CN106145679A - A kind of black matrix locus coeruleus is combined pottery glaze - Google Patents
A kind of black matrix locus coeruleus is combined pottery glaze Download PDFInfo
- Publication number
- CN106145679A CN106145679A CN201610680516.4A CN201610680516A CN106145679A CN 106145679 A CN106145679 A CN 106145679A CN 201610680516 A CN201610680516 A CN 201610680516A CN 106145679 A CN106145679 A CN 106145679A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- black matrix
- oxide
- locus coeruleus
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of black matrix locus coeruleus is combined pottery glaze, it is made up of black matrix glaze and locus coeruleus glaze two parts, described black matrix glaze is prepared by the raw materials in: iron sesquioxide 5 12 parts, silicon dioxide 60 80 parts, aluminium sesquioxide 8 15 parts, calcium oxide 5 10 parts, magnesium oxide 12 parts, potassium oxide 25 parts, sodium oxide 13 parts;To be combined pottery glaze the most penetrating for the black matrix locus coeruleus that the present invention makes, and has a third dimension, and good fluidity is the most easy to foaming, good luster;Black matrix glaze is colour-stable, uniform color, after element tire is painted with black matrix glaze, the local bluing mottled enamels material can formulated on surface, can fire the black matrix locus coeruleus pottery glaze that pattern is basically identical, hinge structure makes great progress, and the black matrix locus coeruleus fired to be combined pottery glaze glossiness good, crackle is few, and resistance to mechanical ability is strong.
Description
Technical field
The invention belongs to pottery manufacturing technology field, be specifically related to a kind of black matrix locus coeruleus and be combined pottery glaze.
Background technology
Pottery is thick for this with glaze, and at the bottom of its color or heavy glaze or in outstanding glaze or floating glaze table, the thick muddy work of glaze, glaze layer opalescence jade-like stone moistens,
Being administrations with multiplied departments lives is intended to drip, and third dimension is extremely strong.Pottery is with transmutation as god, and natural transmutation is the elite place of pottery art, is also
Pottery is rely the four seas of becoming famous, the rare part of porcelain woods of making a name.With executing a kind of glaze in firing, once burning till in multicoloured it is then
" enter kiln of the same colour, kiln discharge ten thousand is color ".Protean transmutation effect, defines the mystery that colors changing hue is infinite, in red inner purple, purple
During in dark blue, blue or green, residence is white, white general red, five colours imbibition, form a brightening, and have the title of ", without right, transmutation is unparalleled for pottery ".
Making pottery when, although present technology has been achieved for remarkable progress, but there are some defects,
Pottery fires finished product in manufacturing process from selecting materials to, and period experiences tens of roads production process, accidentally also making of an operation
All that has been achieved is spoiled for one-tenth, and this is also the reason that pottery yield all the time is extremely low.An ancient unit of weight glaze is one layer of decorative layer on pottery surface, is to determine
The principal element that pottery glaze colours generates, utilizes natural raw mineral materials or adds some industrial chemicals and coordinate according to a certain percentage,
Melt under high temperature reducing atmospheres effect and cover the rich jade-like stone in billet surface and moisten gloss and colorful vitreous body layer, tool
There is abundant dicoration, increase the aesthetic feeling of pottery natural trend, make pottery have certain artistic value and enjoying value.
Pottery it is critical only that enamel, enamel transmutation color after being fired determines the value of pottery, white
Pottery have bluish white, grey dawn, creamy white, beautiful white etc., blue pottery have sky blue, acid blue, powder are blue, sapphire blue, peacock blue.Enamel
The difference of formula, the color burnt out is the most variant, and when tradition fires pottery, is to execute one layer of glaze on element tire surface, according to
Environment an ancient unit of weight glaze generation transmutation is fired, it may appear that some uncontrollable decorative pattern or color lumps, the finished product burnt out is more difficult in kiln
Match or configure complete.Therefore, it is badly in need of a kind of pottery burning process that can fire specific decorative pattern at ad-hoc location.
In prior art, black matrix locus coeruleus is combined formula of pottery glaze and preparation method thereof seldom, and the black matrix prepared
Locus coeruleus is combined pottery glaze surface and easily cracks, and glaze wearability and resistance to mechanical ability are poor, beautiful sense deficiency.
Summary of the invention
In order to solve the problems referred to above, the present invention provides a kind of black matrix locus coeruleus to be combined pottery glaze.
