CN1657561A - 抗静电抗冲击阻燃聚乙烯管道专用料 - Google Patents
抗静电抗冲击阻燃聚乙烯管道专用料 Download PDFInfo
- Publication number
- CN1657561A CN1657561A CN2004100365897A CN200410036589A CN1657561A CN 1657561 A CN1657561 A CN 1657561A CN 2004100365897 A CN2004100365897 A CN 2004100365897A CN 200410036589 A CN200410036589 A CN 200410036589A CN 1657561 A CN1657561 A CN 1657561A
- Authority
- CN
- China
- Prior art keywords
- shock resistance
- antistatic
- pipe compound
- toughner
- proof polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及抗静电抗冲击阻燃聚乙烯管道专用料及其制备方法，它包括首先按以下组分及含量(重量份)备料：高密度聚乙烯60－80、抗静电剂4－9、阻燃剂5－15、阻燃增效剂2－10、增韧剂12－15、增韧剂22－10、光稳定剂0.2－4、抗氧剂0.1－2，然后将阻燃剂、阻燃增效剂、增韧剂、光稳定剂、抗氧剂和20份高密度聚乙烯共混挤出造粒，得到抗静电抗冲击阻燃母粒，再将抗静电抗冲击阻燃母粒和剩余份数高密度聚乙烯树脂经分散共混后，通过双螺杆挤出机挤出、冷却、干燥、切粒，得到产品。与现有传统技术相比，本发明通过选择高效的抗静电、增韧和阻燃体系，可得到抗静电性、冲击强度和阻燃性能极佳的高密度聚乙烯管道专用料，可以满足煤矿等领域的使用要求。
Description
技术领域：
本发明涉及一种抗静电抗冲击阻燃聚乙烯管道专用料及其制备方法。
背景技术：
目前，煤矿井下的通风管和输水管及抽放瓦斯用管均采用铸铁管等金属管道，存在容易生锈腐蚀、安装不方便、使用寿命短、维护频繁、综合成本高等缺点，塑料管道虽然能够克服金属管道的上述不足，但塑料管道的抗静电性能和抗冲击性能较差，而且容易燃烧，现有的煤矿用塑料管道由于大量添加抗静电剂和阻燃剂而降低了管道的冲击强度，难以达到抗静电性能、抗冲击性能、阻燃性能的综合平衡，极大的限制了塑料管道在煤矿等领域的进一步推广应用。
发明内容：
本发明的目的就是为了克服上述现有技术存在的缺陷，提供了一种兼具优异抗静电性能、抗冲击性能和阻燃性能，可满足煤矿等领域要求的抗静电抗冲击阻燃聚乙烯管道专用料及其制备方法。
本发明的目的可以通过以下技术方案来实现：抗静电抗冲击阻燃聚乙烯管道专用料，其特征在于，包括以下组分及含量(重量份)：
高密度聚乙烯 60-80
抗静电剂 4-9
阻燃剂 5-15
阻燃增效剂 2-10
增韧剂1 2-15
增韧剂2 2-10
光稳定剂 0.2-4
抗氧剂 0.1-2
所述的抗静电剂为导电炭黑。
所述的阻燃剂为溴类化合物。
所述的阻燃增效剂为三氧化二锑、锑酸盐、硼酸盐、亚磷酸酯类或这些化合物的混合物。
所述的增韧剂1为氯化聚乙烯。
所述的增韧剂2为乙烯与高级a-烯烃共聚物。
所述的光稳定剂为苯酮、苯并三唑类、受阻胺类、二氧化钛、氧化锌、炭黑或这些化合物的混合物。
所述的抗氧剂为酚类、亚磷酸酯类、金属钝化剂或这些化合物的混合物。
抗静电抗冲击阻燃聚乙烯管道专用料的制备方法，其特征在于，首先将抗静电剂、阻燃剂、阻燃增效剂、增韧剂1、增韧剂2、光稳定剂、抗氧剂共混挤出造粒，得到抗静电抗冲击阻燃母粒，然后再将抗静电抗冲击阻燃母粒和聚乙烯树脂经分散共混后，通过双螺杆挤出机挤出、冷却、干燥、切粒，得到产品。
