CN1364445A - 吸收性物品和吸收性物品用防护剂 - Google Patents
吸收性物品和吸收性物品用防护剂 Download PDFInfo
- Publication number
- CN1364445A CN1364445A CN01133827A CN01133827A CN1364445A CN 1364445 A CN1364445 A CN 1364445A CN 01133827 A CN01133827 A CN 01133827A CN 01133827 A CN01133827 A CN 01133827A CN 1364445 A CN1364445 A CN 1364445A
- Authority
- CN
- China
- Prior art keywords
- absorbent commodity
- protective agent
- powder body
- vitamin
- skin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种能防止由尿布、生理用卫生巾等吸收性物品在穿用者皮肤引起斑疹并没有发粘感的吸收性物品,及一种涂敷在吸收性物品表面上的防护剂。具体地说提供一种含有可以改善触感的粉体或使该粉体附着在表面上的吸收用品防护剂和表面上涂有该防护剂的吸收性物品。
Description
技术领域
本发明涉及能在穿用尿布、生理用卫生巾等吸收性物品时减少发生皮炎(斑疹)，并且没有发粘感的吸收性物品和为了得到这种吸收性物品而涂敷在吸收性物品表面上的防护剂，具体地涉及能防止在穿用尿布或生理用卫生巾等吸收性物品时因大便、尿和经血等体液的化学刺激和因吸收性物品的表面材料同皮肤的摩擦的物理刺激而引起的接触性皮炎(斑疹)，并且无发粘感的吸收性物品和涂敷在该吸收性物品表面上的防护剂。
背景技术
在穿用纸尿布、生理用卫生巾等吸收性物品时会发生下述所谓麻烦的问题：由于大便、尿、经血等体液附着在皮肤上，或为改善吸收性物品的表面的特性而用的表面活剂等化学物质刺激皮肤，而引起的皮炎，和因皮肤与吸收性物品的表面材料接触对皮肤形成摩擦而产生的物理刺激引发的接触性皮炎。
另外，由于这些化学刺激和物理刺激的主要原因交互作用对皮肤的刺激增大，伴随着皮肤的膨润结果，还引起吸收性物品的表面材料与皮肤的摩擦系数增加的问题。
为了防止这类接触性皮炎(斑疹)，在更换该吸收性物品时将附着在皮肤上的体液擦干净，保持皮肤的清洁是重要的。但是在从附着体液直到更换吸收性物品的时间内体液和皮肤的接触是不可能完全避免的，即使为了缩短体液与皮肤接触时间而频繁地更换吸收性物品，也总还有限制。
另外，为了防止这样的接触性皮炎，还有在婴幼儿等穿用者皮肤上涂敷润肤霜、油等方法，在更换尿布时，虽然可以在穿用者的臀部、肛门部等上涂敷润肤霜、油脂等，但每当更换尿布时进行涂敷是烦锁的，并污染涂敷润肤霜等的护理者的手，而且对婴幼儿、高龄人等皮肤抵抗力低的穿用者来说，还会发生通过涂敷润肤霜等的护理者的手指被细菌感染这样的卫生方面的问题。
因此，尝试通过把皮肤护理物质涂敷在吸收性物品的表面上来解决这些问题，作为这样的尝试的之一，在特开平2-1265号公报中公开了在用于失禁者的一次性吸收物品上具有PH调理剂的方法。该方法是基于发现尿布斑疹的原因是来自排泄物的细菌或者因酵素与尿接触而产生氮。从而使皮肤的PH值增加这一见解而开发的。然而在利用PH调理剂时，却不能防止除氮以外的原因引起的斑疹。
