CN1807482A - 一种耐黄变水性tdi聚氨酯乳液及其制备方法 - Google Patents

一种耐黄变水性tdi聚氨酯乳液及其制备方法 Download PDF

Info

Publication number
CN1807482A
CN1807482A CN 200610032775 CN200610032775A CN1807482A CN 1807482 A CN1807482 A CN 1807482A CN 200610032775 CN200610032775 CN 200610032775 CN 200610032775 A CN200610032775 A CN 200610032775A CN 1807482 A CN1807482 A CN 1807482A
Authority
CN
China
Prior art keywords
aqueous polyurethane
stain resistant
polyurethane emulsion
resistant aqueous
yellow stain
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200610032775
Other languages
English (en)
Inventor
陈剑
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FOSHAN KAILIN FINE CHEMICALS Co Ltd
Original Assignee
FOSHAN KAILIN FINE CHEMICALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FOSHAN KAILIN FINE CHEMICALS Co Ltd filed Critical FOSHAN KAILIN FINE CHEMICALS Co Ltd
Priority to CN 200610032775 priority Critical patent/CN1807482A/zh
Publication of CN1807482A publication Critical patent/CN1807482A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐黄变水性TDI聚氨酯胶粘剂乳液及其制备方法。耐黄变水性TDI聚氨酯胶粘剂乳液由重量比为甲苯二异氰酸酯4～8％、具有活性羟基的化合物15～30％、耐黄变剂0.1～1.0％、含羧基二元醇1～5％、溶剂5～10％、中和剂0.5～2％和扩链剂低分子多元胺0～1％、水50～70％物质反应合成。本发明首先在保证制得稳定的水性TDI聚氨酯胶粘剂的前提下，通过添加自己合成的甲脒类耐黄变剂，从而可以大大的改善TDI聚氨酯胶粘剂的黄变性能，同时还可以保持TDI聚氨酯胶粘剂的粘接强度。

Description

一种耐黄变水性TDI聚氨酯乳液及其制备方法
技术领域：
本发明涉及化工技术领域，具体的说是一种耐黄变水性TDI聚氨酯乳液及其制备方法。
背景技术：
水性胶粘剂以水为分散介质，无味、无污染，是环境的友好胶粘剂。目前对于聚氨酯胶粘剂来说，大多数是由TDI为原料合成的，该种胶粘剂很容易黄变，而不黄变的水性聚氨酯胶粘剂大都由脂肪族二异氰酸酯为原料合成，该原料不仅相对于TDI价格很高，而且还需要进口。
发明内容：
本发明的目的在于克服现有技术的不足，提供一种耐黄变水性TDI聚氨酯胶粘剂乳液及其制备方法。
耐黄变水性TDI聚氨酯胶粘剂乳液由重量比为甲苯二异氰酸酯4～8％、具有活性羟基的化合物15～30％、耐黄变剂0.1～1.0％、含羧基二元醇1～5％、中和剂0.5～2％、低沸点溶剂5～10％和扩链剂低分子多元胺0～1％、水50～70％物质反应合成。
耐黄变水性TDI聚氨酯胶粘剂乳液的制备方法包括以下步骤：
(1)将甲苯二异氰酸酯与多元醇、耐黄变剂部分或全部，
(2)以NCO/OH＝1.2～3.0的摩尔比在70～90℃进行预聚反应2～6个小时，
(3)预聚完毕后，加入占聚合物总量的1～10％的二元醇，并加入(或不加)与剩余异氰酸根摩尔比为0.4～0.8∶1的低分子的二元醇扩链剂进行扩链反应2～4小时，
(4)扩链完毕后，将体系降温至40℃，加入溶剂降低粘度，再加入与二元醇之比为70％～100％的中和剂，加水乳化，
(5)待乳化完全后继续加入扩链剂，反应1～3个小时
(6)脱去溶剂，得到体系的pH值为6～9，粘度为10～200s的乳液。
本发明针对现有技术的不足，首先在保证制得稳定的水性TDI聚氨酯胶粘剂的前提下，通过添加自己合成的甲脒类耐黄变剂，从而可以大大的改善TDI聚氨酯胶粘剂的黄变性能，同时还可以保持TDI聚氨酯胶粘剂的粘接强度。
具体实施方式：
以下结合一具体实施例对本发明作进一步的说明，
甲苯二异氰酸酯46.31g与聚醚二元醇(分子量2000)200g、结构为
Figure A20061003277500051
的甲脒类耐黄变剂2g的部分或全部，在80℃进行预聚反应2个小时，加入二羟甲基丙酸12g，进行反应4小时，将体系降温至40℃，加入60g丙酮降低粘度，再加入三乙胺9.04g，加水乳化，继续加入乙二胺2.0g，反应2个小时，脱去溶剂，得到体系的pH值为7.2，粘度为15s的乳液。
得到的胶粘剂乳液色泽：半透明状。固含量：30％。稳定性：在60℃下连续烘烤32个小时粘度变化小于5％。剥离强度以棉布-棉布粘接，拉伸速度为25毫米/分钟，28(牛/厘米)。耐黄变性能：在200℃下哄15分钟无黄变发生。
以上所述之实施例只为本发明的较佳实施例，并非以此限制本发明的实施范围，故凡依本发明之形状、构造及原理所作的等效变化，均应涵盖于本发明的保护范围内。

