CN108424104A - A kind of landscape design environmentally friendly floor tile and preparation method thereof - Google Patents
A kind of landscape design environmentally friendly floor tile and preparation method thereof Download PDFInfo
- Publication number
- CN108424104A CN108424104A CN201810382171.3A CN201810382171A CN108424104A CN 108424104 A CN108424104 A CN 108424104A CN 201810382171 A CN201810382171 A CN 201810382171A CN 108424104 A CN108424104 A CN 108424104A
- Authority
- CN
- China
- Prior art keywords
- parts
- floor tile
- environmentally friendly
- water
- landscape design
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of landscape design environmentally friendly floor tile and preparation method thereof, is related to floor tile technical field, includes the raw material of following parts by weight meter：Discarded 20 30 parts of brick and tile, 8 15 parts of scrap glass, 8 15 parts of blast-furnace cinder, 15 25 parts of flyash, 6 12 parts of diatomite, 6 12 parts of calcium carbonate, 49 parts of barium sulfate, 49 parts of bamboo charcoal powder, 15 22 parts of cement, 49 parts of nano-titanium dioxide, 49 parts of fibroin fiber, 5 10 parts of boron fibre, 38 parts of nano zircite, 38 parts of selenitum powder, 38 parts of magnesium hydroxide, 18 26 parts of waterglass, 1.5 3 parts of water-reducing agent, 1.5 3 parts of air entraining agent, 15 20 parts of 0.8 1.8 parts of retarder and water；Environmental protection floor tile of the invention is prepared using discarded brick and tile, scrap glass and blast-furnace cinder as primary raw material, using waste and old construction material, reduces the pollution to environment, while reducing production cost.
Description
Technical field
The invention belongs to floor tile technical fields, and in particular to a kind of landscape design environmentally friendly floor tile and its preparation side
Method.
Background technology
In the process of construction of garden landscape floor tile as it is a kind of it is common, using very universal construction material, need
The amount of asking is big, huge for the consumption of material resources, in today of non-renewable resources increasingly depleted, when energy conservation and environmental protection becomes
For theme, the problem that other alternative material resources become in the urgent need to address at present is found.
With the rapid development of economic construction of China, each metropolitan groups of building in China are also quickly emerging, thereupon
Also have a large amount of waste and old brick and tile material and discarded building glass.The annual manufactured waste and old construction material in China city has exceeded 50
Hundred million tons, we are while seeing urban economy and building rapid development, it should also be recognized that the wasting of resources is sunk caused by environment
Heavy burden.These waste and old construction materials that can be utilized again are not fully utilized, cause prodigious resource
Waste, serious pollution is also resulted in environment.
Invention content
For problems of the prior art, the object of the present invention is to provide a kind of environmentally friendly floor tile of landscape design and
Preparation method, present invention environmental protection floor tile are prepared using discarded brick and tile, scrap glass and blast-furnace cinder as primary raw material, profit
With waste and old construction material, resource circulation utilization reduces the pollution to environment, while reducing production cost, the ground being prepared
Face brick anti-flammability, crushing resistance and ageing-resistant performance are excellent, and service life is long.
The present invention provides the following technical solutions：
A kind of environmentally friendly floor tile of landscape design, includes the raw material of following parts by weight：
Discarded 20-30 parts of brick and tile, 8-15 parts of scrap glass, 8-15 parts of blast-furnace cinder, 15-25 parts of flyash, diatomite 6-
12 parts, 6-12 parts of calcium carbonate, 4-9 parts of barium sulfate, 4-9 parts of bamboo charcoal powder, 15-22 parts of cement, 4-9 parts of nano-titanium dioxide, fibroin
4-9 parts of azelon, 5-10 parts of boron fibre, 3-8 parts of nano zircite, 3-8 parts of selenitum powder, 3-8 parts of magnesium hydroxide, waterglass
15-20 parts of 18-26 parts, 1.5-3 parts of water-reducing agent, 1.5-3 parts of air entraining agent, 0.8-1.8 parts of retarder and water.
