CN101775878A - Cement tile and manufacturing method thereof - Google Patents
Cement tile and manufacturing method thereof Download PDFInfo
- Publication number
- CN101775878A CN101775878A CN201010046567A CN201010046567A CN101775878A CN 101775878 A CN101775878 A CN 101775878A CN 201010046567 A CN201010046567 A CN 201010046567A CN 201010046567 A CN201010046567 A CN 201010046567A CN 101775878 A CN101775878 A CN 101775878A
- Authority
- CN
- China
- Prior art keywords
- cement
- flyash
- power plant
- tile
- river sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cement tile and a manufacturing method thereof. The cement tile is prepared with the following raw materials in parts by weight: 20-40 of cement, 0-60 of river sand, 10-30 of fly ash, 10-30 of limestone powder, 5-15 of waste ash of biological power plants, 0-15 of slag, 15-25 of construction waste, 30-60 of ballast and 0-0.05 of water repellent. The manufacturing method comprises agitation of raw materials, rolling, pressure filtration, static keeping, blank stacking, natural curing, spraying and painting. The invention has the advantages of simple manufacturing method, low costs of raw materials, high cement tile density, high strength and smooth surface.
Description
Technical field
The present invention relates to building material field, specifically is a kind of cement tile and manufacture method thereof.
Technical field
Along with the progress of society and the fast development of builing industry, clay tile is to be eliminated gradually; The potter's clay glazed roof tile and the cement tile of Chu Xianing thereupon, become new substitute gradually, the potter's clay glazed roof tile cost an arm and a leg because of it, are difficult to generally use, previous cement tile is because of its rough surface, fail generally to use, along with development of technology, cement tile of today has become main watt producing building material, form through the press filtration of high-quality mould by high pressure when it is main, color is various, and service life is long, low cost.Be applicable to common house owed by a citizen, also be applicable to the waterproof and heat-insulating of high-grade villa and highrise building.
Summary of the invention
The invention provides a kind of cement tile and manufacture method thereof, its manufacture method is simple, and cost of material is low, and cement tile density is big, intensity is high, the characteristics of surfacing.
Technical scheme of the present invention is:
A kind of cement tile is characterized in that: each raw material components is by weight than being: cement 20-40, river sand 0-60, flyash 0-30, agstone 0-30, biological power plant residual dust 0-15, slag 0-15, building waste 0-25, rock ballast 0-60, waterproof agent 0-0.05.
Described cement tile is characterized in that: described each raw material components is by weight than being: cement 20-40, flyash 10-30, agstone 10-30, biological power plant residual dust 5-15, slag 5-15, building waste 15-25, rock ballast 30-60, waterproof agent 0-0.05.
Described cement tile is characterized in that: described each raw material components is by weight than for one of following:
(1), cement 28, river sand 24, agstone 12, rock ballast 36;
(2), cement 32, flyash 10, rock ballast 40, biological power plant residual dust 5, slag 13;
(3), cement 28, river sand 10, rock ballast 24, agstone 10, biological power plant residual dust 8, building waste 20;
(4), cement 24, flyash 16, river sand 48, biological power plant residual dust 12, waterproof agent 0.04.
Described cement tile is characterized in that: described building waste comprises the discarded concrete that is produced in construction, the work progress, useless brick and tile the like waste; The fineness modulus of described river sand is 2.3-3.0, mud content＜3%; Described rock ballast is the discarded leftover pieces after the break process of quarry; Described flyash is selected above (the comprising the III level) flyash of III level for use; Described waterproof agent is selected silicone based waterproof agent for use; The ashes that biological power plant residual dust produces when making a living gasification substance.
The manufacture method of described cement tile is characterized in that:
(1), with each raw material components by weight than mixing, add water and stir and mix, stir;
(2), the mass transport that stirs is carried out pressure filtration molding under 10-12MPa to mould cavity, be lined with filter screen on the bed die of mould, and be distributed with uniform drain hole;
(3), unbaked tile that pressure filtration molding is obtained deviates from die cavity, rested 20-28 hour, sign indicating number base stacking then, natural curing, spraying colouring, finished product.
