CN1453384A - 具有良好可切割性的铝合金以及制备锻造制品的方法和锻造制品 - Google Patents
具有良好可切割性的铝合金以及制备锻造制品的方法和锻造制品 Download PDFInfo
- Publication number
- CN1453384A CN1453384A CN03123309A CN03123309A CN1453384A CN 1453384 A CN1453384 A CN 1453384A CN 03123309 A CN03123309 A CN 03123309A CN 03123309 A CN03123309 A CN 03123309A CN 1453384 A CN1453384 A CN 1453384A
- Authority
- CN
- China
- Prior art keywords
- alloy
- quality
- forging
- present
- aluminium alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
试样 | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Zr | Sn | Bi | Pb | 可切割性 | |
本发明 | 1 | 0.18 | 0.24 | 5.92 | 0.00 | 0.00 | 0.00 | 0.00 | 0.96 | 0.00 | 0.00 | 0.88 | 1.19 | 0.00 | A |
2 | 0.19 | 0.24 | 5.02 | 0.00 | 0.00 | 0.01 | 0.00 | 0.53 | 0.01 | 0.00 | 0.61 | 0.69 | 0.00 | A | |
3 | 0.24 | 0.23 | 5.55 | 0.00 | 0.23 | 0.00 | 0.00 | 0.53 | 0.00 | 0.00 | 0.46 | 1.47 | 0.00 | A | |
4 | 0.18 | 1.01 | 5.34 | 0.00 | 0.00 | 0.00 | 0.00 | 0.63 | 0.00 | 0.00 | 0.57 | 0.69 | 0.00 | A | |
5 | 0.22 | 0.24 | 4.81 | 0.00 | 0.00 | 0.00 | 0.00 | 0.78 | 0.10 | 0.00 | 0.54 | 0.71 | 0.00 | A | |
6 | 0.76 | 0.22 | 5.77 | 0.00 | 0.00 | 0 01 | 0.00 | 0.56 | 0.01 | 0.00 | 0.65 | 0.82 | 0.00 | A | |
7 | 0.22 | 0.23 | 5.54 | 0.01 | 0.00 | 0.11 | 0.00 | 0.64 | 0.00 | 0.07 | 0.74 | 0.84 | 0.00 | A | |
8 | 0.17 | 0.21 | 4.38 | 0.46 | 0.01 | 0.00 | 0.00 | 0.50 | 0.01 | 0.00 | 0.55 | 0.67 | 0.00 | A | |
对比例 | 9 | 0.18 | 0.23 | 5.55 | 0.01 | 0.00 | 0.00 | 0.00 | 0.01 | 0.01 | 0.00 | 0.61 | 0.66 | 0.00 | C |
10 | 0.20 | 0.23 | 2.56 | 0.00 | 0.01 | 0.00 | 0.01 | 0.25 | 0.01 | 0.01 | 0.57 | 0.53 | 0.00 | C | |
11 | 0.21 | 0.19 | 5.42 | 0.00 | 0.00 | 0.01 | 0.00 | 0.54 | 0.01 | 0.00 | 0.11 | 0.73 | 0.00 | C | |
12 | 0.20 | 0 23 | 5.61 | 0.01 | 0.01 | 0.00 | 0.00 | 0.48 | 0.01 | 0.00 | 0.51 | 0.24 | 0.00 | C | |
常规实例 | 13(JIS2017) | 0.52 | 0.47 | 4.03 | 0.55 | 0.61 | 0.01 | 0.00 | 0.01 | 0.01 | 0.00 | 0.00 | 0.00 | 0.00 | D |
14(JIS2011) | 0.18 | 0.20 | 5.53 | 0.00 | 0.01 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.59 | 0.61 | B |
试样 | 合金 | 锻造温度(℃) | 锻造载荷(吨) | 水淬火后的裂缝 |
15 | A | 490 | 138 | 观察到 |
16 | 460 | 146 | 观察到 | |
17 | 430 | 157 | 未观察到 | |
18 | 400 | 169 | 未观察到 | |
19 | 370 | 178 | 未观察到 | |
20 | 340 | 189 | 未观察到 | |
21 | 310 | 203 | 未观察到 | |
22 | JIS 2011 | 490 | 163 | 观察到 |
23 | 460 | 170 | 未观察到 | |
24 | 430 | 182 | 未观察到 | |
25 | 400 | 193 | 未观察到 | |
26 | 370 | 207 | 未观察到 | |
27 | 340 | 223 | 未观察到 | |
28 | 310 | 235 | 未观察到 |
Claims (3)