CN1624497A - 透光性片材和荧火屏 - Google Patents

透光性片材和荧火屏 Download PDF

Info

Publication number
CN1624497A
CN1624497A CNA200410087405XA CN200410087405A CN1624497A CN 1624497 A CN1624497 A CN 1624497A CN A200410087405X A CNA200410087405X A CN A200410087405XA CN 200410087405 A CN200410087405 A CN 200410087405A CN 1624497 A CN1624497 A CN 1624497A
Authority
CN
China
Prior art keywords
light
sheet
light diffusing
sheet material
color
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA200410087405XA
Other languages
English (en)
Other versions
CN100356200C (zh
Inventor
大泽太
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Publication of CN1624497A publication Critical patent/CN1624497A/zh
Application granted granted Critical
Publication of CN100356200C publication Critical patent/CN100356200C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种可以抑制透光率降低同时具有良好色再现性的光扩散性片材和荧光屏，是在透光性母材中分散光扩散性微粒子而成的光扩散性片材和(或)着色片材，且涉及一种透光性片材，其特征在于上述光扩散性片材和(或)着色片材满足下式(1)：－0.5％≤T1－T2≤5％(1)(式中，T1表示波长为450nm的光的透光率(％)，T2表示波长为600nm的光的透光率(％))。以及荧光屏用的光扩散性片材和(或)着色片材，和具有上述荧光屏用的光扩散性片材和(或)着色片材的荧光屏。

