CN107056168A - A kind of production technology of New Regenerated concrete azulejo watt - Google Patents
A kind of production technology of New Regenerated concrete azulejo watt Download PDFInfo
- Publication number
- CN107056168A CN107056168A CN201710420179.XA CN201710420179A CN107056168A CN 107056168 A CN107056168 A CN 107056168A CN 201710420179 A CN201710420179 A CN 201710420179A CN 107056168 A CN107056168 A CN 107056168A
- Authority
- CN
- China
- Prior art keywords
- new
- concrete
- tile
- regenerated
- dyestuff
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of production technology of New Regenerated concrete azulejo watt, it is related to building materials field, wherein regenerated aggregate concrete is cement 4 20% respectively by concrete composition, regenerated coarse aggregate 0 46% in regeneration aggregate, admixture 1 8%, pumping agent for concrete is the 1.5 2.5% of cement and admixture sum weight, remaining is water, employ rational raw material and the processing step and condition of science, contain admixture inside raw material, so that the increase of azulejo watt intensity, utilization to building waste can improve resource and environment problem, building waste environmental pollution degree can also be mitigated simultaneously.
Description
Technical field
The present invention relates to building material field, more particularly to a kind of novel fluorescence regeneration concrete waterproof azulejo watt production work
Skill.
Background technology
It is to only increase that either old building or new house, which are built to the demand of color steel tile, in daily life
, color steel tile have prevent rain leakage, it is heat-insulated, prevent the solar radiant heat on daytime to be directly transferred within doors, sound insulation, insulation, every
Heat, antiultraviolet, low-carbon environment-friendly, azulejo watt be using clay as primary raw material, and after clay brick disabling, though walling have material light and
Heat-insulation and heat-preservation preferably air entraining cement building block but investment is big and be difficult popularization, particularly material pineization, hanging is easily de-, does exterior wall
It is easily permeable, low intensity and fail-safe is poor, the manufacture craft of current azulejo watt is not universal high, and the labor intensity of workman is big, simultaneously production
The low intensity of product, color is single, is not suitable for large batch of production.
Current normal concrete gathers materials predominantly natural sand stone, is non-renewable resources, machine instruction statement mining had both destroyed nature life
State environment, causes the pollution of environment again, and with the quickening of China's infrastructure, construction industry enters high speed development stage, concrete
Market is re-rented increasing, causes the extraction industry of natural sand stone bigger, and natural aggregate resources will also tend to be exhausted, to ecological environment
Destruction it is also extremely serious.The stacking industry for the building waste that two house breakings are produced equally causes the pollution of environment, discards mixed
The solidifying native main part as building waste, the mode for being used air storage or landfill is handled, and is caused tight
The environmental pollution of weight, thus caused social and environmental problems are also more and more, therefore the utilization of discarded object turns into National Environmental
One of protection and sustainable development target.And building waste is passed through to processing as new aggregate, and as new
Concrete material be developing way.
A kind of Chinese patent application file of application number 201310349944.5, the processing for being related to construction material prepares neck
Domain, the clay for preparing production azulejo watt disables for country.Regenerated aggregate concrete is prepared material by the present invention, institute
The regenerated aggregate concrete stated is by concrete mix, and composition is the regenerated coarse aggregate 0- in cement 4-20%, regeneration aggregate respectively
46%, admixture 1-8%, pumping agent for concrete are cement and the 1.5-2.5% of admixture sum weight, and remaining is water.Employ
Contain admixture inside the processing step and condition of rational raw material and science, raw material so that the increase of azulejo watt intensity, to building
The utilization of rubbish can improve resource and environment problem, while can also mitigate building waste environmental pollution degree.
The content of the invention
The technical problem to be solved of the present invention is to provide, to solve caused drawbacks described above in the prior art.