Preferably, include the raw material of following parts by weight：Discarded 24-26 parts of brick and tile, 10-13 parts of scrap glass, blast-furnace cinder
10-13 parts, 18-22 parts of flyash, 8-10 parts of diatomite, 8-10 parts of calcium carbonate, 5-8 parts of barium sulfate, 5-8 parts of bamboo charcoal powder, cement
18-20 parts, 5-8 parts of nano-titanium dioxide, 5-8 parts of fibroin fiber, 6-9 parts of boron fibre, 4-7 parts of nano zircite, profound essence
4-7 parts of mountain flour, 4-7 parts of magnesium hydroxide, 21-23 parts of waterglass, 2-2.5 parts of water-reducing agent, 2-2.5 parts of air entraining agent, retarder 1.3-
1.6 parts and 17-19 parts of water.
Preferably, include the raw material of following parts by weight：Discarded 20-30 parts of brick and tile, 8-15 parts of scrap glass, blast-furnace cinder 8-
15 parts, 15-25 parts of flyash, 6-12 parts of diatomite, 6-12 parts of calcium carbonate, 4-9 parts of barium sulfate, 4-9 parts of bamboo charcoal powder, cement 15-
22 parts, 4-9 parts of nano-titanium dioxide, 4-9 parts of fibroin fiber, 5-10 parts of boron fibre, 3-8 parts of nano zircite, selenitum
3-8 parts of powder, 3-8 parts of magnesium hydroxide, 18-26 parts of waterglass, 1.5-3 parts of water-reducing agent, 1.5-3 parts of air entraining agent, retarder 0.8-1.8
15-20 parts of part and water.
Preferably, the water-reducing agent is polycarboxylate dehydragent.
Preferably, the air entraining agent is one or more of rosin acids, arene, aromatic alcohol and aromatic aldehydes
In conjunction with.
Preferably, the retarder be lignin, phosphoric acid salt, tartrates and citric acid salt in one kind or
Several combinations.
A kind of preparation method of the environmentally friendly floor tile of above-mentioned landscape design is also disclosed in the present invention, specifically, including with
Lower step：
(1) according to landscape design raw material is weighed with the parts by weight of environmentally friendly floor tile raw material；
(2) discarded brick and tile are added in pulverizer and are crushed, crossed 100-200 mesh sieve, send into calcining furnace, temperature control to 700-
It 800 degrees Celsius, roasts 5-7 hours；
(3) scrap glass is sent and is crushed into pulverizer, 30-100 mesh sieve is crossed, with product, Blast Furnace Ore made from step (2)
Slag, flyash, diatomite, calcium carbonate, barium sulfate, bamboo charcoal powder, cement, nano-titanium dioxide, fibroin fiber, boron fibre,
Nano zircite, selenitum powder, magnesium hydroxide are uniformly mixed, and obtain mixed material；
(4) water-reducing agent, air entraining agent, retarder are added in water after mixing, are slowly added into mixed in step (3)
Material is closed, after mixing, waterglass is added and continues high-speed stirred after 5-10 minutes, compression moulding in brickmaking machine is added；
(5) by adobe natural air drying after molding to get the environmentally friendly floor tile of the landscape design.
Preferably, it is uniformly mixed using single horizontal shaft mixer in the step (3), incorporation time is 15-20 minutes.
The beneficial effects of the invention are as follows：
(1) the environmentally friendly floor tile of the present invention is prepared using discarded brick and tile, scrap glass and blast-furnace cinder as primary raw material, profit
With waste and old construction material, resource circulation utilization reduces the pollution to environment, while reducing production cost, the ground being prepared
Face brick anti-flammability, crushing resistance and ageing-resistant performance are excellent, and service life is long.
(2) bamboo charcoal powder is added in raw material of the present invention, bamboo charcoal powder has superpower adsorption function and generates anion, radiation
Far infrared, increase alkalinity and other effects, can purify air, moisture absorption damping, fungus-resistant blocks radiation.
(3) boron fibre is added in raw material of the present invention, boron fibre intensity is high, and light weight, physical property is good, and being added in material can
With the rigidity, intensity and pressure-proof and snap-resistent of reinforcing material.
(4) selenitum powder is added in raw material of the present invention, selenitum powder has restraining and sterilizing bacteria performance, while having purification empty
Airway dysfunction.
