CN1293527C - 彩色荧光蓄光发光有机板的制作方法 - Google Patents
彩色荧光蓄光发光有机板的制作方法 Download PDFInfo
- Publication number
- CN1293527C CN1293527C CNB2004100518661A CN200410051866A CN1293527C CN 1293527 C CN1293527 C CN 1293527C CN B2004100518661 A CNB2004100518661 A CN B2004100518661A CN 200410051866 A CN200410051866 A CN 200410051866A CN 1293527 C CN1293527 C CN 1293527C
- Authority
- CN
- China
- Prior art keywords
- organic
- light
- fluorescence
- accumulated luminous
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种彩色荧光蓄光发光有机板的制作方法，包括以下步骤：(一)制备含有蓄光发光粉的荧光溶剂；(二)制备有机板液；(三)制备有机荧光蓄光发光液；(四)喷涂有机荧光蓄光发光液；(五)自然风干或加热到30～70℃热风干即可。经过前述处理后可再增加喷涂一层有机板液的防护层。本发明的有机板的颜色主要由荧光粉的颜色决定，也可加入透明色浆调色。该有机板具有荧光和黑夜发光功能，该制作方法提高了荧光粉等与有机板的结合度，成本低容易推广。
Description
所属技术领域
本发明涉及一种彩色荧光蓄光发光有机板的制作方法。
背景技术
目前装饰用有机板本身不会发光，在黑夜或光线暗时，其上色彩、图画或字就看不见，需要使用灯光才能看见。在指示牌、烛光酒吧、舞厅、城市标志建筑等场合，需要一种同时具有荧光作用和在黑暗中有发光效果的有机板材产品来装饰指示牌或墙体壁画，进一步增强指示效果或视觉效果，满足人们夜生活的美化要求，也可达到节能效果。
发明内容
本发明要解决的技术问题是提供一种荧光蓄光发光有机板的制作方法，该方法简单实用，使荧光粉和蓄光发光粉充分牢固结合在有机板的涂层中，还具备进一步提高彩色荧光蓄光发光有机板在白天时的色泽度功能。
本发明为解决技术问题所采用的技术方案是：彩色荧光蓄光发光有机板的制作方法，包括以下步骤：
(一)制备含有蓄光发光粉的荧光溶剂：在盛有天那水的密闭容器中，加入重量为天那水重量的20~40％的彩色荧光粉，充分搅拌24小时以上，然后静置分层，去除沉淀物，得到上层液体状的荧光溶剂；在荧光溶剂中加入重量为天那水重量的20~40％颗粒度为200目以上的蓄光发光粉后，搅拌均匀，得到含有蓄光发光粉的荧光溶剂；
(二)制备有机板液：把有机板溶入含有甲苯、二甲苯或苯的溶解液中充分搅拌，有机板加入量为溶解液重量的10~20％，得到有机板液；
(三)制备有机荧光蓄光发光液：在密闭容器中把前述制备的含有蓄光发光粉的荧光溶剂和有机板液按重量比为含有蓄光发光粉的荧光溶剂∶有机板液＝1∶0.4~0.6的比例混合，搅拌均匀，得到有机荧光蓄光发光液；
(四)喷涂有机荧光蓄光发光液：在有机板表面上喷涂已经制备好的有机荧光蓄光发光液，分2~3次喷涂，待前一次喷涂液干燥到50~60％时才进行后一次喷涂；
(五)风干：把前一步喷涂好有机荧光蓄光发光液的有机板进行自然风干或加热到30~70℃热风干，得到彩色荧光蓄光发光有机板。
作为改进，前述的彩色荧光蓄光发光有机板的制作方法，增加一个步骤：最后在所述的有机荧光蓄光发光层上再涂有一层透明的有机液形成防护层。
本发明所得到的彩色蓄光发光板的具体颜色主要由荧光粉的颜色决定，如采用单一红色荧光粉最后得到高亮度红色蓄光发光有机板，如采用两种基本颜色或三种红、黄、绿基本颜色按不同份量荧光粉调制不同颜色的明亮彩色蓄光发光有机板。
为进一步提高产品的色泽度，前述的彩色荧光蓄光发光有机板的制作方法，在所述第(一)步所制备的含有蓄光发光粉的荧光溶剂中，还可加入与荧光粉颜色相近的色浆，色浆加入量为重量比0.1~2％。色浆的颜色根据需要选择，如在选用褐色蓄光发光粉时加入FS-01色浆，可得到高亮度红色荧光蓄光发光有机板；如加入FS-03色浆，可得到明亮红色荧光蓄光发光有机板；如在选用褐色蓄光发光粉时加入FS-03色浆，可得到高亮度橙色荧光蓄光发光有机板；如在选用淡黄色蓄光发光粉时加入重量比为0.1％FS-03色浆和1.9％的28号黄色浆，可得到高亮度黄色荧光蓄光发光有机板。