Description

透光性片材和荧光屏
技术领域
本发明涉及一种透光性片材和荧光屏。更详细地说，本发明涉及特别适用于例如LCD(液晶显示器)、DMD(数字微镜器件)等的单光源穿透式投影电视中的光扩散性片材和(或)着色片材以及荧光屏。
背景技术
以往，用于投影电视的光源主要是3管的阴极射线管(CRT)光源，但是最近随着数字化、高精细化、小型化的要求，LCD、DMD等的单管光源的使用增加了。虽然LCD、DMD等的单管光源较之上述CRT具有优点，但是现状是光源输出功率还没有达到CRT的性能。
另一方面，投影电视的显示器必须要有一定的色再现性，通常设定色温在10000K左右。为了保持这样的色温，一般是进行光源以及电路的调节。
发明内容
由于单光源型的光源输出功率低，如果调节色温会产生所谓亮度变低的问题。因此希望尽可能不进行色调节，就能保持色温较高的光扩散性片材和(或)着色片材以及荧光屏。
本发明者们经过各种研究，结果发现通过使得光扩散性片材和(或)着色片材的透光特性具有一定的关系，可以保持色温较高从而实现了本发明。
因此，本发明的透光性片材是在透光性母材中分散光扩散性微粒而形成的光扩散性片材和(或)着色片材，其特征在于上述光扩散性片材和(或)着色片材满足下式(1)
-0.5％≤T1-T2≤5％                  (1)
(式中，T1表示波长为450nm的光的透光率(％)，T2表示波长为600nm的光的透光率(％))
这种根据本发明的透光性片材，优选在上述透光性片材中分散波长选择性的着色剂而成的片材。
这种根据本发明的透光性片材，优选在上述光扩散性片材中含有的光扩散性微粒子中至少一种是无机微粒子。
另外，本发明的荧光屏用的光扩散性片材和(或)着色片材，是在上述光扩散性片材和(或)着色片材的至少一面的全部或者一部分上形成菲涅耳透镜而成。
另外，本发明的其他荧光屏光用的扩散性片材和(或)着色片材由上述光扩散性片材和(或)着色片材构成，其可用作双凸透镜。
而且，本发明的其它荧光屏用的光扩散性片材和(或)着色片材是由上述光扩散性片材和(或)着色片材构成，在双凸透镜的观察者的侧面上形成该光扩散性片材和(或)着色片材。
而且，本发明的其它荧光屏用的光扩散性片材和(或)着色片材是由上述光扩散性片材和(或)着色片材构成，该光扩散性片材和(或)着色片材是定位在双凸透镜的更前面的前面板用的透光性片材。
另外，本发明的荧光屏具有上述荧光屏用的光扩散性片材和(或)着色片材。
根据本发明，提供了在透光性母材中分散光扩散性微粒子而成的光扩散性片材和(或)着色片材，通过上述光扩散性片材和(或)着色片材满足特定式(1)，可以抑制透光率的降低，同时可以得到具有良好色再现性的透光性片材。
这种具有透光性片材的荧光屏，特别适用于例如单光源式穿透式投影电视。
实施发明的最佳方案
本发明提供了在透光性母材中分散光扩散性微粒子而成的光扩散性片材和(或)着色片材，重要的是上述光扩散性片材和(或)着色片材满足下式(1)：
-0.5％≤T1-T2≤5％               (1)
(式中，T1表示波长为450nm的光的透光率(％)，T2表示波长为600nm的光的透光率(％))
其中，透光率具体地说是用分光光度计测定得到的。
用作本发明的透光性母材，只要是透光率高的光学部件，任何一种都可以。作为优选的具体例子，可以例举丙烯、苯乙烯、聚碳酸酯、聚酯，以及上述多个的共聚物等。
在T1-T2不足-0.5％的情况下，色温不充分从而不能达到本发明的目的，另一方面，在超过5％的情况下，能够满足色温，但是难以得到足够的透光率和良好的再现性，因此不优选。
作为一种用于满足上式(1)的具体方法，可列举的是混合波长选择性着色剂、具体讲为蓝色系着色剂的方法。联合使用种类、性状不同的多种着色剂，可将这些混合的比率控制在适当的范围内。
作为蓝色系着色剂，只要满足上式(1)的范围，无论什么样的染料、颜料等均可使用。优选例如群青染料。适于本发明的着色剂可以是例如第一化成公司制造的群青(产品编号1900)等。
以透光性母材为100重量份计，蓝色系着色剂的添加量为0.003-0.05重量份，优选0.03-0.01重量份。此外，该兰色着色剂的添加量越增加，发现色温越易于升高，其透光率降低，因此在满足式(1)的范围内，混合量优选尽可能少量。
作为满足上式(1)的其他方法可以是为满足上式(1)选择使用在透光型母材中混合光扩散性微粒子。混合的光扩散性微粒可以是一类，还可以是同时使用种类、大小、形状、光学特性各异的多种光扩散性微粒子。还可以进一步混合蓝色系着色剂。
在本发明中，例如透光性母材中含有的光扩散性微粒内的至少一种可以是无机微粒子。作为这样的无机微粒子，特别优选为硅石类的玻璃微珠，也可以使用碳酸镁、硫酸镁等。即使仅仅使用玻璃微珠，也可以满足上式(1)，但是也可以和丙烯或丙烯-苯乙烯共聚物等的有机交联微珠同时使用，在同时使用两者的情况下，为了满足式(1)，玻璃微珠的比例通常优选设定在50重量％以上。玻璃微珠的直径优选1-30μm，特别优选5-20μm。
满足上式(1)的本发明的透光性片材可以用于各种用途，那时为了适用于具体的用途，可以适当地加工。例如本发明的透光性片材可以用于透光性荧光屏，特别适用于投影电视使用的透光性荧光屏。而且，在本发明的透光性片材中，在其单面或双面的全部或一部分上可以设有适当透明或半透明的透镜。作为可以那样设有的透明透镜的优选具体例子，可以列举双凸透镜和菲涅尔透镜。另外，本发明的光扩散性片材，可以将其本身加工成双凸形状，作为光扩散性的双凸透镜使用。另外即使不特别设有透镜等，也可以作为在双凸透镜的观察者一侧的平板状的前面板使用。
这种根据本发明的光扩散性片材和(或)着色片材可以适用于各种用途，特别适用于以前用的荧光屏，例如透光式荧光屏，特别是单光源式穿透式投影电视。
实施例
下面例举具体的实施例用于更详细地说明本发明。
<实施例1-9，比较例1-2>
表1-2表示各个实施例以及用于与其比较的采用现有技术的比较例的条件，以及色温测定的结果。
其中根据如下要领形成光扩散性片材和(或)着色片材。
100重量份由丙烯/苯乙烯共聚树脂(新日鐡化学公司制造，商品名MS600)组成的透光性母材中添加表1所示重量份的光扩散性微粒子，或兰色着色剂，采用菲涅耳透镜制造用的挤压成形机形成厚度为2mm的平板片材，然后通过在该平板片材表面上加工成为形菲涅耳透镜形状，得到菲涅耳透镜片材。
而且，在该观察者面侧，配置由在不含有光扩散微粒子的丙烯酸树脂(住友化学会社制造，商品名MH)中添加以及未添加蓝色系着色剂的材料组成的厚度为1mm的双凸透镜片材，构成穿透式荧光屏。该穿透式荧光屏安装在50英寸的液晶光源式背投型投影电视的画面上，向该荧光屏投射白光，在距离画面2m处测定色温。
另一方面，切下上述制成的各种菲涅耳透镜片材的中心部分，用分光光度计(岛津制作所制造，商品名UV-2450)分别测定波长450nm和600nm部分的透光率。结果如表1和表2所示。表2中的评价如下。
◎：非常好
○：良好
×：不好
该结果与比较例1中仅仅使用有机类交联微珠作为光扩散性微粒子相比，使用满足式(1)的蓝色系着色剂或者无机微粒子的实施例可得到良好的色再现性，色温达10000K以上。
表1
                              双凸透镜                                                      菲涅尔透镜
透光性母材      兰色着色剂               透过率  透光性母材                     光扩散性微粒子      兰色着色剂               透过率
  制品名 制品名   重量份    T1(450nm)   T2(600nm)   ΔTT1-T2     制品名              1           2 制品名   重量份   T1(450nm)   T2(600nm)   ΔTT1-T2
制品名   重量份 制品名   重量份
实施例1     MH   无   -    91.5   92   -0.5     MS600 SM10X-12     1.8   无     -   群青   0.005   87   85.5   1.5
实施例2     MH   无   -    91.5   92   -0.5     MS600 SM10X-12     1.8   无     -   群青   0.01   85   80   5
实施例3     MH   无   -    91.5   92   -0.5     MS600 SM10X-12     1.8   无     -   群青   0.003   87.5   87.5   0
实施例4     MH   无   -    91.5   92   -0.5     MS600 SM10X-12     0.9  EMB-20     0.9   无   -   87   87   0
实施例5     MH   无   -    91.5   92   -0.5     MS600 SM10X-12     0.6  EMB-20     12   无   -   87   86   1
实施例6     MH   无   -    91.5   92   -0.5     MS600 EMB-20     1.8   无     -   无   -   87   84.5   2.5
实施例7     MH   群青   0.01    89   87.5   1.5     MS600 SM10X-12     1.8   无     -   无   -   89.5   90   -0.5
实施例8     MH   群青   0.02    87   82   5     MS600 SM10X-12     1.8   无     -   无   -   89.5   90   -0.5
实施例9     MH   群青   0.006    89.5   89.5   0     MS600 SM10X-12     1.8   无     -   无   -   89.5   90   -0.5
比较例1     MH   无   -    91.5   92   -0.5     MS600 SM10X-12     1.8   无     -   无   -   88   90   -2
比较例2     MH   无   -    91.5   92   -0.5     MS600 SM10X-12     1.8   无     -   群青   0.012   83   77   6
MH：住友化学工业公司制造
MS600：新日鐡化学公司制造
SM10X-12JH：積水化学成品工业公司制造
EMB-20：ボッタ一ズバロティ一ニ公司制造
表2
            双凸+菲涅耳   ΔK               评价
              透过率   透过率   色温   综合
  T1(450nm)   T2(600nm)   ΔTT1-T2
实施例1   796   78.7   0.9   10520     ◎   ○   ○
实施例2   77.8   73.6   4.2   11490     ○   ◎   ○
实施例3   80.1   80.5   -0.4   10206     ◎   ○   ○
实施例4   79.6   80.0   -0.4   10200     ◎   ○   ○
实施例5   79.6   79.1   0.5   10362     ◎   ○   ○
实施例6   79.6   77.7   1.9   11110     ◎   ○   ○
实施例7   79.7   78.8   0.9   10520     ◎   ○   ○
实施例8   77.9   73.8   4.1   11490     ○   ◎   ○
实施例9   80.1   80.6   -0.4   10206     ◎   ○   ○
比较例1   80.5   82.8   -2.3   9160     ◎   ×   ×
比较例2   75.9   70.8   5.1   12530     ×   ◎   ×
MH：住友化学工业公司制造
MS600：新日鐡化学公司制造
SM10X-12JH：積水化学成品工业公司制造
EMB-20：ポッタ一ズバロティ一ニ公司制造

