; Ashes of the dead 75 grams, imitative beautiful powder 675 grams, manganese naphthenate 1.5 grams, cyclohexanone peroxide 1 gram.
Adopt the method for above-mentioned materials manufacture technology product, it includes following steps: (1), Mold Making: manufacture inner membrance-rubber mold, and external mold-gypsum mold; (2), pulping process; (3), prepare mould; (4), choose the toning of pigment of all kinds or dyestuff; (5), moulding process; (6), fill process (7), repaired biscuit are made finished product.
(1), Mold Making: manufacture inner membrance-rubber mold, and external mold-gypsum mold: sample is placed on the plank, with brush mold glue is brushed on sample, brush and treat for one time to brush the 2nd time behind its complete drying, brush successively 3-7 time, the sample that rolls that does not stop makes glue even, finishes brush coating work in the most handy 3-7 days; Outer treat to take off after the gypsum sets with the protection of two halves calcium plaster at it behind the complete drying, then adventitia-gypsum mold is promptly made, will become the glue of mould to take off again and be inner membrance-rubber mold.
(2) pulping process: be ashes of the dead and imitative beautiful powder to be joined in the water fat resin in as above ratio mix, stir; Add promotor manganese naphthenate 1.5 grams in as above ratio again, stir slurry standby;
(3), prepare mould: the in type anhydrite overcoat of die needed usefulness is surrounded, fix adventitia-gypsum mold; The internal surface of cleaning inner membrance-rubber mold reaches and do not have other foreign material, and is ready;
(4), choose the toning of pigment of all kinds or dyestuff;
(5), moulding process: measure above-mentioned standby slurry with container, add solidifying agent cyclohexanone peroxide 1 gram according to the above ratio, make mixture slurry, after mixing, rapidly a spot of mixture slurry is poured in inner membrance-rubber mold of having got ready, gently rub rubber mold rapidly, full mixture slurry is filled in each corner in the rubber mold that makes, to fill the rubber mold of full mixture slurry again and put into gypsum mold, pour remaining mixture slurry afterwards again into, the rotation gypsum mold makes the slurry in the rubber mold evenly fully fill each corner; Treat its drying about 10-20 minute, taking off gypsum and rubber mold is that moulding is finished.
After step (4) moulding, carry out fill process again, promptly measure required standby slurry by the volume in the in type product, add the as above solidifying agent of proportioning, uniform mixing is a mixture slurry, chooses the toning of pigment of all kinds or dyestuff; Get final product mixing up the pigment of all kinds of look or mixture slurry that dyestuff is put into fill process.Mixture slurry is poured into rapidly in the in type product, kept the moulding product opening part vertically upward, be placed on stable place and leave standstill, extremely the slurry of filling solidifies, and filling is finished.Repaired biscuit is made finished product.
Embodiment 3: adopt the material of ashes of the dead manufacture technology product, include following composition: artificial Dali resin: 900 grams; Ashes of the dead 45 grams, marble flour 405 grams, zinc naphthenate 0.8 gram, methylethyl ketone peroxide 0.2 gram.
Adopt the method for above-mentioned materials manufacture technology product, it includes following steps: (1), Mold Making: manufacture inner membrance-silicon rubber mould, and external mold-gypsum mold; (2), pulping process; (3), prepare mould; (4), moulding process; (5), repaired biscuit is made finished product;
(1), Mold Making: manufacture inner membrance-silicon rubber mould, and external mold-gypsum mold: sample is placed on the plank, with brush mold glue is brushed on sample, brush and treat for one time to brush the 2nd time behind its complete drying, brush successively 3-7 time, the sample that rolls that does not stop makes glue even, finishes brush coating work in the most handy 3-7 days; Outer treat to take off after the gypsum sets with the protection of two halves calcium plaster at it behind the complete drying, then adventitia-gypsum mold is promptly made, will become the glue of mould to take off again and be inner membrance-rubber mold.
(2) pulping process: be ashes of the dead to be joined in the described water fat resin in as above ratio mix, stir; Add promotor zinc naphthenate 0.8 gram in as above ratio again, stir slurry standby;
(3), prepare mould: the in type anhydrite overcoat of die needed usefulness is surrounded, fix adventitia-gypsum mold; The internal surface of cleaning inner membrance-rubber mold reaches and do not have other foreign material, and is ready;
(4), moulding process: measure above-mentioned standby slurry with container, add solidifying agent methylethyl ketone peroxide 0.2 gram according to the above ratio, make mixture slurry, after mixing, rapidly a spot of mixture slurry is poured in inner membrance-rubber mold of having got ready, gently rub rubber mold rapidly, full mixture slurry is filled in each corner in the rubber mold that makes, to fill the rubber mold of full mixture slurry again and put into gypsum mold, pour remaining mixture slurry afterwards again into, the rotation gypsum mold makes the slurry in the rubber mold evenly fully fill each corner; Treat its drying about 10-20 minute, taking off gypsum and rubber mold is that moulding is finished.Fill ashes of the dead in the finished product after moulding.
