CN1587163A - 抗静电地砖 - Google Patents
抗静电地砖 Download PDFInfo
- Publication number
- CN1587163A CN1587163A CN 200410050316 CN200410050316A CN1587163A CN 1587163 A CN1587163 A CN 1587163A CN 200410050316 CN200410050316 CN 200410050316 CN 200410050316 A CN200410050316 A CN 200410050316A CN 1587163 A CN1587163 A CN 1587163A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- chloride resin
- water
- ground limestone
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
抗静电地砖是属于抗静电材料的改进。本发明就是提供一种具有寿命长、性能好、安装使用方便的抗静电地砖。本发明就是采用如下技术方案：首先，以重质碳酸钙，其颗粒为300－500目，占混合物总重量的50％－70％，同PVC树脂占混合物的总重量30％－50％组成混合物；然后，以CPE增强剂占重质碳酸钙与PVC树脂混合物重量的10％－25％加入重质碳酸钙与PVC树脂混合物中；以亚导体导电粉占重质碳酸钙与PVC树脂混合物重量的0.8％－1.5％加入重质碳酸钙与PVC树脂混合物中，均匀混合、挤压而成。
Description
技术领域：
本发明是属于抗静电材料的改进。
背景技术：
现有防静电地板有树脂、水泥刨花板、钢制板、铝制板四种。树脂、水泥刨花板的表面粘贴0.6-0.8mm的PVC树脂板面，底表面均粘贴0.15-0.2mm铝箔；钢制板、铝制板的表面粘贴0.6-0.8mm的PVC树脂板面。但其缺点是树脂的脆性大，板芯板面极易断裂、寿命短；水泥刨花板防潮性差，板芯遇潮鼓胀、板面断裂；钢制、铝制板面是由胶质板与金属之间的胶合，板面易崩裂。
上述品类的防静电性能均为短暂的周期性，例如，钢制板为例，防静电性能有效期最多保持在三年时间左右；上述品类地板只能空设，不能在地面上直接铺设安装，因此，施工比较复杂。
发明内容：
本发明就是针对上述问题，提供一种具有寿命长、性能好、安装使用方便的抗静电地砖。
本发明就是采用如下技术方案：
首先，以重质碳酸钙(通称为石粉，其分子式为CaCO3)，其颗粒为300-500目，占混合物总重量的50％-70％，同PVC树脂占混合物的总重量30％-50％组成混合物；
然后，以CPE增强剂占重质碳酸钙与PVC树脂混合物重量的10％-25％加入重质碳酸钙与PVC树脂混合物中；以亚导体导电粉占重质碳酸钙与PVC树脂混合物重量的0.8％-1.5％加入重质碳酸钙与PVC树脂混合物中，均匀混合、挤压而成。
本发明的有益效果：
本发明的抗静电地砖材料之一是亚导体导电材料，它使地砖成一个庞大的电容器，当电子设备运行空间产生静电荷时，它能迅速收紧吸纳空间电荷(相当于电容器充电过程)，当吸纳的静电荷达到峰值电压时，它能通过抗静电地砖体内的亚导体导电材料迅速释放集于地砖上的静电荷于大地(相当于电容器的放电过程)，就这样保护了所在空间范围的电子设备不受静电放电的危害。
本发明的地砖能克服现有防静电地板的所有缺点；而且具有不起层、不崩裂、刚度强、韧性好；又具有抗静电、防水、阻燃性能；使用寿命达10年以上。
本发明的地砖既能空设，又可实铺地面，为使用者提供了方便。
经北京化工研究院、四川大学协同试验测得本发明地砖的电阻值为1×105欧姆-1×1011欧姆，均布荷载为7480牛顿/米2；符合行业标准，HJ-T10796-2001标准。
具体实施方式：
为了增强热稳定性、光洁稳定性和润滑性还可在原配料的基础上加上少量硬脂酸铅、硬脂酸钡、硬脂酸、三盐、二盐等。
为使本发明的地砖色彩同整个房间色彩协调，还可在原配料的基础上加入少量载体拼色剂；
为增强光洁度，在原配料的基础上加入少量增塑剂等。
该发明的制砖工艺为常规制砖工艺，其加热温度控制在120-170℃为宜。主要生产设备为双螺杆挤出机组、高低温混料缸、切割机、模具。
附图说明：
图1是本发明的工艺流程图。
实施例1：
重质碳酸钙70％，PVC树脂30％的混合物；
CPE增强剂占重质碳酸钙和PVC树脂混合物重量的10％；
亚导体导电粉占重质碳酸钙和PVC树脂混合物重量的1.5％。
实施例2：
重质碳酸钙55％，PVC树脂45％的混合物；
CPE增强剂占重质碳酸钙和PVC树脂混合物重量的11％；
亚导体导电粉占重质碳酸钙和PVC树脂混合物重量的1.0％。
实施例3：
重质碳酸钙50％，PVC树脂50％的混合物；
CPE增强剂占重质碳酸钙和PVC树脂混合物重量的15％；
亚导体导电粉占重质碳酸钙和PVC树脂混合物重量的1.3％。
Claims (4)
1、抗静电地砖，其特征是以重质碳酸钙，其颗粒为300-500目，占混合物总重量的50％-70％，同PVC树脂占混合物的总重量30％-50％组成混合物；以CPE增强剂占重质碳酸钙与PVC树脂混合物重量的10％-25％加入重质碳酸钙与PVC树脂混合物中；以亚导体导电粉占重质碳酸钙与PVC树脂混合物重量的0.8％-1.5％加入重质碳酸钙与PVC树脂混合物中，均匀混合、挤压而成。
2、根据权利要求1所述的抗静电地砖，其特征是重质碳酸钙70％，PVC树脂30％的混合物；CPE增强剂占重质碳酸钙和PVC树脂混合物重量的10％；亚导体导电粉占重质碳酸钙和PVC树脂混合物重量的1.5％。
3、根据权利要求1所述的抗静电地砖，其特征是重质碳酸钙55％，PVC树脂45％的混合物；CPE增强剂占重质碳酸钙和PVC树脂混合物重量的11％；亚导体导电粉占重质碳酸钙和PVC树脂混合物重量的1.0％。
4、根据权利要求1所述的抗静电地砖，其特征是重质碳酸钙50％，PVC树脂50％的混合物；CPE增强剂占重质碳酸钙和PVC树脂混合物重量的15％；亚导体导电粉占重质碳酸钙和PVC树脂混合物重量的1.3％。