CN105948691B - 一种胶凝剂 - Google Patents
一种胶凝剂 Download PDFInfo
- Publication number
- CN105948691B CN105948691B CN201610122240.8A CN201610122240A CN105948691B CN 105948691 B CN105948691 B CN 105948691B CN 201610122240 A CN201610122240 A CN 201610122240A CN 105948691 B CN105948691 B CN 105948691B
- Authority
- CN
- China
- Prior art keywords
- gelling agent
- agent according
- water
- magnesia
- sio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种胶凝剂。它的组分及重量份数组成为:富镁铝硅酸盐30‑350,高活性硅酸铝80‑150,硼酸(H3BO3)5‑15,柠檬酸(C6H8O7)5‑15,磷酸(H3PO4)2‑15,硅溶胶(SiO2.n H2O)5‑10,硅氧烷防水剂1‑3,轻烧氧化镁800‑1200,六水氯化镁300‑500,七水硫酸镁80‑120,水400‑600。本发明在保留现有技术的防火性能、抗水性能等技术指标的基础上,被胶固、粘结的各种建筑装饰材料不含有甲醛,提高了房屋的使用率,营造了一个绿色环保的居住环境,维护了广大居住者的身体健康。
Description
技术领域
本发明涉及一种建筑材料,尤其是涉及一种广泛用于胶固、粘结建筑装饰板的胶凝剂。
背景技术
迄今为止用于木本、草本秸杆纤维的粘接剂均采用公知的三醛胶、脲醛、酚醛、三聚氰胺缩甲醛与聚合异氰酸酯这两类粘接剂,上述两类粘接剂前者含有甲醛,脲醛胶不燃性耐水性能差,不能应用于热压稻草板,后者价格昂贵使之无法推广应用。特别是使用以上含有甲醛的胶凝剂凝固的板材装修房屋,和使用以上含有甲醛的胶凝剂凝固的板材制作的家具,则需要将房屋空置几个月以使甲醛尽可能挥发方能入住,如此降低了房屋的使用率,且甲醛很难彻底挥发,严重危害了广大居住者的身体健康。
发明内容
本发明所要解决的技术问题是提供一种克服现有技术缺陷的、价格低廉、不含甲醛的胶凝剂。本发明解决其技术问题采用的技术方案是:一种胶凝剂,它的组分及重量份数组成为:富镁铝硅酸盐30-350,高活性硅酸铝80-150,硼酸(H3BO3)5-15,柠檬酸(C6H8O7)5-15,磷酸(H3PO4)2-15,硅溶胶(SiO2.n H2O) 5-10,硅氧烷防水剂1-3,轻烧氧化镁800-1200,六水氯化镁300-500,七水硫酸镁80-120,水400-600。本发明所要解决的技术问题还可进一步通过如下技术方案加以解决:富镁铝硅酸盐的型号为GN-2-20,比重为2.05-2.32g/cm3,粒径为20-40nm,莫氏硬度为2-3;高活性硅酸铝的粒径为1-2微米,比表面积20㎡/g,灼失0.5%,SiO2 54%,Al2O343%;硼酸的比重为1.43g/cm3;硅溶胶的粒径为500-700nm,SiO220-30%,Na2O 0.3%;硅氧烷防水剂的型号为SHP-50,其以D4为单体聚合而成,分子量介于10-100万之间的有机硅聚合物,硅烷分子中的长链基CnH2n-1,n≥4,具有极强的憎水性,有机硅在水和Mg(OH)2碱性的催化作用下,硅烷分子中乙氧基团首先发生水解反应,生成硅羟基,然后硅羟基之间与胶凝材料表面和毛细孔道中的羟基进一步缩合反应生成网状有机硅树脂,通过稳定的硅氧化学健将有机硅分子牢固地固化在凝固体中。