CN1699291A - Method for scraping shift printing pattern and spray painting on priming coat of ceramic products - Google Patents
Method for scraping shift printing pattern and spray painting on priming coat of ceramic products Download PDFInfo
- Publication number
- CN1699291A CN1699291A CN 200510031461 CN200510031461A CN1699291A CN 1699291 A CN1699291 A CN 1699291A CN 200510031461 CN200510031461 CN 200510031461 CN 200510031461 A CN200510031461 A CN 200510031461A CN 1699291 A CN1699291 A CN 1699291A
- Authority
- CN
- China
- Prior art keywords
- glaze
- ground
- coat enamel
- pattern
- aerograph
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for scraping shift printing pattern and spray painting on priming coat of ceramic products, which consists of making bat printing pigment from common glaze powder or color based glaze powder water-stopping oil, scraping patterns on the bottom glaze surface of right amount of cellulose with 80-160 mesh silk screen, spraying over-glaze color onto the product, firing in 1120-1160 deg. C furnace, the pattern glaze can flow by the motivation of the bottom glaze, thus good connection with the bottom glaze can be resulted, and unique visual effects can be achieved.
Description
Technical field
The present invention relates to a kind of on the ceramic ground-coat enamel method of striking bat printing pattern, aerograph; It belongs to the decoration making method of ceramic ware for daily use.
Background technology
Present ceramic industry, painted on the ceramic surface, carrying out pattern decorative is a kind of general effective means that increases product texture and aesthetic feeling, most of impressing patterns are to adopt the oil that blocks water to transfer powdered frit to scrape pattern under glaze, and the effect that scrapes pattern under glaze is generally comparatively inflexible, if it is excessive to scrape area, then be difficult to drawout, and easily produce many defectives such as excess glaze, look dirty, dislocation, influenced the artistic effect of product, reduced the class of product.Afterwards, ceramic boundary invented again a kind of on the product ground-coat enamel striking method of patterning, this method has overcome problems such as excess glaze, but owing to be difficult to scrape evenly, the class of product is difficult to up equally.
Summary of the invention
The objective of the invention is to avoid above-mentioned deficiency and ward off new footpath in addition, provide a kind of on ceramic ground-coat enamel surface the method for striking bat printing pattern, aerograph.
Technical scheme of the present invention: be the powdered frit of common powdered frit or adding color base to be mixed well with the oil that blocks water make transfer printing pigment, after having added an amount of cellulosic fusible glaze, react glaze, had on the glaze of light or unglazed glaze and scrape pattern, having scraped pattern, on glaze, carry out aerograph with 80～160 order silk screens with common glaze.The present invention so-called a kind of on the ceramic ground-coat enamel method of striking bat printing pattern, aerograph, it is characterized in that it comprises transfer printing pigment preparation, the preparation of ground-coat enamel glaze and striking bat printing pattern, modulation aerograph glaze and aerograph, fires all operations, concrete steps are as follows:
A, transfer printing pigment preparation: be powdered frit to be transferred with the oil that blocks water evenly become transfer printing pigment, its powdered frit is 1: 1 with the configuration proportion of the oil that blocks water, and described powdered frit is common powdered frit or the powdered frit that adds color base;
B, the preparation of ground-coat enamel glaze: add Mierocrystalline cellulose in the ground-coat enamel glaze, its ground-coat enamel glaze and cellulosic configuration proportion are 180～200: 0.8～1, and described ground-coat enamel glaze is fusible glaze, reaction glaze, matt glaze or light glaze etc. is arranged;
C, the suitable common glaze of selection are made the aerograph glaze;
D, striking bat printing pattern: at first to washing the ceramic dry body glazing of water, being about to the ground-coat enamel glaze is stained with on the surface of dry body, again with the transfer printing pigment that modulates on the glazed body of being stained with ground-coat enamel, made silk screen striking bat printing pattern on the ground-coat enamel glaze of pattern with 80～160 orders, then pattern has been checked and revised;
E, at the intact bat printing pattern of striking and after the drying room oven dry, adorn an amount of glaze aligning goods with spray gun again and carry out aerograph, see that the glaze of spraying forms the dewdrop shape and gets final product on pattern, ceramic behind the aerograph is fired in 1120 ℃～1160 ℃ kiln, can make the promotion current downflow of the glaze of pattern, and hold in the mouth knot preferably with ground-coat enamel at ground-coat enamel.
