CN107098653A - A kind of environment-friendlyroad road face brick and preparation method thereof - Google Patents
A kind of environment-friendlyroad road face brick and preparation method thereof Download PDFInfo
- Publication number
- CN107098653A CN107098653A CN201710410308.7A CN201710410308A CN107098653A CN 107098653 A CN107098653 A CN 107098653A CN 201710410308 A CN201710410308 A CN 201710410308A CN 107098653 A CN107098653 A CN 107098653A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- road face
- face brick
- friendlyroad road
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of environment-friendlyroad road face brick, it is characterised in that includes the raw material of following parts by weight：15 25 parts of ceramic waste residue, 20 30 parts of slag, 15 25 parts of gangue, 10 20 parts of discarded concrete, 15 25 parts of volcanic ash, 5 15 parts of nano silicon, 20 30 parts of cement, 5 10 parts of improved additives, 37 parts of taste removal additive.Wear-resisting anti-aging, the sterile tasteless, safety and environmental protection of environment-friendlyroad road face brick, good water permeability, the ultraviolet absorption ability of the present invention is stronger, preparing raw material makes full use of industrial waste, saves natural resources, reduces environmental pollution simultaneously, and preparation method is simple, with higher practical value and good application prospect.
Description
Technical field
The present invention relates to pavior brick field of material technology, and in particular to a kind of environment-friendlyroad road face brick and preparation method thereof.
Background technology
Slag is the accessory substance in steelmaking process, and its discharge capacity is big, accounts for the 15-20% of output of steel.With economic high speed
Development, resource rational utilization, environmental protection consciousness are constantly strengthened, and the processing of slag is utilized just generally to be weighed by countries in the world
Depending on developed country differs from one another according to national conditions difference in terms of steel slag utilization, but is mostly used for marine reclamation land, road base layer material
Material, stockyard backfill and returned raw materials for metallurgy and flux etc..
Ceramic waste residue is the damaged blank that ceramics factory produces during production porcelain, and the breakage without calcining, glazing is given up
The semi-finished product of glazing are calcined in product and factory, because there is damaged or crackle to be made pottery into waste product and from construction site useless building
The mixed waste of the residues such as the waste ceramic fragment after porcelain, the place of useless sanitary ceramics and other application ceramics and house decoration.
With China's rapid development of economy, the continuous improvement of people's living standard, requirement of the people to housing construction is also progressively increased.
With the high speed development and the rapid growth of ceramic industry of China's real estate, the yield of waste ceramic is also more and more.
One kind of building waste is also room slag, refer to building building, fit up, repair and demolishing process in produce
Discarded object, is the important component of municipal refuse.With industrialization, the acceleration of urbanization process, China cities and towns are newly-built with changing
The construction speed for building engineering is increasingly accelerated, the building room slag muck product such as discarded brick and tile, discarded concrete produced by demolishing buildings
Such as mountain.At present, the unprocessed building waste directly filled of China just accounts for more than 90%, and the regeneration rate of building waste
9% is only accounted for, is a huge wasting of resources.
At the same time, as Process of Urbanization Construction paces are accelerated, the ecological environment in city subjects huge pressure.Modernization
The earth's surface in city is progressively hardened by material water-proof materials such as building and concrete and covered, and forms " the artificial desert " on ecology,
Great negative effect is brought to the ecological environment in city in these fluid-tight road surfaces.Therefore, how to be realized in urban construction
Environmental protection has attracted increasing attention with economic, society harmonious development.Steel slag ecological type pavior brick arises at the historic moment, and it has
There are preferable water permeation performance and anti-wear performance, precipitation can be made to penetrate into underlying soil by itself, supplement the underground water in city
Resource, the protection to groundwater resources plays positive effect.
At present, to build room slag research more than be combined with building room slag with flyash, and have no will build room slag, steel
The solid waste such as slag, ceramic slag comprehensively utilize the report for pavior brick.
The content of the invention
For the defect of prior art, it is an object of the invention to provide a kind of environment-friendlyroad road face brick, the pavior brick is wear-resisting anti-ageing
Change, sterile tasteless, safety and environmental protection, good water permeability, ultraviolet absorption ability are stronger, while preparing raw material makes full use of Industry Waste
Expect, save natural resources, reduce environmental pollution, and preparation method is simple, with higher practical value and good application
Prospect.
The present invention solves technical problem and adopted the following technical scheme that：
The invention provides a kind of environment-friendlyroad road face brick, include the raw material of following parts by weight：
15-25 parts of ceramic waste residue, 20-30 parts of slag, 15-25 parts of gangue, 10-20 parts of discarded concrete, volcanic ash 15-25
Part, 5-15 parts of nano silicon, 20-30 parts of cement, 5-10 parts of improved additives, 3-7 parts of taste removal additive.
