CN1239752C - 电铸镍钴合金的方法 - Google Patents

电铸镍钴合金的方法 Download PDF

Info

Publication number
CN1239752C
CN1239752C CN 03110817 CN03110817A CN1239752C CN 1239752 C CN1239752 C CN 1239752C CN 03110817 CN03110817 CN 03110817 CN 03110817 A CN03110817 A CN 03110817A CN 1239752 C CN1239752 C CN 1239752C
Authority
CN
China
Prior art keywords
cobalt alloy
nickel
aqueous solution
electroformed nickel
add2
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 03110817
Other languages
English (en)
Other versions
CN1515703A (zh
Inventor
孙凤国
原天壮
顾君业
戚克新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Electromechanical Apptsplant machinery Manufacturing Co Angang Group
Original Assignee
Electromechanical Apptsplant machinery Manufacturing Co Angang Group
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Electromechanical Apptsplant machinery Manufacturing Co Angang Group filed Critical Electromechanical Apptsplant machinery Manufacturing Co Angang Group
Priority to CN 03110817 priority Critical patent/CN1239752C/zh
Publication of CN1515703A publication Critical patent/CN1515703A/zh
Application granted granted Critical
Publication of CN1239752C publication Critical patent/CN1239752C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及电铸镍钴合金的方法，属于电铸领域。其电镀液的较佳配比为：硫酸镍为220g/l、氯化镍为15g/l、硫酸钴为45g/l、氯化钠为1g/l、硼酸为30g/l、十二烷基硫酸钠为0.4g/l。利用本发明电铸的连铸机结晶器铜板，镍钴合金镀层厚度可达2.0～3.0mm，镀层厚、硬度高耐磨损耐冲击；镀层与基体结合力强，结合牢固镀层不剥落；内应力小可减少和消除镀层裂纹；因而结晶器铜板使用寿命长，可拉钢坯达9万多米(过钢量约达25万吨)。

Description

电铸镍钴合金的方法
技术领域
本发明涉及铜板等有色金属电铸镍钴合金层的方法，属于电铸领域。
背景技术
结晶器铜板作为连铸机的关键部件，作业条件很差，在高温钢水与冷却水的同时作用下，承受高温氧化、热疲劳、化学腐蚀、高温气蚀，拉坯引锭和结晶器振动产生的摩擦、磨损、划伤等不利条件。连铸机的结晶器铜板目前普遍存在镀层应力大，易出现裂纹，镀层与板基结合力差，镀层易脱落，镀层薄不耐磨，使用寿命短，这些弊病至今没有彻底解决。
发明内容
本发明的目的就是提供一种电镀镍钴合金的方法，用这种方法生产的连铸机的结晶器铜板能耐磨、镀层不剥落、镀层无裂纹、寿命长。
本发明是在下述电镀液组成及配与工艺条件下实现的：经过电镀前除油、除锈处理的铜板或待镀的其它有色金属板基放入镀槽中，进行电铸镍钴合金层：
A：电镀液的组成及配比为：
NiSO4*7H2O                        180～220g/l，
NiCl2*6H2O                        10～15g/l，
CoSO4*7H2O                        15～45g/l，
NaCl                                 0.2～1g/l，
H3BO3                             30～40g/l，
C12H25SO4Na                       0.3～0.5g/l，
ADD1即糖精及葡萄糖的水溶液           5～20ml/l，
ADD2即甲酸钠及柠檬酸的水溶液         5～15ml/l，
ADD1是糖精10％及葡萄糖5％的水溶液，ADD2是甲酸钠5％及柠檬酸
2％的水溶液；
B、工艺条件为：PH值＝2.4～4.0，电流密度＝1.5～5A/dm2
               温度＝55～60℃  S阴∶S阳＝1∶1～1∶4，
               搅拌方式：机械搅拌或气体搅拌。
由于该工艺的镀层达2～3mm，镀层的应力增大，ADD1可降低镀层内应力，可消除或减少镀层产生裂纹；ADD2添加剂具有良好的整平作用，细化颗粒，提高阴极极化能力的作用。通过调节镀液中的硫酸钴的含量，控制合金镀层中的含钴量。
本发明在连铸机结晶器铜板上电铸镍钴合金复合层具有以下优点和效果：
1、由于待镀铜板在电镀前进行了除油、除锈等前处理，使镍钴合金镀层与基体结合力强。
2、由于添加剂ADD1降低了镀层的内应力，ADD2增大了镀层的整平作用，减少边缘效应，有效利用镀层，降低了成本。
3、由于镍与钴同属一族且原子直径相近，钴与镍之间在电沉积过程中，原子间相互置换，原子键变化小内应力小，可消除或减少镀层出现裂纹。
4、由于铜板在高温下作业，镀层表面形成氧化钴膜，该膜在高温状态下硬度高耐磨。
5、由于镀层可达2～3mm，从而保证了结晶器铜板在连铸拉坯的条件下，尽管受到冲击和摩擦，也具备足够的强度和耐磨性，使用寿命长。
6、可根据需要，可电铸不同厚度的镀层，也可以在多种有色金属基体上进行电铸和覆镀。
具体实施方式
实施例1，
经过电镀前除油、除锈处理的铜板放在镀槽中，电铸镍钴合金层，
电镀液的组成及较佳配比为：
NiSO4*7H2O                          180g/l，
NiCl2*6H2O                          10g/l，
CoSO4*7H2O                          15g/l，
NaCl                                   1g/l，
H3BO3                               30g/l，
C12H25SO4Na                         0.3g/l，
ADD1即糖精及葡萄糖的水溶液             6ml/l，
ADD2即甲酸钠及柠檬酸的水溶液           10ml/l，
工艺条件为：PH值＝2.5，电流密度＝2.5A/dm2  温度55℃
S阴∶S阳＝1∶2，搅拌方式：往返式阴极移动，机械搅拌。
实施例2，将经过电镀前除油、除锈处理的铜板放在镀槽中，电铸镍钴合金层，电镀液的组成及较佳配比为：
NiSO4*7H2O                          220g/l，
NiCl2*6H2O                          15g/l，
CoSO4*7H2O                          45g/l，
NaCl                                   1g/l，
H3BO3                               30g/l，
C12H25SO4Na                         0.4g/l，
ADD1即糖精及葡萄糖的水溶液             8ml/l，
ADD2即甲酸钠及柠檬酸的水溶液           15ml/l，
工艺条件为：PH值＝3，电流密度＝4A/dm2  温度60℃
S阴∶S阳＝1∶3，搅拌方式：机械搅拌或气体搅拌。

