CN1730591A - 一种新型无甲醛环保粘合剂及其制备工艺 - Google Patents
一种新型无甲醛环保粘合剂及其制备工艺 Download PDFInfo
- Publication number
- CN1730591A CN1730591A CN 200510036482 CN200510036482A CN1730591A CN 1730591 A CN1730591 A CN 1730591A CN 200510036482 CN200510036482 CN 200510036482 CN 200510036482 A CN200510036482 A CN 200510036482A CN 1730591 A CN1730591 A CN 1730591A
- Authority
- CN
- China
- Prior art keywords
- auxiliary agent
- formaldehyde
- host
- novel environment
- urea
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种新型无甲醛环保粘合剂及其制备工艺。目前人们在木材加工、电路绝缘板制造、建筑砌块(含人造大理石)生产中，大量使用着含有甲醛、多氯联苯等多种有毒有害物质的粘合剂。本发明包括主剂和助剂，主剂由硅酸钠、聚乙烯醇、聚丙烯铣铵、尿素和硫酸铝组成，助剂由氟硅酸钠和膨润土组成；生产时，将上述主剂成份按一定重量比混合，经加温(90－110℃)、搅拌、完全溶解后，制成主剂；将上述助剂成分按一定重量比经混合、搅拌后，制成助剂；使用时，将主剂和助剂混合搅拌即可。不含有毒有害物质，粘合力强，绝缘环保、生产方便、成本低廉，运用范围十分广泛，粘合建筑砌块时，不受时间、场所等条件限制，可现场调制使用，利于推广。
Description
技术领域
本发明涉及人造木板加工、建筑砌块(包括其它人造石材)生产和电路绝缘板制造领域，特别是涉及一种新型无甲醛环保粘合剂及其制备工艺。
背景技术
目前，人们在木材加工和电路绝缘板的生产中，大量使用粘合剂，而在粘合剂中含有甲醛、多氯联苯等多种有毒有害物质却无法得到彻底解决，污染环境，长期影响着人类的身体健康。
在建筑行业也存在着同样的问题，当废旧的建筑物被拆除后，建筑砌块便成为了垃圾废物，为了移动运输这些废物，人们不得不付出高昂的代价，曾经有人尝试利用水泥粘合建筑砌块以便达到二次使用环保节能的目的，但使用水泥粘合养生期长(28天左右)，加进添加剂也需4-5天，且成本较高，达不到理想的效果。
随着现代经济和科技的迅速发展，大理石的运用范围也越来越广泛，但天然大理石较脆弱、裂纹多，大面积使用或异形处理时较困难，人们不得不利用人造大理石来代替，由于现有的粘合剂达不到所要求的强度，大大影响了人造大理石的运用推广。
发明内容
本发明的目的在于提供一种不含甲醛等有毒物质、快速高效、环保节能的新型粘合剂及其制备工艺。
本发明包括主剂和助剂两部份，主剂由硅酸钠、聚乙烯醇、聚丙烯铣铵、尿素和硫酸铝组成，助剂由氟硅酸钠和膨润土组成。
主剂中各种成份重量(按重量百分比)为：
硅酸钠 95.5-98.7.3％
聚乙烯醇 0.1-0.5％
聚丙烯铣铵 0.1-0.5％
尿素 1-3％
硫酸铝 0.1-0.5％
以上各成份的重量百分比之和为100％；
助剂中各种成份重量为：
氟硅酸钠 17-23％
膨润土 6％
生产时，将硅酸钠、聚乙烯醇、聚丙烯铣铵、尿素和硫酸铝按上述重量比混合，经加温(90-110℃)、搅拌、完全溶解后，进行成品包装即可制成主剂；将氟硅酸钠和膨润土按上述重量比经混合、搅拌后，进行成品包装即可制成助剂。
使用时，将制好的主剂和助剂拆装，混合搅拌即可。
本发明的优点在于不含甲醛、多氯联苯等有毒有害物质，粘合力强，绝缘环保、生产方便、成本低廉，运用范围十分广泛，粘合建筑砌块时，养生期仅为24小时，不受时间、场所等条件限制，可在建筑工地现场调制使用，也可利用各种模具生产不同形状的建筑砌块，具有很高的经济效益和社会效益，开发运用前景非常广阔，利于推广。
具体实施方式
下面以实施例对本发明做进一步详细说明：
实施例一：
本发明包括主剂和助剂两部份，主剂由硅酸钠、聚乙烯醇、聚丙烯铣铵、尿素和硫酸铝组成，助剂由氟硅酸钠和膨润土组成。
主剂中各种成份重量为：
硅酸钠 95.5kg
聚乙烯醇 0.5kg
聚丙烯铣铵 0.5kg
尿素 3kg
硫酸铝 0.5kg
助剂中各种成份重量为：
氟硅酸钠 17kg
膨润土 6kg
生产时，将硅酸钠、聚乙烯醇、聚丙烯铣铵、尿素和硫酸铝按上述重量比混合，经加温(90-110℃)、搅拌、完全溶解后，进行成品包装即可制成100kg主剂；将氟硅酸钠和膨润土按上述重量比经混合、搅拌后，进行成品包装即可制成23kg助剂。
使用时，将制好的主剂和助剂拆装，混合搅拌即可。
实施例二：
本发明主剂中各种成份重量为：
硅酸钠 98.7kg
聚乙烯醇 0.1kg
聚丙烯铣铵 0.1kg
尿素 1kg
硫酸铝 0.1kg
助剂中各种成份重量为：
氟硅酸钠 23kg
膨润土 6kg
生产时，将硅酸钠、聚乙烯醇、聚丙烯铣铵、尿素和硫酸铝按上述重量比混合，经加温(90-110℃)、搅拌、完全溶解后，进行成品包装即可制成100kg主剂；将氟硅酸钠和膨润土按上述重量比经混合、搅拌后，进行成品包装即可制成29kg助剂。
使用时，将制好的主剂和助剂拆装，混合搅拌即可。
Claims (3)
1、一种新型无甲醛环保粘合剂，其特征在于它由主剂和助剂两部份组成，主剂的成份为硅酸钠、聚乙烯醇、聚丙烯铣铵、尿素和硫酸铝，助剂的成份为氟硅酸钠和膨润土。
2、如权利要求1所述的一种新型无甲醛环保粘合剂，其特征在于所述的主剂中各种成份重量(按重量百分比)为：硅酸钠95.5-98.7.3％聚乙烯醇0.1-0.5％ 聚丙烯铣铵0.1-0.5％ 尿素1-3％硫酸铝0.1-0.5％；助剂中各种成份重量为：氟硅酸钠17-23％膨润土6％。
3、一种新型无甲醛环保粘合剂的制备工艺，其特征在于在生产时，将硅酸钠、聚乙烯醇、聚丙烯铣铵、尿素和硫酸铝按上述重量比混合，经加温(90-110℃)、搅拌、完全溶解后，进行成品包装即可制成主剂；将氟硅酸钠和膨润土按上述重量比经混合、搅拌后，进行成品包装即可制成助剂。