Preferably, the environment-friendlyroad road face brick includes the raw material of following parts by weight：
20 parts of ceramic waste residue, 25 parts of slag, 20 parts of gangue, 15 parts of discarded concrete, 20 parts of volcanic ash, nano silicon 10
Part, 25 parts of portland cement, 8 parts of improved additives, 5 parts of taste removal additive.
Preferably, the improved additives are by being 2 according to weight ratio:1:0.5 attapulgite, sepiolite, tourmaline are mixed
Conjunction is formed.
Preferably, the taste removal additive is by being 2 according to weight ratio:1:2:3 boric acid, Boratex, ferrous sulfate, sulfuric acid
Magnesium is mixed.
Present invention also offers a kind of preparation method of environment-friendlyroad road face brick, comprise the following steps：
Step one, ceramic waste residue, slag, gangue, discarded concrete are mixed to add in pulverizer and crushed, cross 50-70 mesh sieves,
Send into calcining furnace and calcined 15-35 minutes at 850-950 DEG C, carefully mistake is ground in cooling, washing, filtering feeding ball mill
150-200 mesh sieves obtain mixture A；
Step 2, mixture A, volcanic ash, improved additives, taste removal additive, nano silicon made from step one are mixed
Close and add in mixer, add appropriate water with 150-250r/min rotating speed, stir 2-4 hours, then place 12-18 hours,
Obtain mixture B；
Step 3, portland cement, appropriate water are added into mixture B and sends into mixer and stirs, speed of agitator 60-
80r/min, mixing time is 1-3 hours, and the adobe of size needed for being pressed into baking-free brick making machine is sent into after stirring,
180-200 DEG C, conserve 8-10 hours under the conditions of 1.6-1.8MPa, invention environment-friendlyroad road face brick is obtained after cooling.
Preferably, the step one is：Ceramic waste residue, slag, gangue, discarded concrete are mixed and added in pulverizer
Crush, cross and calcined 25 minutes at 900 DEG C in 60 mesh sieves, feeding calcining furnace, ground in cooling, washing, filtering feeding ball mill
Mixture A is obtained to the thin mesh sieve of mistake 200.
Preferably, the step 2 is：By mixture A, volcanic ash, improved additives, taste removal addition made from step one
Agent, nano silicon mixing are added in mixer, are added appropriate water with 200r/min rotating speed, are stirred 3 hours, then place
15 hours, obtain mixture B.
Preferably, the step 3 is：Portland cement, appropriate water is added into mixture B to send into mixer and stir
Mix uniform, speed of agitator 70r/min, mixing time is 2 hours, sent into after stirring needed for being pressed into baking-free brick making machine
The adobe of size, conserves 9 hours under the conditions of 190 DEG C, 1.7MPa, invention environment-friendlyroad road face brick is obtained after cooling.
Compared with prior art, the present invention has following beneficial effect：
（1）The environment-friendlyroad road face brick of the present invention makes full use of using ceramic waste residue, slag, gangue, discarded concrete as main component
Solid waste, has on the one hand accomplished twice laid, has on the other hand saved resource, reduced environmental pollution.
（2）The environment-friendlyroad road face brick of the present invention with the addition of volcanic ash, nano silicon, and nano silicon has extremely strong
Ultraviolet radiation absorption and thermal radiation absorption ability, by increasing capacitance it is possible to increase the anti-ultraviolet radiation of pavior brick and the function of heat ageing, additionally it is possible to drop
The tropical island effect in low summer city.
（3）The present invention environment-friendlyroad road face brick add improved additives by attapulgite, sepiolite, tourmaline mixing and
Into, the consumption of cement is reduced on the premise of one side proof strength, mitigates the weight of pavior brick, strengthen its anti-wear performance, it is another
The aspect each composition of face brick that can satisfy the need plays a part of sterilizing.
（4）The taste removal additive that the environment-friendlyroad road face brick of the present invention is added, wherein being reducing agent with ferrous sulfate, magnesium sulfate is
Retention agent mixing boric acid, the Boratex of ferrous sulfate can effectively decompose road surface it is anhydrous in foul smell, reach the mesh de-tasted rapidly
's.
（5）The environment-friendlyroad road face brick of the present invention makes full use of industrial waste, saves natural resources, reduces environmental pollution, and
Preparation method is simple, with higher practical value and good application prospect.
Embodiment
With reference to specific embodiment, the technical scheme in the embodiment of the present invention is clearly and completely described, shown
So, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based on the reality in the present invention
Example is applied, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made all belongs to
In the scope of protection of the invention.
Embodiment 1.
The environment-friendlyroad road face brick of the present embodiment, includes the raw material of following parts by weight：
15 parts of ceramic waste residue, 20 parts of slag, 15 parts of gangue, 10 parts of discarded concrete, 15 parts of volcanic ash, nano silicon 5
Part, 20 parts of cement, 5 parts of improved additives, 3 parts of taste removal additive.