另外，在特表平10-509895号公报，特表平10-509896号公报，特表平11-510082号公报和特表平11-510416号公报中，公开了带有由用于提高柔润性的润肤剂和用于使润肤剂在吸收性物品表面上不动的固定剂组成的柔润剂的一次性吸收性物品。该吸收性物品上的润肤剂因穿用吸收性物品时的体温而溶化附着在皮肤上，从而可以减轻在有润肤剂的皮肤移动而对固体液引起的刺激，或者保护皮肤免受随着吸收性物品表面和皮肤的柔润性提高而产生的物理刺激，这些便是对该一次性吸收性物品的期待的效果。
然而，在本发明人完成试验时，根据特表平10509895号公报，特表平10-509896号公报，特表平11-510082号公报和特表平11-510416号公报公开的吸收性物品还弄清了这四份公报中的方案在防止穿用者的斑疹上是不充分的。
另外如果用这些在皮肤表面上形成油性润肤剂防护层的方法，由于油性成分附着在穿用者皮肤上，会产生以下的问题：产生发粘感或滑溜感，使穿用者的穿着感变差，或者使在与吸收性物品接触时的触感变差。
发明的内容
本发明是为解决上述现有技术中的问题而提出的，即把提供可以防止尿布、生理卫生巾等吸收性物品穿用者的斑疹、并且能提供没有发粘感的吸收性物品、和提供涂敷为了得到的这样吸收性物品而涂敷在吸收性物品的表面上的防护剂作为课题。
更具体地说，把提供无发粘感的防护剂和涂有该防护剂的吸收性物品作为课题：通过把该防护剂涂敷在吸收性物品的表面上，既可以防止体液或表面活性剂等引起的化学刺激，又可防止因皮肤与吸收性物品表面的摩擦产生的物理刺激而引发的接触性皮炎(斑疹)。
本发明人为了解决上述问题，而锐意研究的结果，发现了在接触性皮类(斑疹)的原因中除了上述的体液等引起的化学刺激原因和物理刺激原因以外，还存在作为残留在皮肤上的体液旧废物的氨基酸或皮脂刺激皮肤的这个原因，从而实现了本发明。具体地说，本发明人在上述特表平10-509895号公报、特表平10-509896号公报、特表平11-510082号公报和特表平11-510416号公报中公开的吸收性物品中，发现用润肤剂组成物覆盖体液旧废物附着的皮肤，反而容易引起旧废物的变质，从而又因刺激皮肤而产生斑疹。因此本发明人为了防止旧废物氧化变质而考虑使该防护剂中含有氧化防止剂的方案来实现本发明。
本发明人进一步发现：在把上述清洁剂组成物作为防护剂的吸收性物品中，通过在防护剂中混合用于改善触感的粉体或把该粉体附着在防护剂表面上就可以减少因防护剂的油性润肤剂附着在穿用者的皮肤上而产生的发粘感或滑溜感，从而实现本发明。
即，本发明是关于下述(1)-(9)的吸收性物品防护剂和(10)的吸收性物品。
(1)一种混合用于改善触感的粉体或把该粉体附着在表面上的吸收性物品用防护剂。
(2)上述(1)的吸收性物品用防护剂的粉体是从天然无机物粉体，合成无机物粉体，有机物粉体，金属肥皂和合成高分子粉体中选择的一种以上粉体。
(3)上述(1)和(2)的吸收性物品用防护剂含有油溶性防氧化剂。
(4)上述(3)的吸收性物品用防护剂的防氧化剂是从由维生素A群、维生素B群、维生素D群、维生素E群和维生素K群中组成的维生素群中选出的一种以上的化合物。