Claims (7)

1.一种透光性片材，是在透光性母材中分散光扩散性微粒子而成的光扩散性片材和(或)分散波长选择性的着色剂而成的着色片材，上述光扩散性片材和(或)着色片材满足下式(1)：
-0.5％≤T1-T2≤5％      (1)
式中，T1表示波长为450nm的光的透光率(％)，T2表示波长为600nm的光的透光率(％)。
2.权利要求1记载的光扩散性片材，所述的光扩散性片材中含有的光扩散性微粒子中至少一种是无机微粒子。
3.一种荧光屏用透光性片材，是在权利要求1-2的任一项记载的光扩散性片材和(或)着色片材的至少一面的全部或一部分上形成菲涅耳透镜而成的。
4.一种荧光屏用透光性片材，由权利要求1-2的任一项记载的光扩散性片材和(或)着色片材组成，可用作双凸透镜。
5.一种荧光屏用透光性片材，由权利要求1-2的任一项记载的光扩散性片材和(或)着色片材组成，在双凸透镜的观察者侧面形成该光扩散性片材和(或)着色片材而组成。
6.一种前面板用透光性片材，由权利要求1-2的任一项记载的光扩散性片材和(或)着色片材组成，该光扩散性片材和(或)着色片材位于双凸透镜更前面。
7.一种荧光屏，具有权利要求4-6的任一项记载的荧光屏用光扩散性片材和(或)着色片材。
CNB200410087405XA 2003-09-25 2004-09-24 透光性片材和荧光屏 Expired - Fee Related CN100356200C (zh)