CN101805210B - Preparation method of decorative golden ceramic tile - Google Patents
Preparation method of decorative golden ceramic tile Download PDFInfo
- Publication number
- CN101805210B CN101805210B CN2010101226172A CN201010122617A CN101805210B CN 101805210 B CN101805210 B CN 101805210B CN 2010101226172 A CN2010101226172 A CN 2010101226172A CN 201010122617 A CN201010122617 A CN 201010122617A CN 101805210 B CN101805210 B CN 101805210B
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- printed
- preparation
- blank
- blanks
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to the field of ceramic processing manufacture, in particular to a preparation method of a decorative golden ceramic tile. The invention uses an ordinary ceramic tile as a base material, the ceramic tile is firstly cleaned, granular low-temperature melting blocks are printed on the surface of the ceramic tile, blanks printed with the granular low-temperature melting blocks are baked at a high temperature, cooling the blanks to the room temperature, gold trisulfide paste is coated on the blanks, and then, the tiles coated with the gold trisulfide paste is baked and formed again. The decorative golden ceramic tile prepared by the method has magnificent and egyptian yellow effect, and brings strong visual impact to people. When being used, the decorative golden ceramic tile prepared by the invention has the advantages of sun irradiation resistance, wear resistance and good outdoor weather resisting property. In addition, the work procedures are simple, and the operation is easy.
Description
Technical field
The present invention relates to field of ceramic processing manufacture, be specifically related to a kind of preparation method of decorative golden ceramic tile.
Background technology
At present, cause inside and outside wall brick surface corrosion aggravation for building by environment change because the increase of carbon, sulphur emissions makes, particularly gold brick is just dim colourless after 2 years, and physics scratches in addition, loses decorative value soon; Besides under the microbattery effect directly with the effect of gold layer, cause gold brick gold layer corrosion oxidation and lost efficacy.A kind of preparation method of building decorating glazed tile with golden patterns is disclosed among the one Chinese patent application CN200610012956; It is through covering with protective cover with outside part at pattern; Put into the titanium target that vacuum vessel adds some amount, switched on 20～50 minutes, make ceramic tile surface form plated film.Though it is not the ceramic tile effect that makes like this is true to nature, the not anti-sunshine of plated film that forms, wear-resisting.A kind of golden composite ceramic tile and preparation method thereof is disclosed among the number of patent application CN200710030269.4; Adopt be the liquid coating seasoning that contains cu-zn alloy powder that is coated on the ceramic tile after; Apply the preparation method of priming paint again,, and have gold or approximate gold color though this preparation method is simple; But the ceramic tile outdoor weatherability that this method is made is poor, can not further satisfy the needs of modern architecture industry.
Summary of the invention
The objective of the invention is to solve above-mentioned ceramic tile not anti-sunshine, not wear-resisting, deficiencies such as outdoor weatherability difference, and the preparation method of a kind of decorative golden ceramic tile that provides.
For solving above-mentioned technical problem, the present invention adopts following technical scheme: this preparation method is a base material with common ceramic tile, operates according to the following steps.
Step 1 cleaning ceramic tile surface removes dust, greasy dirt, gravel etc.;
Step 2 is printed granular low temperature clinker with silk screen on the blank surface;
The blank that step 3 will be printed with granular low temperature clinker puts into electric furnace or roller kiln are fired;
Step 4 is taken out burning blanks and is chilled to room temperature, applies the sulfuration gold paste;
Step 5 Air drying half a hour, this moment, the sulfuration gold paste of ceramic tile surface was dried to the bright film of brown;
Step 6 will be coated with the blank of sulfuration gold paste and put into electric furnace or roller kiln are fired;
Unacceptable product is removed in step 7 check.