(5)上述(1)～(4)的吸收性物品用防护剂还包含润肤剂和/或固定剂。
(6)上述(1)～(5)的吸收性物品用防护剂的润肤剂是在25℃时为液体或半固体的油性物质。
(7)上述(6)的吸收性物品用防护剂的润肤剂是甘油脂肪酸酯。
(8)上述(1)～(7)中的吸收性物品用防护剂的固定剂的熔点是40-90℃，在20℃的表面张力为25-45dyn/cm。
(9)上述(8)的吸收性物品用防护剂的固定剂是从甘油脂肪酸酯、石腊和高级乙醇中选取的一种以上物质。
(10)在表面上涂敷上述(1)～(9)中的任意一种防护剂的吸收性物品。
按照本发明，因为在吸收性物品的表面上有用于改善触感的粉体，不仅能减轻穿用者的发粘感或滑溜感，而且特别是在夏季高温多湿时，还可望能防止因发粘感或滑溜感而变得酷暑难过的情形，并且防止吸收性物品的穿用者或购买者欲望减退。并能因减轻发粘感而改善穿用者的皮肤状态。
具体实施方式
下面详细说明本发明，但本发明不受其限定。
在本发明的吸收性物品中可以举出纸尿布，生理用卫生巾、月经垫衬里、失禁垫、训练裤、尿布衬里等。
在这些吸收性物品与皮肤接触的部分例如顶片、立体褶、护翼、腰褶等上可以涂敷本发明的防护剂。特别是最好涂敷在大便、尿附着机会多的顶片部。
本发明用于改善触感所使用的粉体是从粘土矿物等天然无机粉体的粉碎物、合成无机粉体、有机粉体、金属肥皂、合成高分子粉体中选出的一种以上的粉体。该粉体颗粒的平均粒径如果太小就不能抑制防护剂的发粘感，但如太大反而会产生粗糙感。因此优选的范围是0.05～50μm，更优选的范围是0.5～25μm。
作为天然无机粉体被采用的代表物质为：滑石粉、陶土、绢云母、云母等粘土矿物的粉碎物。
作为合成无机粉体，可以举出碳酸钙、碳酸镁、无水硅酸、二氧化锌、氧化钛等物质。
作为合成有机粉体优选的是，氨基酸系的粉体，最优选的是N-月桂酰和L-赖氨酸
合成高分子粉体可以举出：聚乙烯粉末、尼龙粉末、聚丙稀酸、接枝聚本乙烯、甲基硅氧烷网状共聚体、甲基丙稀酸树脂粉等。
作为金属肥皂，可以用对皮肤的刺激少并用作化妆品原料的铝、锌、镁、钙等脂肪酸。具体的是硬脂酸铝、硬脂酸锌、硬脂酸镁、硬脂酸钙、铝锡酸锌、十四烷酸锌、十四烷酸镁、十二烷酸锌、十一碳烯酸锌等。
防氧化剂优选的是具有与油性的柔润剂相溶的油溶性防氧化剂。作为具有油溶性的防氧化机能的物质可以举出：维生素类。如由维生素A群、维生素B群(维生素B2四铬酸酯、维生素B2烟酸酯)、维生素D群、维生素E群和维生素K群等组成的维生素群的化合物、BHT(2，6-2-t-丁基-P-甲酚/6-ジ-t-ブチル-p-クレゾ-ル)、BHA(丁基化羟基苯甲醚)、丙烯没食子酸酯。
这些防氧化剂可以单独使用也可以混合使用。
优选的是维生素群。维生素类由于对人体的安全性高，副作用小所以是非常理想的防氧化剂，而且在与皮肤直接接触的化妆品中更加广泛使用，并发现其在皮肤上的附着效果非常好。
在本发明中，所谓维生素群是指包含维生素和其诱导体的意思。使本发明的特性发挥得特别好的化合物是维生素E群，即，维生素E(胎果酚)，它的异性体以及诱导体：DL-α胎果酚，醋酸DL-α-胎果酚，琥珀酸DL-α-胎果酸，琥珀酸-DL-α胎果酚钙等。因为维生素E是维生素类中抗氧化力最高的，所以是特别优选的。
