CN1866589A - 一种掺杂层状锂离子电池正极材料及其制备方法 - Google Patents

一种掺杂层状锂离子电池正极材料及其制备方法 Download PDF

Info

Publication number
CN1866589A
CN1866589A CNA2005100315572A CN200510031557A CN1866589A CN 1866589 A CN1866589 A CN 1866589A CN A2005100315572 A CNA2005100315572 A CN A2005100315572A CN 200510031557 A CN200510031557 A CN 200510031557A CN 1866589 A CN1866589 A CN 1866589A
Authority
CN
China
Prior art keywords
lithium
anode material
solution
doped
priority
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2005100315572A
Other languages
English (en)
Other versions
CN100403587C (zh
Inventor
黄可龙
唐爱东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Central South University
Original Assignee
Central South University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Central South University filed Critical Central South University
Priority to CNB2005100315572A priority Critical patent/CN100403587C/zh
Publication of CN1866589A publication Critical patent/CN1866589A/zh
Application granted granted Critical
Publication of CN100403587C publication Critical patent/CN100403587C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种掺杂层状锂离子电池正极材料LiMn0.5－x Ni0.5－xMo2xO2及其制备方法，属于能源材料技术领域。本发明将掺杂原料Ni、Mn、Mo以化学计量比混合均匀，溶于水或乙醇中；加入柠檬酸溶液搅拌，加入化学计量锂盐溶液，反应得到Li、Ni、Mn、Mo前驱体；在空气气氛中于300～600℃将得到前驱体的进行预分解；于700～1100℃高温煅烧预分解产物，合成得到层状LiNi0.5－xMn0.5－xMo2xO2材料。本发明采用溶胶－凝胶法制备前驱体，使各反应物能达到原子、分子级水平的混合程度，在空气中焙烧前驱体不需要控制气氛，合成工艺简单，生产成本低，采用本发明获得的层状锂离子电池正极材料，结构稳定，充放电比容量高，循环稳定性好。

