CN1473796A - 非放射性环保蓄能发光陶瓷釉料 - Google Patents

非放射性环保蓄能发光陶瓷釉料 Download PDF

Info

Publication number
CN1473796A
CN1473796A CNA021259631A CN02125963A CN1473796A CN 1473796 A CN1473796 A CN 1473796A CN A021259631 A CNA021259631 A CN A021259631A CN 02125963 A CN02125963 A CN 02125963A CN 1473796 A CN1473796 A CN 1473796A
Authority
CN
China
Prior art keywords
ceramic glaze
energy storage
protection energy
environment protection
glaze material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA021259631A
Other languages
English (en)
Other versions
CN1321093C (zh
Inventor
张贵洲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB021259631A priority Critical patent/CN1321093C/zh
Publication of CN1473796A publication Critical patent/CN1473796A/zh
Application granted granted Critical
Publication of CN1321093C publication Critical patent/CN1321093C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种非放射性环保蓄能发光陶瓷釉料，由碳酸锶、三氧化二铝、硼酸、三氧化二铕、三氧化二镝、硼砂、石英、硝石、石灰石、长石、滑石、氟硅酸钠混合制备成发光陶瓷釉料。本发明具有无放射性物质，发光时间长的优点。

Description

非放射性环保蓄能发光陶瓷釉料
技术领域
本发明涉及一种蓄能发光陶瓷釉料，所述的发光陶瓷釉料是永久发光的陶瓷釉料，采用非放射性的稀土原料和基础釉料生产。
技术背景
中国专利CN1202472A公开了一种发光陶瓷釉料，该专利是将发光粉、基础釉和添加剂混合制成，由于该专利采用的发光粉含有一定的放射性，并且发光的时间较短，需要有严格的防辐射措施，使用不便，不适于实用。因此，需要提出一种非放射性环保蓄能发光陶瓷釉料。
发明内容
本发明的目的在于提供一种非放射性环保蓄能发光陶瓷釉料，该发光陶瓷釉料不含对人体有害的放射性物质，并具有较高的蓄能量，可将这种发光陶瓷釉料用于建筑业中的墙面砖、地板砖，还可用于其它的陶瓷制品，可蓄能发光，使用安全。
本发明的目的是由下述技术方案实现的：一种非放射性环保蓄能发光材料，由下述原料制备而成，其原料的重量比为：
      碳酸锶                        37-38
      三氧化二铝                    26-27
      三氧化二铕                    0.46-0.7
      三氧化二镝                    0.9-1
      硼砂                          34-46
      硼酸                          24-26
      石英                          18-22
      硝石                          3-4
      石灰石                        1-3
      长石                          2-4
      滑石                          0.5-1.5
      氟硅酸钠                      8-12。
本发明与现有技术相比有如下优点：
1、由于本发明不采用硫化锌等有放射性的物质作原料，所以不会产生对人体有害的放射性物质。
2、由于本发明采用了稀土原料的发光材料，因此，本发明的陶瓷釉料具有较强的储蓄光能的能力，本发明的陶瓷釉料只需接收光照5分钟左右，就可在黑暗的环境中保持发光20小时左右。
具体实施方式
实施例一：
一种非放射性环保蓄能发光陶瓷釉料，由下述原料制备而成，其原料的重量比为：
      碳酸锶                         37
      三氧化二铝                     26
      三氧化二铕                     0.46
      三氧化二镝                     0.9
      硼砂                           34
      硼酸                           24
      石英                           18
      硝石                           3
      石灰石                         1
      长石                           2
      滑石                           0.5
      氟硅酸钠                       8。
本发明的制备方法是：
1、按照上述的配比将原料备齐，将碳酸锶、三氧化二铝、硼酸、三氧化二铕、三氧化二镝等原料充分研磨混合过200目筛，后装入氧化铝坩埚内，在原料的上面覆盖一层活性炭，然后将坩埚加装密封盖并将其内的原料压实，将该坩埚倒置在焙烧炉内加热焙烧，自20℃-200℃，温升速度为5-8℃/分钟，200℃以后温升速度为5-10℃/分钟，当温度达到1350℃后保持6-8小时，自然冷却20分钟后将该坩埚从焙烧炉中取出，自然冷却到室温，制备成发光粉。
2、将硼砂、石英、硝石、石灰石、长石、滑石、氟硅酸钠混合均匀，在1200℃温度下烧制3-5小时，制成熔块，研磨成细粉，过300目筛制成基础釉粉。
3、将所述的发光粉和所述的基础釉粉混合均匀，即制得本发明。
实施例二：
一种非放射性环保蓄能发光陶瓷釉料，由下述原料制备而成，其原料的重量比为：
      碳酸锶                         37.7
      三氧化二铝                     26.8
      三氧化二铕                     0.462
      三氧化二镝                     0.98
      硼砂                           35
      硼酸                           25
      石英                           20
      硝石                           4
      石灰石                         2
      长石                           3
      滑石                           1
      氟硅酸钠                       10。
本实施例的制备工艺流程与实施例一相同，在此不一一描述。
实施例三：
一种非放射性环保蓄能发光陶瓷釉料，由下述原料制备而成，其原料的重量比为：
      碳酸锶                         38
      三氧化二铝                     27
      三氧化二铕                     0.7
      三氧化二镝                     1
      硼砂                           46
      硼酸                           26
      石英                           22
      硝石                           4
      石灰石                         3
      长石                           4
      滑石                           1.5
      氟硅酸钠                       12。
本实施例的制备工艺流程与实施例一相同，在此不一一描述。

Claims (2)

1、一种非放射性环保蓄能发光陶瓷釉料，其特征在于：由下述原料制备而成，所述原料的重量比为：
      碳酸锶                         37-38
      三氧化二铝                     26-27
      三氧化二铕                     0.46-0.7
      三氧化二镝                     0.9-1
      硼砂                           34-46
      硼酸                           24-26
      石英                           18-22
      硝石                           3-4
      石灰石                         1-3
      长石                           2-4
      滑石                           0.5-1.5
      氟硅酸钠                       8-12。
2、根据权利要求1所述的非放射性环保蓄能发光材料，其特征在于：由下述原料制备而成，所述原料的重量比为：
      碳酸锶                         37.7
      三氧化二铝                     26.8
      三氧化二铕                     0.462
      三氧化二镝                     0.98
      硼砂                           35
      硼酸                           25
      石英                           20
      硝石                           4
      石灰石                         2
      长石                           3
      滑石                           1
      氟硅酸钠                       10。
CNB021259631A 2002-08-07 2002-08-07 非放射性环保蓄能发光陶瓷釉料 Expired - Fee Related CN1321093C (zh)