在本发明中，柔润剂使皮肤柔软、温和有弹性，且光滑地覆盖皮肤，柔润剂中具有加湿和清洁功能的使润滑性增加的物质。作为柔润剂最好在常温(25℃)下为液体或半固体油性成分。
虽然作为柔润剂可全部使用公知的物质(例如，参照前面所述的特表平10-509895号公报，特表平10-509896号公报，特表平11-510082号公报，以及特表平11-510416号公报)，但是作为有用的物质，可以举出石油系碳化氢、动植物油脂、动植物性蜡、脂肪酸酯系化合物、烷基乙氧基酸、脂肪酸酯乙氧基酸、脂肪醇、聚硅氧烷等。
作为植物油，可推举例如萄萄籽油、红化油、大豆油等的干性油，芝麻油、玉米油、棉籽油、菜籽油、葵花籽油等半干性油；鳄梨油、杏仁油、橄榄油、山茶花油、山茶油、杏仁油、蓖麻油、花生油等不干性油，最好选择经时变化很少的半干性油和不干性油。
作为植物脂，可举出：可可油、棕樟油、棕樟籽油、澳州坚果油、木腊油、椰子油等
作为植物性蜡，可以举出：巴西棕榈蜡、小烛树蜡、泡泡树油(ホホハ油)等。
作为动物性油脂可以举出：海龟油、水貂油、蛋黄油、牛脂、猪油、沙丁鱼油、鱼肝油、鲱鱼油等。
作为动物性蜡可以举出：鲸蜡、蜂蜡、羊毛脂等。
其次，作为碳水化合物，可举出碳原子数为14-15的碳酸二烷、凡士林、石蜡、三十碳烷、十八碳烷、地蜡、丝胶蛋白、微晶蜡等。
这些动植物性油脂也可以是，动植物性蜡或碳水化合物也可以是使不饱和的部分加氢的物质。
柔润剂可以是上述单独的化合物，也可用混合物。
柔润剂优选的是脂肪酸酯，更优选的是甘油脂肪酸酯，甘油脂肪酸酯可以是单酸甘油酯、甘油二酯和甘油三酸酯中的任何一个。甘油酯肪酸酯的脂肪酸的碳原子数为2-35，优选的碳原子数为8-22。特别优选的是椰子油脂肪酸甘油三酸酯。椰子油脂肪酸甘油三酸酯对人体的安全性高，副作用少。而且甘油三酸酯是皮脂的构成成分，因为皮脂被认为在人体皮肤表面有柔润剂的效果，因而作为皮脂中的物质，选择甘油三酸酯特别好。
固定剂是可以使柔润剂在吸收性物质表面不动的物质。固定剂在油和油脂中具有溶解性或者分散性，通过与柔润剂混合可使柔润剂的粘度增加，从而可将固定剂涂敷在吸收性物品的表面上。固定剂优选的融点为40-90℃，20℃时的表面张力为25-45dyn/cm。
作为固定剂可以全部使用例如前述的特表平10-509895号公报，特表平10-509896号公报，特表平11-510082号公报以及特表平11-510416号公报所记载的物质。优选的物质是对人体的安全性高，副作用少的脂肪酸酯、石蜡、高级醇、乙烷基化乙醇，更优选的是融点为40-90℃的甘油脂肪酸酯，碳原子数为12～22的脂肪酸和糊粗酯、石蜡和高级醇。
甘油脂肪酸酯可以是单酸甘油酯、甘油二脂和甘油三酸酯中的任何一种，但优选的是脂肪酸部的碳原子数数为2-35，特别优选的是碳原子数为8-22。最优选的是硬脂精酸单酸甘油酯，十二烷基酸单酸甘油酯。作为脂肪酸糊精酯，可以是例如十六烷酸糊精、硬脂酸糊精、山芋酸糊精、米斯奇林(ミスチリン)酸糊精、椰子油脂肪酸糊精、月桂酸糊精。
优选的石蜡是碳原子数在16-40内，融点在40-90℃，20℃的比重为0.88～0.92的石蜡。
高级醇是碳原子数在14～32，特别优选的是原子数为16-22的醇，最优选的是硬脂醇。
这些固定剂既可以单独用，也可以作为混合物用。
本发明的防护剂，既可由防氧化剂和柔润剂构成，也可由防氧化剂和固定剂构成，还可由防氧化剂、柔润剂和固定剂构成。