In order to realize the purpose of the present invention, a kind of production technology for New Regenerated concrete azulejo watt that the present invention is provided,
Comprise the following steps：
（1）Weigh regenerated aggregate concrete and be equipped with waterproofing agent mediation, and be sufficiently stirred for；
(2) regenerated aggregate concrete is placed in default brick and tile grinding tool and carries out just one-step forming, stand 3-20 hours, and
The waste heat of generation is delivered in dry kiln；
（3）The new tile of the shaping is transferred in dry kiln and is dried, wherein dry kiln internal temperature is 50-80
DEG C, and preliminary deashing is carried out to the new tile using air blower；
（4）Raw material needed for choosing dyestuff according to parts by weight is simultaneously configured to dyestuff, and the parts by weight of raw materials of wherein dyestuff is：Sulfonic acid 60-
190 parts, 130-300 parts of aminobenzoyl, 50-300 parts of diaminobenzene formyl chloride-1,50-150 parts of talan, hydrogen peroxide 30-40
Part, and the dyestuff is added slowly in overflow dyeing machine；
（5）Described new tile is transferred in overflow dyeing machine, the dyestuff is uniformly coated on the outer of the new tile
Surface, and New colorful brick and tile piece is formed, it is calcined while New colorful brick and tile piece is transferred in burning machine, sintering temperature is
650-850℃；
(6) the New colorful brick and tile piece is transferred under ventilation condition and carries out natural cooling, form finished product New colorful brick and tile piece,
And finished product detection is carried out to finished product New colorful brick and tile piece.
It is preferred that, described regenerated aggregate concrete be respectively by concrete composition in cement 4-20%, regeneration aggregate again
Raw coarse aggregate 0-46%, admixture 1-8%, pumping agent for concrete 1.5-2.5%, remaining is water.
It is preferred that, the composition of the regenerated aggregate concrete includes queen closer, concrete, pile crown and mortar.
It is preferred that, the admixture composition includes flyash and volcanic ash ground-slag.
It is preferred that, the step（2）In the composition of waterproofing agent include（Unit kilogram）
Magnesia 30-70
Magnesium chloride 20-30
Sodium alkyl sulfonate 0.005-0.02
Inorganic aluminum 40-80
Water 20-30
It is preferred that, the step（5）Middle dyestuff includes fluorescent material, and the color of wherein fluorescent material uses red fluorescence powder.
The beneficial effects of the present invention are：
1st, New Regenerated concrete process for manufacturing colored tiles employs rational raw material and the processing step and condition of science, raw material
Contain admixture in the inside so that the increase of azulejo watt intensity, improve security.
2nd, degree of adhesion reinforcement is carried out to New colorful brick and tile using adhesive, effectively reduced between regenerated aggregate concrete
Space, improves the pore structure of aggregate surface, and then improve the shrinkage of regeneration concrete.
3rd, the waste heat that one-step forming generation at the beginning of being carried out in default brick and tile grinding tool is placed in using regenerated aggregate concrete is defeated
Deliver in dry kiln, reach the effect for making full use of heat, so as to save production cost, save the energy.
4th, regeneration aggregate is building waste, and composition is queen closer, concrete, pile crown and mortar, makes full use of building waste
Resource and environment problem can be improved, and reduce the consuming to natural resources, while building waste environmental pollution can also be mitigated
Degree.
5th, resin is scribbled in the outer surface of azulejo watt, reduces the uneven phenomenon in azulejo watt outer surface, using resin not
The frictional force between azulejo watt can only be increased, and the rough phenomenon of tile surface can be made up, it is not easy to make human hand quilt
The outer surface of azulejo watt frays, and adds the security that azulejo watt is used.
6th, this New colorful brick and tile and its production craft step are simple, easy to operate, and obtained azulejo watt is lasted a long time,
With preferable water proofing property, using also has good security.
Embodiment
The present invention is described in further details with reference to embodiment.
Embodiment 1
A kind of production technology of New Regenerated concrete azulejo watt, production stage is as follows：
（1）Weigh regenerated aggregate concrete and be equipped with waterproofing agent mediation, and be sufficiently stirred for, regenerated aggregate concrete composition is water respectively
Mud 4%, regeneration aggregate 23%, admixture 5%, pumping agent for concrete 1.5%, remaining is water, and the composition of wherein regeneration aggregate includes
Queen closer, concrete, pile crown and mortar, admixture composition include flyash and volcanic ash ground-slag.
