CN1850931A - 一种石材薄板复合胶及其制备方法 - Google Patents

一种石材薄板复合胶及其制备方法 Download PDF

Info

Publication number
CN1850931A
CN1850931A CN 200610031356 CN200610031356A CN1850931A CN 1850931 A CN1850931 A CN 1850931A CN 200610031356 CN200610031356 CN 200610031356 CN 200610031356 A CN200610031356 A CN 200610031356A CN 1850931 A CN1850931 A CN 1850931A
Authority
CN
China
Prior art keywords
component
amine
modified
weight percentage
inorganic powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200610031356
Other languages
English (en)
Inventor
袁素珍
李东月
王理尧
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUNAN SHENLI INDUSTRIAL Co Ltd
Original Assignee
HUNAN SHENLI INDUSTRIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUNAN SHENLI INDUSTRIAL Co Ltd filed Critical HUNAN SHENLI INDUSTRIAL Co Ltd
Priority to CN 200610031356 priority Critical patent/CN1850931A/zh
Publication of CN1850931A publication Critical patent/CN1850931A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种石材薄板复合用改性环氧胶粘剂,它由A、B两组份构成,A组份由环氧树脂、改性环氧树脂、活性稀释剂、紫外线屏蔽剂、无机粉料制备;B组份由改性胺、促进剂、偶联剂、无机粉料制备;B组份中的改性胺固化剂由脂环胺、脂肪胺、缩水甘油醚分步反应制得。该胶粘剂室温反应固化后,粘接强度高、收缩率极小、耐老化、耐黄变、耐冻融,广泛用于石材、水泥、玻璃、金属的粘接,尤其适用于大理石薄板与瓷板、石质基材的复合。

Description

一种石材薄板复合胶及其制备方法
技术领域
本发明涉及一种胶粘剂及其制备方法,尤其涉及大理石薄板与瓷板、石质基材复合用的胶粘剂及其制备方法。
技术背景
随着石材切割技术的进步,石材薄板厚度从10mm减薄至2mm,甚至0.5mm。高档石材薄板同瓷板、普通石质板材复合制成的装饰材料因装饰效果不受影响,成本价格大幅度降低,受到石材企业和装饰用户的普遍欢迎。一些石材企业试用不饱和聚酯胶粘剂,在石材薄板复合过程中发现了不少缺陷,一是固化速度过快。薄板复合用胶量大、涂刷面宽,调胶、涂胶要花十几分钟,甚至几十分钟,而不饱和聚酯胶粘剂配制一旦完成,几分钟内使用未完就会固化,这给调胶、刷胶带来困难。二是挥发严重,且挥发物有毒。不饱和聚酯胶粘剂含20-30%的溶剂苯乙烯,在室温下易挥发,苯乙烯有较大毒性和刺激性,影响工业卫生和劳动保护。三是该胶收缩率较大,固化收缩造成较大应力,形成复合面空鼓,影响复合材料的强度。
为此,石材企业急需一种质量能满足石材薄板复合要求的胶粘剂。
发明内容
本发明的目的是克服上述胶粘剂的不足,提供一种常温固化、固化速度适中、气味小、无污染、固化收缩率小、固化后强度高、耐老化的石材薄板复合胶粘剂。
本发明是以下述方案实现的,一种石材薄板复合胶粘剂,A组份与B组份的用量比为5∶1(按重量),A组份由环氧树脂、活性稀释剂、无机粉料、紫外线屏蔽剂制成;B组份由自制改性胺、促进剂、偶联剂、无机粉料制成。A组份中的环氧树脂是E-44、E-51、丙烯酸环氧树脂或它们的混合物,重量百分数为38-50%;活性稀释剂为单环氧基化合物,重量百分数为1.2-2.4%;紫外线屏蔽剂重量百分数为0.4-0.6%;无机粉料是石英粉、硅微粉、滑石粉、钛白粉的混合物,重量百分数为48-60%。B组份中改性胺重量百分数为24-36%,由脂环胺、脂肪胺、缩水甘油醚制成;促进剂是咪唑类化合物,重量百分数为8-12%;偶联剂是KH-550,重量百分数为4.8-8.8%;无机粉料是石英粉、硅微粉、滑石粉、钛白粉的混合物,重量百分数为50-60%;A、B两组份各自原料的重量百分数之和均为100%。
改性胺由重量百分数为60-80%的脂环胺、20-30%的脂肪胺、5-10%缩水甘油醚类化合物制得,各组份重量百分数之和为100%。
脂环胺是异佛尔酮二胺、螺环二胺、N一氨乙基哌嗪或它们的混合物;脂肪胺为二乙烯基三胺、三乙烯基四胺、四乙烯基五胺或它们的混合物;缩水甘油醚是聚醚环氧树脂、EA-70环氧树脂、丁基二缩水甘油醚或它们的混合物。
本发明的制备方法包括改性胺的制备方法和薄板复合胶的制备方法。
改性胺的制备方法是:将脂环胺加入反应釜,开动搅拌,慢慢滴加一部分缩水甘油醚,在30分钟内滴加完,继续反应30分钟;接着加入脂肪胺,搅匀后慢慢滴加余下的缩水甘油醚,在30分钟内滴加完,继续反应1小时,即得改性胺。
薄板复合胶A组份的制备方法是:在反应釜中加入环氧树脂、稀释剂、紫外线屏蔽剂搅拌30分钟,加入无机粉料搅拌2小时,出料即成。B组份是在制得改性胺后加入促进剂、偶联剂搅拌30分钟,再加入无机粉料搅拌2小时,过滤即得。
本发明的石材薄板复合胶在使用时,按重量比将A组份5份,B组份1份称好,混合均匀,涂刷于粘接面上,然后贴合、施压,复合胶反应固化将石材薄板和基材牢固地胶接在一起。
本发明中的石材薄板复合胶为A、B双组分改性环氧胶粘剂,通过环氧树脂和改性胺固化剂间的阴离子聚合反应固化,在石材薄板与基板间形成牢固的粘接。阴离子聚合反应的速度是容易控制的,便于现场大面积施工;改性环氧胶粘剂不使用溶剂,采用低分子固化剂预反应的方案可减小固化剂的挥发性,产品更具环保性能;在改性环氧胶粘剂中混配无机粉料,可降低胶的固化收缩率,保证薄合板材的胶合质量。
下面将结合具体实施方式对本发明作进一步说明:
具体实施方式
在1#反应釜中按重量比加入38份E-44、2份丙烯酸环氧树脂、1.5份稀释剂单环氧基化合物,紫外线屏蔽剂0.5份搅拌30分钟,再加入石英粉10份、硅微粉30份、滑石粉9份、钛白粉9份搅拌2小时,过滤得到A组份100份。
在2#反应釜中按重量比加入异佛尔酮二胺70份,开动搅拌慢慢滴加5份缩水甘油醚,在30分钟内滴加完,继续反应30分钟,然后加入二乙烯基三胺23份,搅匀后慢慢滴加2份缩水甘油醚,在30分钟内滴加完,继续反应1小时,过滤出料即得100份改性胺。
在3#反应釜中按重量比加入改性胺30份、咪唑类促进剂10份,KH-550型偶联剂5份搅拌30分钟,再加入石英粉15份、硅微粉25份、滑石粉10份、钛白粉5份搅拌2小时,过滤得B组份100份。
按重量比将A组份5份,B组份1份称好,混合均匀后用于石材薄板复合。

