CN1492012A - 专用于管道外壁的防腐漆 - Google Patents

专用于管道外壁的防腐漆 Download PDF

Info

Publication number
CN1492012A
CN1492012A CNA021332606A CN02133260A CN1492012A CN 1492012 A CN1492012 A CN 1492012A CN A021332606 A CNA021332606 A CN A021332606A CN 02133260 A CN02133260 A CN 02133260A CN 1492012 A CN1492012 A CN 1492012A
Authority
CN
China
Prior art keywords
component
polyethers
solvent
parts
tar pitch
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA021332606A
Other languages
English (en)
Inventor
张晓广
孙锡宁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNA021332606A priority Critical patent/CN1492012A/zh
Publication of CN1492012A publication Critical patent/CN1492012A/zh
Pending legal-status Critical Current

Abstract

专用于管道外壁的防腐漆，属于高分子化合物范畴，为分罐包装的A、B双组份组成，其特征是A组份由异氰酸酯、聚醚a、聚醚b、环氧树脂、二辛脂或二丁酯、磷酸和溶剂构成，B组份由煤焦沥青、环己酮、甲苯和溶剂构成，其中异氰酸酯为多亚甲基多苯基异氰酸酯(PAPI)300#或400#，溶剂为二甲苯或SI000#，聚醚a可从330、3030、3031、3050中取其一，聚醚b可从635、451中取其一。本发明的有益效果是：涂层薄、成本低、涂时省工省力；使用寿命长、防腐效果好；机械物理性能好、具有良好的耐温性及耐温变性。

