CN1398816A - 轻质高强建筑材料 - Google Patents

轻质高强建筑材料 Download PDF

Info

Publication number
CN1398816A
CN1398816A CN 02129638 CN02129638A CN1398816A CN 1398816 A CN1398816 A CN 1398816A CN 02129638 CN02129638 CN 02129638 CN 02129638 A CN02129638 A CN 02129638A CN 1398816 A CN1398816 A CN 1398816A
Authority
CN
China
Prior art keywords
weights
parts
water
building material
heavy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 02129638
Other languages
English (en)
Inventor
张树荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 02129638 priority Critical patent/CN1398816A/zh
Publication of CN1398816A publication Critical patent/CN1398816A/zh
Pending legal-status Critical Current

Abstract

轻质高强建筑材料涉及一种建筑物隔墙材料或屋面保温层材料，由氧化镁和多种无机镁盐以及粒状泡沫聚苯乙烯按适当比例加水配制成料浆并利用预制模具浇铸成型为标准板材、块材或现场浇铸成型为设计形状，其模具成型工艺主要包括配制料浆、浇铸、带模养护和脱模养护等工序。本发明质量轻、强度高并具有良好的保温隔热隔音性能和防火防潮性能，除特别适于作为现代建筑物隔墙材料和屋面保温层材料外，还可广泛用作暖通管道等设备的保温层材料。

Description

轻质高强建筑材料
技术领域
本发明涉及一种建筑物隔墙材料或屋面保温层材料，特别是涉及一种质量轻、强度高且具有良好的保温隔热隔音性能和防火防潮性能的轻质高强建筑材料。
背景技术
按，建筑物隔墙(非承重墙)材料和屋面保温层材料是一种重要的建筑材料，现代建筑物隔墙材料和屋面保温层材料除必须具有一定的强度外，还特别要求其质量轻并具有良好的保温隔热隔音性能和防火防潮性能。现有技术中的隔墙材料和屋面保温层材料的种类很多，如石膏板、泡沫聚苯乙烯板材、水泥珍珠岩保温板材和水泥蛭石保温材料等，这些隔热材料或屋面保温层材料虽然各有其优点和长处，但也都存在某些明显的缺陷和不足。例如，作为隔墙材料的石膏板，其保温隔热隔音和防潮性能都不够理想；而泡沫聚苯乙烯板材虽然质量轻、保温效果也很好，但其强度较低、防火性能也比较差。作为屋面保温层的水泥珍珠岩保温板材和水泥蛭石保温板材虽然保温性能较好，但强度较低，而且吸水率较高、防潮性能差。
发明内容
本发明的目的即在于提供一种质量轻、强度高且具有良好的保温隔热隔音性能和防火防潮性能的建筑物隔墙材料或屋面保温层材料。
为了实现上述目的，本发明利用氧化镁和多种无机镁盐以及粒状泡沫聚苯乙烯按适当的比例加水配制成料浆并利用预制模具浇铸成标准板材或块材，或现场浇铸成型为设计形状。
在上述隔墙材料或屋面保温层材料中，氧化镁和多种无机镁盐加水后通过水化作用可形成以粒状泡沫聚苯乙烯为骨料的混凝材料。因此，上述隔墙材料或屋面保温层材料将是一种质量轻而强度高的建筑材料并且具有良好的保温隔热隔音性能和防火防潮性能。
以下结合具体实施例对本发明轻质高强建筑材料的技术特征作进一步的详细说明。
具体实施方式
本发明轻质高强建筑材料由氧化镁和多种无机镁盐以及粒状泡沫聚苯乙烯按适当比例加水配制成料浆并利用预制模具浇铸成标准板材或块材，或现场浇铸成型为设计形状，其料浆原料配方为：
水                  100           份重
氧化镁              250-350       份重
滑石粉(硅酸镁)      100-210       份重
氯化镁              120-200       份重
硫酸镁              10-40         份重
粒状泡沫聚苯乙烯    20-80         份重
在上述料浆原料配方中，粒状泡沫聚苯乙烯可采用废弃的泡沫聚苯乙烯并利用破碎机破碎成1-5mm的颗粒状。
料浆原料配方实施例1：
水                  100           份重
氧化镁              310           份重
滑石粉              153           份重
氯化镁              167           份重
硫酸镁              16            份重
粒状泡沫聚苯乙烯    57            份重
料浆原料配方实施例2：
水                  100           份重
氧化镁              290           份重
滑石粉              134           份重
氯化镁              158           份重
硫酸镁              13            份重
粒状泡沫聚苯乙烯    38            份重
料浆原料配方实施例3：
水                  100           份重
氧化镁              290           份重
滑石粉              134           份重
氯化镁              158           份重
硫酸镁              13            份重
粒状泡沫聚苯乙烯    38            份重
本发明轻质高强建筑材料可采用预制模具浇铸成型为标准板材或块材，其成型工艺主要包括配制料浆、浇铸、带模养护和脱模养护等工序。配制料浆即按照料浆原料配方将氧化镁和多种无机镁盐以及粒状泡沫聚苯乙烯加水配制成料浆并充分搅拌，以使粒状泡沫聚苯乙烯表面均匀包裹料浆。浇铸时，可直接将料浆浇铸在表面光滑的底模中，也可先在模具底部铺垫脱模薄膜，然后再浇铸料浆。带模养护的周期为1-2天，脱模养护的周期则为2-6天。本发明轻质高强建筑材料也可现场浇铸成型为设计形状。
实施表明，本发明轻质高强建筑材料质量轻(300-500kg/m3)，强度高并具有良好的保温隔热隔音性能和防火防潮性能，除特别适于作为现代建筑物隔墙材料和屋面保温层材料外，还可广泛用作暖通管道等设备的保温层材料。

Claims (4)

1.一种轻质高强建筑材料，其特征在于由氧化镁和多种无机镁盐以及粒状泡沫聚苯乙烯按适当的比例加水配制成料浆并利用预制模具浇铸成型为标准板材、块材或现场浇铸成型为设计形状，料浆的原料配方为：
水                   100             份重
氧化镁               250-350         份重
滑石粉(硅酸镁)       100-210         份重
氯化镁               120-200         份重
硫酸镁               10-40           份重
粒状泡沫聚苯乙烯     20-80           份重
2.根据权利要求1所述的轻质高强建筑材料，其特征在于所述料浆的原料配方为：
水                   100             份重
氧化镁               310             份重
滑石粉               153             份重
氯化镁               167             份重
硫酸镁               16              份重
粒状泡沫聚苯乙烯     57              份重
3.根据权利要求1所述的轻质高强建筑材料，其特征在于所述料浆的原料配方为：
水                   100             份重
氧化镁               290             份重
滑石粉               134             份重
氯化镁               158             份重
硫酸镁               13              份重
粒状泡沫聚苯乙烯     38              份重
4.根据权利要求1所述的轻质高强建筑材料，其特征在于所述料浆的原料配方为：
水                   100             份重
氧化镁               327             份重
滑石粉                 173          份重
氯化镁                 171          份重
硫酸镁                 17.6         份重
粒状泡沫聚苯乙烯       72           份重
CN 02129638 2002-09-06 2002-09-06 轻质高强建筑材料 Pending CN1398816A (zh)