硅氧烷防水剂制备的镁质胶凝剂,成为具备有机硅杂化特征的气硬性胶凝剂;轻烧氧化镁中的氧化镁含量≥85%,且氧化镁中的活性氧化镁≥65%,游离CaO%≤1.5,烧失量 6.5-9.5,细度180目;六水氯化镁中的MgCl2≥46%,钙离子≤0.7%,碱金属氧化物以Cl-计≤1.2%;七水硫酸镁≥99.5%,氯化物≤0.015%,重金属≤0.002(Pb),砷≤0.0005%,铁≤0.002%,灼烧失量48.0-52.0%,酸碱度为pH5-8;水为食用管道水。本发明的各组分在本发明中的作用分别是:富镁铝硅酸盐起到悬浮,分散,稳定作用,能阻止Mg(OH)2的团聚,增加胶凝强度;高活性硅酸铝可增加抗压、抗折强度,提高耐候性,降低渗透性,有效降低氯离子迁移,且与水化产生的Mg(OH)2反应生成高强度的胶凝特性,提高了不同龄期的抗折强度(断裂模量),减少甚至消除了风化,有效降低了胶固体的渗透性,使水渗透极难,具有更高火山灰活性;硼酸交联健羟基增加胶凝强度;柠檬酸是一种调凝剂,加入H2O,其电离离子吸附在活性氧化镁水化层表面,形成一种可以抑制发生水化反应的稳定的有机镁铬合物,阻碍水份与活性氧化镁水化接触,延缓MgO的水化速度。并且增加硼酸的溶解度和溶解速度,与高活性硅酸铝一起形成517,518 与莫来石相,形成以镁氧八面体为骨架的一层层状的,稳定的多元复合高强度晶相结构;磷酸起到缓凝作用;硅溶胶形成SiO-O-OH+HO-Si-OH,因Na2O在硅溶胶中含量低,因而本发明胶固体具有优异耐水性,且致密,高强度,抗污染,并与活性氧化镁水物产物Mg(OH)2反应生成硅酸镁,使得本发明具有很强粘合力;硅氧烷防水剂其以D4为单体聚合而成,分子量介于10-100万之间的有机硅聚合物,硅烷分子中的长链基CnH2n-1,n≥4,具有极强的憎水性,有机硅在水和 Mg(OH)2碱性的催化作用下,硅烷分子中乙氧基团首先发生水解反应,生成硅羟基,然后硅羟基之间与胶凝材料表面和毛细孔道中的羟基进一步缩合反应生成网状有机硅树脂,通过稳定的硅氧化学健将有机硅分子牢固地固化在凝固体中;轻烧氧化镁形成胶凝硬化体,主要是以活性氧化镁水化物氢氧化镁及以三元化物结晶相复盐为主的多元化合物胶凝硬化体。六水氯化镁起到固化作用;七水硫酸镁起到调和固化作用;水稀释本发明中的其它组分。本发明中的所有组分均不含甲醛,胶凝后的硬化体也无甲醛。本发明中的所有组分均为市售产品。本发明的制备方法为均匀搅拌。本发明胶固、粘结的多层板经国家林业局南京人造板质量监督检验站检验(检验报告编号:第15-583-2号),甲醛释放量为“0.0”。本发明由于采用上述技术方案,降低了生产成本和销售价格,既能直接与无机材料牢固结合,又能与有机植物纤维牢固结合,在保留现有技术的防火性能、抗水性能等技术指标的基础上,被胶固、粘结的各种建筑装饰材料不含有甲醛,提高了房屋的使用率,营造了一个绿色环保的居住环境,维护了广大居住者的身体健康。
附图说明
图1—3为本发明的用于制作多层板的检测报告。
具体实施方法
本发明各实施例中组分的份数计量单位均为kg 。
实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 实施例6 | |
富镁铝硅酸盐 | 30 | 94 | 158 | 222 | 286 | 350 |
高活性硅酸铝 | 80 | 94 | 108 | 122 | 136 | 150 |
硼酸 | 5 | 7 | 9 | 11 | 13 | 15 |
柠檬酸 | 5 | 7 | 9 | 11 | 13 | 15 |
磷酸 | 2 | 4.6 | 7.2 | 9.8 | 12.4 | 15 |
硅溶胶 | 5 | 6 | 7 | 8 | 9 | 10 |
硅氧烷防水剂 | 1 | 1.4 | 1.8 | 2.2 | 2.6 | 3 |
活性氧化镁 | 800 | 880 | 960 | 1040 | 1120 | 1200 |
六水氯化镁 | 300 | 340 | 380 | 420 | 460 | 500 |
