CN111411026A - 一种环保型彩焰蜡烛及其制备方法 - Google Patents
一种环保型彩焰蜡烛及其制备方法 Download PDFInfo
- Publication number
- CN111411026A CN111411026A CN202010234898.4A CN202010234898A CN111411026A CN 111411026 A CN111411026 A CN 111411026A CN 202010234898 A CN202010234898 A CN 202010234898A CN 111411026 A CN111411026 A CN 111411026A
- Authority
- CN
- China
- Prior art keywords
- parts
- candle
- wax
- color
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种环保型彩焰蜡烛及其制备方法，包括以质量份计的下列组分：柠檬酸三甲酯20份~50份、石蜡20份~50份、微晶蜡1~5份、天然蜡5~10份、聚乙烯蜡5~‑15份、费托蜡5~10份、硬脂酸1~5份、各色油溶性颜料1~3份。本发明的环保型彩焰蜡烛除了具有环保无污染的优点外，还具有燃烧时间长、挺实、“不流泪”，原料成本低廉，生产工艺简单等特点。
Description
技术领域
本发明涉及一种蜡烛，尤其涉及一种环保型彩焰蜡烛及其制备方法。
背景技术
蜡烛虽然不再是人类的主要光源，但它们的普及和使用仍在不断增长，尤其在文学、艺术和宗教中，蜡烛有着广泛的象征意义，它通常代表着欢乐、对神圣的崇敬。彩焰蜡烛作为蜡烛的一种，就是在点燃蜡烛的时候可以发出红色、橙色、黄色、绿色、蓝色、紫色等颜色的光，主燃剂一般选用非石蜡型有机物质，需要对烛芯进行处理，选择锂、钠、钾、钙、镁、锶、铜等金属离子的无机盐作为发色剂，进而可以得到彩色火焰蜡烛。彩焰蜡烛最早见于本世纪50年代，其中美国、日本研究较多，我国从20世纪90年代才开始对其进行研究。传统的彩焰蜡烛多以石蜡作为主燃剂，然而在点燃的过程中常常燃烧不充分，产生“黑烟”及其他有毒气体，对环境造成污染。
发明内容
本发明的目的是针对现有技术的不足，提供一种工艺简单、性能优良的环保型彩焰蜡烛，解决了现有技术中彩焰蜡烛点燃的过程中常常燃烧不充分，对环境造成污染的问题。
本发明的另一目的在于提供一种环保型彩焰蜡烛的制备方法。
本发明采用的技术方案为：
一种环保型彩焰蜡烛，包括烛体和烛芯，所述的烛体由下列原料按质量份数比制备而成：柠檬酸三甲酯20份～50份、石蜡20份～50份、天然蜡5～10份、聚乙烯蜡5～15份、费托蜡5～10份、硬脂酸1～5份、各色染料1～3份；所述的烛芯为棉芯。
作为技术方案的进一步改进，它还包括以质量份计的微晶蜡1～5份。
作为技术方案的进一步改进，所述的天然蜡为大豆蜡、棕榈蜡或小烛树蜡中的一种或几种。
作为技术方案的进一步改进，所述的各色颜料为各种颜色的有机油溶性染料。
一种环保型彩焰蜡烛的制备方法，包括以下步骤：
(1)将柠檬酸三甲酯、石蜡、费托蜡、天然蜡、聚乙烯蜡和硬脂酸按上述质量份数比例放入容器中加热至80～100℃，并缓慢搅拌均匀；
(2)按上述质量份数比向步骤(1)搅拌均匀的物质中加入油溶性染料，并搅拌均匀；
(3)烛芯处理：a)将棉芯放入质量百分比浓度为3～5％的氢氧化钠溶液中加热至90～100℃进行脱脂处理2～2.5小时，取出后用去离子水反复清洗，晾干；b)将经a)步骤处理后的棉芯在氨基脲和磷酸铵的复配混合溶液中加热至90～100℃进行脱钙脱钠处理2～2.5小时，取出后用去离子水反复清洗，晾干；c)将经过b)步骤处理的棉芯置于发色剂中1.5～2个小时，取出晾干，得烛芯；
