CN1288085A - 不锈钢板耐热垫纸及其生产方法 - Google Patents

不锈钢板耐热垫纸及其生产方法 Download PDF

Info

Publication number
CN1288085A
CN1288085A CN 99113362 CN99113362A CN1288085A CN 1288085 A CN1288085 A CN 1288085A CN 99113362 CN99113362 CN 99113362 CN 99113362 A CN99113362 A CN 99113362A CN 1288085 A CN1288085 A CN 1288085A
Authority
CN
China
Prior art keywords
paper
heat
stainless steel
proof modifier
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 99113362
Other languages
English (en)
Other versions
CN1091822C (zh
Inventor
刘洪文
丁国桢
季纯才
白芳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenyang Rustproof Packaging Material Co., Ltd.
Original Assignee
SHENYANG RUST-PROOF AND PACKAGE MATERIALS CORP
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHENYANG RUST-PROOF AND PACKAGE MATERIALS CORP filed Critical SHENYANG RUST-PROOF AND PACKAGE MATERIALS CORP
Priority to CN99113362A priority Critical patent/CN1091822C/zh
Publication of CN1288085A publication Critical patent/CN1288085A/zh
Application granted granted Critical
Publication of CN1091822C publication Critical patent/CN1091822C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种不锈钢耐热垫纸及其生产方法,是以本色的或漂白的中性化学木浆为原料,经打浆、净化、筛选、抄纸,其特征在于:在抄纸机烘干部的表面施胶或抄成纸后利用涂布机施加耐热改性剂,耐热改性剂的成分包括双氰胺、醇胺、聚乙烯醇、硅油乳液、抗静电剂及水。其配制的方法是:将聚乙稀醇溶于水中,加温至30—95℃搅拌溶解后投入双氰胺继续搅拌进一步溶解,然后加入三乙醇胺、抗静电剂、硅油乳液搅拌均匀。使用时,垫纸呈卷曲形式垫于不锈钢板间,以防止板面划伤。该产品强度高、韧性好、可重复使用。

