CN1340639A - 硅酸铝纺织物纤维 - Google Patents

硅酸铝纺织物纤维 Download PDF

Info

Publication number
CN1340639A
CN1340639A CN 00111347 CN00111347A CN1340639A CN 1340639 A CN1340639 A CN 1340639A CN 00111347 CN00111347 CN 00111347 CN 00111347 A CN00111347 A CN 00111347A CN 1340639 A CN1340639 A CN 1340639A
Authority
CN
China
Prior art keywords
parts
fabrics
raw material
aluminium silicate
zro
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 00111347
Other languages
English (en)
Other versions
CN1123658C (zh
Inventor
鹿成洪
鹿成会
齐元伟
王书义
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Luyang Energy Saving Materials Co Ltd
Original Assignee
Shandong Luyang Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Luyang Co Ltd filed Critical Shandong Luyang Co Ltd
Priority to CN 00111347 priority Critical patent/CN1123658C/zh
Publication of CN1340639A publication Critical patent/CN1340639A/zh
Application granted granted Critical
Publication of CN1123658C publication Critical patent/CN1123658C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

一种硅酸铝纺织物纤维,以二氧化硅、氧化铝为主的陶瓷组份为原料,经熔融、成纤制得玻璃态非晶体纤维,其组成中含氧化锆2～5份,氧化钙2～5份和氧化镁2～5份。它是使用温度可在1000℃以上,同时纺织性能优良的高温纺织纤维,适于作设备、管道隔热保温纤维纺织品的原材料。收得可纺纤维率70～75%,在1000℃的烧失量2%,在1000℃高温下,保温24小时的线收缩率3%,均优于现有技术。