(4)将上述步骤(3)处理好的烛芯固定在模具中；
(5)将上述步骤(2)中均匀的混合物倒入步骤(4)准备的模具中；
(6)冷却、脱模；
(7)包装。
所述的步骤(3)中，氨基脲和磷酸铵按质量比1:2复配混合溶液，其中氨基脲的质量比浓度为1～2％，磷酸铵的质量比浓度为3～4％。
所述的步骤(3)中的发色剂为钠、钾、硼、钡、锶、镁、钙、铜中的几种金属有机盐或无机盐或有机、无机盐的混合物。
本发明的优点效果如下：
本发明相对现有技术具有突出的实质性特点和显著的进步，具体的说，本发明的环保型彩焰蜡烛在燃烧时不产生任何污染，烛体挺实，无“流泪”“干枝”等不良现象产生，制备工艺简单易行。
本发明环保型彩焰蜡烛的主要成分为柠檬酸三甲酯，是相对理想的彩色蜡烛主剂，其熔点为75～78℃，成形性好，燃烧时近似于无色，实验证明在其中加入少量石蜡，既可以提高蜡烛的燃烧性能，解决其燃烧不充分、火焰小的问题，又不会造成污染。天然蜡优选为大豆蜡，其价格低廉，冷却速度快，易脱模，不开裂，色素分散均匀，不起花，无毒环保，其产品不会产生致癌物质，废弃物可生物降解，节省热源，利于操作人员安全生产。本发明所使用的染料均为有机染料，颜色为红色、橙色、黄色、紫色、蓝色等。
微晶蜡、费托蜡和聚乙烯蜡本身具有熔点高的特点，三者的协同作用用于提高主燃剂成分的韧性，使得烛体在燃烧时挺实。
所述的聚乙烯蜡和硬脂酸可以有效增加蜡烛的硬度。
具体实施方式
下面通过具体实施方式，对本发明的技术方案做进一步的详细描述。
实施例1
烛体：将柠檬酸三甲酯30份、石蜡20份、微晶蜡2份、费托蜡5份、大豆蜡5份、聚乙烯蜡6份和硬脂酸2份和油溶红1份按上述质量份数比例放入容器中加热至95℃，并缓慢搅拌均匀；
烛芯：将烛芯放入质量百分比浓度为3％的氢氧化钠溶液中加热至90℃进行脱脂处理2小时，取出后用去离子水反复清洗，晾干；再将处理后的烛芯置于质量比浓度为1％氨基脲和3％磷酸铵按质量比1:2复配混合溶液中加热至90℃进行脱钙脱钠处理2小时，取出后用去离子水反复清洗，晾干；最后将经过上述处理的棉芯置于发色剂氯化锂中1.5小时，取出晾干；
将上述处理好的烛芯固定在模具中，蜡液灌模，冷却，脱模，包装。
实施例2
烛体：将柠檬酸三甲酯35份、石蜡25份、微晶蜡3份、费托蜡6份、大豆蜡6份、聚乙烯蜡8份和硬脂酸2份和油溶蓝1份按上述质量份数比例放入容器中加热至95℃，并缓慢搅拌均匀；
烛芯：将烛芯放入质量百分比浓度为4％的氢氧化钠溶液中加热至90℃进行脱脂处理2小时，取出后用去离子水反复清洗，晾干；再将处理后的烛芯置于质量比浓度为2％氨基脲和3％磷酸铵按1:2复配混合溶液中加热至90℃进行脱钙脱钠处理2小时，取出后用去离子水反复清洗，晾干；最后将经过上述处理的棉芯置于发色剂氯化铜中1.5小时，取出晾干；
将上述处理好的烛芯固定在模具中，蜡液灌模，冷却，脱模，包装。
实施例3
烛体：将柠檬酸三甲酯40份、石蜡30份、微晶蜡5份、费托蜡8份、大豆蜡5份、棕榈蜡5份、聚乙烯蜡8份和硬脂酸2份和油溶紫1份按上述质量份数比例放入容器中加热至95℃，并缓慢搅拌均匀；
烛芯：将烛芯放入质量百分比浓度为4％的氢氧化钠溶液中加热至90℃进行脱脂处理2小时，取出后用去离子水反复清洗，晾干；再将处理后的烛芯置于质量比浓度为2％氨基脲和3％磷酸铵按1:2复配混合溶液中加热至90℃进行脱钙脱钠处理2小时，取出后用去离子水反复清洗，晾干；最后将经过上述处理的棉芯置于发色剂氯化钾中1.5小时，取出晾干；
将上述处理好的烛芯固定在模具中，蜡液灌模，冷却，脱模，包装。
实施例4