Claims (4)

1一种石材薄板复合胶,由A、B两组份构成,其特征是A组份原料的重量百分数组成为环氧树脂和改性环氧树脂38-50%、单环氧基化合物1.2-1.4%、紫外线屏蔽剂0.4-0.6%、无机粉料48-60%;B组份原料的重量百分数组成为改性胺24-36%、咪唑类促进剂8-12%、KH-550偶联剂4.8-8.8%、无机粉料50-60%,A、B两组份各自原料的重量百分数之和均为100%。
2根据权利要求1所述的石材薄板复合胶,其特征在于B组份中的改性胺由重量百分数为60-80%的脂环胺、20-30%脂肪胺、5-10%缩水甘油醚类化合物反应制得,各成份的重量百分数之和为100%。
3、根据权利要求1所述的石材薄板复合胶,其特征在于A、B两组份中的无机粉料是石英粉、硅微粉、滑石粉、钛白粉的混合物。
4、一种石材薄板复合胶的制备方法,A组分由环氧树脂、改性环氧树脂、单环氧基化合物、紫外线屏蔽剂、无机粉料混合反应而成;B组分由改性胺、咪唑类促进剂、KH-550偶联剂、无机粉料混合反应而成,其特征在于B组分中的改性胺是经下述步骤制成的:
在反应釜中加入脂环胺,开搅拌后慢慢滴加一部分缩水甘油醚,30分钟内加完,继续反应30分钟后加入脂肪胺,搅匀后慢慢滴加余下的缩水甘油醚,30分钟滴加完,继续反应1小时,过滤即得改性胺。
CN 200610031356 2006-03-16 2006-03-16 一种石材薄板复合胶及其制备方法 Pending CN1850931A (zh)