本发明的防护剂，除了包含改善触觉的粉体，防氧化剂、柔润剂和固定剂以外，还可以任意地含有用于改善吸收性物品特性的通常使用的物质。还可含有抗炎症的成分，PH值理整剂和用于提高吸收性的表面活性剂。也可含有抗菌剂和保湿剂。
作为抗炎症的成分可用芍药属、肉盘菌属、金丝桃属、春黄菊、甘草、桃花、艾蒿、苏紫提取物等天然抗炎症剂，也可使用脲基海因、甘草酸二钙等合成抗炎症剂。
可以添加作为保持皮肤弱酸性配合剂的PH值调理剂，作为这样的PH值调理剂，可以用莱果酸、琥珀酸、枸橼酸、酒石酸、乳酸等。作为改善吸收性的表面活性剂，可用蔗糖脂肪酸酯等对皮肤刺激小的表面活性剂。
本发明的用于改善触感的粉体，既可以将其与防氧化剂、柔润剂和固定剂组成的防护剂混合起来用，也可以使其附着在防护剂的表面。
以下举例说明上述的实施方式。
(1)将柔润剂、防氧化剂和固定剂构成的三种成分的防护剂同改善触感的粉体混合，使其在吸收性物体的表面形成单一的层。在这种情况下，柔润剂和防氧化剂与固定剂的重量比为5～95∶95～5，优选的比例为30～70∶70～30，粉体与三种成分的防护剂从0.001～70重量％，优选的为0.01～40重量％的比例混合。与粉体混合后的防护剂在吸收性物品的表面上单位面积的含量大约为0.5～50g/m2，优选的为1-30g/m2。
(2)使由柔润剂、防氧化剂和固定剂组成的三种成分的防护剂在吸收性物品的表面形成单一的一层。在这种情况下，柔润剂和防氧化剂与固定剂的重量比为：5～95∶95～5，优选的是30～70∶70～30，防护剂在吸收性物品表面上单位面积的含量是0.5～50g/m2，优选的是1～30g/m2，将改善触感的粉体附着在与穿用者皮肤接触一侧的三种成分构成的防护剂的表面层上，比例为0.001～70重量％，优选的为0.01～40重量％。
(3)另外，也可以使防护剂在吸收性物品的表面以多层的形式存在。在这种情况下，(i)使柔润剂和固定剂两种成分的混合物存在于吸收性物品一侧，使柔润剂、防氧化剂和固定剂三种成分的混合物存在于吸收性物品中与皮肤接触的表面上，或者(ii)优选使柔润剂和固定剂两种成分的混合物存在于吸收性物品的一侧上，使防氧化剂与固定剂两种成分的混合物存在于吸收性物品中与皮肤接触的表面上。
在(i)和(ii)，在吸收性物品的一侧和吸收性物品与皮肤接触面两者上混合改善触感的粉体，或者使粉体仅仅在与皮肤接触的表面上混合，或者使粉体附着在与皮肤接触的面上。
由于这样形成的多层可以增加与皮肤接触部分的防氧化剂的配比量，所以在柔润剂覆盖住皮肤上的旧排泄物前，可以使防氧化剂附着在皮肤上，从而进一步发挥本发明的效果。另外，由于防氧化剂为高价的，只用很少量就能见到效果，所以在与皮肤容易接触的面上多用些防氧化剂的方法是优选的。
在(i)和(ii)中，在吸收性物品一侧的两种成分的混合物中，柔润剂与固定剂的重量比为5～95∶95～5，优选的为30～70∶70～30，吸收性物质的单位面积的用量为0.25～25g/m2，优选的为0.5～15g/m2。
在(i)中，与皮肤接触一侧的三种成分的混合物中柔润剂和防氧化剂与固定剂的重量比为5～95∶95～5，优选的为30～70∶70～30，吸收性物质的单位面积的用量为0.25～25g/m2，优选的为0.5～15g/m2。