烛体：将柠檬酸三甲酯45份、石蜡35份、微晶蜡5份、费托蜡8份、大豆蜡2份、棕榈蜡2份、小烛树蜡2份、聚乙烯蜡10份和硬脂酸3份和油溶黄1份按上述质量份数比例放入容器中加热至100℃，并缓慢搅拌均匀；
烛芯：将烛芯放入质量百分比浓度为5％的氢氧化钠溶液中加热至90℃进行脱脂处理2.5小时，取出后用去离子水反复清洗，晾干；再将处理后的烛芯置于质量比浓度为2％氨基脲和4％磷酸铵按1:2复配混合溶液中加热至90℃进行脱钙脱钠处理2.5小时，取出后用去离子水反复清洗，晾干；最后将经过上述处理的棉芯置于发色剂氯化钠中2小时，取出晾干；
将上述处理好的烛芯固定在模具中，蜡液灌模，冷却，脱模，包装。
实施例5
烛体：将柠檬酸三甲酯50份、石蜡45份、微晶蜡5份、费托蜡10份、大豆蜡3份、棕榈蜡3份、小烛树蜡3份、聚乙烯蜡10份和硬脂酸5份和油溶绿1份按上述质量份数比例放入容器中加热至100℃，并缓慢搅拌均匀；
烛芯：将烛芯放入质量百分比浓度为5％的氢氧化钠溶液中加热至90℃进行脱脂处理2.5小时，取出后用去离子水反复清洗，晾干；再将处理后的烛芯置于质量比浓度为2％氨基脲和4％磷酸铵按1:2复配混合溶液中加热至90℃进行脱钙脱钠处理2.5小时，取出后用去离子水反复清洗，晾干；最后将经过上述处理的棉芯置于发色剂硼酸中2小时，取出晾干；
将上述处理好的烛芯固定在模具中，蜡液灌模，冷却，脱模，包装。
各实施例性能检测表：根据GB/T 4359测定
最后应当说明的是:以上实施例仅用以说明本发明的技术方案而非对其限制；尽管参照较佳实施例对本发明进行了详细的说明，所属领域的普通技术人员应当理解，依然可以对本发明的具体实施方式进行修改或者对部分技术特征进行等同替换；而不脱离本发明技术方案的精神，其均应涵盖在本发明请求保护的技术方案范围当中。
Claims (7)
1.一种环保型彩焰蜡烛，包括烛体和烛芯，其特征在于所述的烛体由下列原料按质量份数比制备而成：柠檬酸三甲酯20份~50份、石蜡20份~50份、天然蜡5~10份、聚乙烯蜡5~15份、费托蜡5~10份、硬脂酸1~5份、各色染料1~3份；所述的烛芯为棉芯。
2.根据权利要求1所述的一种环保型彩焰蜡烛，其特征在于它还包括以质量份计的微晶蜡1~5份。
3.根据权利要求1所述的一种环保型彩焰蜡烛，其特征在于所述的天然蜡为大豆蜡、棕榈蜡或小烛树蜡中的一种或几种。
4.根据权利要求1所述的一种环保型彩焰蜡烛，其特征在于所述的各色颜料为各种颜色的有机油溶性染料。
5.根据权利要求1所述的一种环保型彩焰蜡烛的制备方法，其特征在于包括以下步骤：
将柠檬酸三甲酯、石蜡、费托蜡、天然蜡、聚乙烯蜡和硬脂酸按上述质量份数比例放入容器中加热至80~100℃，并缓慢搅拌均匀；
（2）按上述质量份数比向步骤（1）搅拌均匀的物质中加入油溶性染料，并搅拌均匀；
（3）烛芯处理：a）将棉芯放入质量百分比浓度为3~5%的氢氧化钠溶液中加热至90~100℃进行脱脂处理2~2.5小时，取出后用去离子水反复清洗，晾干；b）将经a）步骤处理后的棉芯在氨基脲和磷酸铵的复配混合溶液中加热至90~100℃进行脱钙脱钠处理2~2.5小时，取出后用去离子水反复清洗，晾干；c）将经过b）步骤处理的棉芯置于发色剂中1.5~2个小时，取出晾干，得烛芯；
（4）将上述步骤（3）处理好的烛芯固定在模具中；
（5）将上述步骤（2）中均匀的混合物倒入步骤（4）准备的模具中；
（6）冷却、脱模；
（7）包装。
6.根据权利5所述的一种环保型彩焰蜡烛的制备方法，其特征在于所述的步骤（3）中，氨基脲和磷酸铵按质量比1:2复配混合溶液，其中氨基脲的质量比浓度为1~2%，磷酸铵的质量比浓度为3~4%。
7.根据权利5所述的一种环保型彩焰蜡烛的制备方法，其特征在于所述的步骤（3）中的发色剂为钠、钾、硼、钡、锶、镁、钙、铜中的几种金属有机盐或无机盐或有机、无机盐的混合物。