CN1376733A - 增强型农用多功能母粒 - Google Patents

增强型农用多功能母粒 Download PDF

Info

Publication number
CN1376733A
CN1376733A CN 01105796 CN01105796A CN1376733A CN 1376733 A CN1376733 A CN 1376733A CN 01105796 CN01105796 CN 01105796 CN 01105796 A CN01105796 A CN 01105796A CN 1376733 A CN1376733 A CN 1376733A
Authority
CN
China
Prior art keywords
agent
sericite
strengthened
mother particles
antioxidant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 01105796
Other languages
English (en)
Inventor
熊小勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI SANCHENG CHEMICAL CO Ltd
Original Assignee
SHANGHAI SANCHENG CHEMICAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI SANCHENG CHEMICAL CO Ltd filed Critical SHANGHAI SANCHENG CHEMICAL CO Ltd
Priority to CN 01105796 priority Critical patent/CN1376733A/zh
Publication of CN1376733A publication Critical patent/CN1376733A/zh
Pending legal-status Critical Current

Abstract

本发明涉及增强型农用多功能母粒,原料组成(重量百分数)包括:聚烯烃40~50%,绢云母25~35%,光稳剂1~3%,热稳剂1~3%,抗氧化剂1~3%,防流滴剂12~18%,分散剂1~4%;与现有技术相比,本发明具有保温性及耐候性好、抗张强度高等优点。

Description

增强型农用多功能母粒
本发明涉及高分子材料原料,尤其涉及一种增强型农用多功能母粒。
普通的农用薄膜一般都是采用聚烯烃母粒加工而成的,这种薄膜在使用过程中,由于其在保温性能和抗候性能等方面的局限性,已经难以满足现有的园艺发展水平及引进的新型水果蔬菜的栽培技术要求,并且由于普通的农用功能薄膜的抗张强度、柔韧性,耐高温和耐酸碱性能所限,无法使园艺产品的品种和质量达到更高的要求。
本发明的目的就是为了克服上述现有技术存在的缺陷而提供一种保温性及耐候性好、抗张强度高的增强型农用多功能母粒。
本发明的目的可以通过以下方式来实现:增强型农用多功能母粒,其特点是,原料组成(重量百分数)包括:
                  聚烯烃       40~50%
                  绢云母       25~35%
                  光稳剂       1~3%
                  热稳剂       1~3%
                  抗氧化剂     1~3%
                  防流滴剂     12~18%
                  分散剂       1~4%
所述的聚烯烃选自低密度聚乙烯,所述的绢云母需经偶联剂活化处理,所述的光稳剂选自受阻胺类光稳剂,所述的热稳剂选自受阻胺类热稳剂,所述的抗氧化剂选自受阻胺类抗氧化剂,所述的防流滴剂选自多元醇脂肪酸酯,所述的分散剂选自低分子量聚乙烯蜡。
所述的原料组成(重量百分数)较佳包括:
                  聚烯烃       43~47%
                  绢云母       28~32%
                  光稳剂       1~2%
                  热稳剂       1~2%
                  抗氧化剂     1~2%
                  防流滴剂     14~16%
                  分散剂       3~5%
所述的绢云母需经偶联剂活化处理。
所述的偶联剂为钛酸酯或铝酸酯。
与现有技术相比,本发明的配方中加入了一种新型化学成份——绢云母。它是一种具有高品质、高强度、高细度粉化的优质原料,通过湿法分级提纯等工艺而制得,它的片状结构、晶体状态、径厚比、丝绢光泽等特性保证其在加工过程中不会有丝毫的损伤,所以加入绢云母的农用母粒主要具备以下特点。
1.它可以使产品具备优良的尺寸稳定性,提高塑料的拉伸强度,极大地改善其热变形温度,增强制品的韧性,防老化,抗龟裂。
2.它对于增强热塑性塑料的突出优点有:硬度高,填料体积大,耐酸碱腐蚀性好,渗透性好,介电性能优良,热膨胀系数小,可燃性低,横压周期短,平面增强,磨耗小,加工设备的磨损小。
3.它对于增强热固性塑料的突出优点有:有良好的介电性能,尺寸稳定性高,硬度和热畸变温度提高,渗透性、绝缘性好。
4.它具有良好的可溶性,可与大量其它填料(特别是滑石、玻璃纤维、玻璃粉、碳酸钙、硅粉)等相容。
下面结合具体实施例,对本发明作进一步说明。
实施例1
原料配方(重量百分数):
         聚烯烃(LDPE-N150)                 45%
         绢云母(超微细经钛酸酯活化处理)    30%
         光稳剂(汽巴-944)                  2%
         热稳剂(汽巴-900)                  2%
         抗氧化剂(汽巴-7072)               2%
         防流滴剂(ATF-2)                   15%
         分散剂(WAX-3)                     4%
将上述配方的原料进行混合、低速搅拌、整理,然后高速搅拌、混炼,最后造粒、筛选得到增强型农用多功能母粒。
实施例2
原料配方(重量百分数):
         聚烯烃(LDPE-N200)                 40%
         绢云母(超微细经铝酸酯活化处理)    35%
         光稳剂(3V-HA88)                   1%
         热稳剂(汽巴-900)                  1%
         抗氧化剂(汽巴-7072)               2%
         防流滴剂(ATF-2)                   18%
         分散剂(WAX-3)                     3%
制造方法与实施例1相同。
实施例3
原料配方(重量百分数):
         聚烯烃(LDPE-N220)               50%
         绢云母(超微细经钛酸酯活化处理)  25%
         光稳剂(汽巴-944)                3%
         热稳剂(汽巴-900)                3%
         抗氧化剂(汽巴-7072)             3%
         防流滴剂(ATF-2)                 14%
         分散剂(WAX-3)                   2%
制造方法与实施例1相同。

Claims (3)

1.增强型农用多功能母粒,其特征在于,原料组成(重量百分数)包括:
                  聚烯烃       40~50%
                  绢云母       25~35%
                  光稳剂       1~3%
                  热稳剂       1~3%
                  抗氧化剂     1~3%
                  防流滴剂     12~18%
                  分散剂       1~4%
所述的聚烯烃选自低密度聚乙烯,所述的绢云母需经偶联剂活化处理,所述的光稳剂选自受阻胺类光稳剂,所述的热稳剂选自受阻胺类热稳剂,所述的抗氧化剂选自受阻胺类抗氧化剂,所述的防流滴剂选自多元醇脂肪酸酯,所述的分散剂选自低分子量聚乙烯蜡。
2.根据权利要求1所述的一种增强型农用多功能母粒,其特征在于,所述的原料组成(重量百分数)较佳包括:
                  聚烯烃       43~47%
                  绢云母       28~32%
                  光稳剂       1~2%
                  热稳剂       1~2%
                  抗氧化剂     1~2%
                  防流滴剂     14~16%
                  分散剂       3~5%
所述的绢云母需经偶联剂活化处理。
3.根据权利要求1或2所述的一种增强型农用多功能母粒,其特征在于,所述的偶联剂为钛酸酯或铝酸酯。
CN 01105796 2001-03-28 2001-03-28 增强型农用多功能母粒 Pending CN1376733A (zh)