七水硫酸镁 | 80 | 88 | 96 | 104 | 112 | 120 |
水 | 400 | 440 | 480 | 520 | 560 | 600 |
实施例7 | 实施例8 | 实施例9 | 实施例10 | 实施例11 | 实施例12 | |
富镁铝硅酸盐 | 30 | 286 | 158 | 222 | 94 | 350 |
高活性硅酸铝 | 150 | 94 | 122 | 108 | 136 | 80 |
硼酸 | 5 | 13 | 9 | 11 | 7 | 15 |
柠檬酸 | 15 | 7 | 11 | 9 | 13 | 5 |
磷酸 | 2 | 12.4 | 7.2 | 9.8 | 4.6 | 15 |
硅溶胶 | 10 | 6 | 8 | 7 | 9 | 5 |
硅氧烷防水剂 | 1 | 2.6 | 2.2 | 1.8 | 1.4 | 3 |
活性氧化镁 | 1200 | 880 | 1040 | 960 | 1120 | 800 |
六水氯化镁 | 300 | 460 | 380 | 420 | 340 | 500 |
七水硫酸镁 | 120 | 88 | 104 | 96 | 112 | 80 |
水 | 400 | 560 | 480 | 520 | 440 | 600 |
实施例13 | 实施例14 | 实施例15 | 实施例16 | 实施例17 | 实施例18 | |
富镁铝硅酸盐 | 30 | 286 | 222 | 158 | 94 | 350 |
高活性硅酸铝 | 122 | 94 | 108 | 80 | 136 | 150 |
硼酸 | 5 | 13 | 11 | 9 | 7 | 15 |
柠檬酸 | 11 | 7 | 9 | 15 | 13 | 5 |
磷酸 | 2 | 12.4 | 9.8 | 7.2 | 4.6 | 15 |
硅溶胶 | 8 | 6 | 7 | 5 | 9 | 10 |
硅氧烷防水剂 | 3 | 1.8 | 2.6 | 1.4 | 2.2 | 1 |
活性氧化镁 | 1040 | 880 | 960 | 800 | 1120 | 1200 |
六水氯化镁 | 300 | 460 | 420 | 380 | 340 | 500 |
七水硫酸镁 | 104 | 88 | 96 | 80 | 112 | 120 |
水 | 400 | 560 | 520 | 480 | 440 | 600 |
Claims (8)
1.一种胶凝剂,其特征是它的组分及重量份数组成为:富镁铝硅酸盐 30-350,高活性硅酸铝80-150,硼酸(H3BO3)5-15,柠檬酸(C6H8O7)5-15,磷酸(H3PO4)2-15,硅溶胶(SiO2.nH2O)5-10,硅氧烷防水剂1-3,轻烧氧化镁800-1200,六水氯化镁300-500,七水硫酸镁80-120,水400-600。
2.根据权利要求1所述的一种胶凝剂,其特征是:高活性硅酸铝的粒径为1-2微米,比表面积20㎡/g,灼失0.5%,SiO2 54%,Al2O343%。
3.根据权利要求1所述的一种胶凝剂,其特征是:硼酸的比重为1.43g/cm³ 。
4.根据权利要求1所述的一种胶凝剂,其特征是:硅溶胶的粒径为500-700nm, SiO220-30%,Na2O 0.3%。
5.根据权利要求1所述的一种胶凝剂,其特征是:硅氧烷防水剂的型号为SHP-50。
6.根据权利要求1所述的一种胶凝剂,其特征是:轻烧氧化镁中的氧化镁含量≥85%,且氧化镁中的活性氧化镁≥65%,游离CaO≤1.5%,烧失量6.5-9.5,细度为180目。
7.根据权利要求1所述的一种胶凝剂,其特征是:七水硫酸镁≥99.5%,氯化物≤0.015%,重金属Pb≤0.002,砷≤0.0005%,铁≤0.002%,灼烧失量48.0-52.0%,酸碱度为pH5-8。
8.根据权利要求1所述的一种胶凝剂,其特征是:水为食用管道水。