Improved additives are by being 2 according to weight ratio in the present embodiment:1:0.5 attapulgite, sepiolite, tourmaline mixing
Form.
Taste removal additive is by being 2 according to weight ratio in the present embodiment:1:2:3 boric acid, Boratex, ferrous sulfate, sulfuric acid
Magnesium is mixed.
The preparation method of the environment-friendlyroad road face brick of the present embodiment, comprises the following steps：
Step one, ceramic waste residue, slag, gangue, discarded concrete are mixed to add in pulverizer and crushed, crossed 50 mesh sieves, send
Enter in calcining furnace and to be calcined 15 minutes at 850 DEG C, be ground in cooling, washing, filtering feeding ball mill and carefully cross 150 mesh sieves and obtain
Mixture A；
Step 2, mixture A, volcanic ash, improved additives, taste removal additive, nano silicon made from step one are mixed
Close and add in mixer, add appropriate water with 150r/min rotating speed, stir 2 hours, then place 12 hours, obtain mixture
B；
Step 3, portland cement, appropriate water are added into mixture B and sends into mixer and stirs, speed of agitator
60r/min, mixing time is 1 hour, and the adobe of size needed for being pressed into baking-free brick making machine is sent into after stirring,
180 DEG C, conserve 8 hours under the conditions of 1.6MPa, invention environment-friendlyroad road face brick is obtained after cooling.
Embodiment 2.
The environment-friendlyroad road face brick of the present embodiment, includes the raw material of following parts by weight：
25 parts of ceramic waste residue, 30 parts of slag, 25 parts of gangue, 20 parts of discarded concrete, 25 parts of volcanic ash, nano silicon 15
Part, 30 parts of cement, 10 parts of improved additives, 7 parts of taste removal additive.
Improved additives are by being 2 according to weight ratio in the present embodiment:1:0.5 attapulgite, sepiolite, tourmaline mixing
Form.
Taste removal additive is by being 2 according to weight ratio in the present embodiment:1:2:3 boric acid, Boratex, ferrous sulfate, sulfuric acid
Magnesium is mixed.
The preparation method of the environment-friendlyroad road face brick of the present embodiment, comprises the following steps：
Step one, ceramic waste residue, slag, gangue, discarded concrete are mixed to add in pulverizer and crushed, cross 50-70 mesh sieves,
Send into calcining furnace at 950 DEG C calcine 35 minutes, cooling, washing, filtering feeding ball mill in be ground to carefully cross 200 mesh sieves obtain
To mixture A；
Step 2, mixture A, volcanic ash, improved additives, taste removal additive, nano silicon made from step one are mixed
Close and add in mixer, add appropriate water with 250r/min rotating speed, stir 4 hours, then place 18 hours, obtain mixture
B；
Step 3, portland cement, appropriate water are added into mixture B and sends into mixer and stirs, speed of agitator
80r/min, mixing time is 3 hours, and the adobe of size needed for being pressed into baking-free brick making machine is sent into after stirring,
200 DEG C, conserve 10 hours under the conditions of 1.8MPa, invention environment-friendlyroad road face brick is obtained after cooling.
Embodiment 3.
The environment-friendlyroad road face brick of the present embodiment, includes the raw material of following parts by weight：
20 parts of ceramic waste residue, 25 parts of slag, 20 parts of gangue, 15 parts of discarded concrete, 20 parts of volcanic ash, nano silicon 10
Part, 25 parts of portland cement, 8 parts of improved additives, 5 parts of taste removal additive.
Improved additives are by being 2 according to weight ratio in the present embodiment:1:0.5 attapulgite, sepiolite, tourmaline mixing
Form.
Taste removal additive is by being 2 according to weight ratio in the present embodiment:1:2:3 boric acid, Boratex, ferrous sulfate, sulfuric acid
Magnesium is mixed.
The preparation method of the environment-friendlyroad road face brick of the present embodiment, comprises the following steps：
Step one, ceramic waste residue, slag, gangue, discarded concrete are mixed to add in pulverizer and crushed, crossed 60 mesh sieves, send
Enter in calcining furnace and to be calcined 25 minutes at 900 DEG C, be ground in cooling, washing, filtering feeding ball mill and carefully cross 200 mesh sieves and obtain
Mixture A；
Step 2, mixture A, volcanic ash, improved additives, taste removal additive, nano silicon made from step one are mixed
Close and add in mixer, add appropriate water with 200r/min rotating speed, stir 3 hours, then place 15 hours, obtain mixture
B；
Step 3, portland cement, appropriate water are added into mixture B and sends into mixer and stirs, speed of agitator
70r/min, mixing time is 2 hours, and the adobe of size needed for being pressed into baking-free brick making machine is sent into after stirring,
190 DEG C, conserve 9 hours under the conditions of 1.7MPa, invention environment-friendlyroad road face brick is obtained after cooling.