The technical solution used in the present invention is:
A kind of black matrix locus coeruleus is combined pottery glaze, is made up of black matrix glaze and locus coeruleus glaze two parts, and described black matrix glaze is
It is prepared by the raw materials in: iron sesquioxide 5-12 part, silicon dioxide 60-80 part, aluminium sesquioxide 8-15 part, oxygen
Change calcium 5-10 part, magnesium oxide 1-2 part, potassium oxide 2-5 part, sodium oxide 1-3 part;
Described locus coeruleus glaze is prepared by the raw materials in: copper oxide 1-3 part, phosphorus pentoxide 1-2 part, oxidation
Titanium 1-2 part, silicon dioxide 60-70 part, aluminium sesquioxide 3-5 part, calcium oxide 10-20 part, magnesium oxide 1-2 part, potassium oxide 1-3
Part, sodium oxide 2-4 part, zinc oxide 2-4 part.
A kind of black matrix locus coeruleus is combined pottery glaze, and described black matrix glaze is prepared by the raw materials in: three
Aoxidize two ferrum 8 parts, silicon dioxide 70 parts, aluminium sesquioxide 12 parts, calcium oxide 8 parts, magnesium oxide 1.5 parts, potassium oxide 3 parts, oxidation
2 parts of sodium;
Described locus coeruleus glaze is prepared by the raw materials in: copper oxide 2 parts, phosphorus pentoxide 1.5 parts, titanium oxide
1.5 parts, silicon dioxide 65 parts, aluminium sesquioxide 4 parts, calcium oxide 15 parts, magnesium oxide 1.5 parts, potassium oxide 2 parts, sodium oxide 3 parts,
Zinc oxide 3 parts.
The present invention also provides for a kind of being combined the method that black matrix locus coeruleus pottery glaze prepared by pottery glaze with above-mentioned black matrix locus coeruleus:
(1) glazing: first immersed by base substrate in the glaze slip of black matrix glaze and take out in a moment, utilizes the water absorption of base substrate, makes glaze slip equal
Even is attached to billet surface;After the slurry of black matrix glaze dries, then dip the glaze slip painting of locus coeruleus glaze with brush pen or brush
Local at base substrate;After glazing, base substrate is loaded saggar;
(2) the glaze firing oxidizing flame stage: first by saggar loading of kiln, then kiln temperature is gradually raised to 1040 DEG C from 0 DEG C, control ventilation
Chimney casket plate is open, and kiln crown skylight is open, in oxidizing atmosphere in kiln, and organic in moisture in saggar, base substrate and kiln and glaze
Things etc. are discharged, and glaze layer starts fusing, and glaze surface is unsintered fine granularity;
(3) the glaze firing reducing flame stage: kiln temperature is at 1040 DEG C-1150 DEG C, and this stage skylight is closed, the closedown of flue casket door or half
Open, coal can not fully burn, and carbon monoxide increases, and in reducing atmosphere in kiln, glaze layer melts, and glaze gradually closes by porous
Close, form rough state;
(4) the neutral flame stage: kiln temperature is raised to 1270 DEG C by 1150 DEG C, in weakly reducing atmosphere in kiln, along with kiln temperature liter
High glaze layer is fused into thick liquid nano and from top to bottom flows, and the melted of glaze layer makes glaze flatten, and glaze layer forms vitreous;
(5) oxidation cooling stage: when kiln temperature is raised to 1250 DEG C-1300 DEG C, soaking is ceased fire after being incubated 1-2 hour, is opened
Wicket, a large amount of oxygen enter in kiln, and in oxidizing atmosphere in kiln, glaze is aoxidized by oxygen, cooling, and glaze colours is formed.
The invention has the beneficial effects as follows: it is the most penetrating that the black matrix locus coeruleus that the present invention makes is combined pottery glaze, has third dimension,
Good fluidity, the most easy to foaming, good luster;Black matrix glaze is colour-stable, uniform color, after element tire is painted with black matrix glaze, and can
With the local bluing mottled enamels material formulated on surface, the black matrix locus coeruleus pottery glaze that pattern is basically identical, hinge structure can be fired
Make great progress, and the black matrix locus coeruleus fired to be combined pottery glaze glossiness good, crackle is few, and resistance to mechanical ability is strong.
Detailed description of the invention
A kind of black matrix locus coeruleus is combined pottery glaze, is made up of black matrix glaze and locus coeruleus glaze two parts, described black matrix glaze
Material is prepared by the raw materials in: iron sesquioxide 5-12 part, silicon dioxide 60-80 part, aluminium sesquioxide 8-15
Part, calcium oxide 5-10 part, magnesium oxide 1-2 part, potassium oxide 2-5 part, sodium oxide 1-3 part;
Described locus coeruleus glaze is prepared by the raw materials in: copper oxide 1-3 part, phosphorus pentoxide 1-2 part, oxidation
Titanium 1-2 part, silicon dioxide 60-70 part, aluminium sesquioxide 3-5 part, calcium oxide 10-20 part, magnesium oxide 1-2 part, potassium oxide 1-3
Part, sodium oxide 2-4 part, zinc oxide 2-4 part.