在(ii)中，与皮肤接触一侧的两种成分混合物中防氧化剂与固定剂的重量比为5～95∶95～5，优选的为30～70∶70～30，吸收性物质的单位面积的用量为0.25～25g/m2，优选的为0.5～15g/m2。
无论在(i)还是在(ii)中，粉体相对于防护剂都按0.001～70重量％，优选的是都按0.01-40重量％混合。使粉体在表面附着时，相对于防护剂按0.001～70重量％，更好的为0.01～40重量％的量附着。
无论在单层存在的(1)(2)的情况，还是在多层存在的(3)的情况下，相对于使皮肤与吸收性物品接触的整个表面，防护剂的附着面积为5-90％，优选的为10-70％。
在吸收性物品的表面上，防护剂的涂敷方法可以采用通常的涂敷方法。
在适用于液体透过性表面材料的情况下，特别在涂敷的部分，因为液体透过率下降的原因，而有必要在片的表面部分上，保持亲水部分与涂敷部分共存。为此，优选的是将防护剂进行图形化涂敷、或印刷技术的凹板涂敷、以及采用苯胺涂敷法。另外，也可以采用热敏粘接剂涂敷技术应用的挤压涂敷法、开槽涂敷法、喷雾涂敷法等。利用这些涂敷法还可以涂敷成多层。
粉体可以在涂敷防护剂时与防护剂混合后涂敷或者在防护剂涂敷后将粉体附着在吸收性物品的表面上。粉体的附着方法包括：(i)先与空气混合，然后用喷嘴吹到基材上的方法，(ii)将粉体供给圆筒状的轧辊或连续的传送带上，然后再使其转印在基材上的方法，(iii)在基材上直接供给粉体的方法，(iv)使粉体带静电，并使粉体在涂敷机内浮游，使基材通过其中的附着方法。
本发明的防护性物质适用于吸收性物品中与皮肤的接触面，即，通常适用于吸收性物品的顶片。防护剂适用的基材虽没有被限定，但通常是具有透液性的片状物，如无纺布、透液性的多孔薄膜等。
在吸收性物品上使用的无纺布为由1～5d纤维制成的面密度为10-50g/m2的无纺布。构成无纺布的纤维可以是聚烯烃、聚酯等合成纤维、人造丝等半合成纤维、棉、木浆粕、真丝等天然纤维中的任何一种。可以使用的多孔薄膜为：把由热塑性高分子组成的薄膜挤出后，用热针、压纹机和热风穿孔的透液性多孔薄膜。作为构成多孔薄膜的热塑性树脂，可以使用聚乙烯(密度为0.86～1.1g/cm3)或聚丙烯(密度为0.89～1.2g/cm3)等单独或多层，或是混合后使用。
具有透液性的片状物质必需具有体液透过性。根据JISL1092(纤维制品的防水性试验法，耐水度试验A法(低水压法))必需的耐水压度至少为0～300mmH2O，其次，水蒸气从表面材料向吸收体的流通，也就是说透气性也是必要的。根据JISL1906(一般长纤维无纺布试验方法，弗雷泽型透气性试验)，透气度必需至少为5-700cm3/cm2/秒。
本发明的防护剂不仅适用于吸收性物品、创可贴、纸巾、手纸等类似的护肤用干擦用纸，还适用于湿的薄卫生巾这样的护肤用湿擦用纸，而且使用本发明的防护剂后就可以防止因上述这些物品使用时引起的接触性皮炎(斑疹)。在用于湿擦纸时，把本发明的防护剂使用在擦纸的表面上后，使其浸含有水药液。用这样的湿擦纸时，因为在纸片表面上存在油性区域和水性区域。而在水性区域上可除去水溶性污物，所以可以期望水溶性的抗炎症剂产生抗炎症的作用。通过擦拭可以防止因附着在皮肤表面上的油性防护剂引起的接触性皮炎(斑疹)。
下面说明本发明的实施例，但本发明不受这些实施例的限制。
[实施例1]