Description

不锈钢板耐热垫纸及其生产方法
本发明涉及一种不锈钢板耐热垫纸，是在不锈钢板轧制过程中呈卷取形式垫于不锈钢板面间，防止板面摩擦划伤，保护不锈钢板面光洁的防护性纸张。
过去曾采用中性牛皮纸作垫纸，但由于不锈钢板在轧制过程中，大量的机械能转化为热能，致使板面温度高达160-180℃。在此高温下构成纸张的纤维素分子将严重脱水、氧化、断链降解。高温氧化时纤维索分子中的醇羟基转化成醛基、羧基促使纤维素分子进一步遭受破坏。纤维素分子的破坏使得纸张失去强度而破碎，不仅不能重复使用，甚至连一次使用也通不过，其碎片粘附在不锈钢表面难以取下。为了改进牛皮纸的耐热性能，多年前曾探索对造纸用纸浆以丙烯腈处理，制成氰乙基纤维索后再抄纸。抄成的纸虽可耐高温，但其未经高温前的基础强度却低于牛皮纸，同时工艺复杂、难以用于工业化生产。近年来，一般地都是采用抄成纸张后向纸张施加三聚氢胺、聚丙烯酰胺、双氰胺等耐热改性剂以求改善不锈钢垫纸的耐热性能。上述耐热改性剂都有一定的耐热效果，但都有其不足之处，主要表现在受热之后，纸质发脆而韧性不好，重复使用性差。
本发明的目的是提供一种耐热性能好，而且受热后仍能保持一定韧性，能多次重复使用的不锈钢板耐热垫纸及其生产方法。
为实现上述目的，本发明采用了如下的技术方案：以本色的或漂白的中性化学木浆为原料，经打浆、净化、筛选、抄纸。在抄纸机烘干部的表面施胶或抄成纸后利用涂布机，施加耐热改性剂。耐热改性剂的主要成分为醇胺与双氰胺。两者的比例为1∶0.5-1∶10(重量份额，以醇胺为1份)两者合计占耐热改性剂总量的40-80％。两者并用的目的是不仅提高耐热压后抗张，撕裂等静态强度，更主要的是提高热压后的动态强度，亦即改善纸张的韧性。在耐热改性剂中添加10-40％聚乙烯醇、变性淀粉类纸张表面增强剂：添加6-15％的石蜡或硅油类乳状液。目的是提高垫纸的表面强度和滑腻性，防止垫纸粘污不锈钢板。在耐热改性剂配方中添加2-10％纸张用的阴离子或非离子抗静电剂，防止不锈钢板与垫纸间产生静电吸引，致使垫纸收卷时与不锈钢板不易脱离。以上的百分比均为重量百分比。
下面将结合具体实施例及附图对本发明作详细的说明。
实施例一：
按重量百分比取双氰胺(DCYDA)    54％
三乙醇胺(TEA)                   6％
聚乙稀醇(PVA)                  28％
硅油乳液(DMPS)                  8％
抗静电剂P                       4％
水                           2900克
用量：固形物对纸0.8％-1.2％施加量。改性剂的浓度依垫纸的吸附量而定，两者之间成反比。
具体的配制方法：将聚乙稀醇28克溶于水2900克，加温至30-95℃搅拌溶解后投入54克的双氰胺继续搅拌进一步溶解，然后加入三乙醇胺6克、抗静电剂4克、硅油乳液8克搅拌均匀。
实施例二：
按重量百分比取双氰胺(DCYDA)    50％
三乙醇胺(TEA)                  10％
聚乙稀醇(PVA)                  30％
硅油乳液(DMPS)                  5％
抗静电剂P                       5％
水                           3000克
其配制方法与实施例一相同。
本发明的使用状态及生产方法由以下的附图给出。
图1为不锈钢板耐热垫纸的使用状态示意图。
图2为不锈钢板耐热垫纸施加改性剂的方法示意图。
参照图1、当不锈钢板2在进入轧制机3前，垫纸1收卷；不锈钢板2经轧制机3轧制后，垫纸4放卷并垫入不锈钢板2之间，以防止板面摩擦划伤，保护不锈钢板面的光洁。
参照图2、原纸5绕弹簧辊8，经施胶辊6后吸附按实施例一、实施例2所制得的改性剂溶液7。
不锈钢板耐热垫纸检测结果及耐热改性效果的评价。
热压条件：    温度    180℃
              压强    5MPa
              时间    3hr
测试条件：    温度     20℃
              湿度       65％RH
耐热改性效果以垫纸经热压后的抗张能量吸收(T、E、A)的保留率％来衡量。
R=P/P    R：热压后保留率
         P：热压前TEA
         P：热压后TEA
检测结果与评价：
NO1 NO2 NO3
热压后撕裂度保留％ 38 56 61
热压后抗张能量吸收保留％T、E、A 40 68 84
NO 1：未施加耐热改性
NO 2：DCYDA单独使用
NO 3：TEA与DCYDA并用
本发明的特点在于：1、不锈钢板耐热垫纸是以中性化学木浆为原料抄制的。在抄制过程中或成纸后采用表面施胶或涂布方式向纸张施加耐热改性剂。2、用上述方法制得的不锈钢板耐热垫纸具有耐160-180℃高温的特殊功能，在不锈钢板轧制过程中可以重复使用多次。3、耐热改性剂的组成，是以醇胺与双氰胺并用为特点，两者对改善垫纸的耐热性能有相辅相成、优势互补的协同效应。4、耐热改性剂中含有表面增强、增进滑腻性、抗静电等助剂，此配方不仅可使不锈钢板垫纸耐高温，而且还可保护不锈钢板面光洁，有利于轧制与精整的工艺操作。5、采用热压后不锈钢板垫纸的抗张能量吸收(T、E、A)用保留率的高低来评价不锈钢板垫纸耐热性能的优劣。由于引进了醇胺，而使不锈钢耐热垫纸的耐热性能有了大幅度的提高，尤其是受热后伸长率的增加，垫纸仍保持一定韧性，克服了现有技术中不锈钢耐热垫纸在高温下易变脆，重复使用次数少的缺点，本发明可重复使用多次，降低了生产成本，提高了生产效率。

Claims (3)

1、一种不锈钢板耐热垫纸及其生产方法，是以本色的或漂白的中性化学木浆为原料，经打浆、净化、筛选、抄纸，其特征在于：在抄纸机烘干部的表面施胶或抄成纸后利用涂布机，施加耐热改性剂，耐热改性剂的成分包括双氰胺、醇胺、聚乙烯醇、硅油乳液、抗静电剂及水。
2、根据权利要求1所述的不锈钢耐热垫纸及其生产方法，其特征在于：所说的耐热改性剂中的醇胺与双氰胺两者的重量比为1∶0.5-1∶10，两者合计占耐热改性剂总量的40-80％；在耐热改性剂中添加10-40％聚乙烯醇、变性淀粉类纸张表面增强剂；添加6-15％的石蜡或硅油类乳状液；添加2-10％纸张用的阴离子或非离子抗静电剂，其配制的方法是：将聚乙稀醇溶于水中，加温至30-95℃搅拌溶解后投入双氰胺继续搅拌进一步溶解，然后加入三乙醇胺、抗静电剂、硅油乳液搅拌均匀，以上百分比均为重量百分比。
3、根据权利要求1、2所述的不锈钢耐热垫纸及其生产方法，其特征在于：所说的醇胺为三乙醇胺。
CN99113362A 1999-09-09 1999-10-22 不锈钢板耐热垫纸及其生产方法 Expired - Fee Related CN1091822C (zh)