Description

一种掺杂层状锂离子电池正极材料及其制备方法
技术领域
一种掺杂层状锂离子电池正极材料LiMn0.5-xNi0.5-xMo2xO2及其制备方法，属于能源材料技术领域。
背景技术
锂离子二次电池以其高能量密度、低自放电率和高电压，自20世纪90年代问世以来，被广泛用于现代通讯、空间技术、信息技术、国防等高科技领域，被誉为高效的“绿色能源”。目前市场广泛使用的锂离子电池正极材料LiCoO2价格贵、容量低(130～140mAh/g)、污染大，难以满足日益增长的二次电池的要求，因此提高锂离子电池正极材料的比容量和稳定性，降低成本，是目前改善锂离子电池性能的重要研究方向。LiNiO2与LiMnO2以价格便宜、污染小作为一种目前商用的LiCoO2正极材料的替代材料正逐渐成为锂离子电池研究与开发的热点。但LiNiO2合成条件苛刻，需严格控制合成中的氧气气氛，循环稳定性差，易引起安全问题等，其商业化应用进程一直较缓慢。具有层状结构的LiMnO2放电容量可达190mAh/g以上，是一种具有极大发展前景的正极材料，层状锂锰氧化物LiMnO2属于热力学亚稳态，起骨架支撑作用的Mn3+极不稳定；一方面，在Li+嵌入与脱出过程中易发生Mn3+向更稳定的高价态变化，使晶体结构畸变，向热力学稳定相尖晶石相转变，另一方面，由于高自旋Mn3+(t2g 3eg 1)引起的Jahn-Teller畸变，使得氧的排列发生畸变，难以形成理想的立方紧密堆积，从而严重地影响了其结构稳定性和电化学稳定性。
发明内容
为了简化生产工艺，以锰氧八面体为骨架改善LiNiO2层状的结构，减少阳离子混排及非计量比产物的生成，提高材料的结构稳定性，获得高容量、高循环稳定性的锂离子电池正极材料，本发明提供一种LiNi0.5-xMn0.5-xMo2xO2电池正极材料及其合成方法。
本发明提供的锂离子电池正极材料，其化学分子式为LiNi0.5-xMn0.5-xMo2xO2，其中0≤x≤0.05。
本发明提供的锂离子电池正极材料的合成方法包括以下步骤：
根据锂离子电池正极材料的分子式，将掺杂原料Ni、Mn、Mo以化学计量比混合均匀，溶于水或乙醇中；加入0.1～3.0mol/L的柠檬酸溶液，搅拌，使形成的溶液充分混合均匀，得掺杂原料混合液；
根据化学计量在掺杂原料混合液中加入锂盐溶液，搅拌，使各原料发生反应后形成均匀的混合溶液，用氨水或乙二胺溶液调PH＝7～11，于70～90℃恒温24h，得到Li、Ni、Mn、Mo前驱体；
在空气气氛中于300～600℃将得到前驱体的进行预分解；在空气气氛中于700～1100℃高温煅烧预分解产物，合成得到层状LiNi0.5-xMn0.5-xMo2xO2材料。
本发明采用溶胶-凝胶法制备前驱体，使各反应物能达到原子、分子级水平的混合程度，在空气中焙烧前驱体不需要控制气氛，合成工艺简单，生产成本低，采用本发明获得的层状锂离子电池正极材料LiMn0.5-xNi0.5-xMo2xO2，结构稳定，充放电比容量高，循环稳定性好。
附图说明
图1：锂离子电池正极材料LiNi0.475Mn0.475Mo0.05O2的X射线衍射图；
图2：锂离子电池正极材料LiNi0.475Mn0.475Mo0.05O2的高倍率扫描电镜图；
图3：锂离子电池正极材料LiNi0.475Mn0.475Mo0.05O2的首次充放电循环曲线图。
具体实施方式
以下通过实施例进一步说明本发明。
实施例1：
将0.0475mol镍盐，0.0475mol锰盐，0.005mol钼盐溶于水中，使其混合均匀；将0.1mol柠檬酸配制2mol/L的柠檬酸溶液，加入上述原料混合液中，不断搅拌，使形成的溶液充分混合均匀；称量0.1mol锂盐溶解于水中加入到上述的均匀溶液中，不断搅拌，用氨水溶液调PH＝9，于80℃恒温24h得到前驱体；在空气气氛中400℃将得到前驱体的进行预分解，冷却后研磨；在空气气氛中于900℃高温煅烧预分解产物合成得到的层状LiNi0.475Mn0.475Mo0.05O2材料。XRD衍射结果表明900℃合成得到的LiNi0.475Mn0.475Mo0.05O2化合物具有层状α-NaFeO2结构，结晶完整，呈单一相，无任何杂质峰出现。
将制得的正极活性物质、乙炔黑和聚四氟乙烯(PTFE)粘结剂按一定的比例(85∶10∶5)充分混合均匀，在容器中80-100℃下干燥24h消除水分后，涂于不锈钢网上，用油压机在20Kpa的压力下压成厚度均匀的正极膜。以金属锂片为负极，电解液为含1mol/LLiPF6的EC∶DMC∶EMC/1∶1∶1(w/w)混合溶液，水份含量小于9.34ppm，游离酸HF含量小于2.55ppm。在惰性气体手套箱内组装模拟电池，手套箱操作系统为高纯Ar气氛，水与氧的含量均小于1ppm，组装好的模拟电池在室温25℃或高温55℃下进行测试。用电池程控测试仪检测充放电容量及循环稳定性，采用恒流充、恒流放的模式，充放电电流均为28mA/g，充放电电压范围为2.5-4.6V。
测试结果表明，首次充放电容量分别为233mAh/g，180mAh/g，循环20次后充放电容量别分为185mAh/g，180mAh/g，充放电效率为97.2％图3为LiNi0.475Mn0.475Mo0.05O2的首次充放电循环曲线图。
实施例2：
将0.0475mol镍盐，0.0475mol锰盐，0.005mol钼盐溶于乙醇中，使其混合均匀；采用0.1mol柠檬酸配制2mol/L的柠檬酸乙醇溶液，加入上述原料混合液中，不断搅拌，使形成的溶液充分混合均匀；称量0.1mol锂盐溶解于乙醇中加入到上述的均匀溶液中，不断搅拌，用氨水或乙二胺溶液调PH＝8，于80℃恒温24h得到前驱体；在空气气氛中400℃将得到前驱体的进行预分解，冷却后研磨；在空气气氛中于900℃高温煅烧预分解产物合成得到的层状LiNi0.475Mn0.475Mo0.05O2材料。XRD衍射结果表明900℃合成得到的LiNi0.475Mn0.475Mo0.05O2化合物具有六方层状结构，结晶完整，呈单一相，无任何杂质峰出现。
测试结果表明，首次充放电容量分别为210mAh/g，180mAh/g，循环20次后充放电容量分别为170mAh/g，165mAh/g，充放电效率为97％。

Claims (2)

1.一种掺杂层状锂离子电池正极材料，其特征在于：化学分子式为LiNi0.5-xMn0.5-xMo2xO2，其中0≤x≤0.05。
2.一种要求1所述锂离子电池正极材料的制备方法，其特征在于：将掺杂原料Ni、Mn、Mo以化学计量比混合均匀，溶于水或乙醇中；加入0.1～3.0mol/L的柠檬酸溶液，搅拌，使形成的溶液充分混合均匀，得掺杂原料混合液；
根据化学计量在掺杂原料混合液中加入锂盐溶液，搅拌，反应后用氨水或乙二胺溶液调PH＝7～11，于70～90℃恒温24h，得到Li、Ni、Mn、Mo前驱体；
在空气气氛中于300～600℃将得到前驱体的进行预分解；在空气气氛中于700～1100℃高温煅烧预分解产物。
CNB2005100315572A 2005-05-20 2005-05-20 一种掺杂层状锂离子电池正极材料及其制备方法 Expired - Fee Related CN100403587C (zh)