Claims (3)

1、一种电铸镍钴合金的方法，其特征在于将经过电镀前除油、除锈处理的铜板或待镀的其它有色金属板基放入镀槽中，进行电铸镍钴合金层：
A：电镀液的组成及配比为：
NiSO4*7H2O                            180～220g/l，
NiCl2*6H2O                            10～15g/l，
CoSO4*7H2O                            15～45g/l，
NaCl                                     0.2～1g/l，
H3BO3                                 30～40g/l，
C12H25SO4Na                          0.3～0.5g/l，
ADD1即糖精及葡萄糖的水溶液               5～20ml/l，
ADD2即甲酸钠及柠檬酸的水溶液             5～15ml/l，
ADD1是糖精10％及葡萄糖5％的水溶液，ADD2是甲酸钠5％及柠檬酸
2％的水溶液，
B、工艺条件为：PH值＝2.4～4.0，    电流密度＝1.5～5A/dm2
               温度＝55～60℃      S阴∶S阳＝1∶1～1∶4，
               搅拌方式：机械搅拌或气体搅拌。
2、根据权利要求1所述的电铸镍钴合金的方法，其特征在于将经过电镀前除油、除锈处理的铜板放入镀槽中，进行电铸镍钴合金层，它的组成及较佳配比为：
NiSO4*7H2O                               220g/l，
NiCl2*6H2O                               15g/l，
CoSO4*7H2O                               45g/l，
NaCl                                       1g/l，
H3BO3                                    30g/l，
C12H25SO4Na                             0.4g/l，
ADD1即糖精及葡萄糖的水溶液                 8ml/l，
ADD2即甲酸钠及柠檬酸的水溶液           15ml/l，
工艺条件为：PH值＝3，电流密度＝4A/dm2温度＝60℃
S阴∶S阳＝1∶3，搅拌方式：机械搅拌或气体搅拌。
3、根据权利要求1所述的电铸镍钴合金的方法，其特征在于将经过电镀前除油、除锈处理的铜板放入镀槽中，进行电铸镍钴合金层，它的组成及较佳配比为：
NiSO4*7H2O                             180g/l，
NiCl2*6H2O                             10g/l，
CoSO4*7H2O                             15g/l，
NaCl                                     1g/l，
H3BO3                                  30g/l，
C12H25SO4Na                           0.3g/l，
ADD1即糖精及葡萄糖的水溶液                6ml/l，
ADD2即甲酸钠及柠檬酸的水溶液              10ml/l，
工艺条件为：PH值＝2.5，电流密度＝2.5A/dm2温度55℃
S阴∶S阳＝1∶2，搅拌方式：往返式阴极移动，机械搅拌。
CN 03110817 2003-01-08 2003-01-08 电铸镍钴合金的方法 Expired - Fee Related CN1239752C (zh)