CN1243148C - 甲壳素整理织物的制造方法 - Google Patents
甲壳素整理织物的制造方法 Download PDFInfo
- Publication number
- CN1243148C CN1243148C CN200310108037.8A CN200310108037A CN1243148C CN 1243148 C CN1243148 C CN 1243148C CN 200310108037 A CN200310108037 A CN 200310108037A CN 1243148 C CN1243148 C CN 1243148C
- Authority
- CN
- China
- Prior art keywords
- chitin
- water
- fabric
- dressing liquid
- soluble chitosan
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种甲壳素整理织物的制造方法,是通过采用织物后整理的方法,以以下技术方案来实现的:以分子量为5000,脱乙酰度大于90%的甲壳素,在常温下按比例1-5%溶于水中,时间6-12小时,得到该溶液,再在其中加入粘合剂等,配制成甲壳素整理剂,将上述整理剂置于轧槽中,对织物进行浸轧,再经过脱液、烘干、定型而制成。其整理织物具有良好的抑菌,防臭,吸湿透气等功能。
Description
一、技术领域
本发明涉及一种具有抑菌防臭,吸湿透气的混纺材料及其制造方法,特别是公开一种甲壳素整理织物的制造方法,
二、背景技术
随着人们对纺织品要求的提高,既具有抑菌,吸湿透气,凉爽舒适,保健的多功能纺织品倍受其关注和青睐。
甲壳素(Chitin)又名甲壳质、壳多糖、壳蛋白,是从海洋的虾、蟹贝壳中提取并纯化,是一种带正电荷的天然含氮多糖聚合物,再通过化工加工纺丝制成甲壳素纤维,其本身带有正电荷,可与带有负电荷的细菌等到微生物电荷中和,从而使细菌活动受到抑制失去活性,达到抑菌防臭、止氧及很好的吸湿、透湿作用。在纺织领域,甲壳素可经过纺纱成为纤维;用其制作的衣物具有吸水性、扩散性、抗菌性等功能。甲壳素还个有增色和固色的作用,可作为直接染料和硫化染料的固色剂,提高染料对织物的染色效果,改善色度,提高色牢度。但由于甲壳素纤维的可纺性较差,且价格昂贵,尚无法满足大众化的需求。近年来,随着甲壳素织物受到人们的重视,为了克服现有技术的缺陷,人们开始采用后整理的方法,将甲壳素结合在纺织品上,以起到预期的效果,如ZL02110608、ZL97125207、EP8931064、USP5、114、788、特开平9-31847等专利所揭示。但是所述前案多是在用有机酸的条件下来溶解甲壳素的工艺,使工艺流程变得复杂化,成本增加,对后续工艺及环境保护都有负面影响。
三、发明内容
本发明的目的在于克服现有技术的缺陷,提出一种具有抑菌防臭,吸湿透气的甲壳素整理织物的制造方法。
本发明的目的是通过采用织物后整理的方法,以下述技术方案来实现:先配制整理液(剂),整理液是以分子量为5000,脱乙酰度大于90%的甲壳素,在常温下按比例1-5%溶于水中,时间6-12小时,得到甲壳素水溶液,再在其中加入无甲醛粘合剂、亲水性柔软剂、渗透剂,再加水至总量(即总量为100%),配制成甲壳素整理剂(液)。具体是整理剂(液)是由重量百分计的:
水溶性甲壳素(脱乙酰度大于90%) 1-5%
无甲醛粘合剂 20-30%
亲水性柔软剂 1-4%
渗透剂 1-3%
水 适量,即余量为水配制而成
将上述整理液置于轧槽中,对织物进行浸渍或浸轧,再经过脱液、烘干、定型而制成。
本发明所公开的甲壳素整理织物及其制造方法的优点表现在于:
1、通过整理将甲壳素固着在织物上,与纤维产生永久性的结合,织物经过水洗后,抑菌性能仍在80%以上,且吸湿透气,凉爽舒适。
2、适用于机织、针织产品和无纺布产品;且所述的纺织品还可进行其他功能性整理,得到更加理想的效果。
3、用途广泛,可用于针织、机织等多种保健纺织品,如内衣、T恤、手套、帽子等。功效长、耐洗性好,对人体无刺激,无静电作用。
四、具体实施方式(实施例)
本甲壳素整理织物及其制造方法可通过以下实施例得以进一步具体的说明。
实施例1:
甲壳素整理剂(液)的配方:
水溶性甲壳素(脱乙酰度大于90%) 2%
无甲醛粘合剂 20%
亲水性柔软剂 4%
渗透剂 3%
水 适量,即余量为水制成
工艺流程:
浸渍法:按织物重的1-3%甲壳素配制整理液(20/L);控制水温30-40℃,加入轧槽内浸透,再脱液(脱液率75%),烘干(90-100℃)。
实施例2
按下述配方配制整理剂(液)。
水溶性甲壳素(脱乙酰度大于90%) 5%
无甲醛粘合剂 30%
亲水性柔软剂 4%
渗透剂 3%
水 适量,即余量为水制成
工艺流程:
浸轧法:按织物重的1-3%甲壳素配制整理液(20/L);控制水温30-40℃,加入到轧槽内浸透,轧液(轧液率70-75%),焙烘固着(<165℃)。
Claims (3)
1、一种甲壳素整理织物的制造方法,是在织物上通过整理方法固着有甲壳素,其特征在于是,配制整理液,整理液是由以重量百分计的:
脱乙酰度>90%的水溶性甲壳素1-5%
无甲醛粘合剂 20-30%
亲水性柔软剂 1-4%
渗透剂 1-3%和余量为水制成,首先是把水溶性甲壳素加入水中,在常温下溶解6-12小时,再加入无甲醛粘合剂、亲水性柔软剂和渗透剂,再加水至总量,将上述整理液置于轧槽中,在30-40℃的水温下,将织物加入到轧槽整理液内浸透,再轧至轧液率为70-75%,在<165℃焙烘固着。
2、根据权利要求1所述的一种甲壳素整理织物的制造方法,其特征在于是,配制整理液,整理液是由以重量百分计的:
脱乙酰度>90%的水溶性甲壳素1-5%
无甲醛粘合剂 20-30%
亲水性柔软剂 1-4%
渗透剂 1-3%和余量为水制成,首先是把水溶性甲壳素加入水中,在常温下溶解6-12小时,再加入无甲醛粘合剂、亲水性柔软剂和渗透剂,再加水至总量,将上述整理液置于轧槽中,在水温30-40℃下,将织物加入到轧槽整理液内浸透,再脱液至脱液率为75%,在90-100℃下烘干。
3、根据权利要求1或2所述的一种甲壳素整理织物的制造方法,其特征在于是,所说的水溶性甲壳素是分子量为5000,脱乙酰度大于90%的水溶性甲壳素。