The environment-friendlyroad road face brick of the present invention takes full advantage of solid waste, has on the one hand accomplished twice laid, on the other hand
Save resource, reduce environmental pollution；The anti-ultraviolet radiation of pavior brick and the function of heat ageing are stronger, the improvement addition of addition
Agent is mixed by attapulgite, sepiolite, tourmaline, reduces the consumption of cement, mitigates the weight of pavior brick, to strengthen its wear-resisting
Performance, additionally it is possible to which each composition of the face brick that satisfies the need plays a part of sterilizing；Can effectively decompose road surface it is anhydrous in foul smell, reach
De-taste rapidly.The environment-friendlyroad road face brick of the present invention makes full use of industrial waste, saves natural resources, reduces environmental pollution, and system
Preparation Method is simple, with higher practical value and good application prospect.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, nothing
By from the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by institute
Attached claim rather than described above are limited, it is intended that will fall in the implication and scope of the equivalency of claim
All changes include in the present invention.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should
Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
It may be appreciated other embodiment.
Claims (8)
1. a kind of environment-friendlyroad road face brick, it is characterised in that include the raw material of following parts by weight：
15-25 parts of ceramic waste residue, 20-30 parts of slag, 15-25 parts of gangue, 10-20 parts of discarded concrete, volcanic ash 15-25
Part, 5-15 parts of nano silicon, 20-30 parts of cement, 5-10 parts of improved additives, 3-7 parts of taste removal additive.
2. environment-friendlyroad road face brick according to claim 1, it is characterised in that the environment-friendlyroad road face brick includes following parts by weight
Raw material：
20 parts of ceramic waste residue, 25 parts of slag, 20 parts of gangue, 15 parts of discarded concrete, 20 parts of volcanic ash, nano silicon 10
Part, 25 parts of portland cement, 8 parts of improved additives, 5 parts of taste removal additive.
3. environment-friendlyroad road face brick according to claim 1 or 2, it is characterised in that the improved additives are by according to weight ratio
For 2:1:0.5 attapulgite, sepiolite, tourmaline are mixed.
4. environment-friendlyroad road face brick according to claim 1 or 2, it is characterised in that the taste removal additive is by according to weight ratio
For 2:1:2:3 boric acid, Boratex, ferrous sulfate, magnesium sulfate are mixed.
5. a kind of preparation method of environment-friendlyroad road face brick according to claim 1 or 2, it is characterised in that comprise the following steps：
Step one, ceramic waste residue, slag, gangue, discarded concrete are mixed to add in pulverizer and crushed, cross 50-70 mesh sieves,
Send into calcining furnace and calcined 15-35 minutes at 850-950 DEG C, carefully mistake is ground in cooling, washing, filtering feeding ball mill
150-200 mesh sieves obtain mixture A；
Step 2, mixture A, volcanic ash, improved additives, taste removal additive, nano silicon made from step one are mixed
Close and add in mixer, add appropriate water with 150-250r/min rotating speed, stir 2-4 hours, then place 12-18 hours,
Obtain mixture B；
Step 3, portland cement, appropriate water are added into mixture B and sends into mixer and stirs, speed of agitator 60-
80r/min, mixing time is 1-3 hours, and the adobe of size needed for being pressed into baking-free brick making machine is sent into after stirring,
180-200 DEG C, conserve 8-10 hours under the conditions of 1.6-1.8MPa, invention environment-friendlyroad road face brick is obtained after cooling.
6. a kind of preparation method of environment-friendlyroad road face brick according to claim 5, it is characterised in that the step one is：Will
Ceramic waste residue, slag, gangue, discarded concrete mixing add pulverizer in crush, cross 60 mesh sieves, feeding calcining furnace in
At 900 DEG C calcine 25 minutes, cooling, washing, filtering feeding ball mill in be ground to carefully cross 200 mesh sieves obtain mixture A.
7. the preparation method of environment-friendlyroad road face brick according to claim 5, it is characterised in that the step 2 is：By step
Mixture A, volcanic ash, improved additives, taste removal additive, nano silicon mixing are added in mixer made from one, are added
Plus appropriate water is with 200r/min rotating speed, stir 3 hours, then place 15 hours, obtain mixture B.
8. the preparation method of environment-friendlyroad road face brick according to claim 5, it is characterised in that the step 3 is：To mixing
Add portland cement, appropriate water in thing B to send into mixer and stir, speed of agitator 70r/min, mixing time is 2
Hour, the adobe of size needed for being pressed into baking-free brick making machine is sent into after stirring, is supported under the conditions of 190 DEG C, 1.7MPa
Shield 9 hours, obtains invention environment-friendlyroad road face brick after cooling.