CN1279119C - 一种阻燃增强塑料及其生产工艺 - Google Patents

一种阻燃增强塑料及其生产工艺 Download PDF

Info

Publication number
CN1279119C
CN1279119C CN 200410101480 CN200410101480A CN1279119C CN 1279119 C CN1279119 C CN 1279119C CN 200410101480 CN200410101480 CN 200410101480 CN 200410101480 A CN200410101480 A CN 200410101480A CN 1279119 C CN1279119 C CN 1279119C
Authority
CN
China
Prior art keywords
flame
retardant
production process
fire
reinforced plastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 200410101480
Other languages
English (en)
Other versions
CN1631979A (zh
Inventor
陈锡伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wenzhou Xinli Plastic Co., Ltd.
Original Assignee
WENZHOU XINLI MACHINERY AND PLASTIC CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WENZHOU XINLI MACHINERY AND PLASTIC CO Ltd filed Critical WENZHOU XINLI MACHINERY AND PLASTIC CO Ltd
Priority to CN 200410101480 priority Critical patent/CN1279119C/zh
Publication of CN1631979A publication Critical patent/CN1631979A/zh
Application granted granted Critical
Publication of CN1279119C publication Critical patent/CN1279119C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种阻燃增强塑料及其生产工艺，其特征是它主要由下列重量比的原料配制而成：38～46%的聚己酰己二胺聚合物、30～38%的玻璃纤维、12～18%的阻燃剂、0.3～0.6%的抗氧剂、1.5～2%的增韧剂、0.4～0.6%的润滑剂、4～6%的三氧化二锑。按照该配方制成的塑料，阻燃性能好，耐高温，热变形尺寸稳定，具有优良的刚性和耐蠕变性，拉伸、弯曲强度高，滑动性能好，广泛应用于汽车、电子以及电气行业。