Gordian technique of the present invention is to add an amount of cellulosic fusible glaze, react glaze, having and scrape pattern on light glaze or the matt glaze and carry out aerograph.Add aerograph on the glaze after scraping pattern, not only enriched the level of product colour, also overcome as above many defectives simultaneously, the artistry and the class of product are promoted greatly.Promptly utilize ceramic pigment at fusible glaze, reaction glaze, unglazed and striking bat printing pattern and aerograph on the light glaze arranged, the visual effect that can make pattern generating sparkling and crystal-clear moist (just like the dewdrop shape), breaks fresh ground, having overcome commonly has under light, the matt glaze glaze striking bat printing pattern easily produce all defectives such as excess glaze, look dirty, dislocation, it be a kind of ideal in the ceramic surface colour, carry out pattern decorative, increase the making method of product texture and aesthetic feeling.Present method is mainly used in fusible glaze, reacts glaze, the decoration on light glaze or the matte glaze product is arranged.
Embodiment
The method of striking bat printing pattern, aerograph on the ceramic ground-coat enamel, its concrete steps are as follows:
A, transfer printing pigment preparation: be the common powdered frit and the oil that blocks water to be transferred evenly be transfer printing pigment, its powdered frit is 1: 1 with the configuration proportion of the oil that blocks water;
B, the preparation of ground-coat enamel glaze: add Mierocrystalline cellulose at ground-coat enamel for reacting in the glaze glaze, its ground-coat enamel glaze and cellulosic configuration proportion are 200: 1;
C, aerograph glaze prepare: mix well with suitable common glaze and make the aerograph glaze;
D, striking bat printing pattern: at first to washing the ceramic dry body glazing of water, being about to the ground-coat enamel glaze is stained with on the surface of dry body, again with the transfer printing pigment that modulates on the glazed body of being stained with ground-coat enamel, made silk screen striking bat printing pattern on the ground-coat enamel glaze of pattern with 80～160 orders, then the bat printing pattern on the product has been checked and revised;
E, the glazed body that striking is intact are sent into drying room suitably dries to pattern and can block water, and carries out aerograph then on glazed body, at last ceramic is sent in 1120 ℃～1160 ℃ the kiln and is fired, and promptly burns till qualified product.
Making method of the present invention is summarized as follows: will prepare qualified ground-coat enamel glaze (fusible glaze, react glaze, have light glaze, matt glaze etc. to add Mierocrystalline cellulose in proportion) glazing on the ceramic dry body of washed water; 1: 1 modulation transfer printing pigment (oil that blocks water is transferred powdered frit) on the glazed body of being stained with ground-coat enamel, adopts 80～160 purposes to make silk screen striking bat printing pattern on the ground-coat enamel glaze of pattern transfer printing pigment in proportion.Then the bat printing pattern is checked and revised, product is carried out glaze spraying, deliver at last and fire in the kiln in the pattern back that can block water.
Claims (1)
1, the method for striking bat printing pattern, aerograph on the ceramic ground-coat enamel is characterized in that described method comprises transfer printing pigment preparation, the preparation of ground-coat enamel glaze, the preparation of aerograph glaze, striking bat printing pattern and carry out aerograph on glazed body, and concrete steps are as follows:
A, transfer printing pigment preparation
Be the powdered frit and the oil that blocks water to be transferred evenly be transfer printing pigment, its powdered frit is 1: 1 with the configuration proportion of the oil that blocks water, and described powdered frit is common powdered frit or the powdered frit that adds color base;
B, the preparation of ground-coat enamel glaze
Add Mierocrystalline cellulose in the ground-coat enamel glaze, its ground-coat enamel glaze and cellulosic configuration proportion are 180～200: 0.8～1, and described ground-coat enamel glaze is fusible glaze, reacts glaze, light or matt glaze are arranged;
C, the preparation of aerograph glaze
There are light or matt glaze or other glaze to mix well with common;
D, striking bat printing pattern
At first to washing the ceramic dry body glazing of water, being about to the ground-coat enamel glaze is stained with on the surface of dry body, again with the transfer printing pigment that modulates on the glazed body of being stained with ground-coat enamel, made silk screen striking bat printing pattern on the ground-coat enamel glaze of pattern with 80～160 orders, then pattern is checked and is revised;
E, product is carried out aerograph
The glazed body that striking is intact is sent into drying room suitably dries to pattern and can block water, carry out aerograph then on glazed body, ceramic is delivered to fire in the 1120-1160 ℃ of kiln at last.