(2) regenerated aggregate concrete is placed in default brick and tile grinding tool and carries out just one-step forming, stand 10 hours,
And the waste heat of generation is delivered in dry kiln, the composition of waterproofing agent includes（Unit kilogram）：
Magnesia 30
Magnesium chloride 30
Sodium alkyl sulfonate 0.02
Inorganic aluminum 40
Water 20
（3）The new tile of the shaping is transferred in dry kiln and is dried, wherein dry kiln internal temperature is 60 DEG C, and
Preliminary deashing is carried out to the new tile using air blower；
（4）Raw material needed for choosing dyestuff according to parts by weight is simultaneously configured to dyestuff, and the parts by weight of raw materials of wherein dyestuff is：Sulfonic acid 60
Part, 200 parts of aminobenzoyl, 210 parts of diaminobenzene formyl, 100 parts of talan, 40 parts of hydrogen peroxide, and the dyestuff is delayed
Slowly it is added in overflow dyeing machine；
（5）Described new tile is transferred in overflow dyeing machine, the dyestuff is uniformly coated on the outer of the new tile
Surface, and New colorful brick and tile piece is formed, it is calcined while New colorful brick and tile piece is transferred in burning machine, sintering temperature is
650 DEG C, dyestuff includes fluorescent material, and the color of wherein fluorescent material uses red fluorescence powder；
（6）The New colorful brick and tile piece is transferred under ventilation condition and carries out natural cooling, finished product New colorful brick and tile piece is formed,
And finished product detection is carried out to finished product New colorful brick and tile piece.
Wherein, New Regenerated concrete process for manufacturing colored tiles employs rational raw material and the processing step and bar of science
Contain admixture inside part, raw material so that the increase of azulejo watt intensity, security is improved, using adhesive to New colorful brick and tile
Degree of adhesion reinforcement is carried out, the space between regenerated aggregate concrete is effectively reduced, improves the pore structure of aggregate surface, and then
Improve the shrinkage of regeneration concrete, be placed in using regenerated aggregate concrete in default brick and tile grinding tool and carry out just one-step forming generation
Waste heat be delivered in dry kiln, reach the effect for making full use of heat, so as to save production cost, save the energy, then
Raw aggregate is building waste, and composition is queen closer, concrete, pile crown and mortar, make full use of building waste can improve resource with
Environmental problem, and the consuming to natural resources is reduced, while building waste environmental pollution degree can also be mitigated, in azulejo watt
Outer surface scribble resin, reduce the uneven phenomenon in azulejo watt outer surface, using resin can not only increase azulejo watt it
Between frictional force, and the rough phenomenon of tile surface can be made up, it is not easy to human hand is frayed by the outer surface of azulejo watt,
The security that azulejo watt is used is added, this New colorful brick and tile and its production craft step are simple, easy to operate, and obtained coloured silk
Lasting a long time for brick and tile, with preferable water proofing property, is used also with good security.
Embodiment 2
A kind of production technology of New Regenerated concrete azulejo watt, production stage is as follows：
（1）Weigh regenerated aggregate concrete and be equipped with waterproofing agent mediation, and be sufficiently stirred for, described regenerated aggregate concrete concrete
Composition is cement 15% respectively, regeneration aggregate 46%, admixture 1%, pumping agent for concrete 2%, and remaining is water, wherein regeneration aggregate
Composition include queen closer, concrete, pile crown and mortar, admixture composition include flyash and volcanic ash ground-slag.
(2) regenerated aggregate concrete is placed in default brick and tile grinding tool and carries out just one-step forming, stand 20 hours,
And the waste heat of generation is delivered in dry kiln, the composition of waterproofing agent includes（Unit kilogram）：
Magnesia 50
Magnesium chloride 20
Sodium alkyl sulfonate 0.005
Inorganic aluminum 60
Water 25
（3）The new tile of the shaping is transferred in dry kiln and is dried, wherein dry kiln internal temperature is 50 DEG C, and
Preliminary deashing is carried out to the new tile using air blower；
（4）Raw material needed for choosing dyestuff according to parts by weight is simultaneously configured to dyestuff, and the parts by weight of raw materials of wherein dyestuff is：Sulfonic acid 190
Part, 130 parts of aminobenzoyl, 50 parts of diaminobenzene formyl chloride-1,50 parts of talan, 35 parts of hydrogen peroxide, and the dyestuff is slow
Added in overflow dyeing machine；
（5）Described new tile is transferred in overflow dyeing machine, the dyestuff is uniformly coated on the outer of the new tile
Surface, and New colorful brick and tile piece is formed, it is calcined while New colorful brick and tile piece is transferred in burning machine, sintering temperature is
700 DEG C, the color of wherein fluorescent material uses red fluorescence powder；
(6) the New colorful brick and tile piece is transferred under ventilation condition and carries out natural cooling, form finished product New colorful brick and tile piece,
And finished product detection is carried out to finished product New colorful brick and tile piece.