Description

专用于管道外壁的防腐漆
所属技术领域
本发明涉及一种防腐漆，进一步说是专用于管道外壁的一种防腐漆，属于高分子化合物范畴。适宜于化工、冶金、管道输送行业的设备防腐时使用。
背景技术
目前.用于石化、冶金、管道输送行业的埋地钢管道或铸铁管道所用防腐漆，大多数性能较差，涂装麻烦、成本高、使用年限短，有的还存在耐候性差、不耐老化、易起泡龟裂及周期短等缺陷。
发明内容
本发明的目的在于克服现有技术的上述不足，通过改进配方，给出一种专用于管道外壁的防腐漆，该防腐漆属于湿固化聚氨酯煤沥青防腐漆系列，为高分子化合物，附着力牢固，柔韧性好，硬度高，抗磨擦力强和抗冲击力大，集优异的机械物理性能为一体，耐酸、碱、盐等化学腐蚀，并具有良好的耐温性及耐温变性。
本发明的技术解决方案是：这种专用于管道外壁的防腐漆为分罐包装的A、B双组份组成，其特点是A组份是由异氰酸酯、聚醚a、聚醚b、环氧树脂、二辛脂或二丁酯、磷酸和溶剂构成的湿固化聚氨酯树脂，B组份是由煤焦沥青、环己酮、甲苯、溶剂和添料构成的煤焦沥青树脂，其中异氰酸酯为多亚甲基多苯基异氰酸酯(PAPI)300#或400#，溶剂为二甲苯或SI000#，聚醚a可从330、3030、3031、3050中取其一，聚醚b可从635、451中取其一，添料为硅灰石粉，
A组份中的各组成物含量为：(重量份数)
多亚甲基多苯基异氰酸酯(PAPI)300#或400#  23.5～25.98
磷酸(试剂型)                               0.039～0.042
聚醚a                                      6.9～7.8
聚醚b                                      1.75～1.93
二辛脂或二丁酯                             5.4～5.8
环氧树脂                                   2.1～2.44
溶剂                                       56～59
B组份中的各组成物含量为：(重量份数)
煤焦沥青                                   61～63
环己酮                                     13.5～14.8
甲苯                                       11.5～12.93
溶剂                                       8.9～9.24
添料(重量百分数)                           15～20％
专用于管道外壁的防腐漆的制备过程是：
(1).A组份，湿固化聚氨酯树脂制备步骤如下
先将多亚甲基多苯基异氰酸酯(PAPI)300#或400#(按重量份数，以下组成物均相同)用泵投入反应釜中，加入磷酸进行乳化，边投料边升温，再加聚醚a，二辛脂或二丁酯，聚醚b，溶剂和环氧树脂，进行加热反应至80～90℃时保温，2～2.5小时后降温至40℃时，出料过滤(丝绢320目)，过滤前按产品标准调固含量至42～46％，检验包装后入库待售；
(2).B组份，煤焦沥青树脂制备步骤如下
将煤焦沥青、环己酮、甲苯、溶剂按重量份数陆续投入反应釜中，边投料边开车搅拌，边升温加热，升温到110～120℃时，保温2小时后排水，然后将料打入冷却罐降温至40℃，过滤前根据防腐漆的用途加入添料，其加入量为料量的15～20％(重量计)，搅拌均匀后在常温下用200目过滤网过滤，过滤前按产品标准调固含量至61～65％，再检验包装后入库待售。
本发明给出的这种专用于管道外壁的防腐漆，由于是双组份，分A、B两罐包装，使用时可在现场将A、B两罐打开，按1∶1的比例混合搅拌均匀后，沉淀10分钟，再喷涂、刷涂、滚涂均可。
本发明给出的这种专用于管道外壁的防腐漆的有益效果是：涂层薄、成本低、涂时省工省力；使用寿命长、应用范围广、防腐效果好；机械物理性能好、具有良好的耐温性及耐温变性。
具体实施方式
实施例1为专用于管道外壁的防腐漆，由分罐包装的A、B双组份组成，使用时可在现场将A、B两罐打开，按1∶1的比例混合搅拌均匀后，沉淀10分钟，再喷涂、刷涂、滚涂均可。其特点是A组份是由异氰酸酯、聚醚a、聚醚b、环氧树脂、二辛脂或二丁酯、磷酸和溶剂构成的湿固化聚氨酯树脂，B组份是由煤焦沥青、环己酮、甲苯、溶剂和添料构成的煤焦沥青树脂，其中异氰酸酯为多亚甲基多苯基异氰酸酯(PAPI)400#，溶剂为二甲苯，聚醚a为330，聚醚b为635，添料为硅灰石粉。制备时先将25.98份多亚甲基多苯基异氰酸酯(PAPI)400#用泵投入反应釜中，加入0.042份磷酸进行乳化，边投料边升温，再加7.8份聚醚330，5.8份二辛脂，1.93份聚醚635，56份二甲苯和2.44份环氧树脂E-44，进行加热反应至80～90℃时保温，2～2.5小时后降温至40℃时，出料过滤(丝绢320目)，过滤前按产品标准调固含量至44％，检验包装后入库待用；再将63份煤焦沥青、14.78份环己酮、12.93份甲苯和9.24份二甲苯，陆续投入反应釜中，边投料边开车搅拌，边升温加热，升温到110～120℃时，保温2小时后排水，然后将料打入冷却罐降温至40℃，加入20％的800～1200目硅灰石粉添料，搅拌均匀后在常温下用200目过滤网过滤，过滤前按产品标准调固含量至63％，再检验包装后入库待用。现场使用时将固含量为44％的A组份湿固化聚氨酯树脂和固含量为63％的B煤焦沥青树脂，按1∶1的比例混合搅拌均匀后，沉淀10分钟，再喷涂、刷涂、滚涂均可。
实施例2为专用于管道外壁的防腐漆，由分罐包装的A、B双组份组，使用时可在现场将A、B两罐打开，按1∶1的比例混合搅拌均匀后，沉淀10分钟，再喷涂、刷涂、滚涂均可。其制备工艺同实施例1一样。其成份为：
(1)A组份湿固化聚氨酯树脂    固含量         42％
多亚甲基多苯基异氰酸酯(PAPI)400            23.5份
磷酸(试剂型)                               0.039份
聚醚330                                    6.9份
聚醚635                                    1.75份
二辛脂                                     5.4份
环氧树脂E-44                               2.1份
SI000#                                     59份
(2).B组份煤焦沥青树脂    固含量            65％
煤焦沥青                                   61份
环己酮                                     14.25份
甲苯                                       12.38份
SI000#                                     9.08份
硅灰石粉(重量百分数)                       18％
实施例3为专用于管道外壁的防腐漆，由分罐包装的A、B双组份组，使用时可在现场将A、B两罐打开，按1∶1的比例混合搅拌均匀后，沉淀10分钟，再喷涂、刷涂、滚涂均可。其制备工艺同实施例1一样。其成份为
(1).A组份湿固化聚氨酯树脂    固含量        46％
多亚甲基多苯基异氰酸酯(PAPI)400            24.8份
磷酸(试剂型)                               0.041份
聚醚330                                    7.4份
聚醚635                                    1.85份
二辛脂                                     5.6份
环氧树脂E-44                               2.32份
二甲苯                                     58份
(2).B组份煤焦沥青树脂    固含量            61％
煤焦沥青                                   62份
环己酮                                    13.5份
甲苯                                       11.5份
二甲苯                                     8.9份
硅灰石粉(重量百分数)                       15％

Claims (1)

1.专用于管道外壁的防腐漆，为分罐包装的A、B双组份组成，其特征在于A组份是由异氰酸酯、聚醚a、聚醚b、环氧树脂、二辛脂或二丁酯、磷酸和溶剂构成的湿固化聚氨酯树脂，B组份是由煤焦沥青、环己酮、甲苯、溶剂和添料构成的煤焦沥青树脂，其中异氰酸酯为多亚甲基多苯基异氰酸酯(PAPI)300#或400#，溶剂为二甲苯或SI000#，聚醚a可从330、3030、3031、3050中取其一，聚醚b可从635、451中取其一，添料为硅灰石粉，
A组份中的各组成物含量为：(重量份数)
多亚甲基多苯基异氰酸酯(PAPI)300#或400#  23.5～25.98
磷酸(试剂型)                               0.039～0.042
聚醚a                                      6.9～7.8
聚醚b                                      1.75～1.93
二辛脂或二丁酯                             5.4～5.8
环氧树脂                                   2.1～2.44
溶剂                                       56～59
B组份中的各组成物含量为：(重量份数)
煤焦沥青                                   61～63
环己酮                                     13.5～14.8
甲苯                                       11.5～12.93
溶剂                                       8.9～9.24
添料(重量百分数)                           15～20％
CNA021332606A 2002-10-24 2002-10-24 专用于管道外壁的防腐漆 Pending CN1492012A (zh)