(5) it is added with nano zircite in raw material of the present invention, nano zircite receives strong, high temperature resistant, change with thermal shock resistance
Learn the features such as stability is good, Material cladding protrudes.Nano zircite is compound with other materials, material can be greatlyd improve
Performance parameter, improve its fracture toughness, bending strength etc..
Specific implementation mode
Embodiment 1
A kind of environmentally friendly floor tile of landscape design, includes the raw material of following parts by weight：
Discarded 20 parts of brick and tile, 8 parts of scrap glass, 8 parts of blast-furnace cinder, 15 parts of flyash, 6 parts of diatomite, 6 parts of calcium carbonate,
4 parts of barium sulfate, 4 parts of bamboo charcoal powder, 15 parts of cement, 4 parts of nano-titanium dioxide, 4 parts of fibroin fiber, 5 parts of boron fibre, nano oxygen
Change 3 parts of zirconium, 3 parts of selenitum powder, 3 parts of magnesium hydroxide, 18 parts of waterglass, 1.5 parts of water-reducing agent, 1.5 parts of air entraining agent, retarder 0.8
15 parts of part and water.
Water-reducing agent is polycarboxylate dehydragent.
Air entraining agent is rosin acids.
Retarder is lignin.
A kind of preparation method of the environmentally friendly floor tile of above-mentioned landscape design is also disclosed in the present embodiment, specifically, including
Following steps：
(1) according to landscape design raw material is weighed with the parts by weight of environmentally friendly floor tile raw material；
(2) will discarded brick and tile be added pulverizer in crush, sieve with 100 mesh sieve, send into calcining furnace, temperature control to 700 degrees Celsius,
Roasting 5 hours；
(3) scrap glass is sent and is crushed into pulverizer, cross 30 mesh sieve, with product made from step (2), blast-furnace cinder,
Flyash, diatomite, calcium carbonate, barium sulfate, bamboo charcoal powder, cement, nano-titanium dioxide, fibroin fiber, boron fibre, nanometer
Zirconium oxide, selenitum powder, magnesium hydroxide are uniformly mixed, and obtain mixed material；
(4) water-reducing agent, air entraining agent, retarder are added in water after mixing, are slowly added into mixed in step (3)
Material is closed, after mixing, waterglass is added and continues high-speed stirred after five minutes, compression moulding in brickmaking machine is added；
(5) by adobe natural air drying after molding to get the environmentally friendly floor tile of the landscape design.
It is uniformly mixed using single horizontal shaft mixer in step (3), incorporation time is 15 minutes.
Embodiment 2
A kind of environmentally friendly floor tile of landscape design, includes the raw material of following parts by weight：
Discarded 30 parts of brick and tile, 15 parts of scrap glass, 15 parts of blast-furnace cinder, 25 parts of flyash, 12 parts of diatomite, calcium carbonate 12
Part, 10 parts of boron fibre, is received 9 parts of barium sulfate, 9 parts of bamboo charcoal powder, 22 parts of cement, 9 parts of nano-titanium dioxide, 9 parts of fibroin fiber
8 parts of zirconium oxide of rice, 8 parts of selenitum powder, 8 parts of magnesium hydroxide, 26 parts of waterglass, 3 parts of water-reducing agent, 3 parts of air entraining agent, retarder 1.8
20 parts of part and water.
Water-reducing agent is polycarboxylate dehydragent.
Air entraining agent is arene.
Retarder is phosphoric acid salt.
A kind of preparation method of the environmentally friendly floor tile of above-mentioned landscape design is also disclosed in the present embodiment, specifically, including
Following steps：
(1) according to landscape design raw material is weighed with the parts by weight of environmentally friendly floor tile raw material；
(2) will discarded brick and tile be added pulverizer in crush, cross 200 mesh sieve, send into calcining furnace, temperature control to 800 degrees Celsius,
Roasting 7 hours；
(3) scrap glass is sent and is crushed into pulverizer, sieved with 100 mesh sieve, with product made from step (2), blast-furnace cinder,
Flyash, diatomite, calcium carbonate, barium sulfate, bamboo charcoal powder, cement, nano-titanium dioxide, fibroin fiber, boron fibre, nanometer
Zirconium oxide, selenitum powder, magnesium hydroxide are uniformly mixed, and obtain mixed material；
(4) water-reducing agent, air entraining agent, retarder are added in water after mixing, are slowly added into mixed in step (3)
Material is closed, after mixing, waterglass is added and continues high-speed stirred after ten minutes, compression moulding in brickmaking machine is added；
(5) by adobe natural air drying after molding to get the environmentally friendly floor tile of the landscape design.