A kind of black matrix locus coeruleus is combined pottery glaze, and described black matrix glaze is prepared by the raw materials in: three
Aoxidize two ferrum 8 parts, silicon dioxide 70 parts, aluminium sesquioxide 12 parts, calcium oxide 8 parts, magnesium oxide 1.5 parts, potassium oxide 3 parts, oxidation
2 parts of sodium;
Described locus coeruleus glaze is prepared by the raw materials in: copper oxide 2 parts, phosphorus pentoxide 1.5 parts, titanium oxide
1.5 parts, silicon dioxide 65 parts, aluminium sesquioxide 4 parts, calcium oxide 15 parts, magnesium oxide 1.5 parts, potassium oxide 2 parts, sodium oxide 3 parts,
Zinc oxide 3 parts.
The present invention also provides for a kind of being combined the method that black matrix locus coeruleus pottery glaze prepared by pottery glaze with above-mentioned black matrix locus coeruleus:
(1) glazing: first entered by base substrate in the glaze slip of black matrix glaze and take out in a moment, utilizes the water absorption of base substrate, makes glaze slip equal
Even is attached to billet surface;After the slurry of black matrix glaze dries, then dip the glaze slip painting of locus coeruleus glaze with brush pen or brush
Local at base substrate;After glazing, base substrate is loaded saggar;
(2) the glaze firing oxidizing flame stage: first by saggar loading of kiln, then kiln temperature is gradually raised to 1040 DEG C from 0 DEG C, control ventilation
Chimney casket plate is open, and kiln crown skylight is open, in oxidizing atmosphere in kiln, and organic in moisture in saggar, base substrate and kiln and glaze
Thing is discharged, and glaze layer starts fusing, and glaze surface is unsintered fine granularity;
(3) the glaze firing reducing flame stage: kiln temperature is at 1040 DEG C-1150 DEG C, and this stage skylight is closed, the closedown of flue casket door or half
Open, coal can not fully burn, and carbon monoxide increases, and in reducing atmosphere in kiln, glaze layer melts, and glaze gradually closes by porous
Close, form rough state;
(4) the neutral flame stage: kiln temperature is raised to 1270 DEG C by 1150 DEG C, in weakly reducing atmosphere in kiln, along with kiln temperature liter
High glaze layer is fused into thick liquid nano and from top to bottom flows, and the melted of glaze layer makes glaze flatten, and glaze layer forms vitreous;
(5) oxidation cooling stage: when kiln temperature is raised to 1250 DEG C-1300 DEG C, soaking is ceased fire after being incubated 1-2 hour, is opened
Wicket, a large amount of oxygen enter in kiln, and in oxidizing atmosphere in kiln, glaze is aoxidized by oxygen, cooling, and glaze colours is formed.
Embodiment 1
A kind of black matrix locus coeruleus is combined pottery glaze, is made up of black matrix glaze and locus coeruleus glaze two parts, and described black matrix glaze is
It is prepared by the raw materials in: iron sesquioxide 8 parts, silicon dioxide 70 parts, aluminium sesquioxide 12 parts, calcium oxide 8 parts,
Magnesium oxide 1.5 parts, potassium oxide 3 parts, sodium oxide 2 parts;
Described locus coeruleus glaze is prepared by the raw materials in: copper oxide 2 parts, phosphorus pentoxide 1.5 parts, titanium oxide
1.5 parts, silicon dioxide 65 parts, aluminium sesquioxide 4 parts, calcium oxide 15 parts, magnesium oxide 1.5 parts, potassium oxide 2 parts, sodium oxide 3 parts,
Zinc oxide 3 parts.
