CN1850716A - Method for forming hidden pattern effect on porcelain product - Google Patents
Method for forming hidden pattern effect on porcelain product Download PDFInfo
- Publication number
- CN1850716A CN1850716A CN 200610031712 CN200610031712A CN1850716A CN 1850716 A CN1850716 A CN 1850716A CN 200610031712 CN200610031712 CN 200610031712 CN 200610031712 A CN200610031712 A CN 200610031712A CN 1850716 A CN1850716 A CN 1850716A
- Authority
- CN
- China
- Prior art keywords
- glaze
- ground
- coat enamel
- flux material
- ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a making method for forming concealed pattern effect on a ceramic product, using easily melting, bright, sub-matt or matt glaze, etc as ground coat on the surface of the ceramic product, then smearing transfer pattern of fluxing material prepared of water stop oil, or gum, or cellulose on the glaze or pasting under-glaze decal made of fluxing material, and then firing by kiln and forming the concealed pattern effect. And its key technique uses fusing temperature differences between various ground coats and fluxing material (the fusing temperature of the fluxing material is lower than those of the ground coats and the fluxing material does not emit color itself) to form the concealed pattern effect. And the invention can form a weakly comparative concealed pattern effect.
Description
Technical field
The present invention relates to a kind of making method that on ceramic, forms hidden pattern effect.
Background technology
At present ceramic industry, pattern decorative is carried out on the ceramic surface adopt bat printing under the glaze more, marble paper under the glaze, decoration firing on the glaze, common methods such as aerograph, effect with as above several trailings making is generally comparatively inflexible, and technology content is lower, the market competitiveness is weakening year by year, nearest for some time, the technician of part factory is many in the test of carrying out bat printing on the glaze, but the method that adopts is to add Mierocrystalline cellulose in ground-coat enamel mostly, and then scrape pattern with silk screen, adding Mierocrystalline cellulose in the glaze can make glaze slip sink to the bottom, the knot plate, the glaze that contracts, and be unfavorable for producing in enormous quantities.
Summary of the invention
The objective of the invention is to overcome above-mentioned weak point, a kind of making method that forms hidden pattern effect on ceramic is provided.
Technical scheme of the present invention: a kind of making method that on ceramic, forms hidden pattern effect, it comprises that to ground-coat enamel on the ceramic dry body, ground-coat enamel glaze layer thickness is 0.15～0.35mm, forms pattern speckling with on the ceramic of ground-coat enamel, deliver to fire in the kiln furnitures and form, it is characterized in that:
Ground-coat enamel is to adopt various glaze to make the ground-coat enamel glaze on A, the described ceramic dry body, its ground-coat enamel glaze fineness requirement is crossed 200 mesh sieves, various ground-coat enamel material packages are drawn together fusible glaze or the light glaze are arranged or inferior light glaze or matt glaze, and the melt temperature of ground-coat enamel glaze is 700 ℃～1400 ℃;
Pattern on B, the described ceramic that speckles with ground-coat enamel is to be made as hidden pattern, it is to adopt flux material with the silk screen bat printing or stick marble paper under the glaze that is attached with one deck flux material and a kind of pattern effect of forming, and described flux material is ground dolomite, no lead frit or AE frit; 700 ℃～1000 ℃ of the melt temperatures of flux material;
Flux material in the silk screen bat printing needs to mix well with block water oil or thickness natural gum water or cellulosic oily mater, and its proportioning is oily mater: flux material ≈ 2: 1, and the thickness of its adhered product is 0.05～0.15mm,
The fineness of flux material is to cross 300 mesh sieves, and the thickness that adheres to the flux material on the marble paper is 0.05～0.15mm.
Be to adopt various glaze to make ground-coat enamel, adhere to the flux material (fusing point is 700～1000 ℃) that one deck is used as flux by means such as marble papers under silk-screen or the glaze at the glaze laminar surface again, use kiln furnitures then at 1120～1400 ℃ of left and right sides once-firings.Concrete steps are as follows:
A, to the glazing of ceramic dry body, be about to the ground-coat enamel glaze and be stained with on the surface of dry body, the glaze layer thickness is 0.15～0.35mm, its ground-coat enamel glaze fineness requirement can mistake 200 mesh sieves;
Pattern on B, the described ceramic that speckles with ground-coat enamel is to be made as hidden pattern, it is to adopt flux material with the silk screen bat printing or stick marble paper under the glaze that is attached with one deck flux material and a kind of pattern effect of forming, and described flux material is ground dolomite, no lead frit or AE frit; 700 ℃～1000 ℃ of the melt temperatures of flux material; Be placed on then in the kiln furnitures at 1120～1400 ℃ of left and right sides once-firings.