Description

一种阻燃增强塑料及其生产工艺
【技术领域】
本发明涉及的是一种塑料，特别涉及的是一种应用于汽车、电子及电气行业等行业的塑料，同时涉及该塑料的生产工艺。
【背景技术】
目前，用于汽车、电子及电气行业的塑料品种很多，最常用的是聚丙烯或者聚乙烯，这些塑料产品，其阻燃性能和耐高温性较差，热变形尺寸不稳定，其刚性和耐蠕变性能也较差，拉伸、弯曲强度低，硬度和熔点低，而且抗腐蚀和耐磨性也有局限性。这就给在汽车、电子及电气行业的应用带来较大的局限性。
【发明内容】
鉴于现有技术存在的问题，本发明要解决的技术问题是提供一种阻燃性能好、耐高温、热变形尺寸稳定、熔点高的阻燃增强塑料。为了达到上述目的，本发明是采取如下方案完成的：该阻燃增强塑料，主要由下列原料配制而成：聚己酰己二胺聚合物、玻璃纤维、阻燃剂、抗氧剂、增韧剂、润滑剂以及三氧化二锑。
本发明原料的配比是经过发明人大量的摸索和试验得出的，各组分用量在下述重量比范围都有良好效果，聚己酰己二胺聚合物：38～46％、玻璃纤维：30～38％、阻燃剂：12～18％、抗氧剂：0.3～0.6％、增韧剂：1.5～2％、润滑剂：0.52％、三氧化二锑4.4％。
优选为：聚己酰己二胺聚合物：41.78％、玻璃纤维：35％、阻燃剂：16％、抗氧剂：0.5％、增韧剂：1.8％、润滑剂：0.52％、三氧化二锑：4.4％。
上述配料中，所述阻燃剂为十溴二苯乙烷。
本发明是采用如下生产工艺制成的：将各原料进行混合，搅拌25～40分钟，均匀后在挤出机中分段加热至220～272℃挤成条状，最后经过冷却、切粒而成。
按照上述配方的重量配比和生产工艺制成的阻燃增强塑料，其阻燃性能好，耐高温，热变形尺寸稳定，具有优良的刚性和耐蠕变性，拉伸、弯曲强度高，硬度高，抗腐蚀而且耐磨性好，熔点高，结晶速度快，滑动性能好。
【具体实施方式】
下面再通过实施例来详细说明本发明的实施过程。
本发明在生产时，将41.78％的聚己酰己二胺聚合物、35％无碱无捻的玻璃纤维、16％的十溴二苯乙烷、0.5％的抗氧剂、1.8％的增韧剂、0.52％的润滑剂、4.4％的Sb2O3，充分搅拌25～40分钟，均匀后在挤出机中分段加热挤出条状，最后经过水槽和冷空气的冷却，并通过切粒机切粒后就成为阻燃增强塑料产品。本发明的聚己酰己二胺聚合物由己二胺与己二酸经过聚合反应而成，其聚合反应方程式为：
，
所述增韧剂的型号为EPDEY-g，润滑剂的型号为TAF，均为市场上的公知配料，所述抗氧剂的型号为168或者1098。本发明的关键在于配方的配比；聚己酰己二胺聚合的分子量越大，效果更佳；在上述中，挤出机为常用的双螺杆挤出机，该双螺杆挤出机是分段连接的，上述的配方在双螺杆挤出机内需要较高的温度，它是这样分段加热的：在挤出机的机头将温度加热至270℃，在挤出机的第二段即与机头连接的段加热至220～235℃，第三段加热到260℃，在随后的各段中加热到260～272℃。在生产的过程中，物料在挤出机的料筒中的停留时间不能超过8分钟，否则会使物料碳化焦燃，本发明还可以根据用户的需要在配料中加入色素，使生产出来的塑料具有各种色彩，经过上述配方和生产工艺得到的塑料产品，经过测验，其理化指标如下：熔点≥260±2℃，拉伸强度≥150Mpa，维卡软化点≥240℃，拉伸段裂伸长率≥2％，弯曲强度≥200Mpa，悬臂梁缺口冲击强度(6.35mm)≥10KJ/m2(23℃)；≥3.5KJ/m2(-40℃)，燃烧性：UL94 V-0，体积电阻率≥1012Ω.m，击穿电压≥20MV/m，耐电弧性≥40S，弯曲弹性模量≥7200Mpa，密度为1.65±0.03g/cm3，洛氏硬度(R)≥120，灰分35±1％。本发明的产品还可以通过注射成型方法能制得薄制品或微型结构件。其综合指标都具有很好的性能，广泛应用汽车、电子以及电气行业。

Claims (6)

1、一种阻燃增强塑料，其特征在于它主要由下列重量比的原料配制而成：38～46％的聚己酰己二胺聚合物、30～38％的玻璃纤维、12～18％的阻燃剂、0.3～0.6％的抗氧剂、1.5～2％的增韧剂、0.4～0.6％的润滑剂、4～6％的三氧化二锑。
2、根据权利要求1所述的阻燃增强塑料，其特征在于它主要由下列重量比的原料配制而成：41.78％的聚己酰己二胺聚合物、35％的玻璃纤维、16％的阻燃剂、0.5％的抗氧剂、1.8％的增韧剂、0.52％的润滑剂、4.4％的三氧化二锑。
3、根据权利要求1或2所述的阻燃增强塑料，其特征在于所述阻燃剂为十溴二苯乙烷。
4、一种按权利要求1或2所述塑料的生产工艺，其特征在于是将各原料进行混合，搅拌均匀后在挤出机中分段加热挤成条状，最后经过冷却、切粒而成。
5、根据权利要求4所述的阻燃增强塑料的生产工艺，其特征在于加热的温度为220～272℃。
6、根据权利要求4所述的阻燃增强塑料的生产工艺，其特征在于搅拌时间为25～40分钟。
CN 200410101480 2004-12-21 2004-12-21 一种阻燃增强塑料及其生产工艺 Expired - Fee Related CN1279119C (zh)