Wherein, New Regenerated concrete process for manufacturing colored tiles employs rational raw material and the processing step and bar of science
Contain admixture inside part, raw material so that the increase of azulejo watt intensity, security is improved, using adhesive to New colorful brick and tile
Degree of adhesion reinforcement is carried out, the space between regenerated aggregate concrete is effectively reduced, improves the pore structure of aggregate surface, and then
Improve the shrinkage of regeneration concrete, be placed in using regenerated aggregate concrete in default brick and tile grinding tool and carry out just one-step forming generation
Waste heat be delivered in dry kiln, reach the effect for making full use of heat, so as to save production cost, save the energy, then
Raw aggregate is building waste, and composition is queen closer, concrete, pile crown and mortar, make full use of building waste can improve resource with
Environmental problem, and the consuming to natural resources is reduced, while building waste environmental pollution degree can also be mitigated, in azulejo watt
Outer surface scribble resin, reduce the uneven phenomenon in azulejo watt outer surface, using resin can not only increase azulejo watt it
Between frictional force, and the rough phenomenon of tile surface can be made up, it is not easy to human hand is frayed by the outer surface of azulejo watt,
The security that azulejo watt is used is added, this New colorful brick and tile and its production craft step are simple, easy to operate, and obtained coloured silk
Lasting a long time for brick and tile, with preferable water proofing property, is used also with good security.
Embodiment 3
A kind of production technology of New Regenerated concrete azulejo watt, production stage is as follows：
（1）Weigh regenerated aggregate concrete and be equipped with waterproofing agent mediation, and be sufficiently stirred for, described regenerated aggregate concrete concrete
Composition is cement 20% respectively, regeneration aggregate 0%, admixture 8%, pumping agent for concrete 2.5%, and remaining is water, wherein Regenerated Bone
The composition of material includes queen closer, concrete, pile crown and mortar, and admixture composition includes flyash and volcanic ash ground-slag.
(2) regenerated aggregate concrete is placed in default brick and tile grinding tool and carries out just one-step forming, stand 20 hours,
And the waste heat of generation is delivered in dry kiln, the composition of waterproofing agent includes（Unit kilogram）：
Magnesia 70
Magnesium chloride 25
Sodium alkyl sulfonate 0.01
Inorganic aluminum 80
Water 30
（3）The new tile of the shaping is transferred in dry kiln and is dried, wherein dry kiln internal temperature is 50 DEG C, and
Preliminary deashing is carried out to the new tile using air blower；
（4）Raw material needed for choosing dyestuff according to parts by weight is simultaneously configured to dyestuff, and the parts by weight of raw materials of wherein dyestuff is：Sulfonic acid 190
Part, 130 parts of aminobenzoyl, 50 parts of diaminobenzene formyl chloride-1,50 parts of talan, 35 parts of hydrogen peroxide, and the dyestuff is slow
Added in overflow dyeing machine；
（5）Described new tile is transferred in overflow dyeing machine, the dyestuff is uniformly coated on the outer of the new tile
Surface, and New colorful brick and tile piece is formed, it is calcined while New colorful brick and tile piece is transferred in burning machine, sintering temperature is
700 DEG C, the color of wherein fluorescent material uses red fluorescence powder；
(6) the New colorful brick and tile piece is transferred under ventilation condition and carries out natural cooling, form finished product New colorful brick and tile piece,
And finished product detection is carried out to finished product New colorful brick and tile piece.