Step (5) repaired biscuit is made after the finished product, chosen the toning of pigment of all kinds or dyestuff, pigment of all kinds or dyestuff are evenly sprayed at the finished product outside surface.
Embodiment 4: adopt the material of ashes of the dead manufacture technology product, include following composition: the agate resin: 1050 grams; Ashes of the dead 250 grams, agate powder 250 grams, naphthenic acid vanadium 1.0 grams, methylethylketone 0.6 gram.
Adopt the method for above-mentioned materials manufacture technology product, it includes following steps: (1), Mold Making: manufacture inner membrance-silicon rubber mould, and external mold-gypsum mold; (2), pulping process; (3), prepare mould; (4), moulding process; (5), fill process; (6) repaired biscuit is made finished product; (7); Make the technology of finished product modelled after an antique;
(1), Mold Making: manufacture inner membrance-silicon rubber mould, and external mold-gypsum mold: sample is placed on the plank, with brush mold glue is brushed on sample, brush and treat for one time to brush the 2nd time behind its complete drying, brush successively 3-7 time, the sample that rolls that does not stop makes glue even, finishes brush coating work in the most handy 3-7 days; Outer treat to take off after the gypsum sets with the protection of two halves calcium plaster at it behind the complete drying, then adventitia-gypsum mold is promptly made, will become the glue of mould to take off again and be inner membrance-silicon rubber mould.
(2) pulping process: be that ashes of the dead 250 grams and agate powder 250 grams are joined mixing in agate resin 1050 grams, stir; Add promotor naphthenic acid vanadium 1.0 grams in as above ratio again, stir slurry standby;
(3), prepare mould: the in type anhydrite overcoat of die needed usefulness is surrounded, fix adventitia-gypsum mold; The internal surface of cleaning inner membrance-rubber mold reaches and do not have other foreign material, and is ready;
(4), moulding process: measure above-mentioned standby slurry with container, add curing agent ethyl methyl ketone 0.6 gram according to the above ratio, make mixture slurry, after mixing, rapidly a spot of mixture slurry is poured in inner membrance-silicon rubber mould of having got ready, gently rub rubber mold rapidly, full mixture slurry is filled in each corner in the rubber mold that makes, to fill the rubber mold of full mixture slurry again and put into gypsum mold, pour remaining mixture slurry afterwards again into, the rotation gypsum mold makes the slurry in the rubber mold evenly fully fill each corner; Treat its drying about 10-20 minute, taking off gypsum and rubber mold is that moulding is finished.Fill ashes of the dead in the finished product after moulding.
(6), repaired biscuit is made finished product;
(7), make the technology of finished product modelled after an antique: the finished product of making is put into potassium permanganate solution, take out rapidly, will wipe attached to the potassium permanganate solution on the finished surface of making, finished product is a finished product modelled after an antique.
Embodiment 5: adopt the material of ashes of the dead manufacture technology product, include following composition: crystal resin: 1200 grams; Ashes of the dead 300 grams, porcelain powder 300 grams, cobaltous linoleate 1.2 grams, methylethyl ketone peroxide 0.6 gram.Manufacture technology such as above-mentioned arbitrary technology.
Embodiment 6: adopt the material of ashes of the dead manufacture technology product, include following composition: crystal resin: 1000 grams; Ashes of the dead 200 grams, calcined kaolin 300 grams, lauryl mercaptan 1.0 grams, methylethyl ketone peroxide 0.2 gram.Manufacture technology such as above-mentioned arbitrary technology.
Embodiment 7: adopt the material of ashes of the dead manufacture technology product, include following composition: crystal resin: 1000 grams; Ashes of the dead 200 grams, titanium dioxide 300 grams, 2-ethylhexoate, as cobalt iso-octoate, isocaprylic acid cadmium, isocaprylic acid potassium, isocaprylic acid tin, any of calcium iso-octoate are 1.0 grams, methylethyl ketone peroxide 0.2 gram.Manufacture technology such as above-mentioned arbitrary technology.
Embodiment 8: adopt the material of ashes of the dead manufacture technology product, include following composition: crystal resin: 950 grams; Ashes of the dead 200 grams, talcum powder 300 grams, xylidene(s) or methyl ethyl diketone are 0.8 gram, dibenzoyl peroxide 0.4 gram.Manufacture technology such as above-mentioned arbitrary technology.
Claims (16)
1, adopt the material of ashes of the dead manufacture technology product, it is characterized in that it includes the following composition in parts by weight:
Artwork unsaturated polyester resin: 60-150 part;
Any of ashes of the dead and stone flour or calcined kaolin: 30 parts-75 parts, wherein by weight ratio, ashes of the dead: stone flour or calcined kaolin are (10-100): (90-0);
Promotor is 0.05-0.15 part;
Solidifying agent is 0.01-0.1 part.
2, a kind of material that adopts ashes of the dead manufacture technology product according to claim 1 is characterized in that, in the described following composition of parts by weight:
Artwork unsaturated polyester resin: 90-120 part;
Any of ashes of the dead and stone flour or calcined kaolin: 45 parts-60 parts, wherein by weight ratio, ashes of the dead: stone flour or calcined kaolin are (10-100): (90-0);
Promotor: 0.08-0.12 part;
Solidifying agent: 0.02-0.08 part.