与现有传统技术相比，本发明通过选择高效的抗静电、增韧和阻燃体系，可得到抗静电性、冲击强度和阻燃性能极佳的高密度聚乙烯管道专用料，可以满足煤矿等领域的使用要求。
具体实施方式：
下面通过具体实施例对本发明作进一步的说明。
实施例1-2：
以高密度聚乙烯为基料，其各组合物的组分含量(重量份)列于表1中。
(1)将抗静电剂、阻燃剂、阻燃增效剂、增韧剂1、增韧剂2、光稳定剂、抗氧剂和20份高密度聚乙烯置于高速混合机中，混合10-15分钟，转速800rpm。将混合后的物料加入到单螺杆挤出机的料斗中，螺杆的各段温度为170-180℃，螺杆转速300rpm，物料经切粒、风干、冷却制成抗静电抗冲击阻燃母粒。
(2)将抗静电抗冲击阻燃母粒和剩余份数高密度聚乙烯经分散共混后，通过双螺杆挤出机熔融、混炼、挤出、冷却、干燥、切粒和包装，得到产品。螺杆的各段温度为240-280℃，螺杆转速为300rpm，再制成标准样条供性能测试，测试结果列于表2中。
表1抗静电抗冲击阻燃聚乙烯管道专用料的组分含量
| 序号 | 材料名称 | 实施例1 | 实施例2 |
| 1 | 高密度聚乙烯 | 60 | 80 |
| 2 | 抗静电剂 | 5 | 7 |
| 3 | 阻燃剂 | 10 | 13 |
| 4 | 阻燃增效剂 | 3 | 4 |
| 5 | 增韧剂 | 8 | 12 |
| 6 | 光稳定剂 | 1.2 | 1.5 |
| 抗氧剂 | 0.3 | 0.5 |
上述的抗静电剂为导电炭黑。
上述的阻燃剂为十溴二苯乙烷。
上述的阻燃增效剂为三氧化二锑。
上述的增韧剂1为氯化聚乙烯。
上述的增韧剂2为乙烯-辛烯共聚物。
上述的光稳定剂为2-羟基-4-辛氧基二苯甲酮。
上述的抗氧剂为2，6-二叔丁基-4-甲酚。
表2抗静电抗冲击阻燃聚乙烯管道专用料的物理力学性能
| 序号 | 性能指标 | 单位 | 实施例1 | 实施例2 |
| 1 | 拉伸强度 | MPa | 20.7 | 21.2 |
| 2 | 断裂伸长率 | ％ | 170 | 180 |
| 3 | 表面电阻 | Ω | 3.6×104 | 3.1×104 |
| 4 | 冲击强度 | KJ/m2 | 28 | 31 |
| 5 | 氧指数 | / | 32 | 33 |
Claims (9)
1.抗静电抗冲击阻燃聚乙烯管道专用料，其特征在于，包括以下组分及含量(重量份)：
高密度聚乙烯 60-80
抗静电剂 4-9
阻燃剂 5-15
阻燃增效剂 2-10
增韧剂1 2-15
增韧剂2 2-10
光稳定剂 0.2-4
抗氧剂 0.1-2
2.根据权利要求1所述的抗静电抗冲击阻燃聚乙烯管道专用料，其特征在于，所述的抗静电剂为导电炭黑。
3.根据权利要求1所述的抗静电抗冲击阻燃聚乙烯管道专用料，其特征在于，所述的阻燃剂为溴类化合物。
4.根据权利要求1所述的抗静电抗冲击阻燃聚乙烯管道专用料，其特征在于，所述的阻燃增效剂为三氧化二锑、锑酸盐、硼酸盐、亚磷酸酯类或这些化合物的混合物。
5.根据权利要求1所述的抗静电抗冲击阻燃聚乙烯管道专用料，其特征在于，所述的增韧剂1为氯化聚乙烯。
6.根据权利要求1所述的抗静电抗冲击阻燃聚乙烯管道专用料，其特征在于，所述的增韧剂2为乙烯与高级a-烯烃共聚物。
6.根据权利要求1所述的抗静电抗冲击阻燃聚乙烯管道专用料，其特征在于，所述的光稳定剂为苯酮、苯并三唑类、受阻胺类、二氧化钛、氧化锌、炭黑或这些化合物的混合物。
7.根据权利要求1所述的抗静电抗冲击阻燃聚乙烯管道专用料，其特征在于，所述的抗氧剂为酚类、亚磷酸酯类、金属钝化剂或这些化合物的混合物。
8.抗静电抗冲击阻燃聚乙烯管道专用料的制备方法，其特征在于，首先将抗静电剂、阻燃剂、阻燃增效剂、增韧剂1、增韧剂2、光稳定剂、抗氧剂共混挤出造粒，得到抗静电抗冲击阻燃母粒，然后再将抗静电抗冲击阻燃母粒和聚乙烯树脂经分散共混后，通过双螺杆挤出机挤出、冷却、干燥、切粒，得到产品。