Technical scheme further is:
The sulfuration gold paste that said step 4 applies is Jinsui River, bright gold or the burnish gold that Foshan city Jin Shulin company produces;
The granularity of low temperature clinker was 35 to 45 orders when said step 2 was printed;
When said step 2 is printed with silk screen≤60 orders;
The firing temperature of said step 3 is 1000 to 1100 ℃, and the firing time is 60 to 70 minutes;
Said step 6 firing temperature is 600 to 800 ℃, and the firing time is 70 to 80 minutes.
Compared with prior art, the invention has the beneficial effects as follows: the present invention adopts is that the blank that will be printed with granular low temperature clinker is put into electric furnace or roller kiln are fired shaping, and the cooling back applies the sulfuration gold paste; The blank that will be coated with the sulfuration gold paste is again put into electric furnace or roller kiln are fired shaping; The decoration ceramic tile of processing with this method has the color of approximate gold, and is splendid, gives the intensive visual impact; The anti-sunshine of decorative golden ceramic tile that this method is made, wear-resisting, outdoor weatherability good; And operation is simple, and easy handling can be widely used in the building decoration field.
Embodiment
Embodiment 1: this preparation method is a base material with common ceramic tile, operates according to the following steps: the cleaning ceramic tile surface, remove dust, greasy dirt, gravel etc.; Using 40 order silk screens to print granularity at ceramic tile surface is 35 purpose low temperature clinkers; The blank that is printed with granular low temperature clinker is put into electric furnace fire, temperature is 1000 ℃ of porcelain glaze firing, and the firing time is 60 minutes; Take out burning blanks and be chilled to room temperature, the Jinsui River that produces in blank surface-coated Foshan city Jin Shulin company then, Air drying half a hour, this moment, the Jinsui River on blank surface was dried to the bright film of brown; The blank that will be coated with Jinsui River is again put into electric furnace and is fired, and temperature is 650 ℃ of porcelain Jinsui River decoration firing, and the firing time is 70 minutes; Unacceptable product is removed in check then.
Embodiment 2: this preparation method is a base material with common ceramic tile, operates according to the following steps: the cleaning ceramic tile surface, remove dust, greasy dirt, gravel etc.; Using 45 order silk screens to print granularity on the blank surface is the granular low temperature clinkers of 40 orders; The blank that is printed with granular low temperature clinker is put into roller kiln fire, forming by a firing temperature is 1100 ℃ of porcelain glaze firing, and the firing time is 70 minutes; Take out burning blanks and be chilled to room temperature, apply the bright gold that Foshan city Jin Shulin company produces, Air drying half a hour, this moment, the bright gold of ceramic tile surface was dried to the bright film of brown; The blank that will be coated with bright gold is again put into roller kiln and is fired, and forming by a firing temperature is 750 ℃ of porcelain Jinsui River decoration firing, and the firing time is 80 minutes; Unacceptable product is removed in check then.
The invention is not restricted to the foregoing description, in the scope of in specification sheets of the present invention, describing, those of ordinary skill in the art also can make some conspicuous changes and all should fall within protection scope of the present invention.
Claims (1)
1. the preparation method of a decorative golden ceramic tile, it is characterized in that: this preparation method is a base material with common ceramic tile, operates according to the following steps:
Step 1 cleaning ceramic tile surface removes dust, greasy dirt, gravel;
Step 2 is printed granular low temperature frit with silk screen on the blank surface;
The blank that step 3 will be printed with granular low temperature frit puts into electric furnace or roller kiln are fired;
Step 4 is taken out burning blanks and is chilled to room temperature, applies the sulfuration gold paste;
Step 5 Air drying half a hour;
Step 6 will be coated with the blank of sulfuration gold paste and put into electric furnace or roller kiln are fired;
Unacceptable product is removed in step 7 check;
The granularity of low temperature clinker was 35 to 45 orders when said step 2 was printed, silk screen≤60 orders;
The firing temperature of said step 3 is 1000 to 1100 ℃, and the firing time is 60 to 70 minutes;
Said step 6 firing temperature is 600 to 800 ℃, and the firing time is 70 to 80 minutes.