CN1566227A - Colored latex paint for external wall of building - Google Patents
Colored latex paint for external wall of building Download PDFInfo
- Publication number
- CN1566227A CN1566227A CN 03145694 CN03145694A CN1566227A CN 1566227 A CN1566227 A CN 1566227A CN 03145694 CN03145694 CN 03145694 CN 03145694 A CN03145694 A CN 03145694A CN 1566227 A CN1566227 A CN 1566227A
- Authority
- CN
- China
- Prior art keywords
- wall
- paint
- emulsion according
- building paint
- building
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a colored latex paint for external wall of building prepared from base paint and pigment, the constituents and content are water, auxiliary, heavy calcium, silica, dielectric aqueous dispersion, polyoxythylene fatty alcohol ether wetting agent, defoaming agent, mildew preventive, film forming auxiliary, thickening agent, ammoniacal liquor, pyrroles (CB12), ferrum red (CB3).
Description
Technical field the present invention relates to a kind of emulsion paint, particularly a kind ofly is used for emulsion paint on the external wall, that adopt the aqueous color paste toning.
Background technology is along with the fast development of Building Trade in China and improving constantly of living standards of the people, and people have had new requirement to the improvement of living environment, and is also more and more higher to the decoration requirement of buildings.As a kind of novel environmental type coating, emulsion paint is because of having advantages such as health, environmental protection, super quality and competitive price, and generally obtains people's favor, and is widely used in the wall decoration and the protection of buildings, also obtained very big development in recent years.But, at present emulsion paint particularly exterior wall latex paint in application, also exist many weak points, mainly show and fade, variable color, grow dim, efflorescence, chap, peel off, easily stain etc., these disadvantages appear, relevant with the production technology level and the used material quality of current Architectural Paint in China, also relevant on the other hand on the one hand with execution of coating and substrate treatment.
Pigment is as the important component part of emulsion paint, and mainly play a part to hide, decorate and protection, and to important influence such as weather-proof, water-fast, alkaline-resisting, the washability of filming and antipollutions.Along with the development of building coating and perfect, simple white construction coating has become a kind of work in-process gradually, and during in particular for the external wall application, coloury emulsion paint coating more and more is subjected to liking of people.The distinct colors collocation not only can be satisfied the personalized painting effect requirement of people, realizes the requirement of environment to product performance, but also can realize that manufacturer increases the purpose of selling, improving profit.
One piece of article about " setting up the discussion of emulsion paint colour system " of being delivered by all will cards is disclosed in " coatings industry " calendar year 2001 o. 11th, wherein, mainly introduce the domestic and international present situation of colour emulsoid paint at present and the application and the composition of emulsion paint colour system, and studied its problem common in application.
Popular along with individual decoration, people are more and more higher to the requirement of building coating color, colorful building coating has been widely used in the engineering of decoration of exterior wall such as some hotels, bank, mansion, residential quarters, because the economy of its good decoration effect and finishing generally is subjected to people's praise.But, owing to there is not the relevant criterion colour atla to seek, the color poor accuracy of the colored paint that causes mixing colours can not reach desired decorative effect, simultaneously, irrationally select that mill base might cause also that the application metope takes place seriously to fade for use, efflorescence, problem such as chap, peel off.
Summary of the invention for fear of the metope of application exterior wall grow dim, fade, the generation of quality problems such as color distortion, satisfy the requirement of people's pursuing individuality color coating, the invention discloses a kind of prescription that is used for the high performance emulsion paint on the external wall, promptly by in specific base paint, adding the mill base of different sorts color in proportion, after toning, stirring, the color of the emulsion paint of preparation is compared with the building coating standard colour card, aberration between the two reduces, and shown in the weathering resistance and the accuracy of color also obtained certain guarantee.
This emulsion paint of the present invention, be to be formed by the outer wall foundation emulsion paint of white and high-quality exterior wall water-borne color paste deployment, its each component content comprises: the water of 14-25% by weight percentage, the solubility promoter of 2.0-2.8%, the pure-acrylic emulsion of 35-39%, the rutile type of 9.5-10.5%, the 700 order coarse whitings of 15-19%, the 1500 order coarse whitings of 5-8%, the wollastonite of 5-7%, the poly-dielectric medium hydrophobicity dispersion agent of 1.0-1.5%, the fatty alcohol polyethenoxy ether class wetting agent of 0.1-0.15%, the defoamer of 0.25-0.3%, the mould inhibitor of 0.1-0.15%, the film coalescence aid of 1.4-1.8%, the thickening material of 0.50-0.6%, the ammoniacal liquor of 0.1-0.15%, 0.93% pyrroles pyrroles red (CB12), 0.12% be the iron oxide red (CB3) of nickel complexing Huang (CB10) and 0.26%.
Wherein, solubility promoter is the agent of water conservation freeze-thaw-; Dispersion agent is that poly-dielectric medium is hydrophobic; Wetting agent is a fatty alcohol polyethenoxy ether class; Defoamer belongs to the fat hydrocarbon defoamer; Mould inhibitor belongs to nitrogen-containing heterocycle compound, and film coalescence aid belongs to pure lipid film coalescence aid; Thickening material belongs to acrylic thickener.