Claims (9)

1、一种耐黄变水性TDI聚氨酯乳液，其特征在于：由重量比为甲苯二异氰酸酯4～8％、具有活性羟基的化合物15～30％、耐黄变剂0.1～1.0％、含羧基二元醇1～5％、中和剂0.5～2％、低沸点溶剂5～10％和扩链剂低分子多元胺0～1％、水50～70％物质反应合成。
2、根据权利要求1所述的一种耐黄变水性TDI聚氨酯乳液，其特征在于：甲苯二异氰酸酯为TDI-100，TDI-80。
3、根据权利要求1所述的一种耐黄变水性TDI聚氨酯乳液，其特征在于：羟基化合物的大分子或低分子为聚醚、聚酯、乙二醇、1，4-丁二醇，1，6-己二醇。
4、根据权利要求1所述的一种耐黄变水性TDI聚氨酯乳液，其特征在于：耐黄变剂为一种甲脒类耐黄变剂其结构为其中R基团为含双键的烃类取代基。
5、根据权利要求1所述的一种耐黄变水性TDI聚氨酯乳液，其特征在于：二元醇是含有COOH基团的小分子二元醇，可以是二羟甲基丙酸、二羟甲基丁酸。
6、根据权利要求1所述的一种耐黄变水性TDI聚氨酯乳液，其特征在于：中和剂可以是有机碱三乙胺、三乙醇胺。
7、根据权利要求1所述的一种耐黄变水性TDI聚氨酯乳液，其特征在于：低沸点溶剂可以是丙酮、丁酮。
8、根据权利要求1所述的一种耐黄变水性TDI聚氨酯乳液，其特征在于：低分子多元胺可以是乙二胺、二乙烯三胺、三乙烯四胺。
9、根据权利要求1所述的一种耐黄变水性TDI聚氨酯乳液的制备方法，其特征在于：该方法的具体步骤为，
(1)将甲苯二异氰酸酯与多元醇、耐黄变剂的部分或全部，
(2)以NCO/OH＝1.2～3.0的摩尔比在70～90℃进行预聚反应2～6个小时，
(3)预聚完毕后，加入占聚合物总量的1～10％的二元醇，并加入(或不加)与剩余异氰酸根摩尔比为0.4～0.8∶1的低分子的二元醇扩链剂进行扩链反应2～4小时，
(4)扩链完毕后，将体系降温至40℃，加入溶剂降低粘度，再加入与二元醇(D)之比为70％～100％的中和剂，加水乳化，
(5)待乳化完全后继续加入扩链剂，反应两个小时后脱去溶剂，得到体系的pH值为6～9，粘度为10～200s的乳液。
CN 200610032775 2006-01-10 2006-01-10 一种耐黄变水性tdi聚氨酯乳液及其制备方法 Pending CN1807482A (zh)