That is to say, the present invention be on ceramic, adopt various meltable, light, inferior light or glaze such as unglazed are arranged as ground-coat enamel, then in striking on the glaze by the bat printing pattern of block water oil or natural gum or the synthetic flux material of Mierocrystalline cellulose or stick marble paper under the glaze of making of flux material, burn till at 1120～1400 ℃ by kiln furnitures then, to form hidden pattern effect.
Gordian technique of the present invention be utilize the melt temperature difference of various ground-coat enamels and flux material (melt temperature of flux material than the ground-coat enamel temperature at the bottom of, and flux material color development not itself.) form the effect of hidden pattern.
In sum, method design of the present invention is unique, make easily, adopt above-mentioned technology to form a kind of weak correlated hidden pattern effect, can make ceramic form pattern seemingly has like nothing, bright and clean moist, strange and new visual effect, it is a kind of ideal carries out pattern decorative on the ceramic glaze a making method, belongs to the texture of the increase product that the ceramic ware for daily use surface colour decorates and the making method of aesthetic feeling.
Embodiment
A kind of making method that on ceramic, forms hidden pattern, the making method that it is characterized in that described formation hidden pattern is to adopt variously to have light, inferior light or glaze such as unglazed to make ground-coat enamel, adhere to ground dolomite or other flux material (fusing point is 700～1000 ℃) that one deck is used as flux by means such as marble papers under silk-screen or the glaze at the glaze laminar surface again, use kiln furnitures then at 1120～1400 ℃ of left and right sides once-firings.Concrete steps are as follows:
Example one, A, to the glazing of ceramic dry body, be about to the ground-coat enamel glaze and be stained with on the surface of dry body, the glaze layer thickness is 0.15mm, the matt glaze glaze that its ground-coat enamel glaze is a black (glaze fusion melting temperatur is 1180 ℃, and fineness be can mistake 200 mesh sieves);
B, use 120 order silk screens striking ground dolomite pattern on ground-coat enamel speckling with on the ceramic of ground-coat enamel, ground dolomite is modulated with the oil that blocks water, and ratio is a ground dolomite: the oil that blocks water is 1: 2, and ground dolomite thickness is 0.08mm;
C, burn till in the pushed bat kiln fast 1160 ℃ of oxidizing atmospheres and to fire, form a kind of weak correlated hidden pattern effect, can make ceramic form pattern seemingly have like do not have, bright and clean moist, the visual effect that breaks fresh ground.
Example two: A, to the glazing of ceramic dry body, be about to the ground-coat enamel glaze and be stained with on the surface of dry body, the glaze layer thickness is 0.15mm, its ground-coat enamel glaze is the matt glaze glaze of white (glaze fusion melting temperatur is 1180 ℃, and fineness be can mistake 200 mesh sieves);
B, speckling with on the ceramic of ground-coat enamel marble paper under the glaze that is stained with the frit powdered frit that the system of subsides makes with 80 orders, frit powdered frit thickness is 0.08mm;
C, burn till in the pushed bat kiln fast 1160 ℃ of oxidizing atmospheres and to fire, form a kind of weak correlated hidden pattern effect, can make ceramic form pattern seemingly have like do not have, bright and clean moist, the visual effect that breaks fresh ground.
Claims (1)
1, a kind of making method that on ceramic, forms hidden pattern effect, it comprises that to ground-coat enamel on the ceramic dry body, ground-coat enamel glaze layer thickness is 0.15～0.35mm, forms pattern speckling with on the ceramic of ground-coat enamel, deliver to fire in the kiln furnitures and form, it is characterized in that:
Ground-coat enamel is to adopt various glaze to make the ground-coat enamel glaze on A, the described ceramic dry body, its ground-coat enamel glaze fineness requirement is crossed 200 mesh sieves, various ground-coat enamel material packages are drawn together fusible glaze or the light glaze are arranged or inferior light glaze or matt glaze, and the melt temperature of ground-coat enamel glaze is 700 ℃～1400 ℃;
Pattern on B, the described ceramic that speckles with ground-coat enamel is to be made as hidden pattern, it is to adopt flux material with the silk screen bat printing or stick marble paper under the glaze that is attached with one deck flux material and a kind of pattern effect of forming, and described flux material is ground dolomite, no lead frit or AE frit; 700 ℃～1000 ℃ of the melt temperatures of flux material;
Flux material in the silk screen bat printing needs to mix well with block water oil or thickness natural gum water or cellulosic oily mater, and its proportioning is oily mater: flux material ≈ 2: 1, and the thickness of its adhered product is 0.05～0.15mm,
The fineness of flux material is to cross 300 mesh sieves, and the thickness that adheres to the flux material on the marble paper is 0.05～0.15mm.