It is uniformly mixed using single horizontal shaft mixer in step (3), incorporation time is 20 minutes.
Embodiment 3
A kind of environmentally friendly floor tile of landscape design, includes the raw material of following parts by weight：
Discarded 24 parts of brick and tile, 10 parts of scrap glass, 10 parts of blast-furnace cinder, 18 parts of flyash, 8 parts of diatomite, calcium carbonate 8
Part, 6 parts of boron fibre, is received 5 parts of barium sulfate, 5 parts of bamboo charcoal powder, 18 parts of cement, 5 parts of nano-titanium dioxide, 5 parts of fibroin fiber
4 parts of zirconium oxide of rice, 4 parts of selenitum powder, 4 parts of magnesium hydroxide, 21 parts of waterglass, 2 parts of water-reducing agent, 2 parts of air entraining agent, retarder 1.3
17 parts of part and water.
Water-reducing agent is polycarboxylate dehydragent.
Air entraining agent is aromatic alcohol.
Retarder is tartrates.
A kind of preparation method of the environmentally friendly floor tile of above-mentioned landscape design is also disclosed in the present embodiment, specifically, including
Following steps：
(1) according to landscape design raw material is weighed with the parts by weight of environmentally friendly floor tile raw material；
(2) will discarded brick and tile be added pulverizer in crush, cross 150 mesh sieve, send into calcining furnace, temperature control to 750 degrees Celsius,
Roasting 6 hours；
(3) scrap glass is sent and is crushed into pulverizer, cross 40 mesh sieve, with product made from step (2), blast-furnace cinder,
Flyash, diatomite, calcium carbonate, barium sulfate, bamboo charcoal powder, cement, nano-titanium dioxide, fibroin fiber, boron fibre, nanometer
Zirconium oxide, selenitum powder, magnesium hydroxide are uniformly mixed, and obtain mixed material；
(4) water-reducing agent, air entraining agent, retarder are added in water after mixing, are slowly added into mixed in step (3)
Material is closed, after mixing, waterglass is added and continues high-speed stirred after 6 minutes, compression moulding in brickmaking machine is added；
(5) by adobe natural air drying after molding to get the environmentally friendly floor tile of the landscape design.
It is uniformly mixed using single horizontal shaft mixer in step (3), incorporation time is 16 minutes.
Embodiment 4
A kind of environmentally friendly floor tile of landscape design, includes the raw material of following parts by weight：
Discarded 26 parts of brick and tile, 13 parts of scrap glass, 13 parts of blast-furnace cinder, 22 parts of flyash, 10 parts of diatomite, calcium carbonate 10
Part, 9 parts of boron fibre, is received 8 parts of barium sulfate, 8 parts of bamboo charcoal powder, 20 parts of cement, 8 parts of nano-titanium dioxide, 8 parts of fibroin fiber
7 parts of zirconium oxide of rice, 7 parts of selenitum powder, 7 parts of magnesium hydroxide, 23 parts of waterglass, 2.5 parts of water-reducing agent, 2.5 parts of air entraining agent, retarder
1.6 parts and 19 parts of water.
Water-reducing agent is polycarboxylate dehydragent.
Air entraining agent is aromatic aldehydes.
Retarder is citric acid salt.