3, a kind of material that adopts ashes of the dead manufacture technology product according to claim 1 and 2 is characterized in that, described stone flour is imitative beautiful powder, marble flour, agate powder, titanium dioxide, talcum powder, porcelain powder.
4, a kind of material that adopts ashes of the dead manufacture technology product according to claim 1 and 2 is characterized in that, described artwork unsaturated polyester resin is crystal resin, agate resin, artificial Dali resin.
5, a kind of material that adopts ashes of the dead manufacture technology product according to claim 1 and 2 is characterized in that, described promotor is any of metallic naphthenate, isocaprylic acid metal-salt, cobaltous linoleate, xylidene(s), methyl ethyl diketone or lauryl mercaptan.
6, a kind of material that adopts ashes of the dead manufacture technology product according to claim 1 and 2, it is characterized in that, described metallic naphthenate is any of cobalt naphthenate, manganese naphthenate, zinc naphthenate, naphthenic acid vanadium, the isocaprylic acid metal-salt is a cobalt iso-octoate, the isocaprylic acid cadmium, isocaprylic acid potassium, isocaprylic acid tin, any of calcium iso-octoate.
7, a kind of material that adopts ashes of the dead manufacture technology product according to claim 1 and 2 is characterized in that, described solidifying agent is ketone peroxide class or dibenzoyl peroxide.
8, a kind of material that adopts ashes of the dead manufacture technology product according to claim 7 is characterized in that, described ketone peroxide class is methylethyl ketone peroxide, cyclohexanone peroxide, methylethyl ketone peroxide.
9, as claim 1 to 3 arbitrary as described in a kind of method that adopts ashes of the dead manufacture technology product, it includes following steps: (1), Mold Making: manufacture inner membrance one rubber mold and external mold one gypsum mold; (2), pulping process; (3), prepare mould; (4), moulding process; (5), repaired biscuit is made finished product;
It is characterized in that,
Described (2) pulping process: be described stone flour to be joined in the described unsaturated polyester resin in as above ratio mix, stir; Add described promotor in ratio as mentioned above again, stir slurry standby;
(4), moulding process: measure described standby slurry with container, add described solidifying agent in as above ratio, make mixture slurry, after described mixture slurry mixed, rapidly a spot of described mixture slurry is poured in the rubber mold of having got ready, gently rub described rubber mold rapidly, full described mixture slurry is filled in each corner in the described rubber mold that makes, to fill the described rubber mold of full described mixture slurry again and put into gypsum mold, pour remaining described mixture slurry afterwards again into, the rotation gypsum mold makes the slurry in the rubber mold evenly fully fill each corner; Treat its drying about 10-20 minute, taking off gypsum and rubber mold is that moulding is finished.
10, a kind of method that adopts ashes of the dead manufacture technology product according to claim 9 is characterized in that, chooses the mill base of pigment of all kinds or dyestuff; Put into the described mixture slurry that step (4) prepares with mixing up the pigment of all kinds of look or the mill base of dyestuff, mix, pour into again in the described rubber mold.
11, a kind of method that adopts ashes of the dead manufacture technology product according to claim 9 is characterized in that, chooses the color paste toning of pigment of all kinds or dyestuff; Put into the described mixture slurry that step (4) prepares with mixing up the pigment described of all kinds of look or the mill base of dyestuff, mix, pour into again in the described rubber mold.
12, a kind of method that adopts ashes of the dead manufacture technology product according to claim 9, it is characterized in that, step (5) repaired biscuit is made after the finished product, chosen the mill base of pigment of all kinds or dyestuff, the mill base of described pigment of all kinds or dyestuff is evenly sprayed at the finished product outside surface.
13, a kind of method that adopts ashes of the dead manufacture technology product according to claim 9, it is characterized in that, after step (4) moulding, carry out fill process again, promptly measure required described standby slurry by the volume in the in type product, add the as above described solidifying agent of proportioning, uniform mixing is a mixture slurry, pours into rapidly in the in type product, keep the moulding product opening part vertically upward, be placed on stable place and leave standstill, to the slurry curing of filling, filling is finished.
14, a kind of method that adopts ashes of the dead manufacture technology product according to claim 13 is characterized in that, chooses the color paste toning of pigment of all kinds or dyestuff; The mixture slurry of the mill base that mixes up the pigment of all kinds of look or dyestuff being put into fill process gets final product.
15, a kind of method that adopts ashes of the dead manufacture technology product according to claim 9 is characterized in that, fills ashes of the dead in the finished product after described moulding.
16, according to the arbitrary described a kind of method that adopts ashes of the dead manufacture technology product of claim 9-15, it is characterized in that, the described finished product of making is put into potassium permanganate solution, take out rapidly, to wipe attached to the potassium permanganate solution on the finished surface of making, described finished product is a finished product modelled after an antique.