Emulsion paint of the present invention, the mill base CB12 that is wherein adopted is that pyrroles pyrroles is red, and its 1/25 weathering resistance is 4～5 grades, and pigment content is 35%; CB10 is a nickel complexing Huang, and its 1/25 weathering resistance is 4 grades, and pigment content is 40%; CB3 is an iron oxide red, and its 1/25 weathering resistance is 4～5 grades, and pigment content is 65%.
When preparing this emulsion paint of the present invention, at first prepare corresponding base paint, and then mill base is added in the base paint in proportion, stir and get final product.Concrete steps can be divided into following three steps: size mixing (1), and with all kinds of SOLVENTS, auxiliary agents such as powder and wetting dispersion add, and by high speed dispersion and sand milling, control makes the fineness of base paint less than 25um; (2) paint adds the viscosity that emulsion, film coalescence aid and thickening material are adjusted coating, the viscosity of control coating, flowability; (3) toning proportionally joins mill base in the base paint, stirs 10～15min.
Compared with prior art, this Outer Wall of Building Paint of Emulsion of the present invention can guarantee the weathering resistance and the accuracy of this color to greatest extent, and the three attributes of color value defined painting color by datumization makes final color have versatility and accuracy concurrently.
Embodiment
Embodiment: prepare the pure third exterior wall colored paint:
The 100g base paint, its component content is:
The component content place of production
Water 20.45
Propylene glycol 2.4
Hydropalat?100 1.0 COGNIS
Hydropalat?306 0.1 COGNIS
FoamStar?A-10 0.15 COGNIS
dehygant?LFM 0.1 COGNIS
Rutile type R-706 10.0
Coarse whiting (700 order) 15.0
Coarse whiting (1500 order) 8.0
Wollastonite (800 order) 7.0
A-10 0.15 COGNIS
PA-237 35.0 Acronal
AS?1130 0.3 DSX
3116 0.25 DSX
Ammoniacal liquor 0.1
According to above-mentioned preparation method, with all kinds of SOLVENTS, auxiliary agents such as powder and wetting dispersion add, and by high speed dispersion and sand milling, control makes the fineness of coating less than 25um; Add emulsion, film coalescence aid and thickening material then and adjust the viscosity of coating, in the base paint of preparation, add toning mill base (Shenzhen Hai Chuan color scientific ﹠ technical corporation) CB12:0.9316g, CB10:0.1268g, CB3:0.2681g at last, stir 10min, make its abundant mixing.
Use the wet film preparing device of 250um to be coated with the brush board face synthetic color, allow the seasoning of filming, use spectrophotometer to detect, measure the LAB value of standard earlier, measure the LAB that films again, calculate aberration=0.32, fully true reappearance color CBCC 108-6.By adopting ISO105-B04 weathering resistance testing method, use the ageing-resistant instrument of hernia lamp to be XEXOTEST BATE LM, draw CBCC108-6 with GB250-1995 gray discoloration card standard rating, 1000 hours measurement results of weathering fastness are 4 grades.
Claims (10)
1, a kind of Outer Wall of Building Paint of Emulsion, be made up of base paint and aqueous color paste, its component content comprises: the water of 14-25% by weight percentage, the solubility promoter of 2.0-2.8%, the pure-acrylic emulsion of 35-39%, the rutile type of 9.5-10.5%, the 700 order coarse whitings of 15-19%, the 1500 order coarse whitings of 5-8%, the wollastonite of 5-7%, the dispersion agent of 1.0-1.5%, the wetting agent of 0.1-0.15%, the defoamer of 0.25-0.3%, the mould inhibitor of 0.1-0.15%, the film coalescence aid of 1.4-1.8%, the thickening material of 0.50-0.6%, the ammoniacal liquor of 0.1-0.15%, 0.93% pyrroles pyrroles red (CB12), 0.12% be the iron oxide red (CB3) of nickel complexing Huang (CB10) and 0.26%.
2, Outer Wall of Building Paint of Emulsion according to claim 1 is characterized in that, described mould inhibitor is a nitrogen-containing heterocycle compound.
3, Outer Wall of Building Paint of Emulsion according to claim 1 and 2 is characterized in that, described wetting agent is the fatty alcohol polyethenoxy ether class compound.
4, Outer Wall of Building Paint of Emulsion according to claim 1 and 2 is characterized in that, described thickening material is an acrylic compounds.
5, Outer Wall of Building Paint of Emulsion according to claim 1 and 2 is characterized in that, described defoamer is an aliphatic compound.
6, Outer Wall of Building Paint of Emulsion according to claim 1 and 2 is characterized in that, described film coalescence aid is the alkoxide compound.
7, Outer Wall of Building Paint of Emulsion according to claim 3 is characterized in that, described thickening material is an acrylic compounds.
8, Outer Wall of Building Paint of Emulsion according to claim 3 is characterized in that, described defoamer is an aliphatic compound.
9, Outer Wall of Building Paint of Emulsion according to claim 3 is characterized in that, described film coalescence aid is the alkoxide compound.
10, Outer Wall of Building Paint of Emulsion according to claim 4 is characterized in that, described defoamer is an aliphatic compound.