作为改进，前述的彩色荧光蓄光发光有机板的制作方法，在前述第(一)步过程搅拌时，同时加入天那水重量3~6％的闪光粉。
本发明所使用的蓄光发光粉为“流星雨”牌某种颜色的蓄光发光粉，如红色，绿色，黄绿色的蓄光发光粉。
由于采用了天那水对荧光粉和蓄光发光粉进行了溶解结合，既改善了荧光粉和蓄光发光粉中不容易与油漆或有机颗粒结合的缺点，又清除了杂质等沉淀物，提高了荧光粉和蓄光发光粉的纯度。
本发明的有益效果是：在有机板表面上增加一层有机荧光蓄光发光层，使荧光粉和蓄光发光粉充分结合在涂层中，使有机板具有荧光和黑夜发光功能，提高夜间视觉效果，节省能源。在涂层中加入色浆，进一步提高了荧光蓄光发光粉在白天时的色泽度。由于采用天那水和有机板液作为溶剂结合荧光粉和蓄光发光粉，进一步提高了该粉与有机板的结合度。本发明所公开的制作方法，简单可靠，成本低容易推广。
具体实施方式
以下通过实施例对本发明作进一步说明，但实施例不用来限制本发明的范围。
实施例1：一种红色荧光蓄光发光有机板，以有机板为基础，在所述的有机板表面上增加一层有机荧光蓄光发光层，该有机荧光蓄光发光层含有20％的荧光粉和20％的蓄光发光粉。
该红色荧光蓄光发光有机板的制作方法，在普通木板材的表面上，进行以下步骤处理：
下面是该彩色荧光蓄光发光有机板的制作方法。在有机板的表面上，进行以下步骤处理：
(一)制备含有蓄光发光粉的荧光溶剂：在盛有1000ml天那水的密闭容器中，加入重量为350g的彩色荧光粉，充分搅拌36小时，然后静置分层，去除沉淀物，得到上层液体状的荧光溶剂；在荧光溶剂中加入重量为400g颗粒度为200目以上的蓄光发光粉后，搅拌均匀，得到含有蓄光发光粉的荧光溶剂；
(二)制备有机板液：把有机板溶入含有500ml二甲苯的天那水中充分搅拌，有机板加入量为50g，得到有机板液；
(三)制备有机荧光蓄光发光液：在密闭容器中把前述制备的含有蓄光发光粉的荧光溶剂和有机板液按重量比为含有蓄光发光粉的荧光溶剂∶有机板液＝1∶0.6的比例混合，搅拌均匀，得到有机荧光蓄光发光液；
(四)喷涂有机荧光蓄光发光液；在其表面上喷涂已经制备好的有机荧光蓄光发光液，分2次喷涂，待前一次喷涂液干燥到50~60％时才进行后一次喷涂；
(五)风干：把前一步喷涂好的有机荧光蓄光发光液的基础板进行自然风干或加热到30~70℃热风干，得到彩色荧光蓄光发光有机板。
该高亮度红色彩色荧光蓄光发光有机板在白天为明亮红色，经过日照或20分钟强光照射后在黑夜会呈现红色光泽，特别适合做无灯光的广告板。
实施例2：在实施例1得到的红色彩色荧光蓄光发光有机板基础上，还有一层0.15毫米厚的透明的有机层。制作方法基本上与实施例1相同，不同的是在风干后再涂上一层0.15毫米厚的无色透明的有机液，再经过自然风干。
Claims (4)
1、彩色荧光蓄光发光有机板的制作方法，其特征是：包括以下步骤：
(一)制备含有蓄光发光粉的荧光溶剂：在盛有天那水的密闭容器中，加入重量为天那水重量的20~40％的彩色荧光粉，充分搅拌24小时以上，然后静置分层，去除沉淀物，得到上层液体状的荧光溶剂；在荧光溶剂中加入重量为天那水重量的20~40％颗粒度为200目以上的蓄光发光粉后，搅拌均匀，得到含有蓄光发光粉的荧光溶剂；
(二)制备有机板液：把有机板溶入含有甲苯、二甲苯或苯的溶解液中充分搅拌，有机板加入量为溶解液重量的10~20％，得到有机板液；
(三)制备有机荧光蓄光发光液：在密闭容器中把前述制备的含有蓄光发光粉的荧光溶剂和有机板液按重量比为含有蓄光发光粉的荧光溶剂∶有机板液＝1∶0.4~0.6的比例混合，搅拌均匀，得到有机荧光蓄光发光液；
(四)喷涂有机荧光蓄光发光液：在有机板表面上喷涂已经制备好的有机荧光蓄光发光液，分2~3次喷涂，待前一次喷涂液干燥到50~60％时才进行后一次喷涂；
(五)风干：把前一步喷涂好有机荧光蓄光发光液的有机板进行自然风干或加热到30~70℃热风干，得到彩色荧光蓄光发光有机板。
2、如权利要求1所述的彩色荧光蓄光发光有机板的制作方法，其特征是：最后在所述的有机荧光蓄光发光层上再涂有一层透明的有机液形成防护层。
3、如权利要求1所述的彩色荧光蓄光发光有机板的制作方法，其特征是：在所述第(一)步所制备的含有蓄光发光粉的荧光溶剂中，还加入与荧光粉颜色相近的色浆，色浆加入量为重量比0.1~2％。
4、如权利要求1所述的彩色荧光蓄光发光有机板的制作方法，其特征是：在前述第(一)步过程搅拌时，同时加入闪光粉。