A kind of preparation method of the environmentally friendly floor tile of above-mentioned landscape design is also disclosed in the present embodiment, specifically, including
Following steps：
(1) according to landscape design raw material is weighed with the parts by weight of environmentally friendly floor tile raw material；
(2) will discarded brick and tile be added pulverizer in crush, cross 140 mesh sieve, send into calcining furnace, temperature control to 750 degrees Celsius,
Roasting 5.5 hours；
(3) scrap glass is sent and is crushed into pulverizer, cross 60 mesh sieve, with product made from step (2), blast-furnace cinder,
Flyash, diatomite, calcium carbonate, barium sulfate, bamboo charcoal powder, cement, nano-titanium dioxide, fibroin fiber, boron fibre, nanometer
Zirconium oxide, selenitum powder, magnesium hydroxide are uniformly mixed, and obtain mixed material；
(4) water-reducing agent, air entraining agent, retarder are added in water after mixing, are slowly added into mixed in step (3)
Material is closed, after mixing, waterglass is added and continues high-speed stirred after 8 minutes, compression moulding in brickmaking machine is added；
(5) by adobe natural air drying after molding to get the environmentally friendly floor tile of the landscape design.
It is uniformly mixed using single horizontal shaft mixer in step (3), incorporation time is 17 minutes.
Embodiment 5
A kind of environmentally friendly floor tile of landscape design, includes the raw material of following parts by weight：
Discarded 20-30 parts of brick and tile, 8-15 parts of scrap glass, 8-15 parts of blast-furnace cinder, 15-25 parts of flyash, diatomite 6-
12 parts, 6-12 parts of calcium carbonate, 4-9 parts of barium sulfate, 4-9 parts of bamboo charcoal powder, 15-22 parts of cement, 4-9 parts of nano-titanium dioxide, fibroin
4-9 parts of azelon, 5-10 parts of boron fibre, 3-8 parts of nano zircite, 3-8 parts of selenitum powder, 3-8 parts of magnesium hydroxide, waterglass
15-20 parts of 18-26 parts, 1.5-3 parts of water-reducing agent, 1.5-3 parts of air entraining agent, 0.8-1.8 parts of retarder and water.
Water-reducing agent is polycarboxylate dehydragent.
Air entraining agent is rosin acids.
Retarder is phosphoric acid salt.
A kind of preparation method of the environmentally friendly floor tile of above-mentioned landscape design is also disclosed in the present embodiment, specifically, including
Following steps：
(1) according to landscape design raw material is weighed with the parts by weight of environmentally friendly floor tile raw material；
(2) discarded brick and tile are added in pulverizer and are crushed, crossed 160 mesh sieve, send into calcining furnace, temperature control to 700-800 is taken the photograph
Family name's degree roasts 6.5 hours；
(3) scrap glass is sent and is crushed into pulverizer, cross 60 mesh sieve, with product made from step (2), blast-furnace cinder,
Flyash, diatomite, calcium carbonate, barium sulfate, bamboo charcoal powder, cement, nano-titanium dioxide, fibroin fiber, boron fibre, nanometer
Zirconium oxide, selenitum powder, magnesium hydroxide are uniformly mixed, and obtain mixed material；
(4) water-reducing agent, air entraining agent, retarder are added in water after mixing, are slowly added into mixed in step (3)
Material is closed, after mixing, waterglass is added and continues high-speed stirred after 8 minutes, compression moulding in brickmaking machine is added；
(5) by adobe natural air drying after molding to get the environmentally friendly floor tile of the landscape design.
It is uniformly mixed using single horizontal shaft mixer in step (3), incorporation time is 18 minutes.
Landscape design made from embodiment 1, embodiment 2 and embodiment 3 is tested for the property with environmentally friendly floor tile, is tested
The results are shown in Table 1：
| Index | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 |
| Flame retardant rating | A grades | A grades | A grades | A grades | A grades |
| Compression strength (MPa) | 47.5 | 46.6 | 48.4 | 47.9 | 55.6 |
| Flexural strength (MPa) | 13.5 | 12.8 | 13.8 | 14.2 | 14.5 |
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although with reference to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution recorded in example is modified or equivalent replacement of some of the technical features, all essences in the present invention
With within principle, any modification, equivalent replacement, improvement and so on should all be included in the protection scope of the present invention god.
Claims (8)
1. a kind of environmentally friendly floor tile of landscape design, which is characterized in that include the raw material of following parts by weight：Discarded brick and tile 20-
30 parts, 8-15 parts of scrap glass, 8-15 parts of blast-furnace cinder, 15-25 parts of flyash, 6-12 parts of diatomite, 6-12 parts of calcium carbonate, sulphur
Sour barium 4-9 parts, 4-9 parts of bamboo charcoal powder, 15-22 parts of cement, 4-9 parts of nano-titanium dioxide, 4-9 parts of fibroin fiber, boron fibre
5-10 parts, 3-8 parts of nano zircite, 3-8 parts of selenitum powder, 3-8 parts of magnesium hydroxide, 18-26 parts of waterglass, water-reducing agent 1.5-3
Part, 1.5-3 parts of air entraining agent, 0.8-1.8 parts of retarder and 15-20 parts of water.