A kind of it is combined the method that black matrix locus coeruleus pottery glaze prepared by pottery glaze with above-mentioned black matrix locus coeruleus:
(1) glazing: first entered by base substrate in the glaze slip of black matrix glaze and take out in a moment, utilizes the water absorption of base substrate, makes glaze slip equal
Even is attached to billet surface;After the slurry of black matrix glaze dries, then dip the glaze slip painting of locus coeruleus glaze with brush pen or brush
Local at base substrate;After glazing, base substrate is loaded saggar;
(2) the glaze firing oxidizing flame stage: first by saggar loading of kiln, then kiln temperature is gradually raised to 1040 DEG C from 0 DEG C, control ventilation
Chimney casket plate is open, and kiln crown skylight is open, in oxidizing atmosphere in kiln, and organic in moisture in saggar, base substrate and kiln and glaze
Thing is discharged, and glaze layer starts fusing, and glaze surface is unsintered fine granularity;
(3) the glaze firing reducing flame stage: kiln temperature is at 1040 DEG C-1150 DEG C, and this stage skylight is closed, the closedown of flue casket door or half
Open, coal can not fully burn, and carbon monoxide increases, and in reducing atmosphere in kiln, glaze layer melts, and glaze gradually closes by porous
Close, form rough state;
(4) the neutral flame stage: kiln temperature is raised to 1270 DEG C by 1150 DEG C, in weakly reducing atmosphere in kiln, along with kiln temperature liter
High glaze layer is fused into thick liquid nano and from top to bottom flows, and the melted of glaze layer makes glaze flatten, and glaze layer forms vitreous;
(5) oxidation cooling stage: when kiln temperature is raised to 1250 DEG C-1300 DEG C, soaking is ceased fire after being incubated 1-2 hour, is opened
Wicket, a large amount of oxygen enter in kiln, and in oxidizing atmosphere in kiln, glaze is aoxidized by oxygen, cooling, and glaze colours is formed.
Embodiment 2
A kind of black matrix locus coeruleus is combined pottery glaze, is made up of black matrix glaze and locus coeruleus glaze two parts, and described black matrix glaze is
It is prepared by the raw materials in: iron sesquioxide 12 parts, silicon dioxide 80 parts, aluminium sesquioxide 15 parts, calcium oxide 10
Part, magnesium oxide 2 parts, potassium oxide 5 parts, sodium oxide 3 parts;
Described locus coeruleus glaze is prepared by the raw materials in: copper oxide 3 parts, phosphorus pentoxide 2 parts, titanium oxide 2
Part, silicon dioxide 70 parts, aluminium sesquioxide 5 parts, calcium oxide 20 parts, magnesium oxide 2 parts, potassium oxide 3 parts, sodium oxide 4 parts, zinc oxide
4 parts.
Embodiment 3
A kind of black matrix locus coeruleus is combined pottery glaze, is made up of black matrix glaze and locus coeruleus glaze two parts, and described black matrix glaze is
It is prepared by the raw materials in: iron sesquioxide 5 parts, silicon dioxide 60 parts, aluminium sesquioxide 8 parts, calcium oxide 5 parts,
Magnesium oxide 1 part, potassium oxide 2 parts, sodium oxide 1 part;
Described locus coeruleus glaze is prepared by the raw materials in: copper oxide 1 part, phosphorus pentoxide 1 part, titanium oxide 1
Part, silicon dioxide 60 parts, aluminium sesquioxide 3 parts, calcium oxide 10 parts, magnesium oxide 1 part, potassium oxide 1 part, sodium oxide 2 parts, zinc oxide
2 parts.
Claims (2)
1. black matrix locus coeruleus is combined a pottery glaze, is made up of black matrix glaze and locus coeruleus glaze two parts, it is characterised in that: described
Black matrix glaze be prepared by the raw materials in: iron sesquioxide 5-12 part, silicon dioxide 60-80 part, three oxidation
Two aluminum 8-15 parts, calcium oxide 5-10 part, magnesium oxide 1-2 part, potassium oxide 2-5 part, sodium oxide 1-3 part;
Described locus coeruleus glaze is prepared by the raw materials in: copper oxide 1-3 part, phosphorus pentoxide 1-2 part, oxidation
Titanium 1-2 part, silicon dioxide 60-70 part, aluminium sesquioxide 3-5 part, calcium oxide 10-20 part, magnesium oxide 1-2 part, potassium oxide 1-3
Part, sodium oxide 2-4 part, zinc oxide 2-4 part.
A kind of black matrix locus coeruleus the most according to claim 1 is combined pottery glaze, it is characterised in that: described black matrix glaze is
It is prepared by the raw materials in: iron sesquioxide 8 parts, silicon dioxide 70 parts, aluminium sesquioxide 12 parts, calcium oxide 8 parts,
Magnesium oxide 1.5 parts, potassium oxide 3 parts, sodium oxide 2 parts;
Described locus coeruleus glaze is prepared by the raw materials in: copper oxide 2 parts, phosphorus pentoxide 1.5 parts, titanium oxide
1.5 parts, silicon dioxide 65 parts, aluminium sesquioxide 4 parts, calcium oxide 15 parts, magnesium oxide 1.5 parts, potassium oxide 2 parts, sodium oxide 3 parts,
Zinc oxide 3 parts.