Wherein, New Regenerated concrete process for manufacturing colored tiles employs rational raw material and the processing step and bar of science
Contain admixture inside part, raw material so that the increase of azulejo watt intensity, security is improved, using adhesive to New colorful brick and tile
Degree of adhesion reinforcement is carried out, the space between regenerated aggregate concrete is effectively reduced, improves the pore structure of aggregate surface, and then
Improve the shrinkage of regeneration concrete, be placed in using regenerated aggregate concrete in default brick and tile grinding tool and carry out just one-step forming generation
Waste heat be delivered in dry kiln, reach the effect for making full use of heat, so as to save production cost, save the energy, then
Raw aggregate is building waste, and composition is queen closer, concrete, pile crown and mortar, make full use of building waste can improve resource with
Environmental problem, and the consuming to natural resources is reduced, while building waste environmental pollution degree can also be mitigated, in azulejo watt
Outer surface scribble resin, reduce the uneven phenomenon in azulejo watt outer surface, using resin can not only increase azulejo watt it
Between frictional force, and the rough phenomenon of tile surface can be made up, it is not easy to human hand is frayed by the outer surface of azulejo watt,
The security that azulejo watt is used is added, this New colorful brick and tile and its production craft step are simple, easy to operate, and obtained coloured silk
Lasting a long time for brick and tile, with preferable water proofing property, is used also with good security.
As known by the technical knowledge, the present invention can be by the embodiment party of other essence or essential feature without departing from its spirit
Case is realized.Therefore, embodiment disclosed above, for each side, is all merely illustrative, and is not only.Institute
Have within the scope of the present invention or be included in the invention in the change being equal in the scope of the present invention.
Claims (6)
1. a kind of production technology of New Regenerated concrete azulejo watt, it is characterised in that comprise the following steps：
（1）Weigh regenerated aggregate concrete and be equipped with waterproofing agent mediation, and be sufficiently stirred for；
(2) regenerated aggregate concrete is placed in default brick and tile grinding tool and carries out just one-step forming, stand 3-20 hours, and
The waste heat of generation is delivered in dry kiln, the new tile being molded；
（3）The new tile of the shaping is transferred in dry kiln and is dried, wherein dry kiln internal temperature is 50-80
DEG C, and preliminary deashing is carried out to the new tile using air blower；
（4）Raw material needed for choosing dyestuff according to parts by weight is simultaneously configured to dyestuff, and the parts by weight of raw materials of wherein dyestuff is：Sulfonic acid 60-
190 parts, 130-300 parts of aminobenzoyl, 50-300 parts of diaminobenzene formyl chloride-1,50-150 parts of talan, hydrogen peroxide 30-40
Part, and the dyestuff is added slowly in overflow dyeing machine；
（5）Described new tile is transferred in overflow dyeing machine, the dyestuff is uniformly coated on the outer of the new tile
Surface, and New colorful brick and tile piece is formed, it is calcined while New colorful brick and tile piece is transferred in burning machine, sintering temperature is
650-850℃；
(6) the New colorful brick and tile piece is transferred under ventilation condition and carries out natural cooling, form finished product New colorful brick and tile piece, and
Finished product detection is carried out to finished product New colorful brick and tile piece.
2. a kind of production technology of New Regenerated concrete azulejo watt according to claim 1, it is characterised in that：The step
Suddenly（1）In regenerated aggregate concrete composition be cement 4-20%, regeneration aggregate 0-46%, admixture 1-8% respectively, concrete is used
Pumping admixture 1.5-2.5%, remaining is water.
3. a kind of production technology of New Regenerated concrete azulejo watt according to claim 2, it is characterised in that：It is described again
The composition of raw aggregate includes queen closer, concrete, pile crown and mortar.
4. a kind of production technology of New Regenerated concrete azulejo watt according to claim 2, it is characterised in that：It is described to mix
Closing material composition includes flyash and volcanic ash ground-slag.
5. a kind of production technology of New Regenerated concrete azulejo watt according to claim 1, it is characterised in that：The step
Suddenly（2）In the composition of waterproofing agent include（Unit kilogram）：
Magnesia 30-70
Magnesium chloride 20-30
Sodium alkyl sulfonate 0.005-0.02
Inorganic aluminum 40-80
Water 20-30.
6. a kind of production technology of New Regenerated concrete azulejo watt according to claim 1, it is characterised in that：The step
Suddenly（5）Middle dyestuff includes fluorescent material, and the color of wherein fluorescent material uses red fluorescence powder.