CN1445350A - 大豆油容器蜡烛 - Google Patents
大豆油容器蜡烛 Download PDFInfo
- Publication number
- CN1445350A CN1445350A CN 03113773 CN03113773A CN1445350A CN 1445350 A CN1445350 A CN 1445350A CN 03113773 CN03113773 CN 03113773 CN 03113773 A CN03113773 A CN 03113773A CN 1445350 A CN1445350 A CN 1445350A
- Authority
- CN
- China
- Prior art keywords
- soybean oil
- candle
- wax
- oil container
- container
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种容器蜡烛。本发明的目的是提出一种新的工艺容器蜡烛，其具有原料来源广泛、加工温度低、蜡体结构稳定、着色性好而且均匀、燃烧时不会产生有害烟雾以及制造成本低等优点，其特征在于蜡烛本体采用如下的配方比例：大豆油：50％～98％；普通石蜡：1％～45％；特种微晶蜡：1％～5％；液体香料：适量；着色剂：适量。与现有石蜡容器蜡对比，本发明有如下显著特点和进步：本发明的大豆油容器蜡有良好的上色性，色泽柔和、均匀、自然、光滑、亮泽；燃烧时火焰高度为1～1.6cm，是普通石蜡容器的一半，由于火焰高度短，使香气的释放放慢，蜡烛总燃烧时间得以延长；燃烧时火焰稳定不闪动，给人以柔和宁静的感觉。
Description
技术领域
本发明涉及一种容器蜡烛。
背景技术
在日常生活中，常见工艺容器蜡烛作为一种装饰摆设或用于餐厅营造气氛，现有的工艺容器蜡烛主要材料为石蜡，而以石蜡为主要原料的工艺容器蜡烛存在如下缺点：
1.在制造蜡烛时所需加工温度较高，导致蜡体结构在制造时加热分
解；
2.蜡体收缩性大，需加入一定量的辅助剂，防止蜡体结构分裂；
3.蜡体上色性差，着色不均匀，不自然，所制造的蜡烛表面粗糙，没
有光泽；
4.当蜡体中的液体香料比例稍大一些时，蜡体硬度变小，结构不稳定，
或者由于时间过长，导致蜡体的着色剂氧化变色；
5.在燃烧过程中由于风或其它情况引起火焰闪动时，会产生有害烟
雾，使室内环境恶化；
6.当吹灭蜡烛时，会产生强烈的令人不愉快的特有气味。
发明内容
本发明的目的是提出一种新的工艺容器蜡烛，其以大豆油为主要原料，具有加工温度低、蜡体结构稳定、着色性好和均匀、燃烧时不会产生有害烟雾而且原料来源广泛，以及制造成本更低等优点。
本发明的目的可通过如下方案来实现：
一种大豆油容器蜡烛，由蜡烛本体、棉芯、以及盛装蜡烛本体的容器所组成，其特征在于蜡烛本体含有50％以上的大豆油。
更进一步的技术方案是蜡烛本体采用如下的配方比例(重量比)：
大豆油：50％～98％；
普通石蜡：1％～45％；
特种微晶蜡：1％～5％。
可进一步根据需要在上述蜡烛本体的配方比例中加入适量的香料及着色剂。
制作工艺：
(1)将纯棉芯浸泡在高温的大豆蜡混熔蜡液(该混熔蜡液的制作方法后
述)里，浸泡时间至少45分钟，然后取出冷却，并将浸泡好的棉
芯固定在容器中间；
(2)在大豆油中加入上述比例的普通石蜡及特种微晶蜡，加热至适当温
度，使混熔；
(3)如需要，可将调好的着色剂及液体香料加入上述混合溶液中并充分
搅拌均匀使混合完全，并加热至制造蜡烛所需温度使成为大豆蜡混
熔蜡液；
(4)将大豆蜡混熔蜡液注入(1)所准备的容器中；
(5)自然冷却至常温，成为成品。
具体实施方式
实施例1
一.原料及比例：
食用大豆油 60份；
普通石蜡，熔点54～60℃，35份；
特种微晶蜡，熔点65～70℃，3份；
液体香料，2份；
液体色料，适量。
二.工艺容器蜡的制作工艺：
(1)将经预先浸泡有大豆蜡混熔蜡液的棉芯固定在要制备蜡烛的容器
中间，这种容器可根据需要设计有各种各样的形状。
(2)在食用大豆油中加入上述比例的普通石蜡及特种微晶蜡，加热至适
当温度，使混熔；(3)将调好的着色剂及液体香料放入上述混合溶液中并充分搅拌均匀使混合完全，并加热至制造所需温度使成为大豆蜡混熔蜡液；(4)将大豆蜡混熔蜡液注入(1)所准备的容器中；(5)自然冷却至常温，成为成品。与现有石蜡容器蜡对比，本发明有如下显著特点和进步：
本发明的大豆油容器蜡有良好的上色性，色泽柔和、均匀、自然、光滑、亮泽；
燃烧时火焰高度为1～1.6cm，是普通石蜡容器的一半，由于火焰高度短，使香气的释放放慢，蜡烛总燃烧时间得以延长。
燃烧时火焰稳定不闪动，给人以柔和宁静的感觉。
实施例2一.原料及比例：食用大豆油 80份；普通石蜡，熔点54～60℃，15份；特种微晶蜡，熔点65～70℃，3份；液体香料，2份；液体色料，适量。二.工艺容器蜡的制作工艺：与实施例1相同。本实例的大豆油容器蜡有与实施例一相同的效果。
Claims (6)
1.一种大豆油容器蜡烛，由蜡烛本体、棉芯、以及盛装蜡烛本体的容器所组成，其特征在于蜡烛本体含有50％以上的大豆油。
2.根据权利要求1所述的大豆油容器蜡烛，其特征在于蜡烛本体采用如下的配方比例：
大豆油：50％～98％；
普通石蜡：1％～45％；
特种微晶蜡：1％～5％。
3.根据权利要求2所述的大豆油容器蜡烛，其特征在于蜡烛本体采用如下的较佳配方比例：
大豆油：50％～70％；
普通石蜡：29％～45％；
特种微晶蜡：1％～5％。
4.根据权利要求1所述的大豆油容器蜡烛，其特征在于蜡烛本体采用如下的较佳配方比例：
大豆油：70％～98％；
普通石蜡：1％～29％；
特种微晶蜡：1％～5％。
5.根据权利要求1或2或3或4所述的任一种大豆油容器蜡烛，其特征在于蜡烛本体的组成成份中还含有适量的香料。
6.根据权利要求1或2或3或4所述的任一种大豆油容器蜡烛，其特征在于蜡烛本体的组成成份中还含有适量的着色剂。