用椰子油脂肪酸甘油三酸酯作为柔润剂，用硬脂醇作为固定剂，用维生素E作为防氧化剂，用滑石粉作为用于改善触感的粉体，将上述物质分别依次按45.0∶45.0∶5.0∶5.0的重量比熔融混合成防护剂。然后把该防护剂按20g/m2在尿布的表面材料上涂敷成纵条纹状图形。
尿布由透液性的顶片，由木浆粕和高吸水性树脂构成以便吸收、保持体液的吸收体和聚乙烯薄膜的底片组成，采用在体部上通过粘接条固定安装的组装式的尿布。顶片采用使聚烯烃纤维以25g/m2融化连接的无纺布，连续供给顶片用无纺布，用涂刷器在无纺布上涂敷预先制造并加热熔融的防护剂，然后进行冷却。用涂敷有防护剂的顶片同吸收体和底片一起制成组合式尿布。
触感试验
将该尿布穿在婴幼儿身上5小时后，用下述的五等级评价法评价尿布表面和臀部的触感。
等级1：非常发粘
等级2：稍发粘
等级3：不发粘
等级4：稍干爽
等级5：非常干爽。
试验结果表明：尿布表面的触感为等级4，婴幼儿臀部的触感为等级3。
油脂氧化臭味的有无
在婴幼儿身上穿上尿布5小时后，用感官判断氧化臭味。
同脂氧化的有无。
通过下述的表皮脂质分析法，判断在婴儿身上穿上尿布5小时后有无油脂氧化反应。
(i)用含浸丙酮∶醚＝1∶1的混合溶剂的脱脂棉从尿布穿用部分取表皮脂质0.4mg。
(ii)从醚中提取脂质，使提取物在30℃下，在氮气流中用吸气器减压干固。
(iii)将(ii)中的干固物0.4mg溶解在100μL的1-丁醛中，将其中10μL注入CL(化学发光)-HPLC系统中。CL-HPLC条件如下：
柱：CAPCELL-PAKC18(25cm×4.6mm)
柱温度：25℃，溶剂：甲醇
发光指示溶剂：(10μg/ml细胞色素C+1.0μg/ml)硼酸纸(PH＝9.3)
流量：1.1ml/min
检测器：化学发光检测分析器
(iv)分析结果：在确认峰值的情况下，判断为油脂氧化已发生。
皮肤状态试验
把尿布穿在外阴部上确认没有红斑等的健康婴幼儿身上，每天平均更换8个尿布，在一周后用肉眼观察皮肤的状态，结果没有发现皮肤状态变化。
其结果列在表2中。
实施例2
除了用使粉体附着在防护剂表面上来代替把粉体混合在防护剂中以外，与实施例1进行相同的实验。触感试验结果是：尿布表面为等级5，婴幼儿臀部的触感为等级4。并且没有油脂的氧化臭味，认为没有发生油脂氧化，进行皮肤试验的皮肤状态也没有变化，结果列在表2中。
实施例3
除用甘油三硬脂酸锌代替改善触感的粉体外，进行与实施例1相同的试验，结果列在表2中。
实施例4
除用甘油三硬脂酸锌代替改善触感的粉体外，进行与实施例2相同的试验，结果列在表2中。
比较例1
在防护剂中不含有粉体，使椰子油脂肪酸甘油三酸酯∶硬脂醇∶维生素E的重量比为47.5∶47.5∶5.0，并将混合物涂敷在尿布上，除这些不同外，进行与实施例1相同的试验，结果尿布表面和婴幼儿的臀部都是所谓非常发粘的等级1，皮肤的状态没有变化。
比较例2
在防护剂中既不含粉体也不含氧化防止剂，使椰子油脂肪酸甘油三酸酯∶硬脂醇的重量比为50.0∶50.0，并将该混合物涂敷在尿布上，除这些不同之外，进行与实施例1相同的试验，结果尿布表面和婴幼儿的臀部都是所谓非常发粘的等级1，有油脂氧化臭味，油质被氧化，可以在皮肤上看到微小的红斑。
将以上的实施例1～4和比较例1、2的结果列在表1及中表2中。
表1