Advantage of the present invention and effect are as follows:
The present invention adopts a large amount of trade wastes, building waste (flyash, biological power plant residual dust) and genius loci resource (cinder, rock ballast, stone flour) to mix production, transform the conventional production equipment weak point, satisfy volume and use above resource to produce qualified cement tile, and reduce product cost in the 30-70% scope.In activities,, utilize high efficiency water reducing agent to improve the mortar flowability according to the character characteristics and the requirement of mixing the different proportion waste resource.In order to solve the trap drainage of slip better, the filter drain hole that processing is evenly distributed to the unbaked tile bed die is with the washmarking and the pore of the unbaked tile outward appearance appearance after the solution moulding.Owing to solved the difficult problem that exists in the novel concrete watt forming process, the cement tile quality of being made can both meet the industry standard requirement, and the prices of raw and semifnished materials are low, and manufacturing process is simple.
The specific embodiment
Embodiment 1
The prescription of cement tile: cement 28%, river sand 24%, agstone 12%, rock ballast 36%.
Embodiment 2
The prescription of cement tile: cement 32%, flyash 10%, rock ballast 40%, biological power plant residual dust 5%, slag 13%.
Embodiment 3
The prescription of cement tile: cement 28%, river sand 10%, rock ballast 24%, agstone 10%, biological power plant residual dust 8%, building waste 20%.
Embodiment 4
The prescription of cement tile: cement 24%, flyash 16%, river sand 48%, biological power plant residual dust 12%, waterproof agent 0.04%.
Building waste comprises the dregs, the spoir that are produced in construction, the work progress, abandons material, surplus mud and other discarded objects;
The fineness modulus of river sand is 2.3-3.0, mud content＜3%;
Rock ballast is the discarded leftover pieces after the break process of quarry;
Flyash is selected the above flyash of III level for use;
Waterproof agent is selected the organosilicon waterproof agent for building for use.
The manufacture method of cement tile:
(1), with each raw material components by weight than mixing, add water and stir the road wheel of going forward side by side and grind;
(2), the mass transport that stirs is carried out pressure filtration molding under 10-12MPa to mould cavity, be lined with filter screen on the bed die of mould, and be distributed with uniform drain hole;
(3), unbaked tile that pressure filtration molding is obtained deviates from die cavity, rested 20-28 hour, sign indicating number base stacking then, natural curing, spraying colouring, finished product.
The embodiment performance sees the following form:
Claims (5)
1. cement tile, it is characterized in that: each raw material components is by weight than being: cement 20-40, river sand 0-60, flyash 0-30, agstone 0-30, biological power plant residual dust 0-15, slag 0-15, building waste 0-25, rock ballast 0-60, waterproof agent 0-0.05.
2. cement tile according to claim 1 is characterized in that: described each raw material components is by weight than being: cement 20-40, flyash 10-30, agstone 10-30, biological power plant residual dust 5-15, slag 5-15, building waste 15-25, rock ballast 30-60, waterproof agent 0-0.05.
3. cement tile according to claim 1 is characterized in that: described each raw material components is by weight than for one of following:
(1), cement 28, river sand 24, agstone 12, rock ballast 36;
(2), cement 32, flyash 10, rock ballast 40, biological power plant residual dust 5, slag 13;
(3), cement 28, river sand 10, rock ballast 24, agstone 10, biological power plant residual dust 8, building waste 20;
(4), cement 24, flyash 16, river sand 48, biological power plant residual dust 12, waterproof agent 0.04.
4. cement tile according to claim 1 is characterized in that: described building waste comprises the discarded concrete that is produced in construction, the work progress, useless brick and tile the like waste; The fineness modulus of described river sand is 2.3-3.0, mud content＜3%; Described rock ballast is the discarded leftover pieces after the break process of quarry; Described flyash is selected above (the comprising the III level) flyash of III level for use; Described waterproof agent is selected silicone based waterproof agent for use; The ashes that biological power plant residual dust produces when making a living gasification substance.
5. the manufacture method of cement tile according to claim 1 is characterized in that:
(1), with each raw material components by weight than mixing, add water and stir and mix, stir;
(2), the mass transport that stirs is carried out pressure filtration molding under 10-12MPa to mould cavity, be lined with filter screen on the bed die of mould, and be distributed with uniform drain hole;
(3), unbaked tile that pressure filtration molding is obtained deviates from die cavity, rested 20-28 hour, sign indicating number base stacking then, natural curing, spraying colouring, finished product.