Description

硅酸铝纺织物纤维
本发明属于耐火绝热材料，涉及一种硅酸铝纺织物纤维，它是使用温度可在1000℃以上，同时纺织性能优良的高温纺织纤维，适于作为设备、管道隔热保温纤维纺织品的原材料。
现有技术中，以石棉、岩棉、玻璃纤维棉或陶瓷纤维等散状纤维为主要原料，添加少量有机纤维，用以生产布、带等类型的隔热保温纤维纺织品。由于材质自身特性等因素的制约，它们存在各自的不足。例如，石棉类制品因其对作业人员的毒害已逐渐被淘汰；岩棉、玻璃纤维棉类制品，因其耐热性差(约为600℃)、柔软性差、强度低、纤维脆性大，不能作为耐温1000℃的高温纺织品用原材料；陶瓷纤维因其自身的脆性，在纺织加工过程中纤维可纺收得率低，一般在40～55％±，生产过程又必须添加较多的有机纤维，此举又限制了此类隔热保温纤维纺织品的适用范围仅为600～900℃。
综上所述，现有技术中缺乏既能耐温1000℃，又同时具备良好纺织性能的无机纤维。
本发明目的是提供一种使用温度可在1000℃以上，同时纺织性能优良的。
本发明一种硅酸铝纺织物纤维，包括二氧化硅、氧化铝为主要成分的陶瓷组份为原料，经熔融、成纤制得玻璃态非晶体纤维，其特征在于陶瓷组份中还含有氧化锆、氧化钙和氧化镁，其重量组为氧化锆2～5份，氧化钙2～5份和氧化镁2～5份。
其重量组成中含有二氧化硅40～60份；其重量组成中含有氧化铝30～50份。
本发明硅酸铝纺织物纤维与现有技术陶瓷纤维比较，优势明显：
1.投入同台设备进行纺织试验结果
   对比物    加入有机纤维量    收得可纺纤维率％    备    注
本发明纤维       3～5％           70～75％
陶瓷纤维         10～15％         40～55％      需要增加长丝纤维加强
2.烧失量
   对比物                      在1000℃的烧失量
本发明纤维纺织出的布                2％
陶瓷纤维纺织出的布                12～18％
3.纤维纺织品的加热线收缩
   对比物              在1000℃高温下，保温24小时的线收缩率
本发明纤维纺织品                  3％
陶瓷纤维纺织品                    6.5％
以下结合实施例对本发明作进一步阐述：
实施例一
原料重量组成：SiO2 40份，Al2O3 50份，MgO 5份，CaO 2.5份，ZrO2 2份。
工艺过程  配量原料过筛混合，在电阻炉中1800～2000℃熔融成液态，利用喷吹法或甩丝法进行纤维生产。本发明硅酸铝纺织物纤维，产品具有丝一般光泽，柔软性好，纤维长度一般大于30mm，且渣球等未纤维化物少，强度大，用本发明纤维生产纺织品时，在受剪切、拉伸、弯曲等复杂应力的作用下，梳棉、粗纺等生产工序中，纤维切断极少，提高纤维可纺率，生产出高强度纱条。加入有机纤维量3～5％，收得可纺纤维率％70～75％；本发明纤维纺织出的布，在1000℃的烧失量为2％±；本发明纤维纺织品在1000℃高温下，保温24小时的线收缩率为3％±。
实施例二  原料重量组成：SiO2 45份，Al2O3 45份，MgO 4.5份，CaO 3份，ZrO2 2.5份。其余同例一。
实施例三  原料重量组成：SiO2 50份，Al2O3 48份，MgO 4份，CaO 3.5份，ZrO2 3份。其余同例一。
实施例四  原料重量组成：SiO2 53份，Al2O3 40份，MgO 3.5份，CaO 4份，ZrO2 3.5份。其余同例一。
实施例五  原料重量组成：SiO2 55份，Al2O3 38份，MgO 3份，CaO 4.5份，ZrO2 4份。其余同例一。
实施例六  原料重量组成：SiO2 57份，Al2O3 32份，MgO 2.5份，CaO 5份，ZrO2 4.5份。其余同例一。
实施例七  原料重量组成：SiO2 60份，Al2O3 30份，MgO 2份，CaO 2份，ZrO2 5份。其余同例一。
实施例八  原料重量组成：SiO2 48份，Al2O3 36份，MgO 2份，CaO 2.5份，ZrO2 4份。其余同例一。
实施例九  原料重量组成：SiO2 50份，Al2O3 34份，MgO 2份，CaO 3份，ZrO2 4.5份。其余同例一。
实施例十  原料重量组成：SiO2 55份，Al2O3 42份，MgO 2份，CaO 3.5份，ZrO23.5份。其余同例一。
实施例十一  原料重量组成：SiO2 40份，Al2O3 30份，MgO 3.7份，CaO 2.7份，ZrO2 5份。其余同例一。
实施例十二  原料重量组成：SiO2 42份，Al2O3 50份，MgO 2份，CaO 2.8份，ZrO24.5份。其余同例一。
实施例十三  原料重量组成：SiO2 47份，Al2O3 33份，MgO 2份，CaO 3.9份，ZrO23份。其余同例一。
实施例十四  原料重量组成：SiO2 58份，Al2O3 35份，MgO 2.2份，CaO 5份，ZrO22.5份。其余同例一。
实施例十五  原料重量组成：SiO2 43份，Al2O3 37份，MgO 2份，CaO 3.3份，ZrO24份。其余同例一。
实施例十六  原料重量组成：SiO2 46份，Al2O3 41份，MgO 4.1份，CaO 2份，ZrO23.5份。其余同例一。
实施例十七  原料重量组成：SiO2 52份，Al2O3 43份，MgO 2.6份，CaO .5份，ZrO2 2份。其余同例一。
实施例十八  原料重量组成：SiO2 53份，Al2O3 47份，MgO 2份，CaO 2.9份，ZrO2 5份。其余同例一。
实施例十九  原料重量组成：SiO2 60份，Al2O3 49份，MgO 5份，CaO 3份，ZrO24.3份。其余同例一。

Claims (3)

1.一种硅酸铝纺织物纤维，包括二氧化硅、氧化铝为主要成分的陶瓷组份为原料，经熔融、成纤制得玻璃态非晶体纤维，其特征在于陶瓷组份中还含有氧化锆、氧化钙和氧化镁，其重量组为氧化锆2～5份，氧化钙2～5份和氧化镁2～5份。
2.一种按照权利要求1所述的硅酸铝纺织物纤维，其特征在于其重量组成中含有二氧化硅40～60份。
3.一种按照权利要求1所述的硅酸铝纺织物纤维，其特征在于其重量组成中含有氧化铝30～50份。
CN 00111347 2000-09-01 2000-09-01 硅酸铝纺织物纤维 Expired - Lifetime CN1123658C (zh)