| 柔润剂 | 固定剂 | 氧化防止剂 | 粉体 | ||||||
| 成分名 | 配比温度 | 成分名 | 配比温度 | 成分名 | 配比温度 | 成分名 | 添加方法 | 添加量 | |
| 实施例1 | 椰子油脂肪酸甘油三酸酯 | 45.0 | 硬脂醇 | 45.0 | 维生素E | 5.0 | 滑石粉 | 混合 | 5.0 |
| 实施例2 | 椰子油脂肪酸甘油三酸酯 | 45.0 | 硬脂醇 | 45.0 | 维生素E | 5.0 | 滑石粉 | 表面附着 | 5.0 |
| 实施例3 | 椰子油脂肪酸甘油三酸酯 | 45.0 | 硬脂醇 | 45.0 | 维生素E | 5.0 | 甘油三硬质酸锌 | 混合 | 5.0 |
| 实施例4 | 椰子油脂肪酸甘油三酸酯 | 45.0 | 硬脂醇 | 45.0 | 维生素E | 5.0 | 甘油三硬质酸锌 | 表面附着 | 5.0 |
| 比较例1 | 椰子油脂肪酸甘油三酸酯 | 47.5 | 硬脂醇 | 47.5 | 维生素E | 5.0 | 无 | ||
| 比较例2 | 椰子油脂肪酸甘油三酸酯 | 50.0 | 硬脂醇 | 50.0 | 维生素E | 0.0 | 无 | ||
表2
| 尿布表面 | 婴儿臀部 | 油脂氧化臭味 | 油脂氧化 | 皮肤状态 | |
| 实施例1 | 等级4 | 等级3 | 无 | 无 | 无变化 |
| 实施例2 | 等级5 | 等级4 | 无 | 无 | 无变化 |
| 实施例3 | 等级4 | 等级3 | 无 | 无 | 无变化 |
| 实施例4 | 等级5 | 等级4 | 无 | 无 | 无变化 |
| 比较例1 | 等级1 | 等级1 | 无 | 无 | 无变化 |
| 比较例2 | 等级1 | 等级1 | 有 | 有 | 轻微斑疹 |
通过把本发明的吸收性物品防护剂涂敷在吸收性物品的表面上，即使长时间穿用吸收性物品，也不会产生发粘感，并且可以获得在皮肤上没有发现任何斑疹的效果。
Claims (10)
1.一种吸收性物品用防护剂，其特征在于：混合有改善触感的粉体或使该粉体附着在表面上。
2.如权利要求1所述的吸收性物品用防护剂，其特征在于：所述粉体是从天然无机粉体、合成无机粉体、有机粉体、金属肥皂、和合成高分子粉体中选出的一种以上粉体。
3.如权利要求1或2所述的吸收性物品用防护剂，其特征在于：含有油溶性防氧化剂。
4.如权利要求3所述的吸收性物品用防护剂，其特征在于：防氧化剂是从维生素A群、维生素B群、维生素D群、维生素E群以及维生素K群组成的维生素群中选择的一种以上的化合物。
5.如权利要求1-4中任意一项所述的吸收性物品用防护剂，其特征在于：含有柔润剂及/或固定剂。
6.如权利要求1-5中任意一项所述的吸收性物品用防护剂，其特征在于：柔润剂在25℃时为液体或半固体油性物质。
7.如权利要求6所述的吸收性物品用防护剂，其特征在于：柔润剂是甘油脂肪酸酯。
8.如权利要求1-7中任意一项所述的吸收性物品用防护剂，其特征在于：固定剂的融点是40℃～90℃，且在20℃时的表面张力为25-45dgn/cm。
9.如权利要求8所述的吸收性物品用防护剂，其特征在于：固定剂是从甘油脂肪酸酯、石蜡和高级醇中选择的一种以上的物质。
10.一种吸收性物品，其特征在于：在表面上涂有权利要求1-9中任一项所述的防护剂。