2. the environmentally friendly floor tile of landscape design according to claim 1, which is characterized in that include the original of following parts by weight
Material：Discarded 24-26 parts of brick and tile, 10-13 parts of scrap glass, 10-13 parts of blast-furnace cinder, 18-22 parts of flyash, diatomite 8-10
Part, 8-10 parts of calcium carbonate, 5-8 parts of barium sulfate, 5-8 parts of bamboo charcoal powder, 18-20 parts of cement, 5-8 parts of nano-titanium dioxide, fibroin egg
5-8 parts of white fiber, 6-9 parts of boron fibre, 4-7 parts of nano zircite, 4-7 parts of selenitum powder, 4-7 parts of magnesium hydroxide, waterglass 21-
17-19 parts of 23 parts, 2-2.5 parts of water-reducing agent, 2-2.5 parts of air entraining agent, 1.3-1.6 parts of retarder and water.
3. the environmentally friendly floor tile of landscape design according to claim 1, which is characterized in that include the original of following parts by weight
Material：Discarded 20-30 parts of brick and tile, 8-15 parts of scrap glass, 8-15 parts of blast-furnace cinder, 15-25 parts of flyash, 6-12 parts of diatomite,
6-12 parts of calcium carbonate, 4-9 parts of barium sulfate, 4-9 parts of bamboo charcoal powder, 15-22 parts of cement, 4-9 parts of nano-titanium dioxide, fibroin albumen are fine
4-9 parts of dimension, 5-10 parts of boron fibre, 3-8 parts of nano zircite, 3-8 parts of selenitum powder, 3-8 parts of magnesium hydroxide, waterglass 18-26
Part, 1.5-3 parts of water-reducing agent, 1.5-3 parts of air entraining agent, 0.8-1.8 parts of retarder and 15-20 parts of water.
4. the environmentally friendly floor tile of landscape design according to claim 1, which is characterized in that the water-reducing agent is polycarboxylate
Water-reducing agent.
5. the environmentally friendly floor tile of landscape design according to claim 1, which is characterized in that the air entraining agent is resin acid
One or more of class, arene, aromatic alcohol and aromatic aldehydes combine.
6. the environmentally friendly floor tile of landscape design according to claim 1, which is characterized in that the retarder is lignin
One or more of class, phosphoric acid salt, tartrates and citric acid salt combine.
7. a kind of landscape design as described in claim 1-6 any one preparation method of environmentally friendly floor tile, feature exist
In including the following steps：
(1) according to landscape design raw material is weighed with the parts by weight of environmentally friendly floor tile raw material；
(2) discarded brick and tile are added in pulverizer and are crushed, crossed 100-200 mesh sieve, send into calcining furnace, temperature control to 700-800 is taken the photograph
Family name's degree roasts 5-7 hours；
(3) scrap glass is sent and is crushed into pulverizer, cross 30-100 mesh sieve, with product made from step (2), blast-furnace cinder,
Flyash, diatomite, calcium carbonate, barium sulfate, bamboo charcoal powder, cement, nano-titanium dioxide, fibroin fiber, boron fibre, nanometer
Zirconium oxide, selenitum powder, magnesium hydroxide are uniformly mixed, and obtain mixed material；
(4) water-reducing agent, air entraining agent, retarder are added in water to the mixing being slowly added into after mixing in step (3)
Material is added waterglass and continues high-speed stirred after 5-10 minutes, compression moulding in brickmaking machine is added after mixing；
(5) by adobe natural air drying after molding to get the environmentally friendly floor tile of the landscape design.
8. a kind of landscape design as claimed in claim 7 preparation method of environmentally friendly floor tile, which is characterized in that the step
(3) it is uniformly mixed using single horizontal shaft mixer in, incorporation time is 15-20 minutes.